A Dual Protection System for Heterostructured 3D CNT/CoSe2/C as High Areal Capacity Anode for Sodium Storage

Abstract 3D electrode design is normally opted for multiple advantages, however, instability/detachment of active material causes the pulverization and degradation of the structure, and ultimately poor cyclic stability. Here, a dually protected, highly compressible, and freestanding anode is presented for sodium‐ion batteries, where 3D carbon nanotube (CNT) sponge is decorated with homogeneously dispersed CoSe2 nanoparticles (NPs) which are protected under carbon overcoat (CNT/CoSe2/C). The 3D CNT sponge delivers enough space for high mass loading while providing high mechanical strength and faster conduction pathway among the NPs. The outer amorphous carbon overcoat controls the formation of solid electrolyte interphase film by avoiding direct contact of CoSe2 with electrolyte, accommodates large volume changes, and ultimately enhances the overall conductivity of cell and assists in transmitting electron to an external circuit. Moreover, the hybrid can be densified up to 11‐fold without affecting its microstructure that results in ultrahigh areal mass loading of 17.4 mg cm−2 and an areal capacity of 7.03 mAh cm−2 along with a high gravimetric capacity of 531 mAh g−1 at 100 mA g−1. Thus, compact and smart devices can be realized by this new electrode design for heavy‐duty commercial applications.

Moreover, mixing of the binder is required in traditional electrode preparation which decreases the overall conductivity of the electrode, increase cell resistance, and more profound to the volume variations. While these volume changes during repeated charging/discharging produce cracks and cause pulverization of electrode, hence bringing poor electrical contact of active material with the current collector or even detaching of the active materials from the current collector. [19,20] To resolve these issues various electrode architecture designs have been proposed using copper as current collector. [21] But, copper-based current collector electrodes may increase the overall volume and decrease the energy density of the device. To resolve this issue 3D, freestanding electrode configurations are very attractive, where the active materials are directly grown over 3D conductive scaffold alleviating the need of any dead additives. [22] Among various 3D conductive scaffolds, 3D carbon nanotube (CNT) sponges have found a lot of attention lately due to their ultrahigh porosity, conductivity, and well-interconnected 3D networks that not only provide high mass flow but also allow high mass loading in minimal area. [23][24][25][26] However, several challenges limit the application of 3D CNT sponge as conductive host; for instance: (i) the selected material should be compatible with the substrate (CNT sponge) and should have enough adsorption energy between the active material and substrate surface to guarantee the tight bond. [27] (ii) The solubility of two precursors (i.e., transition metal precursor and Se precursor) together is another big issue where poor solubility results in suspension/precipitation instead of the clear transparent solution. Poor solubility affects efficient infiltration of the precursor into the porous host (iii) inability of current approaches to load high amounts of active materials, (iv) detaching of active materials from CNT surface, and (v) poor control over direct electrode/electrolyte contact, and (vi) inhomogenous solid electrolyte interphase (SEI) film formation.
In this work, a novel dually protected electrode design was presented by fabricating CNT/CoSe 2 /C as an anode for SIB. The CoSe 2 nanoparticles (NPs) are decorated on each individual CNT which comprised a 3D network by simply two-step hydrothermal processes and then externally protected with amorphous carbon layers through a carbonization process. This unique composite greatly improves the Na + storage by harnessing the unique morphological and electronic features and surface properties. In particular, the highly conductive and compressible 3D CNT sponge provides multichannel and continuous pathways for ionic and electronic conduction, enough space, and porosity for high mass loading of active CoSe 2 and electrolyte infiltration as well as accommodate the volume expansion upon cycling. In contrast to conventional 3D electrodes, the external dual protection by carbon layers on individual CNT through the 3D matrix not only increases the overall conductivity but also buffers the volume expansion and controlled the SEI film thickness by preventing active material from direct contact with corrosive surrounding. By harnessing all the features, our hybrid is used as a freestanding electrode for SIBs (i.e., without dead elements such as binders, conductive additives, and current collector) and its fabrication is simpler and lighter. It delivers a high gravimetric capacity of 531 mAh g −1 at 100 mA g −1 after 100 cycles at high mass loading of 17.4 mg cm −2 which corresponds to the exceptional areal and volumetric capacity of >7 mAh cm −2 and 185.2 mAh cm −3 , respectively. Hence, by extending such a unique designing to other transition metal chalcogenides will take the electrochemical energy storage devices to the doorstep of commercial installations.
