Abstract
The influence of laser surface alloying (LSA) with niobium (Nb) on the corrosion and mechanical properties of Zircaloy-4 was examined by potentiodynamic polarization testing in a chloride solution at 80°C and microhardness testing. The results are discussed with the structural and compositional variations in the LSA layer determined by X-ray diffraction (XRD), a scanning electron microscope (SEM) and a wavelength dispersive spectrometer (WDS). The LSA on Zircaloy-4 precoated with Nb produced a Nb-alloyed layer 200~300 µrn thick with 1.3~2.5 wt.% Nb, depending on the laser beam power. The alloyed layer was composed of a mixed structure of α-Zr and β-Zr phases with the (β-Zr phase increasing with the Nb content in the alloyed layer. The LSA with Nb increased the microhardness of Zircaloy-4, which was attributed primarily to the grain-size refinement of rapid cooling and, also, to the solid solution hardening with Nb. The resistance to the localized corrosion of Zircaloy-4 in a chloride solution significantly improved through LSA with Nb, which was attributed to the combined effects of the fine rapidly cooled microstructure and to the Nb alloying.
Similar content being viewed by others
References
E. Hillner,Proc. Zirconium in the Nuclear Industry, ASTM STP 633 (eds., A. L. Lowe, Jr. and G. W. Parry), p. 211, ASTM, Philadelphia (1977).
E. H. Novendstern,Meetings on Fuel Performance, KEPCO/ KINS/Westinghouse, KAERI, Taejon (1994).
G. P. Sabol, G. R. Klip, M. G. Balfour and E. Roberts,Proc. 8th Int. Symp on Zirconium in the Nuclear Industry, ASTM STP 1023 (eds., L. F. P. Van Swan and C. M. Eucken), p. 227, ASTM, Philadelphia (1989).
A. V. Nikulina, V. A. Markelov, M. M. Peregud, Y. K. Bibilashvili, V. A. Kotrekhov, A. F. Lositsky, N. V. Kuzmenko, Y. P. Shevnin, V. K. Shamardin, G. P. Kobylyansky, A. E. Novoselov,Proc. 11th Int. Symp on Zirconium in the Nuclear Industry, ASTM STP 1295 (eds., E. R. Bradley and G. P. Sabol), p. 785, ASTM, Philadelphia (1996).
R. J. Comstock, G. Schoenberger and G. P. Sabol,Proc. 11th Int. Symp on Zirconium in the Nuclear Industry, ASTM-STP 1295 (eds., E. R. Bradley and G. P. Sabol), p. 711, ASTM, Philadelphia (1996).
W. Kim, K. S. Jung, B. H. Choi, H. S. Kwon, S. J. Lee, J. G. Han and M. I. Guseva,Surf. Coat. Tech. 16-11, 595 (1995).
G. Tang, B. H. Choi, W. Kim, K. S. Jung, H. S. Kwon, S. J. Lee, J. H. Lee, T. Y. Song, D. H. Shon and J. G. Han,Surf. Coat. Tech. 89, 252 (1997).
S. J. Lee, H. S. Kwon, W. Kim and B. H. Choi,Mater. Sci. Eng. A 263, 23 (1999).
W. Reitz and J. Rawers,J. Mater. Sci. 27, 2437 (1992).
H. S. Kwon and S. J. Lee,A Study on the Improvement of Corrosion Resistance of Fuel Cladding Material by Surface Modification, p. 64, EESRI 97-015, EESR1 (1998).
J. P. Abriata and J. C. Bolcich,Bull. Alloy Phase Diagrams 3, 1710 (1982).
D. M. Follstatedt,Laser and Electwn-Beam Interactions with Solids: Proc. of the Materials Research Society Annual Meeting (eds., B. R. Appleton and G. K. Celler), p. 377, North Holland, New York (1982).
D. L. Piron,The Electrochemistry of Corrosion, p.164, NACE International, Houston, TX (1991).
J. Barnilkel, T. Seefeld, A. Emmel, E. Schubert and H. W. Bergmann,JOM 48, 29 (1996).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lee, SJ., Kwon, HS. & Kim*, JS. Analysis of microstructure and corrosion behavior of laser surface alloyed zircaloy-4 with niobium. Metals and Materials 6, 145–149 (2000). https://doi.org/10.1007/BF03026358
Issue Date:
DOI: https://doi.org/10.1007/BF03026358