The role of humidity in the photooxidation of acrylic melamine coatings

doi:10.1016/0141-3910(93)90141-5

Polymer Degradation and Stability

Volume 40, Issue 3, 1993, Pages 349-355

https://doi.org/10.1016/0141-3910(93)90141-5 Get rights and content

Abstract

Predicting the weatherability of acrylic melamine coatings commonly used as enamel clearcoats requires a detailed understanding of each of the factors that influence photooxidation kinetics. Previous work¹ has shown that the photooxidation rate in coatings can be written as the following function of hydroperoxide concentration: photooxidation rate = K[YOOH] + M. The existence of a measurable photooxidation rate in the absence of hydroperoxide (i.e. a non-zero value of the intercept, M) has been observed only in melamine crosslinked coatings. It has also been observed that the photooxidation rate in acrylic melamine coatings increases with increasing humidity. In contrast, for urethane crosslinked coatings the value of M is zero, and the photooxidation rate is independent of humidity. In this paper, infrared spectroscopic measurements of functional group changes (e.g. carbonyl growth and crosslink scission) are used to measure photooxidation rates in acrylic melamine coatings during UV exposures at different humidities. Comparisons of these rates to measured hydroperoxide concentrations for the same coatings and exposures reveal that the increase in photooxidation rate with humidity is due to the fact that the intercept M increases with increasing humidity. Since the intercept is zero under dry conditions, the chemical reactions responsible for the intercept in melamine crosslinked coatings must involve both UV light and moisture. These results confirm the importance of accurately controlling the humidity during UV exposure for predicting the weatherability of melamine crosslinked coatings.

References (16)

D.R. Bauer et al.
Polym. Deg. Stab.
(1992)
D.R. Bauer et al.
Polym. Deg. Stab.
(1990)
D.R. Bauer et al.
Polym. Deg. Stab.
(1990)
J.L. Gerlock et al.
Polym. Deg. Stab.
(1986)
J.L. Gerlock et al.
Polym. Deg. Stab.
(1986)
D.F. Mielewski et al.
Polym. Deg. Stab.
(1991)
D.R. Bauer et al.
Polym. Deg. Stab.
(1992)
D.R. Bauer et al.
Polym. Deg. Stab.
(1992)

There are more references available in the full text version of this article.

Cited by (33)