The carbon-coated 3D CNT/CoSe 2 hybrid was obtained via three steps as shown in Figure 1a; initially, in situ Co 3 O 4 NPs were uniformly decorated in a CNT sponge by a hydrothermal process, then, selenization of Co 3 O 4 into crystalline CoSe 2 , resulting in a 3D CoSe 2 @CNT hybrid without disturbing the morphology. The NaBH 4 was used to reduce the Se atoms into Se −2 anions and Co 3 O 4 into Co +2 cations, which then reacted at 180 °C to form CoSe 2 . [28][29][30][31] Finally, every individual CNT/CoSe 2 hybrid structure was coated with a carbon shell by carbonization using glucose at high temperature under a neutral atmosphere. During the cell assembly various hybrid sponges with an initial thickness h i were compressed into dense framework with a final thickness h c and directly used as freestanding anodes in the coin-type cell (Figure 1b). The areal mass loading (M a ) or density (d) of as-obtained electrode was determined by M a = dV/A = dh, where d, V, A, and h are the density, volume, base area, and thickness of the hybrid sponge, respectively. This indicates that the hybrid sponge having same percentage of active mass loading (CoSe 2 ) may proportionally increase the d and M a by simply choosing the CNT framework with larger h i and compressing it to fitting h c into coin cell. In this way, a densified framework was achieved and so enhanced the density, areal mass loading, and areal capacity. Figure S1 (Supporting Information) shows that the CNTs have a smooth surface with interconnected nanotubes networks as an ideal surface to decorate the active materials. Importantly, it is found that the decoration of Co 3 O 4 NPs did not bring any change in the 3D network of CNTs, however, rough surface confirms the formation of CNTs/Co 3 O 4 coreshell structure (Figure 2a). The in situ grafting of Co 3 O 4 NPs on the surface of CNT ensures enhanced contact between them. Upon conversion of Co 3 O 4 into CoSe 2 NPs on CNTs surface ( Figure 2b) and coating of the carbon shell on the CNT/CoSe 2 hybrid (Figure 2c), the 3D structural integrity is well-maintained pointing the high strength of 3D framework and carbon shell which has no effect on the morphology. Our hybrid morphology is unique and different from previously reported CNT/CoSe 2 composites, where a simple combination of CNT and CoSe 2 was obtained. The previous composites are in powder form and may aggregate during long electrochemical cycling. [32,33] However, in our hybrid, a core-double shell structure like morphology was obtained, which is homogenous in its nature and unique from reported literature. Besides our glucose-derived carbon shell was homogenously coated over the entire core-shell (CNT/CoSe 2 ) structure that has strong interaction with active material and beneficial for long cycling, while its thickness kept as low which allows faster ionic flow between electrode and electrolyte. [32,33] The transmission electron microscopy (TEM) analysis is used to determine the size of NPs (both Co 3 O 4 and CoSe 2 ), the diameter of nanotube in each hybrid, and thickness of carbon coating. Figure 2d,g reveals that fine Co 3 O 4 NPs having a size of ≈8 nm are well-adhered to the CNTs surface which are about 40 nm in diameter. The analysis of CNT/CoSe 2 revealed up to ≈25 nm increase in particle size due to the ripening of NPs under hydrothermal/calcination reactions as shown in Figure 2e,h. Figure 2f,i are showing the uniform coating of carbon on the surface of a hybrid with an average thickness of ≈4.0 nm. This carbon overcoat is uniformly covering every CoSe 2 NP forming an intertwined structure in which CoSe 2 NPs are tightly bound with 3D CNT networks. The new physical properties (such as high conductivity and mechanical strength) and synergistic effect between CoSe 2 and dual conductive network can be benefitted from no or low volume expansion, limited and stable SEI film, enhanced capacity, and structural integrity upon cycling. To verify the conversion of Co 3 O 4 to CoSe 2 , high-resolution