The Effect of Si Morphology on Machinability of Al-Si Alloys

Many of the cast parts require some sort of machining like milling, drilling to be used as a finished product. In order to improve the wear properties of Al alloys, Si is added. The solubility of Si in Al is quite low and it has a crystallite type structure. It behaves as particulate metal matrix composite which makes it an attractive element. Thus, the wear and machinability properties of these type of alloys depend on the morphology of Si in the matrix. In this work, Sr was added to alter the morphology of Si in Al-7Si and Al-12Si. Cylindrical shaped samples were cast and machinability characteristics of Sr addition was studied. The relationship between microstructure and machinability was evaluated.

Al-Si Alaþýmlarýnda Si Morfolojisinin Ýþlenebilirliðe Etkisi

Birçok döküm yöntemi ile üretilen parçalar kalýptan çýkartýldýðý gibi kullanýlýrken bazýlarýnda torna, freze, matkap vb. yöntemlerle son iþleme tabi tutulurlar. Alüminyumun alaþýmlandýrýlmasýnda özellikle aþýnmaya karþý etkisinden dolayý Si ilavesi yapýlýr. Silisyum alüminyum içerisinde çok düþük bir çözünürlüðe sahiptir ve mikro yapýda kristalin olarak yer alýr. Týpký seramik katkýlý bir kompozit gibi davranýþ gösterir. Dolayýsýyla Al-Si alaþýmlarýnýn aþýnma ve iþlenebilirlik karakteristiði direk olarak Si morfolojisine baðlýdýr. Bu doðrultuda bu çalýþmada, ticari olarak kullanýlan Al-7Si ve Al-12Si alaþýmýna Sr modifikasyonu yapýlarak Si morfolojisi deðiþtirilmiþtir. Her iki alaþýmda da Sr ilavesi öncesi ve sonrasý olmak üzere silindirik numuneler dökülmüþ ve bu numuneler iþlenebilirlik testine tabi tutulmuþtur. Mikroyapýsal analizler ile iþlenebilirlik arasýndaki iliþki ortaya çýkartýlmýþtýr.