Abstract
The mechanical behavior of solution heat-treated and pre-aged Mg–6Zn–1Gd–1Er alloys during hot compression (from 180 to 330 °C) has been investigated. The results showed that the flow stress curves of the pre-aged sample (PAS) intersected with that of the solution heat-treated sample (SHTS) during hot compression. At 180 °C, when the true strain is 0.27 and 0.47, the PAS showed larger and smaller stress (210.80 MPa vs. 207.58 MPa and 205.67 MPa vs. 207.93 MPa) than the SHTS, respectively. These phenomena were due to the stronger interaction of W phase and dislocations/twins under the strain of 0.27, while dynamic recrystallization softening occurred under the strain of 0.47. When the temperature increased to 330 °C, the flow stress of PAS and SHTS showed an opposite trend to that of 180 °C. Continuous dynamic recrystallization and particle stimulated nucleation based on slip operations are the main deformation mechanisms under 330 °C. At the true strain is 0.33 and 0.53, the PAS has smaller and larger stress (61.32 MPa vs. 63.69 MPa and 58.75 MPa vs. 57.09 MPa) than the SHTS, respectively. The increasing deformation resistance of dynamic precipitation improved the flow stress under smaller strain and dynamic recrystallization decreased the flow stress under high strain, which resulted the opposite phenomena of SHTS.
Similar content being viewed by others
References
X.C. Ma, S.Y. Jin, R.Z. Wu, J.X. Wang, G.X. Wang, B. Krit, S. Betsofen, T. Nonferr, Metal. Soc. 31, 3228 (2021)
B. Che, L.W. Lu, W. Kang, J. Luo, M. Ma, L.F. Liu, J. Alloys Compd. 862, 158700 (2021)
S.Y. Jin, X.C. Ma, R.Z. Wu, T.Q. Li, J.X. Wang, B.L. Krit, L.G. Hou, J.H. Zhang, G.X. Wang, Int. J. Min. Met. Mater. 29, 1453 (2022)
B. Wu, J.B. Li, L.Z. Liu, X.H. Chen, J. Tan, J.F. Song, M. Rashad, F.S. Pan, Acta Metall. Sin.-Engl. Lett. 34, 606 (2021)
L.B. Tong, J.H. Chu, D.N. Zou, Q. Sun, S. Kamado, H.G. Brokmeier, M.Y. Zheng, Acta Metall. Sin.-Engl. Lett. 34, 265 (2021)
B. Che, L.W. Lu, J.L. Zhang, J.H. Zhang, M. Ma, L.F. Wang, F.G. Qi, Mater. Sci. Eng. A 832, 142475 (2022)
H.B. Liao, L.L. Mo, X. Zhou, B. Zhao, J. Du, J. Mater. Res. Technol. 12, 807 (2021)
P.D. Huo, F. Li, R.Z. Wu, R.H. Gao, A.X. Zhang, Mater. Des. 219, 110696 (2022)
H. Zhang, M.X. Yang, M.J. Hou, L.F. Wang, Q. Zhang, J.F. Fan, W.G. Li, H.B. Dong, S.M. Liu, B.S. Xu, Mater. Sci. Eng. A 744, 456 (2019)
Y.W. Gui, Y.J. Cui, H.K. Bian, Q.N. Li, L.X. Ouyang, A. Chiba, J. Mater. Sci. Technol. 80, 279 (2021)
B.J. Lv, S. Wang, T.W. Xu, F. Guo, J. Magnes. Alloys 9, 840 (2021)
Y. Zhao, D.F. Zhang, R.J. Lei, P. Wang, J.K. Feng, X. Chen, B. Jiang, F.S. Pan, J. Mater. Res. Technol. 9, 12737 (2020)
L.X. Yang, L. Xiao, H.T. Zhou, Y. Tian, F. Li, X.Q. Zeng, B.D. Sun, Z.Q. Li, Aerosp. Shanghai 36, 38 (2019)
