Review
Oxide-free hybrid silicon nanowires: From fundamentals to applied nanotechnology

https://doi.org/10.1016/j.progsurf.2012.12.001Get rights and content

Abstract

The ability to control physical properties of silicon nanowires (Si NWs) by designing their surface bonds is important for their applicability in devices in the areas of nano-electronics, nano-photonics, including photovoltaics and sensing. In principle a wealth of different molecules can be attached to the bare Si NW surface atoms to create e.g. Si–O, Si–C, Si–N, etc. to mention just the most prominent ones. Si–O bond formation, i.e. oxidation usually takes place automatically as soon as Si NWs are exposed to ambient conditions and this is undesired is since a defective oxide layer (i.e. native silicon dioxide – SiO2) can cause uncontrolled trap states in the band gap of silicon. Surface functionalization of Si NW surfaces with the aim to avoid oxidation can be carried out by permitting e.g. Si–C bond formation when alkyl chains are covalently attached to the Si NW surfaces by employing a versatile two-step chlorination/alkylation process that does not affect the original length and diameter of the NWs. Termination of Si NWs with alkyl molecules through covalent Si–C bonds can provide long term stability against oxidation of the Si NW surfaces. The alkyl chain length determines the molecular coverage of Si NW surfaces and thus the surface energy and next to simple Si–C bonds even bond types such as Cdouble bondC and Ctriple bondC can be realized. When integrating differently functionalized Si NWs in functional devices such as field effect transistors (FETs) and solar cells, the physical properties of the resultant devices vary.

Highlights

► We show how to fabricate SiNWs by Bottom-up and top-down technique. ► We show a simple approach to terminate the SiNW with organic molecules by employing a versatile two-step chlorination/alkylation process. ► The stability of the hybrid surface depends on the type of the molecules and coverage. ► Hybrid surface decrease the surface states density and tune the electrical properties of the SiNW. ► Hybrid Solar cells show an increased open-circuit voltage (Voc), an increased short-circuit current (Jsc) and a higher fill factor (FF).

Introduction

Much effort has been devoted to developing new nanomaterial-based technological devices with significant performance improvements at a reduced cost [1], [2], [3], [4]. In this quest, a substantial number of nanomaterials have been developed, including but not limited to nanoparticles [5], [6], [7], [8], [9], [10], [11], [12], [13], [14], nanorods [15], [16], [17], [18], and nanowires [18], [19], [20], [21], [22], [23], [24], [25]. Nanowires provide additional advantages compared to the other nanostructures in terms of their strong light absorbance, efficient charge separation and direct charge transport path. This makes them a promising candidate for many technological applications. In short, nanowires are important one-dimensional nanostructures that have demonstrated advantageous characteristics for applications in electronics [26], [27], [28], photovoltaics [29] and sensing [30], [31], [32], [33].

Up till now, nanowires of many different inorganic materials have been synthesized and characterized, including silicon [34], gallium nitride [35] and lead selenide [18], [36] among others. The use of silicon nanowires (Si NWs) in particular to further miniaturize devices while avoiding major process changes and their corresponding costs has been a topic of much research in the past decade. Thus, Si NWs are generally considered to be an essential class of nanodevice building blocks [37], [38], [39]. Si NWs have shown significant potential for field effect transistors (FETs). Potential applications of Si NWs in FETs includes aligning on insulating substrate surface, selective deposition of the source and drain contacts on the Si NW edges, and the configuration of either a bottom or top gate electrode [26], [40]. Another significant potential application of Si NWs is solar power generation. The indirect optical band gap of 1.12 eV, low absorption co-efficient of 104/cm and high wafer cost of bulk Si reduces the suitability of this material for photovoltaic and optoelectronic devices. Differently engineered band gaps (1.4 eV) and a high absorption co-efficient (at least 105/cm) are required to significantly improve the solar cell efficiency. Si NWs are promising alternatives to bulk Si for use in solar cell applications due to their high light harvest; convenient band gap tuneability from 1.1 to 1.4 eV, which is achievable through decreases in the diameter [41]; and the possibility of fabricating the structures with a axial and lateral junction to decrease the charge bath separation [25], [42], [43], [44].

Surface treatment is one of the main obstacles to Si NW application. A large body of chemistry has been developed for chemically linking moieties to oxidized Si NW surfaces, generally through –OH chemistry. Many pertinent applications have been illustrated [28], [45], [46], [47], [48]. Although Si NWs offer unique opportunities as building blocks for nanoelectronic devices, the presence of native oxide (SiOx), which instantly forms on the Si NW surfaces upon air exposure, is undesirable [49], [50]. This is because of the poor quality of the oxide that forms on the surface, which induces a large number of unwanted and uncontrolled interfacial states in the Si band gap [50], [51]. The low quality, highly impure oxides that form in ambient conditions have a tendency to cause uncontrolled oxide/silicon interfaces and surface states. This necessitates the protection of Si NW surfaces against oxidation. Moreover, due to the larger surface to volume ratio, surface properties become more significant in smaller Si NWs and dominate the properties of the device as a whole [26]. Therefore, it is necessary to explore models and methods to predict and control the surface physical characteristics of oxide-free Si NW.

