Reaction mechanism in carbon-liquid silicon systems at elevated temperatures
Abstract
The mechanism of reactions which occur in the carbon-liquid silicon system at elevated temperatures is far from being understood although the reactions are utilised for producing manu interesting SiC materials. In the present paper the formation of fibrous β-SiC in this system, which occurs with the SILCOMP SiC/Si material, has been investigated by observing the evolution of the microstructure at successive stages of the reaction and by measuring the thermal effects accompanying the reaction. A model has been developed which permits a rational explanation of the main features of the reaction rate and of the microstructure of the products formed at the first and intermediate stages of the reaction; the microstructure is of a decisive importance for the formation of fibrous β-SiC in the final product. An explanation is given for: (1) the preferential formation of small β-SiC crystals disseminated at random in the Si matrix in localised zones which were previously occupied by the carbon fibres; (2) the high rate of reaction in spite of the low solubility of carbon in silicon at the temperatures, attained by external heating, which are usually used to produce SILCOMP (1680–1880 K). Because analogous reactions occur in the production of SILCOMP, REFEL SiC and other similar materials, the model developed may have a wider range of applications.
References (18)
- W. Forest et al.
- G.R. Sawyer et al.
J. Mat. Sci.
(1978) - G.G. Gnesin et al.
J. Poroshk. Metall.
(1973) - W.B. Hillig et al.
Am. Ceram. Soc. Bull.
(1975) - R.L. Mehan et al.
J. Mat. Sci.
(1976) - G.G. Trantina et al.
J. Am. Ceram. Soc.
(1977) - R.L. Mehan
J. Mat. Sci.
(1978) - R. Pampuch et al.
- R. Pampuch et al.
Cited by (113)
Additive manufacturing of high-performance CCF/SiC composites under dual protection
2024, Ceramics InternationalIn this work, chopped carbon fibre reinforced silicon carbide (CCF/SiC) composites were fabricated by selective laser sintering (SLS) combined with reaction melt infiltration (RMI), using the SiC interface and pyrolytic carbon layer as a dual protection to protect the CCF from the erosion of molten silicon. The pyrolytic carbon layer encapsulates the CCF@SiC and the outer carbon preferentially reacts with silicon to form a β-SiC layer, which hinders the reaction of liquid silicon to CCF. Moreover, the fine-crystal β-SiC generated by the Si–C reaction optimizes the microstructure and enhances the mechanical performance of CCF/SiC composites. The CCF under the dual protection maintains its original high strength and high modulus, and the toughness of the CCF/SiC composites is significantly improved through the fibre debonding and fibre pull-out mechanism. The bending strength and toughness of CCF/SiC composites are 265.2 MPa and 3.5 MPa m1/2, respectively. The insights gained from this study contribute to a better understanding of microstructural engineering in SLS&RMI-fabricated CCF/SiC composites. This paves the way for future breakthroughs in composite material design and low-cost manufacturing for extreme environments.
Modifying C/C–SiC brake pads with different Fe–Si alloy phases to improve the wear resistance of full-carbon/ceramic brake pair
2024, Ceramics InternationalThe full-carbon/ceramic brake pair is designed to meet the increased demands for reliable braking at high speeds, heavy loads and complex service environments for vehicle and power machinery. In this paper, braking performance of different Fe–Si modified C/C–SiC composites have been studied using laboratory scale dynamometer. The phase composition/microstructure and mechanical properties of the material were studied. By mating with C/C–SiC brake disc, the effect of Fe–Si alloy modification on the friction and wear performance of full carbon/ceramic brake pair was investigated. The results indicated that the Fe–Si modification can effectively improve the wear resistance of both C/C–SiC disc and pads, and the disc/pads will have the least amount of wear only when the appropriate type of Fe–Si alloy and the suitable amount of Fe–Si alloy phase are introduced. When FeSi75 was used as the fusion infiltration material, the wear of disc/pad was 115.4 and 13.3 mm, respectively. Compared to the unmodified C/C–SiC disc/pad, the wear of Fe–Si modification disc/pad was reduced by 72.7 % and 87.2 %, respectively.
The corrosion behavior of various CVD SiC coatings in molten silicon
2024, Ceramics InternationalCorrosion by molten silicon of different SiC CVD coatings has been investigated at 1450 °C and 1550 °C by analyzing the deteriorated zone with electron microscopies. The influence of the microstructure on the corrosion mode is finely considered. The most resistant material consists of wide and aligned <111> oriented columns, perpendicular to the substrate, corresponding to an arrangement of dense {111} planes parallel to the surface in contact with the molten silicon. Structural disorder (grain boundaries, structural defects) and disorientations (growth direction other than <111>, secondary growth, column misalignment) make the CVD SiC coating more vulnerable to corrosion.
