Development of Silver-Coated Gold Nanoparticles and its Conjugation for Labeling on Lateral Flow Immunoassay

Siti Rabizah Makhsin; Khairunisak Abdul Razak; Rahmah Noordin

doi:10.4028/www.scientific.net/AMR.1024.273

Paper Titles

Effect of Sintering Duration on Pure PZT for Piezofan Application
p.255

Effect of Different Thickness of Core Layer on Tensile Properties of Laminated Natural Rubber Latex Film
p.259

Utilization of Sludge from Sidoarjo Mudflow for Zeolite Synthesis
p.263

Effect of Needle Punching Direction on Nonwoven Fiber Mat to the Mechanical Properties of Kenaf Reinforced Epoxy Composites Produced by Vacuum Assisted Resin Transfer Molding
p.267

Development of Silver-Coated Gold Nanoparticles and its Conjugation for Labeling on Lateral Flow Immunoassay
p.273

The Effect of Oxygen Precursor Concentration to the Iron Oxide Nanoparticles Properties for Lateral Flow Immunoassay Application
p.277

Crytallization and Properties of SiO₂-Al₂O₃-K₂O-ZrO₂ Glass-Ceramics for Dental Applications
p.281

The Design of Elastin-Like Polypeptides (ELPs) as a Nanoparticulate-Based Therapeutic and Diagnostic Imaging Agent
p.287

Loading and Unloading Properties of Encapsulated Methylene Blue in Silica Nanoparticles for Photodynamic Applications
p.292

HomeAdvanced Materials ResearchAdvanced Materials Research Vol. 1024Development of Silver-Coated Gold Nanoparticles...

Development of Silver-Coated Gold Nanoparticles and its Conjugation for Labeling on Lateral Flow Immunoassay

Abstract:

This work describes the formation of silver-coated gold nanoparticles (Ag-AuNPs) using the seeding-growth method. 15 nm AuNPs seeds were synthesized using the citrate reduction method. In the growth stage, the adding sequence of seeds, ascorbic acid (AA), gold chloride (HAuCl₄) and silver nitrate (AgNO₃) was explored. The effect AgNO₃ volume (20 mM) was varied at 0.10, 0.25, 0.50, 1.00, 1.25 and 1.50 ml. Morphology of Ag-AuNPs was observed using a Transmission Electron Microscope (TEM) while UV-Vis Spectrophotometer was used to study the concentration and absorption spectra of colloidal Ag-AuNPs. Zeta-sizer analysis was used to study the particle size distribution of Ag-AuNPs in colloidal form. In the growth stage, the optimum adding sequence was found by adding AA as a reducing agent into AuNPs seeds followed by the addition of HAuCl₄ and AgNO₃. This reshuffle sequence is chosen due to the presence of two absorbance peaks at 398 nm and 501 nm compared to others. From TEM images, increasing concentration of silver ions affected the optical properties, end size of Ag-AuNPs as well as raises the concentration of the colloids suspension. The biological properties of samples Ag-AuNPs (0.1 ml to 0.5 ml AgNO₃) were studied by performing the conjugation process between samples and antibody; goat anti-human IgA (GaHIgA). An additional washing process was required to perform conjugation for Ag-AuNPs in order to remove by-product or unreacted chemical produced during synthesis process. The Ag-AuNPs was successfully conjugated with GaHIgA and required a minimum concentration of antibody (9µg/ml) after washing process. In addition, the washed Ag-AuNPs also improved its binding capability with GaHIgA by giving higher intense signal when tested with lined Human IgA on the lateral flow immunoassay (LFI) compared to un-washed Ag-AuNPs.