Abstract
Cadmium telluride (CdTe) is being widely used for passivating the HgCdTe p-n diode junction. Instead of CdTe, we tried a compositionally graded HgCdTe as a passivation layer that was formed by annealing an HgCdTe p-n junction in a Cd/Hg atmosphere. During annealing, Cd diffuses into HgCdTe from the Cd vapor, while Hg diffuses out from HgCdTe, forming compositionally graded HgCdTe at the surface. The Cd mole fraction at the surface was constant regardless of the annealing temperature in the range of 250–350°C. Capacitance versus voltage (C-V) curves for p-type HgCdTe that were passivated with compositionally graded HgCdTe formed by Cd/Hg annealing at 260°C showed a smaller flat-band voltage than the one passivated by thermally deposited CdTe, indicative of the better quality of the passivation. A long-wave infrared (LWIR) HgCdTe p-n junction diode passivated by compositionally graded HgCdTe showed about a one order of magnitude smaller RdA value than the one passivated by thermally deposited CdTe, confirming the effectiveness of the compositionally graded HgCdTe as a passivant.
Similar content being viewed by others
References
J.B Varesi, R.E. Bornfreund, A.C. Childs, W.A. Radford, K.D. Maranowski, J.M. Peterson, S.M. Johnson, L.M. Giegerich, T.J. de Lyon, and J.E. Jenson, J. Electron. Mater. 30, 566 (2001).
G. Brill, S. Velicu, P. Boieriu, Y. Chen, N.K. Dahr, T.S. Lee, Y. Selamet, and S. Sivananthan, J. Electron. Mater. 30, 717 (2001).
P. Mitra, F.A. Case, and M.B. Reine, J. Electron. Mater. 27, 510 (1998).
M.B. Reine, Infrared Detectors and Emitters: Materials and Devices, ed. P. Capper and C.T. Elliot (Boston, MA: Kluwer Academic Publishers, 2001), p. 313.
Y. Nemirovsky, N. Amir, and L. Djaloshinski, J. Electron. Mater. 24, 647 (1995).
Y. Nemirovsky, N. Amir, D. Goren, G. Asa, N. Mainzer, and E. Weiss, J. Electron. Mater. 24, 1161 (1995).
V. Ariel, V. Garber, D. Rosenfeld, G. Bahir, V. Richter, N. Mainzer, and A. Sher, J. Electron. Mater. 24, 1169 (1995).
C.A. Cockrum, D.R. Rhiger, and E.F. Schulte, U.S. patent 5,880,510 (1999).
J. Tunnicliffe, S.J.C. Irvine, O.D. Dosser, and J.B. Mullin, J. Cryst. Growth 68, 245 (1984).
S.H. Suh, J.H. Song, and S.W. Moon, J. Cryst. Growth 159, 1132 (1996).
J.H. Song, J.W. Kim, M.J. Park, J.S. Kim, K.W. Jung, and S.H. Suh, J. Cryst. Growth 184/185, 1232 (1998).
S.M. Sze, Physics of Semiconductor Devices, 2nd ed. (New York: John Wiley & Sons, 1981), p. 362.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
An, S.Y., Kim, J.S., Seo, D.W. et al. Passivation of HgCdTe p-n diode junction by compositionally graded HgCdTe formed by annealing in a Cd/Hg atmosphere. J. Electron. Mater. 31, 683–687 (2002). https://doi.org/10.1007/s11664-002-0219-z
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-002-0219-z