Abstract
Fuchs and Kaplan carried out experiments in an attempt to ascertain whether oxide bifilms were present in a vacuum-cast Ni-base superalloy but concluded negatively. Although this author challenged their interpretation of their findings, both parties had overlooked the presence in the alloy of boron which is now known to inhibit bifilm formation. However, even though boron can help significantly, improved filling system designs remain important if other damaging entrainment defects are to be avoided.
Similar content being viewed by others
References
G E Fuchs and M A Kaplan. MMTA, 2016, vol 47A, 2346-2375.
J Campbell; Correspondence; MMTA, 2016, 47A, 3803-3805
G E Fuchs and M A Kaplan; Response; MMTA, 2016, 47A, 3806-3809.
J Campbell; Complete Casting Handbook 2nd Edition 2015; Elsevier, Oxford, UK.
N Verma, P C Pistorius, R J Fruehan, M S Potter, H Goltman, E B Pretorius; MMTB, 2012, 43B, 830-840.
J. Campbell (2017) Steel Res. Int. 88(1):1–13
J Campbell and M Tiryakioglu; MMTB, 2012, 43B, 902-914.
Transportation Safety Board Report LP010/2006; Reference A06P0010; “CT Turbine Blade Failure”.
J Campbell; MMTB, 2011, 42B (6), 1091-1097
J. Campbell: Mini Casting Handbook; 2017 Published by Aspect Design, Malvern, UK.
Author information
Authors and Affiliations
Corresponding author
Additional information
*G.E. Fuchs and M.A. Kaplan: Metall. Mater. Trans. A, 2016, vol 47A, pp. 2346–75.
Manuscript submitted April 21, 2017.
Rights and permissions
About this article
Cite this article
Campbell, J. Discussion of “Investigation of Oxide Bifilms in Investment Cast Superalloy IN100 Parts I and II”*. Metall Mater Trans A 48, 5151–5153 (2017). https://doi.org/10.1007/s11661-017-4223-6
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-017-4223-6