Abstract
A novel UV-curable oligmer 1,4-cyclohexanedimethanol glycidyl ether acrylate (CHDMGEA) was synthesized by utilizing 1,4-cyclohexanedimethanol glycidyl ether (CHDMGE) and acrylic acid (AA) as starting materials, triphenyl phosphine as catalyst and p-hydroxyanisole as inhibitor. The optimum synthetic conditions were that the concentration of triphenyl phosphine was 0.90% of reactants by weight, the concentration of p-hydroxyanisole was 0.20% of reactants by weight, the reaction temperature was 90–100 °C, and the molar ratio of CHDMGE to AA was 0.5:1.1. The experimental results show that CHDMGEA is a kind of good UV-curable oligmer. The impact resistance of the UV-cured films with CHDMGEA as oligmer to prepare UV-curing coating was superior to that of the UV-cured films with bisphenol A diglycidyl ether diacrylate (BPGEA) as oligmer to prepare UV-curing coating.
Similar content being viewed by others
References
Masamitsu Shirai. Reworkable UV Curing Materials [J]. Prog. Org. Coat, 2007, 58: 158–165
sangermano M, lak N, Malucelli G, et al. UV-curing and Characterization of Polymer-clay Nanocoatings by Dispersion of Acrylatefuntionalized Organoclays [J]. Prog. Org. Coat, 2008, 61: 89–94
HUANG Biwu, CHEN Weiqing, YANG Zhihong, et al. Synthesis of a Novel UV-curable Prepolymer Hexanediol Diglycidyl Ether Diacrylate and Its Cured Film Tensile Property[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26(1):4–9
Wang F, Hu JQ, Tu WP. Study on Microstructure of UV-curable Polyurethane Acrylate Films [J]. Prog. Org. Coat, 2008, 62: 245–250
Güay Bayramoğlu, M Vezir Kahraman, Nilhan Kayaman-Apohan, et al. Synthesis and Characterization of UV-curable Dual Hybrid Oligomers Based on Epoxy Acrylate Containing Pendant Alkoxysilane Groups[J]. Prog. Org. Coat, 2006, 57: 50–55
LIU Hai-tao, MO Jian-hua, HUANG Xiao-mao. Research on the Mechanical of Accelerator for Photocurable Resin in 3D Printing[J]. Journal of Donghua University (Eng. Ed.), 2009, 26(1):16–19
Ferry PW Melchels, Jan Feijen, Dirk W Grijpma. A Review on Stereolithography and Its Applications in Biomedical Engineering[J]. Biomaterials, 2010, 31(24): 6 121–6 130
Salmoria GV, Klauss P, Pires ATN, et al. Investigations on Cure Kinetics and Thermal Degradation of Stereolithography RenshapeTM5260 Photosensitive Resin[J]. Polym. Test., 2008, 27: 698–704
Salmoria GV, Ahrens CH, Beal VE, et al. Evaluation of Post-curing and Laser Manufacturing Parameters on the Properties of SOMOS 7110 Photosensitive Resin Used in Stereolithography[J]. Mater. Des., 2009, 30: 758–763
Decker C, Moussa K. Kinetic Study of Light-induced Polymerization by Real-time UV and IR Spectroscopy [J]. J. Polym. Sci., Polym. Chem., 1993, 30(5):913–928
Pappas SP. UV-curing Science and Technology [M]. New York: Plenum Press, 1992, 64–71
Crivello JV, Ortiz RA. Synthesis of Epoxy Monomers That undergo Synergistic Photopolymerization by a Radical-induced Cationic Mechanism [J]. J. Polym. Chem., 2001, 39(20): 3 578–3 592
Decker C, Thi Viet TN, Thi HP. Photoinitiated Cationic Polymerization of Epoxides[J]. Polym Int, 2001, 50(9): 986–997
Kumar V, Bhardwaj YK, Goel NK, et al. Coating Characteristics of Electron Beam Cured Bisphenol A Diglycidyl Ether Diacrylate-co-Aliphatic Urethane Diacrylate Resins [J]. Surf Coat Technol, 2008, 202(21): 5 202–5 209
Young-Jun Park, Dong-Hyuk Lim, Hyun-Joong Kim, et al. UV- and Thermal-Curing Behaviors of Dual-curable Adhesives Based on Epoxy Acrylate Oligomers [J]. Int. J. Adhes., 2009, 29: 710–717
Crivello JV, Ortiz RA. Design and Synthesis of Highly Reactive Photopolymerizable Epoxy Monomers[J]. J. Polym. Sci. Polym. Chem., 2001, 39(14):2385–2395
Stanislovaityte E, Priola A, Sangermano M, et al. Cationic Photopolymerization of Bisphenol-A-based Vinyl Ether Systems[J]. Prog. Org. Coat, 2009, 65: 337–340
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the Natural Science Foundation of Jiangxi Province(20142BAB206029)
Rights and permissions
About this article
Cite this article
Huang, B., Deng, C., Xu, Q. et al. Synthesis of a novel UV-curable oligmer 1,4-cyclohexanedimethanol glycidyl ether acrylate and study on its UV-curing properties. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 29, 1283–1289 (2014). https://doi.org/10.1007/s11595-014-1082-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-014-1082-5