A study on the safety and efficacy of bovine bone-derived bone graft material(OCS-B)

Inorganic bovine bone mineral has been widely researched as bone substitution materials in orthopedic and oral and maxillofacial application. OCS-B(NIBEC, Korea) is newly-developed inorganic bovine bone mineral. The aim of this study is to evaluate the safety and efficacy of bovine bone-derived bone graft material(OCS-B).

Micro-structure of newly-developed inorganic bovine bone mineral(OCS-B) was analyzed by scanning electron microscope(SEM). Round cranial defects with eight mm diameter were made and filled with OCS-B in rabbits. OCS-B was inserted into femoral quadrant muscle in mouse. In scanning electron microscope, OCS-B was equal to natural hydroxyapatite. Rabbits were sacrificed at 2 weeks and 4 weeks after surgery and mice were sacrificed at 1 week and 2 weeks after surgery. Decalcified specimens were prepared and observed by microscope. In calvarial defects, osteoid and new bone were formed in the neighborhood of OCS-B at 2 weeks after surgery. And at 4 weeks after surgery osteoid and new bone bridge formed flourishingly. No inflammatory cells were seen on the surface of OCS-B at 1 week and 2 weeks in mouse experimental group.

It is concluded that newly-developed inorganic bovine bone mineral(OCS-B) is a flourishing bone-forming material and biocompatible material.