TEM (HRTEM) images of CNT/CoSe 2 /C were obtained that represent the lattice spacing of ≈0.30 nm correspond to the (011) plane of CoSe 2 (Figure 3a). The selected area electron diffraction (SAED) pattern of CNT/ CoSe 2 /C is given in Figure 3b, which is well matched with the X-ray diffraction (XRD) measurements ( Figure 3c). XRD patterns were noted at each synthesis process and are presented in Figure S2 Figure S3 (Supporting Information) displays an energy-dispersive X-ray (EDX) mapping recorded with the help of scanning electron microscopy (SEM) for carbon, cobalt, and selenium where carbon concentrated at the core, and cobalt and selenium uniformly dispersed along the CNTs. The high-angle annular dark-field scanning TEM (HAADF-STEM) and corresponding EDX mappings are given in Figure 3d. An intense signal of carbon is observed in the middle, whereas the cobalt and selenium are concentrated over the CNT core across the shell. A weak signal of carbon is also observed across the CoSe 2 NPs because of the thinner carbon overcoat. Figure 4a displays the Raman spectrum of CNT, CNT/CoSe 2 , and CNT/CoSe 2 /C. In addition to the G-band (1583 cm −1 ) and D-band (1348 cm −1 ) coming from CNTs, the sharp peak at 188 cm −1 in both CNT/CoSe 2 and CNT/CoSe 2 /C corresponds to the SeSe stretching mode of cubic CoSe 2 , [34][35][36] whereas a small peak at about 672 cm −1 is associated with A 1g mode of CoSe 2 . [37] The valence states of different element in CNT/ CoSe 2 /C were evaluated using X-ray photoelectron spectroscopy (XPS) technique. The survey spectrum shows the peaks of Co, Se, C, and O indicating high purity of hybrid ( Figure S4, Supporting Information). The high-resolution spectrum of Co 2p region indicates binding energies of Co 2p 3/2 and Co 2p 1/2 located at 778.4 and 793.45 eV, respectively, confirming the Co 2+ cations in CoSe 2 ( Figure 4b). [34][35][36] Moreover, two peaks located at 780.83 and 796.2 eV correspond to CoO (a thin oxide layer on the surface) and one satellite peak at 801.13 eV was also observed in Co 2p region (Figure 4b). [38,39] Figure 4c shows the doublet of Se 3d, the peaks at 54.12 and 54.98 eV are related to Se 3d 5/2 and Se 3d 1/2 , respectively, well-consistent with metal selenide bond in CoSe 2 , while the peaks at  59.12 and 60.82 eV arise from Co 3p 3/2 and Co 3p 1/2 of Co 2+ . [40,41] The C 1s spectrum presented four subpeaks at 284.35, 284.77, 285.71, and 289.2 eV corresponding to CC, CC, CO, and OCO bonds, respectively, originating from CNTs core and amorphous carbon shell ( Figure 4d). [42] The thermogravimetric analysis (TGA) was carried out in the air to determine the exact amount of carbon in each composite at various stages (the procedure to calculate the carbon content in various hybrid sponges is provided in the Supporting Information). In CNT/Co 3 O 4 hybrid, a major weight loss occurred at between 300 and 500 °C, while for CNT/CoSe 2 hybrid, first, the weight increased till 400 °C due to oxidation of Se into SeO 2 and then decreased due to the removal of CNTs through oxidation ( Figure 4e). The final products mainly consisted of Co 3 O 4 and a small amount of residual Fe catalyst used to grow CNTs sponge in all composites. The calculated amount of carbon in CNT/Co 3 O 4 , CNT/CoSe 2 , and CNT/CoSe 2 /C is ≈35.07%, ≈11.84%, and 25.6%, respectively. The content of amorphous carbon coating in CNT/CoSe 2 /C hybrid is calculated to be 17.3%. Moreover, Brunauer-Emmett-Teller (BET) surface area and pore size distribution for various hybrids are shown in Figure 4f and Figure S5 (Supporting Information), respectively, and corresponding values are presented in Table S1 (Supporting Information). The CNT sponge used here has a higher surface area of 135.98 m 2 g −1 . [43] The lower surface area in case of CNT/CoSe 2 (50.24 m 2 g −1 ) is due to the homogenous coating of CoSe 2 NPs. However, increased surface area in case of CNT/CoSe 2 /C (74.02 m 2 g −1 ) is attributed to uniform encapsulating and intertwining of amorphous