Role of moisture in photo-ageing -macromolecular architecture evolution of acrylic-urethane network
2021, Polymer Testing
Citation Excerpt :
POOH is a key intermediate for determining the rate of photo-oxidation. Based on previous investigations [2,35], POOH groups might be kept at a low concentration throughout the ageing process in a wet environment. As another possibility, the decomposition of POOH via an ionic mechanism might be considered in a wet environment.
In this work, the role of moisture in photo-ageing was discussed for the case of an acrylic-urethane network. Ageing behaviours were characterised by Fourier transform infra-red spectroscopy, positron annihilation lifetime spectroscopy, sol-gel analysis, and differential scanning calorimetry. Two common features between dry and wet photo-ageing, namely, decrease in the mean free volume and increase in the glass transition temperature were observed as photo-oxidation progressed. The characteristics of the final internal structure of the wet photo-aged sample differed from those of the dry photo-aged sample. Although the dry photo-aged samples suggested network densification due to extensive crosslinking formation, wet photo-ageing led to an inhomogeneous structure wherein the average molar mass between crosslinks (at a scale of several nanometres) increased and some domains crosslinked at the sub-nanoscale. Considering the physical (plasticisation) and chemical (hydrolysis) effects induced by water, a possible mechanism for the evolution of the macromolecular architecture was proposed for photo-ageing in dry and wet environments.
Graphene/polymer nanocomposite degradation by ultraviolet light: The effects of graphene nanofillers and their potential for release
2020, Polymer Degradation and Stability
Citation Excerpt :
Photoproduct removal was likely due to the conversion of smaller chain photoproducts, formed from acetylurethane cleavage, to gas (i.e., CO2 and CO) in the presence of moisture [14]. Similar moisture-enhanced photodegradation processes have been observed for several polymers, including polycarbonates and acrylic melamine [37-40]. Furthermore, the formation of carboxylic acids likely accelerated the hydrolysis of acetylurethanes and other photoproducts while moisture absorbed from the air likely contributed to dissolution and washing away of hydrophilic photoproducts such as alcohols, hydroperoxides, carboxylic acids, water soluble amines, and carbamic acid (which can further photodecompose) [41-44].
The ultraviolet (UV)-induced degradation of graphene/polymer nanocomposites was investigated in this study. Specifically, the effect of few-layer graphene nanofillers on the degradation of a thermoplastic polyurethane (TPU) and the release potential of graphene from the degraded nanocomposite surfaces were assessed. Graphene/TPU (G/TPU) nanocomposites and neat TPU were UV-exposed under both dry and humid conditions in the NIST SPHERE, a precisely controlled, high intensity UV-weathering device. Neat TPU and G/TPU were characterized over the time course of UV exposure using color measurements and infrared spectroscopy, for appearance and chemical changes, respectively. Changes in thickness and surface morphology were obtained with scanning electron microscopy. A new fluorescence quenching measurement approach was developed to identify graphene sheets at the nanocomposite surface, which was supported by contact angle measurements. The potential for graphene release from the nanocomposite surface was evaluated using a tape-lift method followed by microscopy of any particles present on the tape. The findings suggest that graphene improves the service life of TPU with respect to UV exposure, but that graphene becomes exposed at the nanocomposite surface over time, which may potentially lead to its release when exposed to small mechanical forces or upon contact with other materials.
Why is service life prediction of polymers and plastics exposed to outdoor weathering important? An industrial perspective
2020, Service Life Prediction of Polymers and Coatings: Enhanced Methods
The ability to predict the service life of materials is central to effective risk assessment for many products. Like the tools and methodologies for the broader evaluation of risk, service life prediction (SLP) is a methodology that is both well established and continuously improving, challenging researchers to increase the insight and accuracy of prediction within acceptable ranges of speed and cost. As our collective understanding of accelerated aging, failure modes, and predictive models improves, so does our ability to elucidate the relationship between environmental variables and a given material’s response. However, formidable challenges—both technical and practical—remain. Understanding failure modes and underlying mechanisms is essential to accurately predicting service life via accelerated testing. Importantly, the real world can be much more complex than accelerating exposure to a single factor. Thus, useful testing in support of lifetime analysis requires that the operative mechanism that governs a given material’s service life is activated in the accelerated test. One of the enduring challenges of successfully implementing SLP into the product development lifecycle is the difficulty of predicting the results of often complex real-world usage. This work provides a roadmap to the SLP process followed by two case studies that highlight the practical intersection of SLP and risk assessment in industry. One study establishes how SLP has been used effectively to describe lithium ion battery performance in an electronic device to facilitate operational choices to extend lifetime. A second study demonstrates the unintended service life reduction due to formulation change in a building sealant.
Service life prediction of PV materials
2019, Durability and Reliability of Polymers and Other Materials in Photovoltaic Modules
The photovoltaic (PV) industry has seen rapid change and a great deal of turmoil, particularly over the past 2 decades. Rapidly decreasing cost-per watt module prices, the loss of government and utility subsidies and incentives, and decreasing fossil fuel prices and import tariffs have driven out many manufacturers, shifted global production, and forced promising technologies to the periphery. A majority of the installed megawatts of PV power are in large investor-financed commercial and utility-scale projects; for example, the 1000 MW Kurnool Ultra Mega Solar Park (India) consists of over four million modules. When completed, the Pavagada (India) solar park is expected to produce 2000 MW of electricity, with no size limit in sight for future projects.
An innovative approach to construct photodegradation curves for TiO<inf>2</inf> incorporated latex coatings via probing localized degradation
2016, Polymer Degradation and Stability
The main objective of this study was to establish a new approach to construct local photodegradation curves for TiO₂ incorporated latex coatings via innovatively probing polymer photodegradation in the vicinity of nanoparticle agglomerates using laser scanning confocal microscope (LSCM) under a wet and a dry conditions. First, nanoparticle dispersion in surface/subsurface of latex coatings was investigated with LSCM. Second, 2D LSCM images were used to show how nanoparticles were gradually revealed with UV exposure. Third, 3D and ortho LSCM images were applied to illustrate how polymer surface was gradually decreased and how the polymer/nanoparticle interface regions were gradually degraded. The ortho images were also used to calculate the relative vertical height change in polymer matrix and in interface regions referred to the front of nanoparticle agglomerates. Finally, local photodegradation curves in the polymer matrix and in the interface regions were obtained under the wet and dry conditions by plotting the relative changes in height as a function of the UV exposure time. By comparison of the local photodegradation curves in different stages, at different locations and under different exposure conditions, it was found that under UV radiation, after the exposure of nanoparticles onto polymer surface, the photocatalytic effect of nanoparticles could significantly affect the photodegradation of the interface of filled coatings, which would result in severely inhomogeneous photodegradation, especially under the wet condition.
Nanocharacterization techniques for investigating the durability of wood coatings
2012, European Polymer Journal
Citation Excerpt :
In order to enhance the durability of the wood coating, a better understanding is needed on the surface characteristics of the coating films during, and following, the UV exposition to detect the early stages of physical degradation that occur at a submicrometer length scale. Under weathering exposure, ultra-violet (UV) radiation, presence of H2O and O2 are critical factors for coating degradation [1–4]. Photo-initiated oxidation produces peroxides, ketones and aldehydes, and further photo-oxidation of peroxides and ketones yields peracids, which continue the oxidative degradation as oxidants [5].
Nanocharacterization techniques such as nanoindentation and atomic force microscopy were used to investigate the exterior durability of waterborne coatings improved with inorganic nanosized UV-absorbers. Nanocomposite coatings for exterior uses of wood were formulated with different type of nanoparticles and their performance was evaluated trough artificial aging. Nanoindentation in continuous stiffness mode was used to demonstrate the changes of hardness and Young’s modulus of the coatings after accelerated weathering. The degradation mechanism of the surface coatings was investigated with atomic force microscopy that has provided valuable information on the morphological and microstructural changes of the surface coatings with the artificial aging. Additionally, the glass transition temperature and optical appearance changes were reported. The results obtained have shown that the nanoindentation technique in conjunction with atomic force microscopy can be satisfactorily used for durability investigation and service life prediction of nanocomposite coatings for wood.

View all citing articles on Scopus

View full text

The role of humidity in the photooxidation of acrylic melamine coatings

Abstract

Polym. Deg. Stab.

Polym. Deg. Stab.

Polym. Deg. Stab.

Polym. Deg. Stab.

Polym. Deg. Stab.

Polym. Deg. Stab.

Polym. Deg. Stab.

Polym. Deg. Stab.