Preparation of Nd(III) carbonate by precipitation stripping of Nd(III)-loaded VA10

Abstract

The preparation of fine particles of Nd(III) carbonate from kerosene solution, from which Nd(III) was extracted with versatic acid 10 (VA10) by a precipitation stripping technique using an aqueous NH₃-(NH₄)₂CO₃ solution as stripping medium, was studied.

In preliminary experiments, we were unable to recover simple Nd(III) carbonate from Nd(III)-loaded VA10 by CO₂ gas bubbling, when water, (NH₄)₂CO₃, NH₄HCO₃, NaHCO₃, or NA₂CO₃ solution saturated with CO₂ was used as the stripping solution.

To obtain simple Nd(III) carbonate, it is necessary to use more than the stoichiometric amount of NH₃ compared to VA10 and about 10 times as much (NH₄)₂CO₃ as Nd(III). The solution mixture of NH₃-(NH₄)₂)CO₃ acts as a pH buffer, an adductor for VA10, and a CO ²⁻₃ ion source. Although it was concluded that the precipitates are Nd₂(CO₃)₃·xH₂O (x⊧4), their X-ray pattern does not coincide with that quoted by JCPDS. By heating these precipitates, cubic Nd₂O₃ was obtained at 823 K, while, at 973 K, hexagonal Nd₂O₃ was formed. Since the stripping solution consisting of NH₃-(NH₄)₂CO₃ was highly alkaline, VA10 was also stripped in the aqueous phase. To use a closed-circuit system for the precipitation stripping of Nd(III) carbonate from Nd(III)-loaded VA10, it is important to regenerate VA10 in the organic phase. For this purpose, evaporation of NH₃ by air bubbling was studied. By bubbling air into a stripping solution warmed at 333 K, almost all the VA10 can be transferred to the organic phase.