Abstract
Electron microscopy was used to determine the nature of the structural changes in 45Kh26N33S2B2 alloy’ and the nature and chemical composition of proeutetoid constituents’ based on tests of samples of this material for long-term strength at high temperature.
Similar content being viewed by others
References
A. S. Oryshchenko’ Yu. A. Utkin’ and N. B. Odintsov’ “Effect of structure factor on mechanical properties of 45Kh26N33S2B2 alloy’” Tyazh. Mashinostr.’ No. 2’ 18–21 (2006).
V. V. Rybin’ A. S. Oryshchenko’ Yu. A. Utkin’ and N. B. Odintsov’ “Effect of alloying and production techniques for cast products on the mechanical properties and structure of heat-resistant steels and alloys’” Vopr. Materialoved.’ No. 3 (39)’ 5–19 (2004).
V. V. Rybin’ A. S. Rubtsov’ and E. V. Nesterova’ “Application of the single-reflection method in electron microscopy of dispersed phases’” Zavod. Labor.’ No. 5’ 21–26 (1982).
Author information
Authors and Affiliations
Additional information
__________
Translated from Metallurg’ No. 3’ pp. 61–66’ March’ 2008.
Rights and permissions
About this article
Cite this article
Oryshchenko, A.S., Nesterova, E.V. & Utkin, Y.A. Comparative analysis of structure and phase composition for alloys 45Kh26N33S2B2 and 45X25H20C2 after long-term exposure to high temperatures and static load. Metallurgist 52, 182–191 (2008). https://doi.org/10.1007/s11015-008-9029-8
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11015-008-9029-8