Natural rubber latex for the development of high performance cement mortar

  • Technical Paper
  • Published:
Innovative Infrastructure Solutions Aims and scope Submit manuscript

Abstract

Performance enhanced concrete and mortar with cost-effective and renewable materials are essential for sustainable construction. The use of synthetic polymeric latexes in construction applications is quite common. The use of natural polymers like natural rubber latex (NRL) with very low embodied energy compared to synthetic latexes has become essential in the construction industry. This study attempts to develop a high-performance mortar using natural rubber latex. The effect of natural rubber latex addition (from 0.5 to 2% by weight of cement) on the flow, strength, and durability of mortar is investigated. Challenges in the concrete modified with natural rubber latex are addressed by the inclusion of defoamer. The influence of defoamer in reducing the air entrainment of NRL-modified mortar is studied and the optimum percentage of defoamer to be incorporated in modified mortar is suggested. Macroscopic and microscopic images have confirmed the formation of latex film and network formation in the mortar which explains the improvement in mechanical properties and durability of NRL-modified mortar compared to the reference mortar without latex. The effect of natural rubber latex incorporation on mortar mixture composition and interactions on strength parameters has been verified by ANOVA at 5% significance level. NRL increases the flexural strength capacity and causes a significant reduction in permeable porosity (58%) and sorptivity (86.4%), demonstrating its huge potential in terms of durability properties. The results indicate that natural rubber latex-modified mortar can be effectively utilized for field applications, particularly those exposed to aggressive environments and repair works.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20
Fig. 21
Fig. 22
Fig. 23

Similar content being viewed by others

References

  1. Kardon JB (1997) Polymer-modified concrete. J Mater Civ Eng 9(2):85–92. https://doi.org/10.1061/(ASCE)0899-1561(1997)9:2(85)

    Article  CAS  Google Scholar 

  2. Sreekala R, Muthumani K, Sathish Kumar K, Gopalakrishnan N (2009) Natural rubber latex modified fibre concrete—Initial studies for structural performance. Indian Concr J 83(10):29

    Google Scholar 

  3. Sukmak G, Sukmak P, Horpibulsuk S, Yaowarat T, Kunchariyakun K, Patarapaiboolchai O, Arulrajah A (2020) Physical and mechanical properties of natural rubber modified cement paste. Constr Build Mater 244:118319. https://doi.org/10.1016/j.conbuildmat.2020.118319

    Article  CAS  Google Scholar 

  4. Diab AM, Elyamany HE, Ali AH (2013) Experimental investigation of the effect of latex solid/water ratio on latex modified co-matrix mechanical properties. Alex Eng J 52(1):83–98. https://doi.org/10.1016/j.aej.2012.11.002

    Article  Google Scholar 

  5. Nagaraj TS, Iyengar KSR, Rao BK (1988) Super-plasticized natural rubber latex modified concretes. Cem Concr Res 18(1):138–144

    Article  CAS  Google Scholar 

  6. Muhammad B, Ismail M (2012) Performance of natural rubber latex modified concrete in acidic and sulfated environments. Constr Build Mater 31:129–134. https://doi.org/10.1016/j.conbuildmat.2011.12.099

    Article  Google Scholar 

  7. Yao SY, Ge Y (2012) Effect of styrene butadiene rubber latex on mortar and concrete properties. Adv Eng For. vol 5. Trans Tech Publications Ltd, pp 283–288. https://doi.org/10.4028/www.scientific.net/AEF.5.283

  8. Ohama Y (1995) Handbook of polymer-modified concrete and mortars: properties and process technology. William Andrew, Norwich

    Google Scholar 

  9. Joseph R (2013) Practical guide to latex technology. Smithers Rapra, Shrewsbury

    Google Scholar 

  10. Vo ML, Plank J (2018) Evaluation of natural rubber latex as film forming additive in cementitious mortar. Constr Build Mater 169:93–99. https://doi.org/10.1016/j.conbuildmat.2017.12.098

    Article  CAS  Google Scholar 

  11. Khamput P, Suweero K (2011) Properties of mortar mixing with medium ammonia concentrated latex. Energy Proc 9:559–567. https://doi.org/10.1016/j.egypro.2011.09.065

