Effect of Geometry and Distribution of Inclusions on the VHCF Properties of a Metastable Austenitic Stainless Steel

Article Preview

Abstract:

The effect of inclusions on the VHCF properties of a metastable austenitic stainless steel in undeformed and predeformed condition was studied. The material contains an inhomogeneous distribution of elongated oxide inclusions. TEM investigations of foils extracted by means of FIB technique show that the stress concentration at the inclusions is compensated by plastic deformation in the austenite phase preventing internal crack initiation in the VHCF regime for the non-predeformed, i.e., almost martensite-free condition. The effect of the spatial distribution and geometry of the inclusions on the VHCF strength was systematically investigated for the predeformed condition. Samples were monotonically predeformed at -80°C resulting in a martensite content of about 60% and then fatigued in high frequency testing machines. Since mechanical components are in practice subjected to complex cyclic loading situations, samples were tested both parallel and transversal to the rolling direction, in order to cover a broad field of applications. The higher notch sensitivity of the martensite phase leads to internal crack initiation from inclusions supported by the formation of a fine granular area (FGA). The change in testing direction perpendicular to the rolling direction reduces the number of cycles to failure due to the increased stress intensity factor at inclusions which leads to internal crack initiation without the formation of a fine granular area. These findings are discussed on the basis of a detailed microstructural characterization of the material focusing on the effect of martensite content, the inclusion morphology with respect to the rolling direction and the load axis applied

You might also be interested in these eBooks

Info:

Periodical:

Advanced Materials Research (Volumes 891-892)

Pages:

440-445

Citation:

Online since:

March 2014

Export:

Price:

* - Corresponding Author

[1] P. Lukáŝ, L. Kunz, Specific features of high-cycle and ultra-high-cycle fatigue, Fatigue & Fract. Engng Mater Struct, 25 (2002) 747-753.

DOI: 10.1046/j.1460-2695.2002.00562.x

Google Scholar

[2] H. Mughrabi, On Multi-stage, fatigue life diagrams and the relevant life-controlling mechanisms in ultrahigh-cycle fatigue, Fatigue & Fract Engng Mater Struct, 25 (2002) 755-764.

DOI: 10.1046/j.1460-2695.2002.00550.x

Google Scholar

[3] C. Müller-Bollenhagen, M. Zimmermann, H. -J. Christ, Very high cycle fatigue behaviour of austenitic stainless steel and the effect of strain-induced martensite, Int. J. Fatigue, 32 (2010) 936-942.

DOI: 10.1016/j.ijfatigue.2009.05.007

Google Scholar

[4] A. Kolyshkin, A. Grigorescu, E. Kaufmann, M. Zimmermann and H. -J. Christ, Development of a probabilistic model for the prediction of fatigue life in the very high cycle fatigue (VHCF) range based on inclusion population, contribution to Fatigue (2014).

DOI: 10.4028/www.scientific.net/amr.891-892.1093

Google Scholar

[5] A. Grigorescu, C. Müller-Bollenhagen, P. Hilgendorff, M. Kübbeler, M. Zimmermann, C. -P. Fritzen, H. -J. Christ, Characterization and simulation of the damage accumulation in the very high cycle fatigue (VHCF) regime in a metastable austenitic stainless steel based on the resonant behavior, Proceedings of MS&T, Ohio (2011).

DOI: 10.1016/j.mspro.2014.06.185

Google Scholar

[6] J. Talonen, H. Hänninen, P. Nenonen, G. Pape, Effect of strain rate on the strain-induced γ→ α'-martensite transformation and mechanical properties of austenitic stainless steels, Metall. Mater. Trans. A, 36 (2005) 421-432.

DOI: 10.1007/s11661-005-0313-y

Google Scholar

[7] K. Spencer, K. T. Conlon, Y. Brechet, J. D. Embury, The strain-induced martensite transformation in austenitic stainless steels: part 2 effect of internal stresses on mechanical response, Mater. Sci. Tech., 25 (2009) 18-28.

DOI: 10.1179/174328408x295980

Google Scholar

[8] J.A. Rodríguez-Martínez, R. Pescib, A. Rusinekc, Experimental study on the martensitic transformation in AISI 304 steel sheets subjected to tension under wide ranges of strain rate at room temperature, Mater. Sci. Eng. A, 528 (2011) 5974-5982.

DOI: 10.1016/j.msea.2011.04.030

Google Scholar

[9] P. Hedström, L. E. Lindgren, J. Almer, U. Lienert, J. Bernier, M. Terner, M. Odén, Load partitioning and strain-induced martensite formation during tensile loading of a metastable austenitic stainless steel, Metall. Mater. Trans. A, 40 (2009).

DOI: 10.1007/s11661-009-9807-3

Google Scholar

[10] P. Grad, B. Reuscher, A. Brodyanski, M. Kopnarski and E. Kerscher, Mechanism of fatigue crack initiation and propagation in the very high cycle regime of high-strength steels, Scripta. Mater., 67 (2012) 838-841.

DOI: 10.1016/j.scriptamat.2012.07.049

Google Scholar

[11] T. Sakai, Review and prospects for current studies on very high cycle fatigue in metallic materials for machine structural use, J. Solid Mech. Mater. Eng., 3 (2009) 425-439.

DOI: 10.1299/jmmp.3.425

Google Scholar

[12] Y. Murakami, H. Matsunaga, The effect of hydrogen on fatigue properties of steels used for fuel cell system, Int. J. Fatigue, 28 (2006) 1509-1520.

DOI: 10.1016/j.ijfatigue.2005.06.059

Google Scholar