Surface Engineering and Design Strategy for Surface‐Amorphized TiO2@Graphene Hybrids for High Power Li‐Ion Battery Electrodes

Surface amorphization provides unprecedented opportunities for altering and tuning material properties. Surface‐amorphized TiO2@graphene synthesized using a designed low temperature‐phase transformation technique exhibits significantly improved rate capability compared to well‐crystallized TiO2@graphene and bare TiO2 electrodes. These improvements facilitates lithium‐ion transport in both insertion and extraction processes and enhance electrolyte absorption capability.

DOI: 10.1002/advs.201500027 materials may offer higher capacity and better stability relative to the well-crystallized phases. [ 9 ] Interestingly, very recent work has demonstrated that amorphous/disordered materials may form percolation pathways via the opening of active diffusion channels, which could not only potentially facilitate ionic and electronic diffusion, but also enhance mass transport within these phases. [ 10 ] The Li-ion diffusion in amorphous materials proceeds more rapidly than in crystalline materials with similar particle size and morphology. [ 9,11 ] For instance, Siegel et al. have shown that the ionic conductivity of amorphous Li 2 O 2 is 2 × 10 −7 S cm −1 , which is 12 orders of magnitude larger than that in the crystalline phase. [ 12 ] In addition, defects induced by amorphous phases, such as dangling bonds and oxygen vacancies, typically lead to unexpected electronic states in the band gap that result in improved electrical conductivity. [ 13 ] Once a certain limit is reached, however, a change in the opposite direction is inevitable. Samuelis et al. found that amorphous-rich material exceeding certain levels of oxygen vacancies is detrimental to the lithium-ion diffusivity because they represent defects that hinder the mobility of lithium ions. [ 14 ] Therefore, the approach of introducing amorphous phases requires well-designed surface microstructures and combination with other strategies to further improve the electrochemical performance.
Fortunately, surface-amorphization (SA) provides unprecedented opportunities for altering and tuning material properties. SA could facilitate lithium diffusion into the bulk materials and alter the electrochemical reactivity to Li, thus increasing the accessible volume to near-full capacity. Based on these considerations, we propose a robust hierarchical network architecture with anti-aggregation properties through the assembly of graphene and SA-TiO 2 , which provides (i) large surface area and electrolyte absorption capability compared with other nanostructures, leading to adequate electrode-electrolyte contact; (ii) lower Li + interfacial transfer resistance due to close packing of the TiO 2 and graphene, and (iii) improved electronic conductivity and rapid ion/electron transport pathways induced by the SA, which are of benefi t to the high power performance. Inspired by these unique properties of SA-TiO 2 , we can imagine that the lithium-ion storage properties of TiO 2 electrodes could be further optimized by combining a hierarchical network architecture and with the surface amorphization of TiO 2 .
Here, we report a unique SA-TiO 2 @graphene architecture with a remarkable high rate capability, achieved by coupling the advantages of the highly conductive network offered by graphene with the surface amorphization. The surface amorphization was achieved by a low temperature (65 °C) phase transition using titanium glycolate as precursor. The low temperature drives the Electrode materials with battery-like high capacity and capacitorlike rate performance are highly desirable, since they would signifi cantly advance next-generation energy storage technology. [ 1 ] TiO 2 has received increasing attention as an anode material for lithium-ion batteries (LIBs) due to its good reversible capacity and low volume expansion upon lithiation, as well as its low cost and safe lithiation potential. [ 2 ] The low lithium-ion mobility within the crystalline phase TiO 2 , however, together with its poor electrical conductivity, means that only a thin surface layer of the host material is available for Li intercalation at high rates. [ 3 ] These issues are still challenges that hinder the electrochemical performance of this material.
