Inelastic constitutive relations for solids: An internal-variable theory and its application to metal plasticity
Abstract
This paper is a study of the theoretical foundations of constitutive relations at finite strain for a class of solids exhibiting inelasticity as a consequence of specific structural rearrangements, on the microscale, of constituent elements of material. Metals deforming plastically through dislocation motion are of this class and form the primary application of the theory. The development is in terms of a general internal-variable thermodynamic formalism for description of the microstructural rearrangements, and it is shown how metal plasticity may be so characterized.
The principal result is in the normality structure which is shown to arise in macroscopic constitutive laws when each of the local microstructural rearrangements proceeds at a rate governed by its associated thermodynamic force. This provides a theoretical framework for time-dependent inelastic behavior in terms of a “flow potential”, and reduces to statements on normality of strain increments to yield surfaces in the time-independent case. Conventional characterizations of the stress-state dependence of metallic slip are noted to be in accord with this concept of associated forces governing rates, so that the resulting normality structure may be considered directly applicable to metal plasticity.
References (19)
- G.M. Brown
J. Mech. Phys. Solids
(1970) - R. Hill
J. Mech. Phys. Solids
(1966) - R. Hill
J. Mech. Phys. Solids
(1967) - R. Hill
J. Mech. Phys. Solids
(1968) - J.W. Hutchinson
J. Mech. Phys. Solids
(1964) - M.A. Biot
J. appl. Phys.
(1954) - J.F.W. Bishop et al.
Phil. Mag.
(1951) - B.D. Coleman et al.
J. Chem. Phys.
(1967) - S.R. de Groot et al.
Non-Equilibrium Thermodynamics
(1962)
Cited by (1501)
Effect of grain boundary on scratch behavior of polycrystalline copper
2024, International Journal of Mechanical SciencesThe anisotropy in the elastoplastic response of crystalline solids influences substantially their scratch resistance at the microscale. While grain boundaries typically act as obstacles to the motion of dislocations at the grain level, the scratch behavior in the vicinity of the grain boundary is influenced by other factors such as crystallographic orientation and pile-up topography. We performed a systematic set of nano-scratch simulations using the mechanism-based strain gradient crystal plasticity to study the evolution of scratch force and depth near grain boundaries. To validate our model, we conducted a nano-scratch test on a polycrystalline copper sample and compared the scratch depth profile for a specific grain boundary with the simulated result, where a good qualitative agreement was achieved. Our simulations showed that the scratch depth, force, and hardness vary between the corresponding values for the individual constitutive grains, and the variation decreases by reducing the grain size. Additionally, we analyzed the scratch response in terms of the pile-up topography and subsurface stresses and distinguished different regimes when the indenter approaches and scratches across the boundary. Our findings offer a new direction to optimize the scratch resistance of polycrystalline metals by tailoring the size and orientation of grains near the surface. Additionally, it introduces scratching as a robust material characterization method.
Incremental variational approach to gradient damage coupled with poroelasticity of saturated media
2024, Journal of the Mechanics and Physics of SolidsIn this study, we aim at investigating the coupling between poroelasticity (including the fluid flow) and gradient damage phenomena in saturated porous media. To this end, we first extend the thermodynamics-based Biot–Coussy theory of poroelasticity in order to incorporate gradient damage processes. Taking advantage of this framework, we establish a variational formulation for the proposed model, expressed as a four-field incremental minimization problem of a total energy functional which includes poroelastic energy as well as dissipated energy related to damage growth together with Darcy-like fluid flow. Moreover, after a careful analysis of the so-called kinetic porosity in each increment, the incremental minimization is reduced to that of three fields, namely, the displacement and damage fields of the skeleton phase of the porous media as well as the pore fluid pressure. Subsequently, we proceed to the numerical implementation of the variational problem via a semi-staggered optimization algorithm and apply it to a first benchmark modeling for which corresponding solution as well as numerical results for hydraulic fracturing are available. Finally, we perform an application of the proposed model for the evaluation of an Excavation Damage Zone (EDZ) around an underground waste storage gallery. The model is shown to be able to deliver sufficiently reliable predictions.
