Abstract
The structure and properties of the glass-ceramics were tested with X-ray diffraction testing instrument, correlative software, and other modern testing means. Then the effect of Al2O3 content on internal stresses in CaO-Al2O3-SiO2 glass-ceramics was studied deeply. In order to study the relationship of Al2O3 to the residual stress of CaO-Al2O3-SiO2 glass-ceramics, X-ray diffraction “sin2 ψ” was used. The means utilized the x radial incidence produced from cathode radial tube, and took the space between crystals as measurement of strain. When the stresses produced, the space between crystals changed and the diffraction peak moved during Bragg diffraction. The magnitude of movement is related to the stresses. The experimental results show the residual stress is considerably high and Al2O3 can influence the mechanical properties of this material hugely.
Similar content being viewed by others
References
W Höland, G Beall. Glass-Ceramic Technology[J]. USA. American Ceramic Society, 2002, 88(7):1886–1891
Güngör S. Residual Stress Measurements in Fibre Reinforced Titanium Alloy Composites[J]. Acta Materialia, 2002, 50:2053–2073
Valmor R Mastelare, Edgar D Zanotto. Residual Stresses in a Soda-lime-silica Glass-ceramic[J]. Journal of Non-crystalline Solids, 1996, 194:297–304
O Durand, R Bisaro, C J Brierley, et al. Residual Stresses in Chemical Vapor Deposition Free-standing Diamond Films by X-ray Diffraction Analyses[J]. Materials Science and Engineering A, 2000, 228:217–222
Windischmann H, Gray KJ. Stress Measurement of CVD Diamond Films[J]. Diamond and Related Materials, 1995, 4:837–842
Vaidya RU, Rangaswamy P, Bourke MAM, et al. Measurement of Bulk Residual Stresses in Molybdenum Desilicide/Stainless Steel Joints Using Neutron Scattering[J]. Acta Mater., 1998, 46(6):2047–2061
Fitzpatrick ME, Hutchings MT, Withers PJ. The Determination of the Profile of Macrostress and Thermal Mismatch Stress Through an Al/SiCp Composite Plate from the Average Residual Strains Measured in Each Phase[J]. Physica B, 1995, 213:790–792
V K Marghussian, M H Dayi Niaki. Effects of Composition Changes on the Crystallization Behaviour and Properties of SiO2-Al2O3-CaO-MgO (Fe2O3-Na2O-K2O) Glass-ceramics[J]. Journal of European Ceramic Society, 1995, 15:343–348
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the Open Fund Project of Key Laboratory of New Processing Technology for Nonferrous Metal and Materials, Ministry of Education (Guangxi University)(No.063006-5C-22), the National Natural Science Foundation of China(50272043) and Key Technology R&D Program of China(2006BAJ02B00)
Rights and permissions
About this article
Cite this article
Xie, J., Long, X., Cheng, J. et al. Effect of Al2O3 content on residual stress and properties of CAS glass-ceramics. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 23, 889–892 (2008). https://doi.org/10.1007/s11595-007-6889-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-007-6889-x