Several strategies have been proposed to address each of the issues mentioned above individually. The low lithiumion mobility has been addressed by (i) decreasing the length of the lithium-ion diffusion pathways, for example, by using mesoporous, [ 3 ] nanostructured, or nanosized materials; or by (ii) facilitating the lithium-ion mobility, for example, by using less dense structural phases. [ 4 ] On the other hand, the conductivity has been improved by (i) coating TiO 2 with carbon [ 5 ] or Al 2 O 3 , [ 6 ] or (ii) linking TiO 2 with carbon nanotubes (CNTs) or graphene or other conductive networks, [ 7 ] or (iii) doping the TiO 2 . Traditionally, electrode materials have been sought that have well-crystallized phases, so that nearly all high energydensity cathodes for rechargeable lithium batteries are wellcrystallized materials in which lithium and other cations occupy distinct sites. [ 8 ] This "ordering paradigm" may have led the community to overlook a large class of materials in which there are atomic arrangements with only short-range order that appear to exist in a random (disordered) fashion; some of these titanium glycolate to transform into anatase phase and allows a surface-amorphized layer to be generated under mild conditions during the phase transition. After that, a simple ultraviolet (UV)-assisted reduction technique was used to construct hybrid architectures combining SA-TiO 2 with graphene as complementary building blocks. The resulting SA-TiO 2 @graphene architecture offers the unique characteristics needed for high-power anode materials. As a consequence, the optimal SA-TiO 2 @graphene hybrid architecture exhibits substantial improvements in both cycling stability and rate capability. The composite electrode exhibits a high specifi c capacity of 103 mA h g −1 at a rate of 50 C, 9.3 times higher than that of the reference TiO 2 . It also shows superior cycling capacity (≈108 mA h g −1 ) over 1500 cycles at the high rate of 20 C, together with ≈100% Coulombic effi ciency, proving its excellent tolerance of ultrafast insertion and extraction of lithium ions for long-life LIBs.
In order to prepare surface-amorphized TiO 2 , a low temperature phase transformation method was used in our work, because it offers the possibility of better controlling the reaction pathways on the molecular level. [ 15 ] It has been reported that the synthesis of TiO 2 by conventional sol-gel methods is diffi cult to achieve, as the hydrolysis rates of the precursors are too fast, which, in turn, does not allow separation between the nucleation and growth stages. In order to overcome this problem, ethylene glycol (EG) was selected as a solvent as well as a reactant. Glycols are attractive, as when mixed with alkoxide, they are reactive enough to form glycolate precursors or mixed alkoxide/ glycolate derivatives displaying much lower hydrolysis rates.
They not only act as an oxygen-supplying agent for the metal oxide, but also strongly infl uence surface, particle size, morphology, and assembly properties. The slow hydrolysis rates, mainly a consequence of the moderate reactivity of the C-O bond, in combination with the stabilizing effect of the organic species, lead to the formation of low-crystallinity products that are often characterized by uniform particle morphologies and tunable crystallite sizes in the range of just a few nano meters. [ 15 ] Inspired by these advantages, uniform titanium glyco late spheres were prepared and chosen as precursor, because materials with a spherical morphology have high packing density and good particle mobility to form a compact electrode layer, and actually exhibit the optimal material morphology in conventional electrode fabrication. [ 16 ] Our investigation of the synthetic processes indicated that the reaction temperature was the most important factor, because it critically infl uences the crystallization and the surface microstructure of the product. If the temperature was too low (room temperature), no anatase phase or crystalline product could be obtained. If the reaction temperature was too high (above 120 °C), however, the rate of reaction and the crystallinity of the product were high, and there was no surface-amorphized layer generated under these conditions. During the phase transformation, the density difference between titanium glycolate and TiO 2 results in cracks on the sphere's surface. Since the titanium glycolate spheres have low density, and the spheres are quite loose, H 2 O can penetrate through the cracks on the surface and enter the inner part of the titanium glycolate sphere ( Figure 1 a). Thus, hydrolysis also  occurs within the precursor spheres and leads to the formation of small TiO 2 particles in the surface layer. These small TiO 2 particles could act as nuclei for further growth. As the phase transformation proceeds, the TiO 2 particles grow gradually into interconnected nanoparticles. [ 17 ] We found that at relatively low temperatures (65 °C), the surfaces of the interconnected nanoparticles was constructed from even smaller primary TiO 2 particles with only short-range order and unbonded atoms. The hierarchical nanoporous structure of TiO 2 with a surface-amorphized layer is thus formed under mild conditions during the phase transformation.
