Abstract
Yttria-stabilized zirconia (YSZ) fiber was introduced as the reinforcement for porous YSZ ceramics fabricated by tert-butyl alcohol-based gel-casting process and pressureless sintering. Effect of YSZ fiber addition on the microstructure and properties of porous YSZ ceramics was studied systematically. Results showed that YSZ fiber obviously obstructed densification during the sintering process and therefore higher porosity could be achieved with the same solid loading of the initial slurry. Mean pore size regularly increased with increasing fiber addition. The reinforcing effect reached its optimum with 10 wt% YSZ fiber addition, yet decreased with increasing porosity. Fiber addition significantly changed the fracture mode of the porous ceramics from brittle to quasi-ductile with increasing fiber additions; fiber pull-out and crack deflection play major roles in the process. Compared with the porous ceramics without fibers, the thermal conductivity decreased a little. With improved mechanical and thermal properties, YSZ fiber-reinforced porous YSZ ceramics are more applicable in thermal insulation materials.
Similar content being viewed by others
References
Vassen R, Cao XQ, Tietz F, Basu D, Stover D (2000) J Am Ceram Soc 83:2023
Clarke DR, Phillpot SR (2005) Mater Today 8:22
Abbas A, Mohsen S, Akira K (2008) Mater Sci Eng A 478:264
Hass DD, Slifka AJ, Wadley HNG (2001) Acta Mater 49:973
Saremi M, Afrasiabi A, Kobayashi A (2008) Surf Coat Technol 202:3233
Lima RS, Marple BR (2008) Mater Sci Eng A 485:182
Hamling BH, Schaffer PC (1972) Am Ceram Soc Bull 51:426
Hamling HC, Hamling BH (1984) Am Ceram Soc Bull 63:1016
Schlichting KW, Padture NP, Klemens PG (2001) J Mater Sci 36:3003. doi:10.1023/A:1017970924312.20
Chi W, Sampath S, Wang H (2008) J Am Ceram Soc 91:2636
Hu LF, Wang CA (2010) Ceram Int 36:1697
Robinson RC, Smialek JL (1999) J Am Ceram Soc 82:1817
Jacobson NS (1993) J Am Ceram Soc 76:3
Parthasarathy TA, Boakye E, Cinibulk MK, Petry MD (1999) J Am Ceram Soc 82:3575
Cinibulk MK, Parthasarathy TA, Keller KA, Mah T-I (2002) J Am Ceram Soc 85:2703
Levi CG, Yang JY, Dalgleish BJ, Zok FW, Evans AG (1998) J Am Ceram Soc 81:2077
Hu LF, Wang CA, Huang Y (2010) J Mater Sci 45:3242. doi:10.1007/s10853-010-4331-9
Rice RW (1993) J Mater Sci 28:2187. doi:10.1007/BF00367582
Rosen BW (1965) Mechanics of composite strengthening, fiber composite materials, Chapt 3. American Society of Metals, Metal Park
Holmquist M, Lundberg R, Sudre O, Razzell AG, Molliex L, Benoit J, Adlerborn J (2000) J Euro Ceram Soc 20:599
Simon RA (2005) Int J Appl Ceram Technol 2:141
Nait-Ali B, Haberko K, Vesteghem H, Absi J, Smith DS (2007) J Euro Ceram Soc 27:1345
Acknowledgements
The authors would like to thank the financial support from the National Natural Science Foundation of China (NSFC-No. 90816019, 51172119 and 51102140).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Dong, Y., Wang, CA. & Zhou, J. Effect of YSZ fiber addition on microstructure and properties of porous YSZ ceramics. J Mater Sci 47, 6326–6332 (2012). https://doi.org/10.1007/s10853-012-6555-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-012-6555-3