carbon, which is useful for the better contact between the electrolyte and active material, resulting in enhanced pseudocapacitive contribution in Na storage. [44] The cyclic voltammetry (CV) of the CNT/CoSe 2 /C at a scan rate of 0.30 mV s −1 in the voltage range of 0.01-3.00 V was recorded to evaluate its Na + storage capability (Figure 5a). In the first discharge process, one weak and one dominating cathodic peaks were observed at 1.03 and 0.52 V, respectively. The weak peak located at 1.03 V is associated with the intercalation process with the formation of Na x CoSe 2 intermediate, [45] whereas the strong peak at 0.52 V is attributed to the conversion Adv. Sci. 2020, 7,1902907  reaction from Na x CoSe 2 into metallic Co and Na 2 Se along with decomposition of electrolyte and formation of stable SEI film. [46][47][48] During the first charge process, a strong oxidation peak at 2.01 V was observed that ascribed to the recovery of CoSe 2 from the Co metal and Na 2 Se. [46][47][48] In the following cycles, two reduction peaks located at ≈0.43 and ≈0.97 V and one oxidation peak at ≈2.02 V were observed and almost remain steady and overlapped that reveals the stability and reversibility of the hybrid for the sodiation and desodiation processes (Figure 5a). The galvanostatic discharge/charge voltage profile curves of Adv. Sci. 2020, 7,1902907   CNT/CoSe 2 and CNT/CoSe 2 /C at a current density of 100 mA g −1 are displayed in Figure 5b. In the first discharge cycle, long voltage plateaus at 0.9 and 0.5 V were observed with a gradual voltage drop and consistent with CV findings. The CNT/CoSe 2 and CNT/CoSe 2 /C showed initial discharge and charge capacities (normalized to active mass of the electrodes) of 857 and 535, 952, and 544 mAh g −1 , respectively. Whereas normalized to the total mass of electrodes, the corresponding discharge and charge capacities would be 755 and 471, 708, and 404 mAh g −1 , respectively. The initial Coulombic efficiency of CNT/CoSe 2 and CNT/CoSe 2 /C was 62.47% and 57.09%, respectively. The slightly low Coulombic efficiency for the initial cycles in CNT/CoSe 2 /C is due to the formation of SEI film for thermodynamic stability of the cell and amorphous carbon coating which leads to a large surface area that causes irreversible loss of electrolyte for the first cycle. [49,50] However, a smaller difference between first and second charge capacities of CNT/CoSe 2 /C (5 mAh g −1 ) than CNT/CoSe 2 (37 mAh g −1 ) and so on for next cycles (Table S2, Supporting Information) was observed, highlighting the advantages of protective carbon coating.
The effect of carbon coating on the electrochemical Na + storage is further evaluated by a comparative study of cycling behaviors. It can be concluded that discharge capacity almost remains stable with increasing the cycle number in the CNT/CoSe 2 /C electrode, that is, 531 mAh g −1 at 100 mA g −1 after 100 cycles (Figure 5d). However, the specific capacity of CNT/CoSe 2 electrode gradually decreased with cycle number and retained only 223 mAh g −1 after 100 cycles, highlighting the significance of carbon overcoat in improving cyclic stability and control over SEI film with ongoing cycles. Theoretically, the gravimetric capacity (C g ) of the CNT/CoSe 2 and CNT/CoSe 2 /C electrodes can be calculated from the capacity of the pure CNT sponge (87.1 mAh g −1 ) at 100 mA g −1 in this work (Figure 5d), theoretical capacity of CoSe 2 (494.34 mAh g −1 ), and the percentage loading of CoSe 2 in CNT/CoSe 2 (88. 