After successful preparation of the SA-TiO 2 , we mixed it with graphene oxide (GO) in ethanol and subjected it to steady state UV irradiation. The total amount of GO used for assembly with TiO 2 was 2.0 wt%. A change in color from ivory white to dark brown can be observed as the reduction of GO proceeds ( Figure S1, Supporting Information). This color change has previously been suggested as refl ecting partial restoration of the network within the carbon structure and has been witnessed through chemical reduction of the GO sheets. Since TiO 2 particles carry surface charge in suspensions, they can be readily suspended in polar solvents. Thus, the SA-TiO 2 -GO composite becomes readily soluble in polar solvents. Upon UV irradiation of a de-aerated suspension of SA-TiO 2 , one observes charge separation. In the presence of ethanol, the holes are scavenged to produce ethoxy radicals, thus leaving the electrons to accumulate within the TiO 2 particles, as described in Reaction ( 1) . [ 18 ] The accumulated electrons then interact with the graphene oxide sheets and reduce the amounts of certain functional groups [Reaction ( 2) ]. In the present experiments, graphene oxide, with its extended epoxy and carboxylate groups, readily interacts with TiO 2 particles and undergoes reduction under UV irradiation. The surface hydroxyl groups of TiO 2 undergo charge transfer interaction with carboxylic acid functional groups on GO, and thus, the direct interaction between SA-TiO 2 and graphene provides the basis to obtain SA-TiO 2 @ graphene composite (1) TiO (e ) graphene oxide(GO) TiO graphene 2 2 (2) The morphology and microstructure of the SA-TiO 2 on graphene sheets were investigated by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). It is interesting to see from the TEM images ( Figure 2 a,b) that the nanospheres consist of closely interconnected nanoparticles forming a mesoporous network of TiO 2 , where the uniform TiO 2 nanospheres have a size of ≈100 nm. This sort of porous structure could also offer excellent capability to accommodate strain and structural changes during battery cycling. The corresponding selected area electron diffraction (SAED) pattern (inset image in Figure 2 b) shows clear diffraction rings, and it, along with the EDS spectrum ( Figure S2, Supporting Information) recorded from the corresponding area, suggests the polycrystalline nature of the whole nanosphere, and matches well with tetragonal anatase. A high resolution TEM (HRTEM) image confi rms the crystalline features of the closely interconnected TiO 2 nanoparticles inside the nanospheres by clear lattice fringes (Figure 2 c, Figure S3, Supporting Information). The lattice fringes with a spacing of 3.5 Å can be assigned to the most stable and frequently observed anatase TiO 2 (101) planes, although it is interesting to fi nd from the HRTEM image (Figure 2 c) that the outer part of the nanoparticles consists of surface-amorphized structures forming an amorphous shell. The magnifi ed TEM image shows that the thickness of the amorphous shell in Figure 2 e,g is about 3.0 nm. TEM image of individual sphere ( Figure S3a, Supporting Information) shows the SA-TiO 2 nanoparticles were composed of numerous primary nanocrystals with sizes in the range of 5-6 nm. Due to the low crystallization temperature and nucleation rate, great deals of primary nanocrystals with poor crystallinity were produced fi rstly in the reaction solution. Moreover, these tiny TiO 2 nanocrystals have a large surface to volume ratio and high surface energy, which make them unstable and tend to spontaneous aggregation into larger spherical particles in terms of minimization of the total interfacial energy. A careful view of the individual nanosphere indicates that these tiny nanoparticles loosely contacted with each other, resulting in lots of small pores/channels between them, which was consist with the results of nitrogen isotherm adsorption-desorption curves, the N 2 hysteresis loop demonstrating the presence of mesopores formed by aggregation of primary particles and the pore size distribution (average pore size ≈7 nm). Compared to the C-TiO 2 solid sphere consisted of closely packed particles with size about 50 nm, the much smaller particle size and a large number of mesopores/channels