The Effect of Heat Treatment Temperature on Property and Structure of Ni Group Core-Shell Particles ER

Suo Kui Tan; Xiao Ping Song; Li Qiao; Hong Yan Guo; Song Ji; Hong Zhao

doi:10.4028/www.scientific.net/AMR.213.437

Paper Titles

Influence of Electromagnetic Stirring Parameters and Isothermal Extruding on Semi-Solid Forming Performance of ZA27 Alloys
p.414

Linear Static Response of Suspension Arm Based on Artificial Neural Network Technique
p.419

Production of Activated Carbon from Ligin: Optimization Using Response Surface Methodology
p.427

Biosorption of C. I. Reactive Red 2 by Immobilized Fungal Biomass
p.432

The Effect of Heat Treatment Temperature on Property and Structure of Ni Group Core-Shell Particles ER
p.437

Application of Imprinted Functionalized Silica Gel Sorbent for Selective Removal of Cadmium (II) from Industial Wastewaters
p.441

Analysis of Influence Factors on Anti-Rutting Performance of Fiber Asphalt Mastic and Fiber Asphalt Mixture
p.445

Manufacturing Process Planning to Evaluation on Failure Causes for Lithography Machine: Analytic Hierarchy Process
p.450

Using Data Envelopment Analysis to Measurement Patent Performance of Medical Instruments Industry
p.454

HomeAdvanced Materials ResearchAdvanced Materials Research Vol. 213The Effect of Heat Treatment Temperature on...

The Effect of Heat Treatment Temperature on Property and Structure of Ni Group Core-Shell Particles ER

Abstract:

By means of mechanical properties test and microstructure graph observation，the relationship of heat treatment temperature of core-shell Ni/TiO2 group particles with mechanical properties under different electric field has been researched .It is found that the FT-IR，XRD morphology of heat treatment at350°C is different from the one at100°C，the shear stress of same composition ER decreased with heat treatment temperature increasing. But the leakage current density of ER shows contrary result. That is because the leakage current density of ER decreased with the increasing heat treatment temperature.