Abstract
Portland cement was prepared by adding 1,3,5 and 6 wt% gypsum to Egyptian clinker. Each sample was mixed with 25wt% water and was hydrated at 1,3,7,28 and 90 days. The Mössbauer spectra showed two doublets, one represents the tetrahedral ferric ions and the other the octahedral ferric ions in addition to the iron metal. The degree of hydration was calculated from the spectra. The compressive strength test was performed. The time at which complete hydration takes place and the corresponding value of compressive strength were expected by calculations. The 5wt% sample showed the highest value of strength at the same degree of hydration. It showed also the lowest degree of hydration at the same value of compressive strength. It could be concluded that the optimum amount of gypsum addition should be 5 wt%, and the rate of hydration didn't affect by the different amount of gypsum.
Similar content being viewed by others
References
G. Pickett, Proc. Am. Concr. Inst. 44, (1948) 149.
K. Murakami, Proc. of the 5th Int. Symp. on Chem. of Cement, Tokyo, 1968, ed. (Cement Association of Japan, Tokyo, IV, 1969) p. 457.
A.A. Tabikh and M. Miller, J. Cem. and Conc. Res. 1 (1971) 663.
F.M. Lea, The Chemistry of Cement and concrete, 3rd. edition, (Edward Arnold Pub. Ltd., 1983) p. 308.
K.S. Harchand, R. Kumar, Vischwamittar and K. Chandra, Proc. Int. Conf. Appl. Mössbauer Effect, Indian National Science Acad., New Delhi, (1982) 296.
K.S. Harchand, Vischwamittar and K. Chandra, J. Cem. and Conc. Res. 10 (1980) 243.
F. Wittmann, J. Ind. Chem. Belg., 39 (1974) 693.
F. Wittmann, F. Pobell and Wiedemann, Z. Angew. Physik, 19 (1965) 281.
N.A. Eissa, M.Y. Hassaan, H.A. Sallam, S.H. Salah and S.A. Abo-El Enein TIZ-Fachberichte, 106, No. 9 (1982) 664.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hassaan, M.Y. Effect of gypsum on the strength development of portland cement by Mössbauer spectrometry. Hyperfine Interact 42, 1199–1202 (1988). https://doi.org/10.1007/BF02395606
Issue Date:
DOI: https://doi.org/10.1007/BF02395606