should lead to high surface areas for the SA-TiO 2 . In addition, more gaseous molecules could be adsorbed on the oxygen vacancies/Ti 3+ after polarization with an end-on bound structure and thus lead to high adsorption capacity and then high surface area. [ 10b ] The structure diagram from the simulation of the corresponding surfaceamorphized TiO 2 shows that the amorphous shell could be constructed of TiO 2 particles with only short-range order and unbonded atoms, and these disordered structures not only provide more entrances for Li ions, but also offer plentiful surface oxygen vacancies, signifi cantly increasing the specifi c surface area and assisting the adsorption capability of the electrolyte (Figure 2 f). A thick and milky diffraction background can also be observed in the SAED pattern beside the TiO 2 diffraction rings, which suggests that the SA-TiO 2 contains amorphous or disordered phases, consistent with the HRTEM observations. It is well-known that graphene fabricated by the UV-assisted technique has restored sp 2 networks and multiple available oxygencentered surface groups, which will allow unifi ed connection between the GO and the exposed oxygen atoms at the surface of the TiO 2 nanoparticles. [ 18 ] The SEM images in Figure 2 d also clearly show that the uniform TiO 2 nanospheres with a size of ≈100 nm are well encapsulated by the graphene sheets.
The crystal structure and microstructure of the samples were further analyzed by X-ray diffraction (XRD). peaks of anatase TiO 2 , no obvious diffraction peak of graphene is observed for the SA-TiO 2 @graphene sample, suggesting that the stacking of the graphene sheets remains disordered. We further conducted Raman measurements ( Figure S4, Supporting Information). Two obvious carbon bands, the D band and G band peaks, could be observed for both samples. Compared to the crystallized-TiO 2 @graphene (C-TiO 2 @graphene) samples, a peak at around 148.7 cm −1 , corresponding to the characteristic vibrational modes of anatase with a large featureless background, was observed for the SA-TiO 2 @graphene samples, with the large background in the Raman spectra suggesting that a thin amorphous phase/layer possibly exists on the surface of the SA-TiO 2 @graphene. Nitrogen isotherm adsorption-desorption curves together, with the pore size distribution for the SA-TiO 2 @graphene, are presented in Figure 3 b. For SA-TiO 2 @graphene, a type IV isotherm is observed, which is characteristic of mesoporous materials. Based on the Barrett-Joyner-Halenda (BJH) equation, the main pore size (inset in Figure 3 b) in SA-TiO 2 @graphene is 8 nm. The specifi c surface area of SA-TiO 2 @graphene is 326 m 2 g −1 .
In order to further confi rm the existence of the amorphous surface layer of TiO 2 in the samples, electron paramagnetic resonance (EPR) measurements and X-ray photoelectron spectroscopy (XPS) were conducted to investigate the surface and physical properties of TiO 2 . Compared to the heat-treated (600 °C in argon) C-TiO 2 samples, the appearance of an intense signal for the SA-TiO 2 @graphene can be ascribed to oxygen vacancies, which may due to the single electron trapped on the oxygen vacancy states in the EPR spectra (Figure 3 c). Notably, the creation of surface-amorphized TiO 2 not only results in oxygen vacancy formation, but also creates Ti 3+ interstitials in the TiO 2 matrix. In both cases, Ti is in excess with respect to O, and they both decrease the optical band gap of TiO 2 . Moreover, oxygen vacancies are not only the most important defects in TiO 2 , but also the most prevalent defects in many oxides, which greatly affect their chemical and physical properties. We have also studied the surface chemical bonding and valence bands of the samples with XPS. The binding energies from the samples were calibrated with respect to the C 1s peak from the carbon tape at 284.8 eV. Ti 2p and O 1s XPS peaks confi rmed the formation of TiO 2 ( Figure S5, Supporting Information). The oxygen vacancies close to the surface lead to shifting of the core level of O 1s and the valence band to higher binding energies. The broad and asymmetric nature of the peak is ascribed to  the various coordinations of oxygen in the SA-TiO 2 . The O 1s XPS peak could be fi tted into three peaks. The