16 The gravimetric capacity obtained in CNT/CoSe 2 /C hybrid after 100 cycles at 100 mA g −1 normalized to total mass of electrode is larger (395.1 mAh g −1 ) than theoretical capacity of the electrode (390.05 mAh g −1 ) and this can be attributed to the synergistic effects in the hybrid structure. The rate performances of the CNT/CoSe 2 /C at different current densities ranging from 100 to 2400 mAh g −1 are further evaluated as presented in Figure 5e. The CNT/CoSe 2 /C anode exhibits high reversible capacities of 378.5 and 223.6 mAh g −1 even at high current rates of 1200 and 2400 mAh g −1 , respectively. Interestingly, as the currents were reversibly changed from 2400 to 1200, 600, 300, and 100 mA g −1 , the discharge capacities were fully recovered to 223.6, 348, 486, 560, and 609 mAh g −1 , respectively. Further, Figure 5f   the long cyclic stability of the CNT/CoSe 2 /C at 500 mA g −1 and the discharge capacity of 396 mAh g −1 is still maintained after 300 cycles. The discharging/charging curves at 500 mA g −1 of various cycles are provided in Figure S7a (Supporting Information), which clearly shows similar behavior regardless of number of time electrode is charged or discharged. We have also calculated the Coulombic efficiency of our CNT/CoSe 2 /C sponge. It is low in initial cycles mainly due to amorphous carbon coating due to irreversible Na ions in initial cycles because of formation of SEI film. However, after few cycles the Coulombic efficiency almost remains stable nearly equal to 100% ( Figure S7b, Supporting Information) that reveals the high reversibility of our hybrid sponge. These electrochemical results reveal the CNT/ CoSe 2 /C electrode has good reversibility and high cyclic stability due to the synergistic effect of multicomponent hybrid. The CNT frameworks provide 3D conductive pathways for efficient charge transport and faster electrolyte penetration due to the intrinsic porous structure of the sponge. The CoSe 2 provides sufficient active sites for Na + storage, whereas the carbon overcoat not only provides the mechanical robustness for volume expansion during long cycling but also prevents the corrosive surrounding between the active material (CoSe 2 ) and electrolyte.
In addition, areal or volumetric capacity is also important battery metrics for real applications like in compact devices and has gained less attention in previous studies for SIBs. Our CNT/CoSe 2 /C sponge can be densified by compaction and using this unique property, the high mass loading and areal capacity can be achieved. The hybrid sponges with various initial thicknesses of 2.1, 2.5, 2.8, 3.3, and 4.2 mm were compacted into coin cell electrodes corresponding to a compression ratio of 6.17, 7.24, 7.74, 9.7, and 11.02, respectively. It indicates that hybrid sponge consists of highly porous microstructure that after a high degree of compaction still, it can maintain desirable porosity (Figure 6a,b) like 11 times reduction in thickness corresponding to the compressive strain of ≈90%. The compressive stress-strain curves of CNT/CoSe 2 /C sponge indicate elastic deformation and good reversibility of the hybrid sponge after 30%, 60%, and 90% compressive strain (Figure 6c). During the compressive unidirectional stress, the base area and side size of the hybrid sponge did not change, showing that close stacking of nanotubes and decrease of inherent porosity of the sponge are responsible for the reduction of thickness.
The mechanism of areal capacity for Na + storage with different mass loading of 4.  Figure 6f and Figure S8 (Supporting Information). The highest thickness sponge (4.2 mm) anode resulted in higher density, areal mass loading, and areal capacity (Figure 6f). We can pack the sponges with more thickness into the cells during assembling to further enhance the mass loading and density. But, indiscriminate packing might consequence the capacity fading and poor cyclic stability. [51] Therefore, the areal capacity of a compressible electrode could be tuned by selecting the appropriate initial thickness to reveal an anticipated mass loading. To the best of our knowledge, this mass loading and areal capacity for SIBs achieved in our CNT/CoSe 2 /C hybrid sponge are much higher compared with reported literature as shown in Figure 6g and presented in Table 1. This enhanced areal capacity is ascribed to the high surface area, porosity, and dense compaction of hybrid sponge, which on compression can load more mass in small area and consequently enhance the areal capacity.