High strength and high toughness C<inf>sf</inf>/SiC composites prepared by laser powder bed fusion/ reactive melt infiltration with the impregnation of boron-and silicone-containing phenolic resin
2024, Ceramics InternationalLaser powder bed fusion (LPBF) has emerged as an effective method for preparing complex structured silicon carbide (SiC) ceramics. However, the SiC components demonstrate low strength and high brittleness, which remain major challenges limiting its application. To overcome this limitation, short carbon fiber reinforced silicon carbide (Csf/SiC) composites are prepared by combining LPBF and phenolic resin binder impregnation (PRBI)-reactive melt infiltration (RMI), in which high char yield boron-and silicone-containing phenolic resin (BSiPF) impregnation is used to adjust the carbon density of green bodies and to reduce the pore size of green bodies. By optimizing the impregnation process, the carbon density can be brought close to the theoretical optimal value of 0.84 g/cm3, and the reduction of the pore size is conducive to the improvement of the reaction rate at the early stage of the reaction, which enhance the SiC phase content of Csf/SiC composites obtained by RMI. Meanwhile, the application of BSiPF results in a protective pyrolytic carbon (PyC) coating on the surface of Csf, which can reduce the erosion of Csf by molten Si during the RMI process, thus improving the fracture toughness of Csf/SiC composites. The final Csf/SiC composites exhibit the enhanced bulk density, bending strength and fracture toughness, reaching 2.90 ± 0.01 g/cm3, 257 ± 20 MPa, 3.52 ± 0.15 MPa m1/2, respectively. This study provides a new strategy for effective impregnation technique for the additive manufacturing (AM) of high strength and high toughness SiC composites.
A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration
2024, Composites Part A: Applied Science and ManufacturingSiC/SiC composites, prepared by reactive melt infiltration (RMI), exhibit exceptional properties. However, the presence of residual Si in the composite matrix can significantly compromise their high-temperature mechanical properties. Addressing the issue of high-content residual Si aggregation remains a crucial focus of research in order to fully unlock the application potential of SiC/SiC composites prepared by RMI. In this work, a special porous carbon (Cg) is successfully synthesized and introduced into the porous 2D SiC/SiC composites prepared by CVI. The unique pore structure of the SiC/SiC-Cg is thoroughly analyzed, along with its liquid Si infiltration process. The difference in coefficient of thermal expansion (CTE) between SiC and Cg can cause thermal stress, which can destory the Cg structure. Consequently, the C particles detach from the Cg skeleton and react with liquid Si to create SiC. This process effectively separates residual Si and helps alleviate the negative effects of residual Si aggregation. The microstructure and phase distribution of SiC/SiC composites obtained by liquid Si infiltrating different C structures are investigated and compared, and it demonstrates the positive effect of Cg on the uniform phase distribution of matrix in the composites. The as-received SiC/SiC composites possess a density of 2.94 g/cm3 with open porosity of 1.23 %, and a flexural strength of 808.7 ± 10.2 MPa, a fracture toughness of 25.5 ± 1.8 MPa·m1/2, a tensile strength of 317.4 ± 12.4 MPa and a proportional ultimate stress of 157.33 ± 4.1 MPa. Acoustic emission (AE) and digital image correlation (DIC) technology are used to study the special mechanical behavior of composites.
Preparation of SiC/SiC composites with high toughness by reaction of the SiC<inf>P</inf>+C double-cladding layer with liquid silicon
2023, Journal of the European Ceramic SocietySiC/SiC composites prepared by liquid silicon infiltration (LSI) have the advantages of high densification, matrix cracking stress and ultimate tensile strength, but the toughness is usually insufficient. Relieving the residual microstress in fiber and interphase, dissipating crack propagation energy, and improving the crystallization degree of interphase can effectively increase the toughness of the composites. In this work, a special SiC particles and C (SiCP +C) double-cladding layer is designed and prepared via the infiltration of SiCP slurry and chemical vapor infiltration (CVI) of C in the porous SiC/SiC composites prepared by CVI. After LSI, the SiC generated by the reaction of C with molten Si combines with the SiCP to form a layered structure matrix, which can effectually relieve residual microstress in fiber and interphase and dissipate crack propagation energy. The crystallization degree of BN interphase is increased under the effects of C-Si reaction exotherm. The as-received SiC/SiC composites possess a density of 2.64 g/cm3 and a porosity of 6.1%. The flexural strength of the SiC/SiC composites with layered structure matrix and highly crystalline BN interphase is 577 MPa, and the fracture toughness reaches up to 37 MPa·m1/2. The microstructure and properties of four groups of SiC/SiC composites prepared by different processes are also investigated and compared to demonstrate the effectiveness of the SiCP +C double-cladding layer design, which offers a strategy for developing the SiC/SiC composites with high performance.