K. Wang, X.X. Dou, J.F. Wang, Y.D. Huang, S. Gavras, N. Hort, S.J. Liu, H. Hu, J.X. Wang, F.S. Pan, Mater. Sci. Eng. A 790, 139635 (2020)
P. Liu, H.T. Jiang, Z.X. Cai, Q. Kang, Y. Zhang, J. Magnes. Alloys 4, 188 (2016)
J.S. Wang, X.B. Li, J. Alloys Compd. 803, 689 (2019)
F. Guo, L.Q. Fang, X.P. Zhao, Y.G. Li, H.S. Cai, J. Alloys Compd. 862, 158543 (2021)
K. Liu, J.X. Liu, S.B. Li, Z.H. Wang, W.B. Du, Q.F. Wang, T. Nonferr, Metal. Soc. 28, 890 (2018)
J. Wei, Q.D. Wang, L. Zhang, D.D. Yin, B. Ye, H.Y. Jiang, W.J. Ding, Mater. Lett. 246, 125 (2019)
D. Wang, S.J. Liu, R.Z. Wu, S. Zhang, Y. Wang, H.J. Wu, J.H. Zhang, L.G. Hou, J. Alloys Compd. 881, 160663 (2021)
C.J. Wang, J.W. Kang, K.K. Deng, K.B. Nie, W. Liang, W.G. Li, J. Magnes. Alloys 8, 441 (2020)
W. Kang, L.W. Lu, L.B. Feng, F.C. Lu, C.L. Gan, X.H. Li, J. Magnes. Alloys (2021). https://doi.org/10.1016/j.jma.2021.05.019
M. Rashad, F.S. Pan, M. Asif, Mater. Sci. Eng. A 649, 263 (2016)
K. Yan, H.A. Liu, X.W. Xue, J. Bai, H.H. Chen, S.Q. Fang, J.J. Liu, Acta Metall. Sin.-Engl. Lett. 34, 217 (2021)
S.H. Jeong, Y.J. Kim, K.H. Kong, T.H. Cho, Y.K. Kim, H.K. Lim, W.T. Kim, D.H. Kim, Met. Mater. Int. 24, 391 (2018)
L.F. Wang, Z.Y. Zhang, H. Zhang, H.X. Wang, K.S. Shin, Mater. Sci. Eng. A 798, 140126 (2020)
Y.L. Zhu, F.Y. Liu, B. Song, R.L. Xin, Mater. Sci. Eng. A 779, 139158 (2020)
J.H. Cho, S.H. Han, H.T. Jeong, S.H. Choi, J. Alloys Compd. 743, 553 (2018)
B. Che, L.W. Lu, M.Y. Wu, W. Kang, L.Y. Tang, D.Q. Fan, Mater. Rep. 35, 21249 (2021)
Y.L. Zhu, F.Y. Liu, R.L. Xin, B. Song, Q. Liu, Mater. Sci. Eng. A 779, 139156 (2020)
S.W. Xu, N. Matsumoto, S. Kamado, T. Honma, Y. Kojima, Mater. Sci. Eng. A 517, 354 (2009)
L. Luo, Z.Y. Xiao, Q.H. Huo, Y. Yang, W.Y. Huang, J.C. Guo, Y.X. Ye, X.Y. Yang, J. Alloys Compd. 740, 180 (2018)
H. Zhang, X.Q. Bai, M.J. Hou, L.F. Wang, Q. Zhang, J.F. Fan, Y.C. Wu, H.B. Dong, B.S. Xu, Mater. Sci. Eng. A 772, 138686 (2020)
X.X. Wei, L. Jin, S. Dong, F.H. Wang, J. Dong, Mater. Charact. 169, 110670 (2020)
J. Gubicza, K. Máthis, Z. Hegedűs, G. Ribárik, A.L. Tóth, J. Alloys Compd. 492, 166 (2010)
X.L. Ma, S.E. Prameela, P.Y.M. Fernandez, N.M. Krywopusk, L.J. Kecskes, T. Sano, M.L. Falk, T.P. Weihs, Acta Mater. 172, 185 (2019)
S.S.A. Shah, M.G. Jiang, D. Wu, U. Wasi, R.S. Chen, Acta Metall. Sin.-Engl. Lett. 31, 923 (2018)
J.D. Robson, N. Stanford, M.R. Barnett, Scr. Mater. 63, 823 (2010)
M.A. Kumar, L. Capolungo, R.J. McCabe, C.N. Tomé, Sci. Rep. 9, 3846 (2019)
J.S. Hong, S. Kang, J.G. Jung, Y.K. Lee, Scr. Mater. 174, 62 (2020)
X.S. Xia, K. Zhang, M.L. Ma, T. Li, J. Magnes. Alloys 8, 917 (2020)
Z.Q. Yang, A.B. Ma, H. Liu, D. Song, Y.N. Wu, Y.C. Yuan, J.H. Jiang, J.P. Sun, Mater. Charact. 152, 213 (2019)
M.G. Jiang, C. Xu, H. Yan, G.H. Fan, T. Nakata, C.S. Lao, R.S. Chen, S. Kamado, E.H. Han, B.H. Lu, Acta Mater. 157, 53 (2018)