Etched Si NWs with surface-bound hydrogen atoms, the simplest termination group, show low charge carrier surface recombination velocities [41], [52]. However, these surfaces tend to oxidize within a few minutes of exposure to ambient air, leading to higher surface recombination velocities [40]. Therefore, it is of considerable interest to develop a sound strategy to prevent extensive Si NW surface oxidation while preserving the low surface recombination velocities. A promising method for controlling the surface properties of Si is termination through the use of organic molecules (polar and non-polar) which form Si–C surface bonds. Functionalization by Si–C bonds causes the stability time to increase to a few hundred hours at room temperature [53], [54], [55]. Therefore, termination of the dangling surface bonds with chemical and biochemical moieties [39], [56], [57], [58] can affect the device reliability over time. This is expected to have extreme significance on the final physical and chemical properties of the Si NWs. Generally speaking; the functionalization of organic molecules introduces a net electrical dipole perpendicular to the surface/interface. The dipole, in turn, modifies the work function and electron affinity, alters the band offset and band bending, and tunes the surface Fermi level [26]. Moreover, many future devices will require their building blocks to be selectively sensitive to the environment. Indeed, the main objectives of molecular functionalization can be outlined as follows: (1) to increase the oxidation resistance of Si NWs; (2) to allow a systematic tuning of the desired physical properties of an electric device by appropriate choice of the functional groups [59], [60]; (3) to exhibit selectivity to different environmental species, depending on the type of molecules and their coverage [61]. In order to achieve the above objectives, several techniques that induce a high density of organic molecules attachments to the silicon surface have been suggested. Here we will describe one of these techniques while showing the disadvantages of the others. The most widely reported organic monolayers on the oxide-free Si surface are alkyl chains. As a starting step, the oxide is removed and surfaces are covered with either hydrogen or halogens. The H-terminated monolayer can be converted to alkyl monolayers through the use of alkyl-magnesium reagents [31], [53], [54], [55], [62], [63], [64] while the halogenated surfaces can be alkylated using alkyl-magnesium or alkyl-lithium reagents [65]. Alkylation has been successfully carried out on two dimensional surfaces through free radical initiation methods such as irradiation with ultraviolet light [66], [67], chemical free-radical activation [68], thermal activation [69], Lewis acid catalyzed hydrosilylation [70], [71], and visible-light-initiated modification [72]. However, these methods have as yet not been applied on Si NW. Unless extreme measures are taken, these reactions may result in an incomplete coverage of the organic monolayer (i.e. less than one monolayer of coverage) as well as significant amounts of oxygen on the surface [73], [74]. Alternative reactions such as terpyridine termination have been directly demonstrated on hydrogenated Si NW [75]. However, these reactions are limited to terpyridine and cover the surface only partially. The current review describes strategies used to prepare organic monolayers on Si NWs, which achieve both electrical and chemical passivation, and allow for the introduction of productive oxide free components into practical nanodevices. A detailed report on scientific progress in the production and characterization of oxide-free high-density organic monolayers (single and multiple) on Si NW, through a two-step process involving chlorination/alkylation is described in Section 2. The kinetics of the alkylation process and the effect of organic chain length as well as second monolayer functionalization are also discussed. The stability of the hydrogen and organic molecules on the Si NW and the effect of molecular coverage and bonding type are demonstrated. Section 3 presents two examples of functional devices based on hybrid Si NWs: Field Effect Transistors (FETs) and solar cells. The electrical characteristics of molecularly-modified Si NW-based devices are presented, analyzed and compared to pristine Si NWs. Fig. 1 schematically illustrates the organization of the current review.

Section snippets

Fabrication of Si NWs

The fabrication of Si NWs with a controlled diameter, length, and electronic properties is essential to technical application [76], [77], [78]. Significant progress has been made in recent years in the development of superficially controlled methods of Si NW fabrication [79]. There are two general Si NW fabrication approaches: bottom-up and top-down.