Moreover, the volumetric capacity (Q v ) of CNT/CoSe 2 /C hybrid sponge was also computed using the formula  Figure S9b (Supporting Information) indicates that high volumetric capacity and density would be achieved by using initial larger sponge thickness. Additionally, we have also added some published results on the volumetric capacity comparison in particular and results are summarized in Table S3 (Supporting  Information). It is obvious from the table that our volumetric capacity (185.2 mAh cm −3 ) is higher than most of the reported literature values and this is ascribed to higher tap density of hybrid sponge (Table S3, Supporting Information). However, some reported electrodes also showed higher volumetric capacity than our CNT/CoSe 2 /C electrode because of larger thickness of our electrode (0.34-0.38 mm) to maintain high stability by providing continuous pathway for mass flow.
The electrochemical kinetics insights of the electrodes after Na + insertion were further investigated by CV at various scan rates and electrochemical impedance spectroscopy (EIS) analysis. Figure 7a shows the CV curves of the CNT/CoSe 2 /C electrode after 100 cycles at various scan rates. All CV curves almost show identical behavior and consist of three reductions and one oxidation peak. The relationship between the peak current (i) and voltage (v) scan rates is given as In Equation (3), the value of b is the most important parameter as explains the charge storage behavior (diffusion controlled if b ≤ 0.5 or pseudocapacitive if b ≥ 1) in the electrode material. The value of b was determined by the slope of Equation (3) [log(v) vs log (i)] and it is 0.78, 0.84, 0.89, and 0.64 for the peaks 1, 2, 3, and 4, respectively (Figure 7b). The value of b for all peaks is greater than 0.5 and near to 1 suggesting mixed behavior, i.e., diffusion controlled and pseudocapacitive. Such properties are useful for better electrochemical ion storage. [65,66] The exact pseudocapacitive and diffusion controlled contribution at a fixed scan rate can be determined by Equation (4) 1 2 where k 1 and k 2 are equation parameters and their values can be determined by the slope and intercept of Figure S10 (Supporting Information) (iv− 1/2 vs v 1/2 ). The fraction of capacitive behavior is provided by the quantity k 1 (v) while diffusion controlled behavior is provided by the term k 2 (v 1/2 ). Figure 7c shows the trend of measured pseudocapacitive behavior that increases with increasing the scan rate. In addition, at a scan rate of 0.3 mV s −1 pseudocapacitive contribution is provided by the shaded region in Figure 7d. Furthermore, the effect of carbon coating in the compo sites was also evaluated using EIS analysis after battery testing. Nyquist plots of the CNT/CoSe 2 and CNT/CoSe 2 /C battery electrodes after 30 cycles as an anode of SIB are shown in Figure 7e, which delineate that R ct of the CNT/CoSe 2 electrode is higher than the CNT/CoSe 2 /C electrode (Table S3, Supporting Information). This indicates the continuous formation of SEI and the lack of electronic conductivity on the broken NPs surface during insertion/de-insertion in case of CNT/CoSe 2 , resulting in poor cycling life. The circuit diagram to fit the EIS data is drawn and presented in Figure S11 (Supporting Information). Typically, R s , CPE-1, and R f show the ohmic resistance of the electrolyte, constant phase element (CPE), and SEI layer resistance, respectively, in the low frequency region. R ct and CPE-2 are attributed to charge transfer resistance and CPE of the electrolyte/electrode interface, respectively, whereas Z w presents the sodium-ion Adv. Sci. 2020, 7, 1902907 Figure 6. Mechanical and electrochemical tests for CNT/CoSe 2 /C electrodes with various mass loadings: a) Photos of compressible test at original, pressed, and after released states. b) SEM image of compacted CNT/CoSe 2 /C with porous networks. c) Compressive stress-strain curves at different strain = 30%, 60%, and 90%. d,e) The first discharge/charge curves and areal capacity versus cycle number of hybrid sponge anodes with various mass loadings at 100 mA g −1 , respectively. f) The relationship between areal capacities of hybrid sponges with different areal mass loadings. g) Literature survey of areal performance metrics of some representative SIB anodes. diffusion process in low frequency region. In this region, the Na + diffusivity (D Na ) of the electrodes can be calculated using Equation (5) /2 Na 2 2 2 4 4 Na In Equation (5), R, T, A, n, F, C Na , and σ ω are the universal gas constant, absolute temperature, the surface area of the electrode, number of electron transfer during oxidation, Faraday's constant, molar concentration of Na + in the electrolyte (moles per cubic centimeter), and Warburg factor, respectively. All the terms used in Equation (5) are constant except σ ω which can be obtained from the slope of Z re versus ω −1/2 (Figure 7f), using Equation (6) Re re ct Using the preceding calculation, the σ ω and D Na values of two composites are listed in Table S3 (Supporting Information). For CNT/CoSe 2 /C electrode, the D Na value (2.3 × 10 −10 cm 2 s −1 ) is ≈2.76 times higher than that of CNT/CoSe 2 (8.33 × 10 −11 cm 2 s −1 ), respectively. The EIS result in the high and low frequency region of the Nyquist plot shows that both the electronic conductivity and ionic diffusivity would significantly affect the electrochemical performance of CNT/CoSe 2 /C-based electrodes. Without carbon overcoat on the NPs, the electronic conductivity and ionic transport are lower, consequently lower the electrochemical performance.