C. Liu, P. Shanthraj, J.D. Robson, M. Diehl, S. Dong, J. Dong, W. Ding, D. Raabe, Acta Mater. 178, 146 (2019)
X.L. Ma, Q. Jiao, L.J. Kecskes, J.A. El-Awady, T.P. Weihs, Acta Mater. 189, 35 (2020)
Y.Z. Meng, J.M. Yu, G.S. Zhang, Y.J. Wu, Z.M. Zhang, Z. Shi, J. Magnes. Alloys 8, 1228 (2020)
L.Y. Jia, W.B. Du, J.L. Fu, Z.H. Wang, K. Liu, S.B. Li, X. Du, Acta Metall. Sin.-Engl. Lett. 34, 39 (2021)
L.M. Zhu, Q.N. Li, X.Y. Chen, Q. Zhang, J. Alloys Compd. 865, 158648 (2021)
H.W. Miao, H. Huang, S.F. Fan, J.Y. Tan, Z.C. Wang, W.J. Ding, G.G. Yuan, Mater. Des. 196, 109122 (2020)
J.W. Kang, C.J. Wang, K.K. Deng, K.B. Nie, Y. Bai, W.J. Li, J. Alloys Compd. 720, 196 (2017)
X.Y. Liu, L.W. Lu, K. Sheng, T. Zhou, Acta Metall. Sin.-Engl. Lett. 32, 710 (2019)
S.H. Park, S.G. Hong, J.H. Lee, Y.H. Huh, J. Alloys Compd. 646, 573 (2015)
H.H. Lu, Y. Li, L. Lu, W.G. Zhang, W. Liang, Acta Metall. Sin.-Engl. Lett. (2022). https://doi.org/10.1007/s40195-022-01441-3
K. Sheng, L.W. Lu, Y. Xiang, M. Ma, Z.C. Wang, Acta Metall. Sin.-Engl. Lett. 32, 235 (2019)
Y. Yan, W.P. Deng, Z.F. Gao, J. Zhu, Z.J. Wang, X.W. Li, Acta Metall. Sin.-Engl. Lett. 29, 163 (2016)
S.H. Lu, D. Wu, R.S. Chen, E.H. Han, Mater. Des. 191, 108600 (2020)
I. Basu, T. Al-Samman, Acta Mater. 96, 111 (2015)
C. Liu, J.B. Zhang, Y.K. Yang, X.C. Xia, T. He, J. Ding, Y. Tang, Z. Zhang, X.G. Chen, Y.C. Liu, Acta Metall. Sin.-Engl. Lett. 35, 1383 (2022)
Q. Wu, H.G. Yan, J.H. Chen, W.J. Xia, M. Song, B. Su, Mater. Charact. 160, 110131 (2020)
Y.Z. Du, Y.F. Ge, B.L. Jing, JOM 71, 2202 (2019)
M. Rezaee, A. Zarei-Hanzaki, A. Mohamadizadeh, E. Ghasemi, Mater. Sci. Eng. A 673, 346 (2016)
R. Sarkar, A. Mukhopadhyay, P. Ghosal, T.K. Nandy, K.K. Ray, Philos. Mag. 100, 399 (2020)
Acknowledgements
This work was partly supported by the National Natural Science Foundation of China (Grant Nos. 52174362, 51975207, and 11772127), the Hunan Provincial Natural Science Foundation for Excellent Young Scholars of China (Grant No. 2019JJ30010), the Hunan Provincial Natural Science Foundation of China (Grant No. 2018JJ3101), the Scientific Research Fund of Hunan Provincial Education Department (Grant No. 17B059) and the Leading Plan for Scientific and Technological Innovation of High-Tech Industries—Heavy Haul Equipment R&D and Intelligent Handling (No. 2021GK4008).
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors state that there are no conflicts of interest to disclose.
Additional information
Available online at http://link.springer.com/journal/40195.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Che, B., Lu, L., Liu, L. et al. Hot Compression Mechanical Behavior of Solution Heat-Treated and Pre-aged Mg–Zn–Gd–Er Alloys. Acta Metall. Sin. (Engl. Lett.) 36, 469–485 (2023). https://doi.org/10.1007/s40195-022-01482-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-022-01482-8