The bottom-up approach is an assembly process joining Si atoms to form Si NWs and includes the vapor–liquid solid (VLS) growth technique [80]. The

Hybrid Si NW electronic properties and devices

Systematic alteration of the Si NW physical surface properties via the formation of hybrid surfaces permits diverse custom-tailoring possibilities for optimization for application in a variety of functional devices. Molecular functionalization can be used to modify the surface properties of Si NWs, which affect performance of the Si NW-based devices such as the surface dipole, surface Fermi level, surface band bending, concentration of surface states, etc. In this section, two different

Concluding remarks

In the current review, the fundamental physical surface properties and applications of hybrid systems composed of Si NWs functionalized by different organic and inorganic molecules were discussed. A two-step chlorination/alkylation process has been applied to connect organic molecular (C–C, Cdouble bondC and Ctriple bondC) functionalities with Si NWs. Among the alkyl functionalities, methyl provided the highest coverage. Increasing the chain length from methyl to pentyl decreased the coverage to 50–70%. However,

Acknowledgments

M.Y.B gratefully acknowledges the LCAOS and Max-Planck Society for the Post-Doctoral fellowship. K.S wishes to thank University of Erlangen-Nürnberg and the Elite Advanced Materials and Processes (MAP) graduate program for the MS thesis scholarship. S.H.C. and H.H. acknowledge the financial support by the FP7 EU project LCAOS (nr. 258868, HEALTH priority). P. M and S.C acknowledge the NAWION project funded by German Ministry of research and education (BMBF). Ms. Heidemarie Embrechts’s help with

References (121)

  • M. Sirota et al.

    IV-NI semiconductor nanocrystals for passive Q-switching of eye-safe laser

    P. Soc. Photo-Opt. Ins.

    (2003)
  • I. Gur et al.

    Air-stable all-inorganic nanocrystal solar cells processed from solution

    Science

    (2005)
  • O.I. Micic et al.

    Core-shell quantum dots of lattice-matched ZnCdSe2 shells on InP cores: experiment and theory

    J. Phys. Chem. B

    (2000)
  • S.A. McDonald et al.

    Solution-processed PbS quantum dot infrared photodetectors and photovoltaics

    Nat. Mater.

    (2005)
  • V.I. Klimov

    Detailed-balance power conversion limits of nanocrystal-quantum-dot solar cells in the presence of carrier multiplication

    Appl. Phys. Lett.

    (2006)
  • T. Saraidarov et al.

    Synthesis, structural and electrical characterization of PbSNCs in titania sol–gel films

    J. Sol–Gel Sci. Technol.

    (2007)
  • M. Bashouti et al.

    PbS sub-micrometer structures with anisotropic shape: ribbons, wires, octapods, and hollowed cubes

    Inorg. Chem.

    (2008)
  • W.U. Huynh et al.

    Hybrid nanorod-polymer solar cells

    Science

    (2002)
  • L.E. Greene et al.

    ZnO–TiO2 core–shell nanorod/P3HT solar cells

    J. Phys. Chem. C

    (2007)
  • B.M. Kayes et al.

    Comparison of the device physics principles of planar and radial p–n junction nanorod solar cells

    J. Appl. Phys.

    (2005)
  • E. Lifshitz et al.

    Synthesis and characterization of PbSe quantum wires, multipods, quantum rods, and cubes

    Nano Lett.

    (2003)
  • O.L. Muskens et al.

    Design of light scattering in nanowire materials for photovoltaic applications

    Nano Lett.

    (2008)
  • K.S. Leschkies et al.

    Photosensitization of ZnO nanowires with CdSe quantum dots for photovoltaic devices

    Nano Lett.

    (2007)
  • H. Xin et al.

    Polymer nanowire/fullerene bulk heterojunction solar cells: how nanostructure determines photovoltaic properties

    ACS Nano

    (2010)
  • C. Colombo et al.

    Gallium arsenide p–i–n radial structures for photovoltaic applications

    Appl. Phys. Lett.

    (2009)
  • L.Y. Cao et al.

    Semiconductor nanowire optical antenna solar absorbers

    Nano Lett.

    (2010)
  • A. Kandala et al.

    General theoretical considerations on nanowire solar cell designs

    Phys. Status Solidi A

    (2009)
  • B.Z. Tian et al.

    Coaxial silicon nanowires as solar cells and nanoelectronic power sources

    Nature

    (2007)
  • M.Y. Bashouti et al.

    Tuning the electrical properties of Si nanowire field-effect transistors by molecular engineering

    Small

    (2009)
  • S. Hoffmann et al.

    Axial p–n junctions realized in silicon nanowires by ion implantation

    Nano Lett.

    (2009)
  • Y. Cui et al.

    Functional nanoscale electronic devices assembled using silicon nanowire building blocks

    Science

    (2001)
  • V. Sivakov et al.

    Silicon nanowire-based solar cells on glass: synthesis, optical properties, and cell parameters

    Nano Lett.