Adv. Sci. 2020, 7,1902907   We further investigated the structural analysis of CNT/CoSe 2 /C electrodes after battery testing. CoSe 2 NPs are still tightly deposited on CNT and the original morphology of the hybrid is maintained ( Figure S12a,b, Supporting Information). From Figure S12c (Supporting Information), C-overcoat and CoSe 2 NPs with the size of ≈25-30 nm coated on CNT can be clearly seen without agglomeration of NPs. HRTEM reveals that CoSe 2 have transformed into amorphous after long battery cycling ( Figure S12, Supporting Information). The repeated insertion-extraction of Na + in the active materials may turn the highly crystalline structure into amorphous that improved the electrochemical process. [43] In summary, a dual protection strategy is applied on CNT/ CoSe 2 /C electrode to achieve high cyclic stability, mass loading, and areal capacity. The Co 3 O 4 NPs grafted onto CNT are converted into CoSe 2 using safe and environmental friendly hydrothermal/calcination process with core-shell structure (CNT/CoSe 2 ) and then intertwined with ≈4 nm thick carbon overcoat by carbonization approach. The CNT/CoSe 2 /C presented a high discharge capacity of 531 mAh g −1 at 100 mA g −1 after 100 cycles. Moreover, it was densified by compaction with preserving its 3D networks and morphology due to high inherent porosity of hybrid sponge. Using this approach a high areal capacity up to 7.04 mAh cm −2 corresponds to an ultrahigh areal loading (17.4 mg cm −2 ). The novel synthesis and improved areal capacity of the CNT/CoSe 2 /C sponge make it an appropriate anode material for practical energy storage devices.

Experimental Section
Information about the synthesis of CNT/Co 3 O 4 , used characterization tools, and electrochemical methods are provided in the Supporting Information.
Synthesis of CNT/CoSe 2 : The CNT/Co 3 O 4 was converted into CNT/CoSe 2 by novel solvothermal/calcination process. In a typical synthesis, 4.0 mmole NaBH 4 was first dissolved into 10 mL deionized (DI) water and then 2.0 mmole Se powder was mixed by magnetic stirring. Afterward, CNT/Co 3 O 4 sponge was immersed into the freshly prepared solution and then the solution containing CNT/Co 3 O 4 sponge transferred into a 20 mL Teflon lined autoclave for the solvothermal reaction at 180 °C for 10 h. After the reaction, the sponge was again washed with ethanol and DI water and then freeze-dried. Finally, to remove the Se impurity and attain a highly crystalline structure of CoSe 2 , the hybrid sponge was annealed at 400 °C for 2 h and obtained highly crystalline CNT/CoSe 2 sponge.
Synthesis of CNT/CoSe 2 /C: The CNT/CoSe 2 /C was obtained by the carbonization process. First, the as-synthesized CNT/CoSe 2 sponge was dipped into 1.0 m aqueous glucose solution and executed for hydrothermal reaction in an electric oven at 180 °C for 10 h. The glucosecoated CNT/CoSe 2 sponge was washed with ethanol and DI water to remove impurity. Finally, glucose-coated CNT/CoSe 2 sponge was carbonized by heat treatment at 450 °C for 2 h in the inert environment and the final product CNT/CoSe 2 /C was obtained.

Supporting Information
Supporting Information is available from the Wiley Online Library or from the author.