A range of phospho-tellurite glasses containing gadolinium was prepared and infrared absorption spectra were measured. Structural changes, as recognized by analyzing band shapes of IR spectra, revealed that Gd2O3 causes a higher extent of network polymerization as far as x ≤ 15 mol% because the conversion of [TeO4] to [TeO3] structural units is supported by the increase of metaphosphate structural groups. While for x between 20 and 30 mol% Gd2O3 show some drastic structural modifications which lead to the increase in the glass fragility. Thus the addition of V2O5 resulted in gradual depolymerization of the phosphate chains and formation of short phosphate units, which are linked to vanadium through P–O–V bonds. The formation of P–O–V bonds increases the cross-link between the phosphate chains and the bending mode of Te–O–Te or O–Te–O linkages.
Similar content being viewed by others
References
Ehrt D, Seeber W (1991) J Non-Cryst Solids 129:19. doi:https://doi.org/10.1016/0022-3093(91)90076-I
Weber MJ, Layne C, Saroyan R, Milan D (1976) Opt Commun 18:171. doi:https://doi.org/10.1016/0030-4018(76)90658-1
Federighi M, Massarek I, Trwoga PF (1993) IEEE Photon Technol Lett 5:227. doi:https://doi.org/10.1109/68.196013
Hattori K, Kitagawa T, Ohmori Y (1996) J Appl Phys 79:1238. doi:https://doi.org/10.1063/1.361017
Bouderbala M, Mohmoh H, Bahtat A, Bahtat M, Ouchetto M, Druetta M et al (1999) J Non-Cryst Solids 259:23. doi:https://doi.org/10.1016/S0022-3093(99)00535-9
Shaw CM, Shelby JE (1988) Phys Chem Glasses 29:87
Donald IW (1993) J Mater Sci 28:2841. doi:https://doi.org/10.1007/BF00354689
Brow RK (1996) J Am Ceram Soc 76:913. doi:https://doi.org/10.1111/j.1151-2916.1993.tb05315.x
Brow RK, Arens CM, Yu X, Day DE (1994) Phys Chem Glasses 35:132
Weber MJ (1990) J Non-Cryst Solids 123:208. doi:https://doi.org/10.1016/0022-3093(90)90786-L
Fuxi G (1991) Optical and spectroscopic properties of glass. Springer-Shanghai Scientific and Technical Publications, Shangai, p 69
Jiang S, Myers M, Peyghambarian N (2000) J Non-Cryst Solids 263:3
Ajithkumar G, Gupta PK, Jose G, Unnikrishnan NV (2000) J Non-Cryst Solids 275:93. doi:https://doi.org/10.1016/S0022-3093(00)00244-1
Sekiya T, Mochida N, Ogawa S (1994) J Non-Cryst Solids 176:105. doi:https://doi.org/10.1016/0022-3093(94)90067-1
Shaltout I, Tang Y, Braunstein R, Abu-Elazm AM (1995) J Phys Chem Solids 56:141. doi:https://doi.org/10.1016/0022-3697(94)00150-2
Rada S, Culea E, Rus V, Pica M, Culea M (2008) J Mater Sci 43(10):3713. doi:https://doi.org/10.1007/s10853-008-2601-6
Anderson GW, Compton WD (1970) J Chem Phys 52:6166. doi:https://doi.org/10.1063/1.1672922
Janakirama Rao BHV (1965) J Am Ceram Soc 48:311. doi:https://doi.org/10.1111/j.1151-2916.1965.tb14748.x
El-Mallawany R (1989) Infrared Phys 29(2–4):781. doi:https://doi.org/10.1016/0020-0891(89)90125-5
El-Zaidia MM, Ammar AA, El-Mallawany R (1985) Phys Stat Sol 91(A):637
Culea E, Pop L, Simon V, Neumann M, Bratu I (2004) J Non-Cryst Solids 337:62. doi:https://doi.org/10.1016/j.jnoncrysol.2004.03.104
Pop L, Culea E, Bosca M, Neumann M, Muntean R, Pascuta P et al (2008) J Optoelectr Adv Mater 10(3):619
Rada S, Pascuta P, Bosca M, Culea M, Pop L, Culea E (2008) Vib Spectrosc. doi:https://doi.org/10.1016/j.vibspec.2007.12.005
Rada S, Culea E, Bosca M, Culea M, Muntean R, Pascuta P (2008) Vib Spectrosc. doi:https://doi.org/10.1016/j.vibspec.2008.04.001
Dimitriv Y, Dimitriv V, Arnaudov M, Topalov D (1983) J Non-Cryst Solids 57:147. doi:https://doi.org/10.1016/0022-3093(83)90417-9
Rada S, Culea M, Neumann M, Culea E (2008) Chem Phys Lett 460(1–3):196. doi:https://doi.org/10.1016/j.cplett.2008.05.088
Pascuta P, Pop L, Rada S, Bosca M, Culea E (2008) J Mater Sci Mater Electron 19(5):424. doi:https://doi.org/10.1007/s10854-007-9359-5
Lambson EF, Saunders GA, Bridge B, El-Mallawany R (1984) J Non-Cryst Solids 69:117. doi:https://doi.org/10.1016/0022-3093(84)90128-5
Sammet M, Bruckner R (1987) Glastech Ber 60:55
Dayanad C, Bhikshamaiah G, Tyagaraju VJ, Salagram M, Krishnamurthy ASR (1996) J Mater Sci 31:1945. doi:https://doi.org/10.1007/BF00356615
Almieda RM, Mackenize JD (1980) J Non-Cryst Solids 40:535. doi:https://doi.org/10.1016/0022-3093(80)90128-3
Corbridge DEC, Lowe JE (1954) J Chem Soc Part I:493. doi:https://doi.org/10.1039/jr9540000493
Rulmont A, Cahay R, Liegois-Duyckaerts M, Tarte P (1991) Eur J Solid State Inorg Chem 28:207
Tananaev LV (1985) Atlas of infrared spectra of phosphates and condensed phosphates. Izv. Nauka, Moscow
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Rada, S., Culea, M., Rada, M. et al. Effect of the introduction of vanadium pentaoxide in phospho-tellurite glasses containing gadolinium ions. J Mater Sci 43, 6122–6125 (2008). https://doi.org/10.1007/s10853-008-2939-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-008-2939-9