Abstract
B2O3 is selected as fluxing agent of CaO-based ladle refining slag to decrease the melting temperature as well as to improve the speed of slag forming and the refining efficiency. The effects of B2O3 on the melting temperature of two series of refining slags including the low basicity slags (the mass ratio of CaO/SiO2 is 3–4) and the high basicity slags (the mass ratio of CaO/SiO2 is 5–8.75) were investigated. The slag melting temperature was measured using the hemisphere method. The results indicate that the fluxing action of B2O3 is better than that of CaF2 and Al2O3. For the CaO-based refining slag with low basicity, the melting temperature is decreased effectively when B2O3 is used to substitute for equal mass of CaF2, Al2O3 and SiO2, respectively. For the CaO-based refining slag with high basicity, when CaF2 is substituted by B2O3, the melting temperature can be decreased remarkably. Especially, when the mass ratios of CaO/Al2O3 and CaO/SiO2 are in the range of 1.1–4.0 and 5.25–8.0, respectively, the slag melting temperature is lower than 1300 °C. Therefore, the B2O3-containing refining slags with high ratios of CaO/Al2O3 and CaO/SiO2 have ultra low melting temperature.
Similar content being viewed by others
References
Zhang L, Zhi J, Mei F, et al. Basic Oxygen Furnace Based Steelmaking Processes and Cleanliness Control at Baosteel [J]. Ironmaking and Steelmaking, 2006, 33(2): 129.
WANG Hong-ming, LI Gui-rong, DAI Qi-xun, et al. Effect of Additives on Viscosity of LATS Refining Ladle Slag [J]. ISIJ Int, 2006, 46(5): 637.
Kang Y J, Yu L, Du S C. Study of Inclusion Removal Mechanism around Open Eye in Ladle Treatment [J]. Ironmaking and Steelmaking, 2007, 34(3): 253.
Andersson E, Du S C. The Effect of CaF2 in the Slag in Ladle Refining [J]. Steel Research International, 2009, 80(8): 544.
LI Gui-rong, WANG Hong-ming, DAI Qi-xun, et al. Physical Properties and Regulating Mechanism of Fluoride-Free and Harmless B2O3-Containing Mould Flux [J]. Journal of Iron and Steel Research, International, 2007, 14(1): 25.
Hideaki S, Ryo I. Dissolution Behavior and Stabilization of Fluorine in Secondary Refining Slag [J]. ISIJ Int, 2002, 42 (8): 921.
Wang Hong-ming, Li Gui-rong, Dai Qi-xun, et al. CAS-OB Refining: Slag Modification With B2O3-CaO and CaF2-CaO [J]. Ironmaking and Steelmaking, 2007, 34(4): 350.
Shahbazian F, Du S C, Seetharaman S. The Effect of Addition of Al2O3 on the Viscosity of CaO- “FeO” -SiO2-CaF2 Slag [J]. ISIJ Int, 2002, 42(2): 155.
WANG Hong-ming, LI Gui-rong, DING Zhen-tao, et al. Effect of Additives on Melting Point of LATS Refining Ladle Slag [J]. Journal of Iron and Steel Research, 2007, 14(2): 25.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National High Technology Research and Development Program (863 Program) of China (2007AA03Z548); Natural Science Foundation of Jiangsu Province of China (BK2010355)
Rights and permissions
About this article
Cite this article
Wang, Hm., Li, Gr., Li, B. et al. Effect of B2O3 on Melting Temperature of Cao-Based Ladle Refining Slag. J. Iron Steel Res. Int. 17, 18–22 (2010). https://doi.org/10.1016/S1006-706X(10)60177-X
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(10)60177-X