lowest binding energy peak located at 530.4 eV can be assigned to the lattice oxygen species. The highest binding energy peak at 533.9 eV is attributed to the near-surface oxygen, such as from surface hydroxylation, adsorbed H 2 O. In addition, a new peak located at 532.2 eV is observed in the SA-TiO 2 sample, which can be assigned to oxygen vacancies. [ 19 ] There is no clear evidence, however, for Ti 3+ . This is because Ti 3+ is susceptible to oxidation by O 2 in air and cannot survive long. [ 20 ] The oxygen vacancies are more likely to be located in the disordered outer layer, considering that the crystalline phases are almost identical and large structural alteration was observed in this layer. The UV/ visible (UV/Vis) spectroscopy of SA-TiO 2 and SA-TiO 2 @graphene demonstrated higher absorbance over the full region (200-800 nm) than for the Degussa P25, and a steep increase in light absorbance is observed in both these two samples at wavelengths below 400 nm, which indicates that the photon trapping capacity of SA-TiO 2 was signifi cantly enhanced, so that it maintains a high level of absorbance throughout the entire region. The reason for the color change from white (TiO 2 ) to ivory white (SA-TiO 2 ) can be explained as follows: a surface-engineered amorphous TiO 2 nanoparticle consists of two phases (a crystalline TiO 2 nanocrystal as a core inside, and a highly disordered surface layer where dopants [oxygen/Ti 3+ vacancies] are introduced outside). Although an ensemble of single nanocrystals retains the benefi ts of crystalline TiO 2 structures, the introduction of disorder and dopant at their surface would enhance visible and infrared absorption, with the additional benefi t of carrier trapping. [ 10c ] UV/Vis spectroscopy was used to confi rm the presence of oxygen vacancies. It was reported that the SA-TiO 2 spectrum features an increase in absorption between 400 and 800 nm due to free electrons, local Ti 3+ centers (a band at 620 nm), and oxygen vacancies (bands at 1060, 441, and 486 nm). [ 4a ] From the UV/Vis refl ectance spectra of SA-TiO 2 (Figure 3 d), a signifi cant increase in the absorbance compared to Degussa P25 in the visible light region for SA-TiO 2 can be observed, which confi rms the presence of oxygen vacancies.
To demonstrate the effectiveness of the surface-amorphized structure of SA-TiO 2 @graphene in improving rate-capacity, the lithium-insertion/extraction properties of SA-TiO 2 @graphene as anode were investigated by galvanostatic charge-discharge measurements. Figure 4 a shows the discharge (Li + insertion) and charge (Li + extraction) curves of a SA-TiO 2 @graphene electrode at the rate of 0.5 C (84 mA g −1 ). In a voltage window of 1-3 V, the discharge and charge capacities of the 1st cycle are 332 and 273.4 mA h g −1 , respectively. Clearly, this electrode shows superior cyclic retention to 100 cycles. Both the SA-TiO 2 @graphene and the SA-TiO 2 are found to be effective in improving Li-storage, showing a greatly enhanced discharge capacity after 100 cycles (205.1 mA h g −1 for SA-TiO 2 @graphene, and 141.7 mA h g −1 for SA-TiO 2 ), while only 61.8 mA h g −1 was achieved with C-TiO 2 . In Figure 4 c and Figure S6, Supporting Information, the SA-TiO 2 @graphene showed the typical electrochemical characteristics of anatase TiO 2 , exhibiting cathodic insertion of lithium at 1.75 V and anodic extraction of lithium at 1.95 V versus Li/Li + . The better Li + storage performance of the SA-TiO 2 @ graphene in comparison with that of C-TiO 2 @graphene can be observed from the cyclic voltammograms (CVs) ( Figure S6, Supporting Information). The voltage difference between the anodic and cathodic peaks (Δ E p ) refl ects the degree of polarization of the electrode. SA-TiO 2 @graphene has a much lower Δ E p value than www.MaterialsViews.com www.advancedscience.com Adv. Sci. 2015, 2, 1500027   Figure 3. XRD patterns of a) SA-TiO 2 @graphene and b) SA-TiO 2 . b) Nitrogen adsorption and desorption isotherms (inset: pore size distribution) of SA-TiO 2 @graphene. c) EPR spectra for SA-TiO 2 @graphene and C-TiO 2 (C-TiO 2 heated in air, details in the Supporting Information). d) UV-vis diffuse refl ectance spectra of SA-TiO 2 @graphene, SA-TiO 2 , and commercial Degussa P25 TiO 2 as reference.