Crystal plasticity simulations reveal cooperative plasticity mechanisms leading to enhanced strength and toughness in gradient nanostructured metals
2024, Acta MaterialiaHeterogeneous deformation is thought to provide the strengthening in gradient nanostructured metals, but the underlying plasticity mechanisms and optimal gradient structures for attaining improved mechanical performance remain elusive. Through crystal plasticity simulations of three-dimensional heterogeneous nanostructures, we reveal the heterogeneous-deformation-induced plasticity mechanisms which evoke increased flow strength and strain hardening. We have developed a synthetic microstructure generation algorithm which replicates both the microstructural features and external geometry of experimentally characterized samples—providing a direct comparison between the mechanical response recorded in simulations and experiments. Aligning well with experiments, the simulations show synergistically enhanced mechanical properties. High strain hardening rates directly correlate to large stress gradients that emerge due to heterogeneous deformation. Samples with smooth grain size gradients exhibit the most extreme stress gradients and correspondingly higher strain hardening rates. Large increases in dislocation density—especially within larger grains—and high intra- and inter-granular crystal rotation are plasticity mechanisms common to samples which exhibit high mechanical performance. Although the nanostructural gradients have pronounced influence over the mechanical performance, samples with the same grain size and dislocation density gradients exhibit varied mechanical properties. We show that the distribution of initial grain orientations and the microstructural constraints placed on larger grains also influence the active plasticity mechanisms providing improved mechanical properties.
The characterization of frictional behavior in ductile metals is a crucial aspect of materials science, as it relates to the plastic deformation of the material. However, due to the intricate dislocation evolution at the submicron/nanometer scale, the isolation of the basic plastic mechanisms remains challenging. In this study, nanoscratching technology is employed to investigate submicron/nanometer-level plastic deformation in individual grains of polycrystalline copper. To achieve this, a crystal plastic constitutive model for copper materials is developed by incorporating geometrically necessary dislocation effects. The calibration of the constitutive model is conducted with great precision and specificity, leveraging mechanical responses, surface accumulation morphology, and indentation size effects from nanoindentation experiments of 110-oriented single crystal copper. Through the combination of crystal plastic finite element simulation and nanoscratching experiments, the plastic flow of the material is thoroughly analyzed. The results demonstrate that the anisotropic scratching behavior is influenced by different orientations of individual grains, taking into account both statistical storage dislocations and geometrically necessary dislocations. The insights gleaned from this study offer a valuable contribution to our understanding of the plastic mechanisms of metals at a small scale, enhancing the design and performance of advanced materials for a wide range of applications.
Interface shearing promoted plastic flow instability of nanolaminated composites
2024, International Journal of Mechanical SciencesNanocrystalline laminated composites (NLCs) with alternating phases exhibit exceptional mechanical properties, thermal stability, and resistance to radiation damage and shock. However, inherent plastic flow instability poses a persistent challenge, independent of loading direction. This study explores the mechanisms of buckling and kinking in soft-hard and soft-soft NLCs under compression loading, attributing plastic deformation to dislocation slips and interface shearing/sliding. Despite these merits, plastic flow instability remains a challenge in NLCs under compression, irrespective of loading direction. This study focuses on elucidating the mechanisms of plastic flow instability, particularly buckling and kinking, observed in soft-hard and soft-soft NLCs. A mesoscale crystal plasticity model integrating the interfacial shear (IS) and confined layer slip (CLS) mechanisms is developed. In soft-soft Cu-Nb multilayers, the model reveals that easy interface sliding promotes plastic strain in the interface, inducing strain softening by lowering interface shear resistance. Conversely, the contribution of interface shear to plastic deformation diminishes with increasing Cu/Nb layer thickness, reducing the likelihood of strain softening. For soft-hard Al-Al2Cu eutectics, easier interface shear intensifies plastic deformation in Al layers but suppresses it in Al2Cu layers, triggering structural instability in the latter. The critical strain for bulking in the same thick Al2Cu layer decreases with increasing Al layer thickness. In summary, lowering interface resistance will promote compression instability of NLCs, while thickening soft layer will retard the occurrence of compression instability regardless of soft-soft or soft-hard NLCs.
Prediction of the fatigue life in a textured AZ31 Mg alloy as a function of orientation using fatigue indicator parameters
2024, Materials Science and Engineering: AComputational homogenization was used to simulate the mechanical response of a textured AZ31Mg alloy subjected to fully-reversed cyclic deformation. The behavior of each grain in the polycrystal followed a phenomenological crystal plasticity model that considered different deformation mechanisms, namely pyramidal, basal, and prismatic slip, as well as twinning and detwinning. It also accounted for both kinematic and isotropic hardening effects. The crystal plasticity model's parameters were adjusted to replicate the cyclic stress-strain curves along three different orientations (rolling direction, normal direction and at 45° between the rolling and normal directions) at different cyclic strain semi-amplitudes. Three different fatigue indicator parameters were calculated from the simulations, based on the accumulated plastic shear strain in one stabilized fatigue cycle from basal slip and pyramidal slip, and from the shear strain accommodated by twinning/de-twinning during one fatigue cycle. The predictions of the fatigue life based on the fatigue indicator parameters were compared with the experimental results for the three orientations. It was found that the most accurate prediction was obtained by using the fatigue indicator parameter associated with twinning/de-twinning. Thus, it is concluded that fatigue cracks nucleated at twin boundaries control the fatigue life of textured Mg alloys.