    Article  CAS  Google Scholar 

  12. Mathew LA, Jose J, Joseph G (2021) Mechanical performance of natural rubber latex modified mortars. In: Adv Sust Constr Mater: select proceedings ASCM 2020 Springer Singapore, pp 765–774

  13. Muhammad B, Ismail M (2013) Performance of hydrocarbon particles on the drying shrinkage of cement mortar. Constr Build Mater 48:868–873. https://doi.org/10.1016/j.conbuildmat.2013.07.011

    Article  Google Scholar 

  14. Yaowarat T, Suddeepong A, Hoy M, Horpibulsuk S, Takaikaew T, Vichitcholchai N, Chinkulkijniwat A (2021) Improvement of flexural strength of concrete pavements using natural rubber latex. Constr Build Mater 282:122704. https://doi.org/10.1016/j.conbuildmat.2021.122704

    Article  Google Scholar 

  15. Awoyera PO, Althoey F, Ajinomisan H, Othuman Mydin MA, Bheel N, Sabri Sabri MM, Hadidi HM, Jayanthi V, Ahmad M (2023) Potential of natural rubber latex in cement mortar for thermal insulating material in buildings. Frontr Mater 10:1152492. https://doi.org/10.3389/fmats.2023.1152492

    Article  Google Scholar 

  16. IS 12269 (1987) Specification for 53-grade Ordinary Portland cement, Bureau of Indian Standard, New Delhi

  17. IS 3812-1 (2003) Specification for Pulverized Fuel Ash, Part 1: For Use as Pozzolana in Cement, Cement Mortar and Concrete, Bureau of Indian Standard, New Delhi

  18. IS 383 (1970) Specification for coarse and fine aggregates from natural sources for concrete, Bureau of Indian Standard, New Delhi

  19. IS 5430 (1981) Specification for Ammonia Preserved Concentrated Natural Rubber Latex, Bureau of Indian Standard, New Delhi

  20. ASTM C150-07: Standard Specification for Portland Cement, ASTM International, West Conshohocken, PA

  21. ASTM C618-22: Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. ASTM International, West Conshohocken, PA

  22. Muhammad B, Ismail M, Yussuf AA, Muhammad ARB (2011) Elastomeric influence of natural rubber latex on cement mortar at high temperatures using thermal degradation analysis. Constr Build Mater 25(5):2223–2227. https://doi.org/10.1016/j.conbuildmat.2010.11.006

    Article  Google Scholar 

  23. IS 4031-8 (1988) Methods of physical tests for hydraulic cement, Part 8: Determination of transverse and compressive strength of plastic mortar using prism, Bureau of Indian Standard, New Delhi

  24. IS 10890 (1984) Specification for planetary mixer used in tests of cement and pozzolana, Bureau of Indian Standard, New Delhi

  25. Shafer HH, Eash RD (1975) Reactions of polymer latexes with Portland cement concrete. Transp Res Rec 542:1–8

    Google Scholar 

  26. Li M, Zhang X, Tay YWD, Ting GHA, Lu B, Tan MJ (2022) Three-dimensional (3D) printing for building and construction. Digit Manuf 2022:345–385. https://doi.org/10.1016/B978-0-323-95062-6.00004-8

    Article  Google Scholar 

  27. ASTM C1437-07 (2007) Standard test method for flow of hydraulic cement mortar, Annual Book of ASTM Standards, ASTM International, West Conshohocken, PA

  28. IS 5512 (1983) Specification for flow table for use in tests of hydraulic cements and pozzolanic materials, Bureau of Indian Standard, New Delhi

  29. IS 2250 (1981) Code of practice for preparation and use of masonry mortars, Bureau of Indian Standard, New Delhi

  30. ASTM C348-21 (2021) Standard test method for flexural strength of hydraulic-cement mortars, ASTM International, West Conshohocken, PA

  31. ASTM C642-21 (2021) Standard test method for density, absorption, and voids in hardened concrete, ASTM International, 2021, West Conshohocken, PA

  32. ASTM C1403-15 (2015) Standard test method for rate of water absorption of masonry mortars, ASTM International, West Conshohocken, PA

  33. ASTM C1585-20 (2020) Standard test method for measurement of rate of absorption of water by hydraulic-cement concretes, West Conshohocken, PA

