Summary
Foamed materials in general, and aluminium foams in particular, demonstrate a number of interesting properties due to their porous structure, which makes them usable in a wide range of applications. The capability of absorbing the impact energy is one of the most interesting properties of foams. This paper studies the influence of chemical composition, density and shape of aluminium foams on energy absorption. Samples of aluminium foam were produced from an "Alulight" precursor. The ability of samples to absorb mechanical energy was estimated from the results of compression tests. Tests were carried out by a universal test machine. During tests, the sample "force–elongation" diagram was written down. Test results showed that aluminium foams have good energy absorption and the capability of absorption decreases with the density of foam. Alulight AlMgSi 0.6 TiH2-0.4 foam can absorb more energy than Alulight AlSi 10 TiH2-0.8 foam.
Summary
Schaumstoffe im Allgemeinen und Aluminiumschäume im Besonderen zeigen zahlreiche interessante Eigenschaften wegen ihrer porösen Struktur und haben breite Anwendungen. Das Energieabsorptionsvermögen gehört zu den interessantesten Eigenschaften des Schaumes. In der vorliegenden Arbeit wurde der Einfluss der chemischen Zusammensetzung, der Dichte und der Form von Aluminiumschaum auf die Energieabsorption untersucht. Die Probestücke wurden durch das "Alulight"-Verfahren hergestellt. Das Energieabsorptionsvermögen der Probestücke wurde durch die Ergebnisse der Druckfestigkeitsprüfung abgeschätzt. Die Prüfungen wurden mit Hilfe der universellen Prüfmaschine durchgeführt. Bei der Druckfestigkeitsprüfung wurde das Spannungs-Dehnungs-Diagramm erhalten. Die Ergebnisse zeigten, dass die Aluminiumschäume ein gutes Energieabsorptionsvermögen haben. Das Energieabsorptionsvermögen nimmt mit der Schaumdichte ab. Der Alulight AlMgSi 0.6 TiH2-0.4-Schaum kann mehr Energie als der Alulight AlSi 10 TiH2-0.8-Schaum absorbieren.
Similar content being viewed by others
References
Simancik, F., H.P. Degischer and H. Wörz: Foamed Aluminium - Light Structural and Insulation Material. Euromat '95, Venice/Padua, Italy, 25.– 28.09.1995., Associazione Italiana di Metallurgia, Milan, 1995
http://www.alulight.com/en/downloads/alulight_datasheets_en2006.pdf
Degischer, H.P., and B. Kriszt: Handbook of Cellular Metals: Productions, Processing, Applications. Wiley-VCH, 2002
Yu, C.J., H.H. Eifert, J. Banhart and J. Baumeister: Metal Foaming by a Powder Metallurgy Method: Production, Properties and Applications. Materials Research Innovations (1998) 2: 181–188
Baumeister, J., J. Banhart and M. Weber: Aluminium Foams for Transport Industry. Materials & Design (1997) 18(4/6), 217–220
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Grilec, K., Marić, G. & Jakovljević, S. A Study On Energy Absorption of Aluminium Foam. Berg Huettenmaenn Monatsh 155, 231–234 (2010). https://doi.org/10.1007/s00501-010-0567-6
Issue Date:
DOI: https://doi.org/10.1007/s00501-010-0567-6