C-TiO 2 @graphene. Therefore, the SA-TiO 2 @graphene is less polarized and has faster electrochemical reaction kinetics. This result agrees well with the electrochemical performance results shown in Figure 4 b. The CV curves of both samples remained almost unchanged after three cycles, demonstrating that the electrochemical reaction was stable and reversible. More strikingly, with respect to the reference TiO 2 , the specifi c capacity of SA-TiO 2 @graphene is substantially increased at all investigated charge-discharge rates, as demonstrated in Figure 4 b,d. Figure 4 b and Figure S7, Supporting Information, illustrate the specifi c charge obtained at different C-rates (0.5, 1, 2, 5, 10, 20, and 50 C, equal to 0.084, 0.168, 0.336, 0.840, 1.680, 3.360, and 8.400 A g −1 , respectively) as a function of the number of cycles. For example, the specifi c capacity of SA-TiO 2 @graphene at the rate of 50 C is as high as 103 mA h g −1 , 9.3 times higher than that of the reference C-TiO 2 . Importantly, after the high rate measurements, the specifi c capacity of SA-TiO 2 @graphene at 0.5 C can recover to the initial value, indicating its high reversibility. It also shows superior cycling capacity (≈108 mA h g −1 ) over 1500 cycles at the high rate of 20 C, along with ≈100% Coulombic effi ciency, proving its excellent tolerance of ultrafast insertion and extraction of lithium ions for long-life LIBs.
In a control experiment, C-TiO 2 @graphene was synthesized following the same procedures as for the synthesis of the SA-TiO 2 @graphene and then heat-treated in air at 600 °C to eliminate the surface-amorphized layer. The capacity for C-TiO 2 @graphene is 139.7 mA h g −1 (Figure 4 a), which is lower than that of the SA-TiO 2 @graphene (205.1 mA h g −1 ) and higher than that of C-TiO 2 (61.8 mA h g −1 ). That is because the particle size and the surface-amorphized layer of TiO 2 are of great importance for its electrochemical performance. The distance from the surface to the core drastically affects the ability to store charge at high C-rates. Because the surface atomic arrangement affects the specifi c charge at moderate C-rates, for example, from 0.5 to 50 C, the effective diffusion length for lithium ions is 24 nm under the charge/discharge rate of 0.5 C, and 3.2 nm under 50 C. [ 21 ] The lithium-ion mobility also becomes extremely low for lithium-ion content higher than that of Li 0. 5   indeed be formed in ultrasmall TiO 2 as a result of the quantumsize confi nement effect. [ 22 ] In our work, the thickness of the surface layer is ≈3 nm. The amorphous-layer-induced defects such as dangling bonds and oxygen vacancies typically lead to unexpected electronic states in the band gap that result in improved electrical conductivity ( Figure S8, Supporting Information). The calculated band gaps for crystalline TiO 2 and amorphous TiO 2 are 3.2 and 1.0 eV, respectively. [ 13 ] The surface amorphous layer in our work is different from an amorphous structure with only poor crystallinity. [ 23 ] The surface amorphous layer with its narrow band gap (≈1.0 eV) has plenty of oxygen vacancies and Ti 3+ ions, which together with the crystalline structure inside (band gap, E g = 3.2 eV) induces an electric fi eld during the charge/discharge process to facilitate deeper charge diffusion within the materials ( Figure 5 ). We believe that the TiO 2 with different band gaps creates an electric fi eld effect for lithium storage that may occur in the deep region of TiO 2 and thus increases the capacity to some extent. Below the plateau of phase transformation from tetragonal to orthorhombic (≈1.75 V), a sloping curve appears, in which the capacity comes from the lithium-ion intercalation beyond Li 0.5 TiO 2 (Figure 4 d). The capacity beyond Li 0.5 TiO 2 for SA-TiO 2 @graphene is about 137.7 mA h g −1 , which is nearly double that of C-TiO 2 @graphene (60.6 mA h g −1 ).
