The paper deals with melting of titanium and chromium metal powders in plasma of abnormal glow discharge which results in the formation of the hexagonal С36 Laves phase compound TiCr2 with a = 4.928 Å and c = 15.983 Å lattice parameters. The hydrogenation–dehydrogenation process is used to prepare the powder of C36 Laves phase intermetallic compound TiCr. The hydrogenation–dehydrogenation process is performed at 100°C, 2 atm hydrogen pressure and 30 min ageing followed by vacuum cooling. The prepared metal powder is characterized by rounded lamellar and coarse particles 6 ± 2 μm and 21 ± 7 μm in size, respectively.
Similar content being viewed by others
References
B. P. Tarasov, M. V. Lototskii, and V. A. Yartys’, Russ. J. Gen. Chem., 77, No. 4, 694–711 (2007). https://doi.org/10.1016/j.ijhydene.2014.12.093.
A. N. Perevezentsev, B. M. Andreev, V. K. Kapyshev, et al., Fiz. Elem. Chastits At. Yadra, 19, No. 6, 1386–1439 (1988). https://doi.org/10.1016/j.ijhydene.2013.07.073.
V. A. Yartys’, V. V. Burnasheva, and K. N. Semenenko, Russ. Chem. Rev., 52, No. 4, 299 (1983). https://doi.org/10.1016/j.jallcom.2013.02.019.
B. A. Kolachev, R. E. Shalin, and A. A. Il’in, Alloys for Hydrogen Accumulation [in Russian], Metallurgiya, Moscow (1995).
A. Kawasuso, H. Arashima, M., Maekawa, et al., J. Alloy. Compd., 486, 278–283 (2009). https://doi.org/10.1016/j.jallcom.2009.06.125.
Z. Chen, X. Xiao, L. Chen, et al., Int. J. Hydrogen Energ., 38, No. 29, 12803–12810 (2013).
Z. Hang, X. Xiao, S. Li, et al., J. Alloy. Compd., 529, 128–133 (2012).
N. Takeichi, H. T. Takeshita, H. Tanaka, et al., Mater. Lett., 57, No. 8, 1395–1399 (2003). https://doi.org/10.1016/S0167-577X(02)00995-3.
N. Takeichi, H. T. Takeshita, T. Oishi, et al., Mater. Trans., 43, No. 8, 2161–2164 (2002).
V. N. Verbetskii, “Synthesis and properties of multicomponent metal hydrides”, DSc Dissertation [in Russian], Moscow (1998).
V. V. Kotunov, D. A. Shumakov, V. S. Kraposhin, and K. O. Bazaleeva, Materialoved., No. 5, 23–27 (2007).
D. V. Sidelev, G. A. Bleikher, M. Bestetti, et al., Vacuum, 143, 479–485 (2017).
W. Baumann, A. Leineweber, and E. J. Mittemeijer, Intermetallics, 19, No. 4, 526–535 (2011).
G. A. Bleikher and V. P. Krivobokov, Surface Erosion of Solids under Powerful Beams of Charged Particles [in Russian], Nauka, Novosibirsk (2014).
L. Luo, C. Wu, S. Yang, et al., J. Alloy. Compd., 645, S178–S183 (2015).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Izvestiya Vysshikh Uchebnykh Zavedenii, Fizika, No. 10, pp. 172–177, October, 2018.
Rights and permissions
About this article
Cite this article
Murashkina, T.L., Syrtanov, M.S. & Laptev, R.S. Structural Changes in С36 Laves Phase Intermetallic Compound TiCr2 During Hydrogenation–Dehydrogenation Process. Russ Phys J 61, 1940–1946 (2019). https://doi.org/10.1007/s11182-019-01621-2
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11182-019-01621-2