Preparation of Lithium Niobate Powders by Mechanochemical Process

Ju Hua Luo

doi:10.4028/www.scientific.net/AMM.121-126.3401

Paper Titles

Operation Parameter Recorder for Construction Machinery Based on Embedded Technology
p.3381

Optimization Design on Ribbed Slab for Crossbeam of Heavy NC Gantry Moving Boring & Milling Machine
p.3386

Point-Line Meshing Gear Drive
p.3391

Prediction and Analysis for Chinese Machinery Manufacturing System Based on the ARMA
p.3396

Preparation of Lithium Niobate Powders by Mechanochemical Process
p.3401

Pressure Coordinated Control System of Regenerative Braking Based on Hardware of ABS for HEV
p.3406

Reliability-Based Sensitivity Design of Gear Pairs with Non-Gaussian Random Parameters
p.3411

Reseach on Back-Pressure Problems of the Twin-Scroll Compressors
p.3419

The Strategy Research and Application of Product Function Innovation
p.3426

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 121-126Preparation of Lithium Niobate Powders by...

Preparation of Lithium Niobate Powders by Mechanochemical Process

Abstract:

Lithium niobate powders were prepared by mechanochemical treatments using Li2CO3 and Nb2O5 as raw materials. Scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) were employed to evaluate the morphologies and structures of samples. The mechanism of LiNbO3 formation of the ground mixture samples was discussed. The crystal structure of mixture was collapsed into a disordered structure, which increased with increasing grinding time. At the same time, the specific surface area increase and the bond energy reduction of the mixture occurred. Consequently, high energy ball milling enables increase of the internal energy, reduction of the activation energy, and improvement of the uniform mixing stage, which resulted in direct formation of singal phase LiNbO3 at a low temperature (500°C). However, the temperature must reach 1200°C for the traditional method.