The plastic deformation of TiAl

Abstract

The deformation substructure of TiAl (Llo type ordered lattice) tested in compression, and the factors determining it were investigated. Two types of dislocations take part in the plas-tic deformation, namely a/2 [110] and a/2 [Oil]. The latter type will disorder the Llo super-lattice and therefore would be expected to move in pairs as superdislocations. Some obser-vations are essentially in agreement with the predictions, however the large proportion and morphology of a/2 [O1l] dislocations observed was unexpected. Twins of the [112] (111) type play an important role in the deformation of the alloy, and the early stages of their formation have been recorded. Finally, equi-Schmid factor lines have been constructed in an attempt to evaluate the importance of the sense of the applied stress on the deformation capability of the alloy.