The narrow band gap of the surface amorphous layer also improves the electronic conductivity and rapid ion/electron transport pathways, and it also has benefi ts for high power performance. Moreover, the amorphous layer with high surface area possesses better adsorption capability for ions and molecules to facilitate Li + transfer across the electrolyte/TiO 2 interface, due to the higher local concentration. In addition, the weak connections between the SA-TiO 2 nanospheres are responsible for the poor cycling and rate performance during lithium insertion/extraction processes. When the SA-TiO 2 nanospheres are well encapsulated by the graphene, however, using a simple UV-assisted reduction technique, the graphene provides an interconnected conductive network which significantly improves the cycling and rate performances. The excellent high-rate performance is attributed to the substantial decrease in charge-transfer resistance due to the unique structure of the SA-TiO 2 @graphene. [ 24 ] The stable cycling of an electrode has strict requirements in terms of structural stability at the particle level, because small changes in particle morphology could cause electrode-level cracking and failure. After 10 deep cycles at the current density of 336 mA g −1 , the morphology of the SA-TiO 2 @graphene was examined with SEM and there is no obvious structural change after cycling. As the SEM Figure 5. Summary of the enhanced high rate performance mechanism of the SA-TiO 2 @graphene in the Li battery system. The surface amorphous layer (Region A) with its narrow band gap ≈1.0 eV) has plenty of oxygen vacancies and Ti 3+ ions, which together with the crystalline structure inside (band gap, E g = 3.2 eV) (Region B) induces an electric fi eld during the charge/discharge process to facilitate deeper charge diffusion within the materials (Region C). In the meanwhile, the graphene matrix provides an effective and continuous electrically conducting network. The highly porous surface amorphous layer also helps in electrolyte absorption.  Figure S10d, Supporting Information, demonstrate, we can see a thin solid electrolyte interphase (SEI) fi lm on the sample surface after 10 cycles. The partially reversible SEI formation might also contribute to the enhanced capacity.
We have designed and successfully fabricated surface amorphized (SA)-TiO 2 @graphene composites. A thin amorphous TiO 2 layer was created on crystalline TiO 2 nanospheres under mild conditions and assembled with graphene via an UVassisted reduction technique. We evaluated the SA-TiO 2 @graphene as an electrode material for lithium-ion batteries and found that it exhibited greatly improved lithium insertion/extraction performance compared with crystalline TiO 2 . The optimal SA-TiO 2 @graphene hybrid architecture exhibits a substantial improvement in lithium specifi c capacity from 0.5 to 50 C. More strikingly, the specifi c capacity of the composite at the rate of 50 C is as high as 103 mA h g −1 , 9.3 times higher than that of the reference TiO 2 . We attributed the greatly enhanced lithium storage properties of the SA-TiO 2 @graphene nanocrystals to the lower lithium-ion diffusion and electronic conduction resistance, and better surface adsorption in the amorphous layer. These improvements benefi t from the electric fi eld introduced by the surface-amorphization within the nanocrystals, which leads to much lower lithium-ion diffusion resistance, facilitates its transport in both insertion and extraction processes, and also enhances the electrolyte absorption capability. This concept thus offers an innovative and general approach toward designing battery materials with better performance.

Supporting Information
Supporting Information is available from the Wiley Online Library or from the author.