    (2009)
  • Y. Paska et al.

    Interactive effect of hysteresis and surface chemistry on gated silicon nanowire gas sensors

    ACS Appl. Mater. Inter.

    (2012)
  • Y. Paska et al.

    Molecular gating of silicon nanowire field-effect transistors with nonpolar analytes

    ACS Nano

    (2012)
  • Y. Paska et al.

    Enhanced sensing of nonpolar volatile organic compounds by silicon nanowire field effect transistors

    ACS Nano

    (2011)
  • C. Tessarek et al.

    Self-catalyzed, vertically aligned GaN rod-structures by metal-organic vapor phase epitaxy

    Phys. Status Solidi C

    (2012)
  • A. Sashchiuk et al.

    PbSe nanocrystal assemblies: synthesis and structural, optical, and electrical characterization

    Nano Lett.

    (2004)
  • Y. Cui et al.

    High performance silicon nanowire field effect transistors

    Nano Lett.

    (2003)
  • K.Q. Peng et al.

    Silicon nanowires for rechargeable lithium-ion battery anodes

    Appl. Phys. Lett.

    (2008)
  • G.F. Zheng et al.

    Multiplexed electrical detection of cancer markers with nanowire sensor arrays

    Nat. Biotechnol.

    (2005)
  • H. Haick et al.

    Electrical characteristics and chemical stability of non-oxidized, methyl-terminated silicon nanowires

    J. Am. Chem. Soc.

    (2006)
  • D.D.D. Ma et al.

    Small-diameter silicon nanowire surfaces

    Science

    (2003)
  • E.C. Garnett et al.

    Silicon nanowire hybrid photovoltaics

    IEEE Phot. Spec. Conf.

    (2010)
  • M.C. Putnam et al.

    Si microwire-array solar cells

    Energ. Environ. Sci.

    (2010)
  • Y.J. Dong et al.

    Coaxial group III-nitride nanowire photovoltaics

    Nano Lett.

    (2009)
  • Y. Cui et al.

    Nanowire nanosensors for highly sensitive and selective detection of biological and chemical species

    Science

    (2001)
  • M.D. Kelzenberg et al.

    Photovoltaic measurements in single-nanowire silicon solar cells

    Nano Lett.

    (2008)
  • Y. Paska et al.

    Controlling surface energetics of silicon by intermolecular interactions between parallel self-assembled molecular dipoles

    J. Phys. Chem. C

    (2009)
  • Y. Paska et al.

    Systematic cross-linking changes within a self-assembled monolayer in a nanogap junction: a tool for investigating the intermolecular electronic coupling

    J. Am. Chem. Soc.

    (2010)
  • H. Haick et al.

    Effect of molecular binding to a semiconductor on metal/molecule/semiconductor junction behavior

    J. Phys. Chem. B

    (2005)
  • Cited by (46)

    • Semiconducting silicon nanowires and nanowire composites for biosensing and therapy

      2021, Semiconducting Silicon Nanowires for Biomedical Applications
    • Design and fabrication of silicon nanowires towards efficient solar cells

      2016, Nano Today
      Citation Excerpt :

      Exposure to ambient air induces unwanted and uncontrolled interfacial states in the Si band gap [235]. Therefore, it is essential to explore models and methods to predict and control the surface physical characteristics of oxide-free SiNW when considering surface recombination [236]. Fortunately, the surface defects can be conquered by inorganic and organic surface bonds, such as Al2O3 [56,237,238], a-Si [239,240], SiNx [241–243], thermal SiO2 [235,241,244], in-situ chlorine [239,245–247], and UV ozone [248], etc.

    • Adsorption of heterobifunctional 4-nitrophenol on the Ge(100)-2 × 1 surface

      2016, Surface Science
      Citation Excerpt :

      Organic functionalization is of interest as a technique to control the interfacial properties of semiconductor surfaces [1–5].

    • Solution p-doped fluorescent polymers for enhanced charge transport of hybrid organic-silicon nanowire photovoltaics

      2016, Organic Electronics
      Citation Excerpt :

      The sample under test then received in-situ spectroscopy analysis after each sputtering treatment without breaking the vacuum. Previous reports of interfacial engineering techniques for hybrid organic-silicon solar cells primarily focus on modifying the organic wettability, energy band alignment, and/or surface passivation in order to achieve high short-circuit current (Jsc) and Voc [8,17–24]. In this work, the carrier conduction across the heterojunction interface is improved by introducing a p-doped organic interlayer, while maintaining a preferable energy band alignment at the interface.

    • Surface physics of semiconducting nanowires

      2016, Progress in Surface Science
    View all citing articles on Scopus
    View full text