  34. ASTM C596-18 (2018) Standard test method for drying shrinkage of mortar containing hydraulic cement, West Conshohocken, PA

  35. IS: 9459 (1980) Specification for apparatus for use in measurement of length change of hardened cement paste, mortar, and concrete, Bureau of Indian Standard, New Delhi (Reaffirmed 2008)

  36. ASTM C1329-05 (2005) Standard Specification for Mortar Cement, West Conshohocken, PA

  37. Knapen E, Dionys VG (2015) Polymer film formation in cement mortars modified with water-soluble polymers. Cem Concr Comp 58:23–28. https://doi.org/10.1016/j.cemconcomp.2014.11.015

    Article  CAS  Google Scholar 

  38. Sun B, Zheng L, Li P, Li X, Zuo Y (2023) Modified natural rubber latex film-forming enhances bamboo scraps/magnesium oxychloride composites. J Build Eng 63:105506. https://doi.org/10.1016/j.jobe.2022.105506

    Article  Google Scholar 

  39. Liu Q, Li Y, Ming X, Sun Z, Li Z, Sun G (2023) Enhanced flexural strength and crack resistance of concrete by constructing a polymer-cement network. SSRN 4370410. https://doi.org/10.2139/ssrn.4370410

  40. Childers MI, Nguyen MT, Rod KA, Koech PK, Um W, Chun J, Glezakou VA, Linn D, Roosendaal TJ, Wietsma TW, Huerta NJ (2017) Polymer-cement composites with self-healing ability for geothermal and fossil energy applications. Chem Mater 29(11):4708–4718. https://doi.org/10.1021/acs.chemmater.7b00344

    Article  CAS  Google Scholar 

  41. Franceschini A, Abramson S, Mancini V, Bresson B, Chassenieux C, Lequeux N (2007) New covalent bonded polymer–calcium silicate hydrate composites. J Mater Chem 17(9):913–922

    Article  CAS  Google Scholar 

  42. Gao JM, Qian CX, Wang B, Morino (2002) Experimental study on properties of polymer-modified cement mortars with silica fume. Cem Concr Res 32(1):41–45. https://doi.org/10.1016/S0008-8846(01)00626-3

    Article  CAS  Google Scholar 

  43. Pei M, Kim W, Hyung W, Ango AJ, Soh Y (2002) Effects of emulsifiers on properties of poly (styrene–butyl acrylate) latex-modified mortars. Cem Concr Res 32(6):837–841. https://doi.org/10.1016/S0008-8846(01)00733-5

    Article  CAS  Google Scholar 

  44. Yu Z, Guang Y (2013) The pore structure of cement paste blended with fly ash. Constr Build Mater 45:30–35. https://doi.org/10.1016/j.conbuildmat.2013.04.012

    Article  CAS  Google Scholar 

  45. Rath B, Praveenkumar TR, Misgana D (2022) Porosity of calcined clay-based geopolymer concrete incorporating natural rubber latex. Innov Infrastruct Solut 7:163. https://doi.org/10.1007/s41062-022-00769-0

    Article  Google Scholar 

  46. Sakthieswaran N, Sophia M (2018) Effect of superplasticizers on the properties of latex modified gypsum plaster. Constr Build Mater 179:675–691. https://doi.org/10.1016/j.conbuildmat.2018.05.150

    Article  CAS  Google Scholar 

  47. Bhogayata AC, Arora NK (2018) Workability, strength, and durability of concrete containing recycled plastic fibers and styrene-butadiene rubber latex. Constr Build Mater 180:382–395. https://doi.org/10.1016/j.conbuildmat.2018.05.175

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. School of Engineering, Cochin University of Science & Technology, Kochi, Kerala, India

    Liji Anna Mathew & Glory Joseph

Authors
  1. Liji Anna Mathew
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Glory Joseph
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Liji Anna Mathew.

Ethics declarations

Conflict of interest

The authors declare that there is no conflict of interest.

Ethical approval

Studies using human or animals are not included in the results presented.

Informed consent

Informed consent is obtained from all individuals involved in the study.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mathew, L.A., Joseph, G. Natural rubber latex for the development of high performance cement mortar. Innov. Infrastruct. Solut. 9, 97 (2024). https://doi.org/10.1007/s41062-024-01398-5

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s41062-024-01398-5

Keywords

Search

Navigation