Abstract
The yield stress and fracture strain of irradiated ferritic alloys were measured using a small-punch test. The characteristics of hardening and intergranular embrittlement induced during neutron irradiation (0.94×1023 n m−2) at 395‡C in ferritic alloys doped with Cu, P and/or C were investigated. The effect of neutron irradiation on hardening was found to be greater in alloys doped with Cu and/or P than in C-containing alloys. The neutron irradiation produced a more substantial increase in the ductile-brittle transition temperature in the Cu-doped alloy compared with the other alloys and cause a significant decrease in the ductility of the Cu-doped alloy. Intergranular and transgranular fracture occurred in the alloys doped without and with C, respectively. The neutron irradiation did not alter the fracture mode.
Similar content being viewed by others
References
L. E. Steele, L. M. Davies, T. Ingham andM. Brumovsky, ASTM STP 870 (American Society for Testing and Materials, Philadelphia, PA, 1985) p. 863.
J. R. Hawthorne, ASTM STP 782 (American Society for Testing and Materials, Philadelphia, PA, 1982) p. 375.
S. Wood, R. G. Lott, J. A. Spitznagel, S. S. Brenner andM. K. Miller,Trans. Amer. Nucl. Soc. 44 (1983) 228.
L. E. Rehn andR. P. Okamoto, in “Phase Transformations During Irradiation”, edited by F. V. Nolfi Jr (Elsevier, New York, 1983) p. 247.
C. L. Briant andS. K. Banerji,Int. Met. Rev. 4 (1978) 163.
J. M. Baik, J. Kameda andO. Buck, ASTM STP 888 (1986) p. 92.
J. Kameda andA. J. Bevolo,Acta Metall., submitted.
X. Mao, T. Shoji andH. Takahashi,J. Test. Eval. 15 (1987) 30.
X. Mao andH. Takahashi,J. Nucl. Mater. 150 (1987) 42.
H. Kimura, H. Matsui, A. Kimura, T. Kimura andK. Oguri, in “Hydrogen Effects in Metals”, edited by I. M. Bernstein and A. W. Thompson (Metallurgical Society of AIME, Warrendale, PA, 1981) p. 191.
H. Wagenblast andA. C. Damask,J. Phys. Chem. Solids 23 (1962) 211.
K. Abiko, S. Suzuki andH. Kimura,Trans. Jpn Inst. Metals 23 (1982) 43.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mao, X., Kameda, J. Small-punch technique for measurement of material degradation of irradiated ferritic alloys. J Mater Sci 26, 2436–2440 (1991). https://doi.org/10.1007/BF01130192
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01130192