On the compressive failure of fiber reinforced composites

https://doi.org/10.1016/0020-7683(94)00157-RGet rights and content

Abstract

In this paper a combination of experimentation and analysis is used to identify and study the mechanisms that govern the failure of unidirectional fiber composites under compression. The experimental part includes experiments in which the compressive strength and the prevalent failure mechanisms of AS4/PEEK composite are established, tests for establishing the constitutive properties of the composite and its constituents, and an evaluation of the extent of misalignment of fibers in manufactured composites. The failure load of the composite was confirmed to be affected by geometric imperfections in the form of fiber waviness, and failure was found to lead to kink bands with distinct orientations and widths.

Motivated by the experimental findings, the composite was idealized as a two-dimensional solid with alternating fiber and matrix layers, each having the measured properties of the two constituents. The compressive responses of microsections of finite width with imperfections of various spatial distributions were established numerically. The calculated responses are characterized by an initially stiff, stable regime terminated by a limit load instability which is associated with the strength of the composite. Following the limit load, the deformation localized into inclined bands with distinct widths. It has been verified that, as the localization process progresses, the fiber bending stresses at the ends of these bands grow to values comparable to those of the fiber strength. The sensitivity of the calculated response to the geometric characteristics of the imperfections was studied parametrically.

References (58)

  • C.T. Sun et al.

    A simple flow rule for characterizing nonlinear behavior of fiber composites

    J. Compos. Mater.

    (1989)
  • A.M. Waas et al.

    A mechanical model for elastic fiber microbuckling

    ASME J. Appl. Mech.

    (1990)
  • S.W. Yurgartis et al.

    A micrographic study of bending failure in five thermoplastic carbon fibre composite laminates

    J. Mater. Sci.

    (1988)
  • M. Arcan et al.

    A method to produce uniform plane stress states with applications to fiber-reinforced materials

    Expl Mech.

    (1978)
  • R. Arseculeratne

    The compressive failure of aligned fiber composite materials

  • I.Y. Babich et al.

    Stability of fibrous composites

    Appl. Mech. Rev.

    (1992)
  • E.T. Camponeschi

    Compression of composite materials: a review

  • C.R. Chaplin

    Compressive fracture in unidirectional glass-reinforced plastics

    J. Mater. Sci.

    (1977)
  • S.N. Chatterjee et al.

    Inelastic shear instability in composite materials under compression

  • A.S. Crasto et al.

    Nonlinear stress-strain behavior in advanced fibers and composites

  • J.-B. Donnet et al.

    Carbon Fibers

    (1990)
  • J.F. Dow et al.

    Determination of most needed, potentially possible improvements in materials for ballistic and space vehicles

  • P.D. Ewins et al.

    Some observations on the nature of fibre reinforced plastics and the implications for structural design

    Phil. Trans. R. Soc. London

    (1980)
  • N.A. Fleck et al.

    Prediction of kink width in fiber composites

  • H.J. Garala

    Experimental evaluation of graphite-epoxy composite cylinders subjected to external hydrostatic compressive loading

  • G. Geymonat et al.

    Homogenization of nonlinearly elastic materials: microscopic bifurcation and macroscopic loss of rank-one convexity

    Arch. Rational Mech. Anal.

    (1993)
  • L.B. Greszczuk

    Microbuckling failure of circular fiber-reinforced composites

    AIAA J.

    (1975)
  • E.G. Guynn et al.

    A parametric study of variables that affect fiber microbuckling initiation in composite laminates Part 1—Analyses. Part 2—Experiments

    J. Compos. Mater.

    (1992)
  • H.T. Hahn et al.

    Compression failure mechanisms in unidirectional composites

    H.T. Hahn et al.
  • Cited by (0)

    View full text