Next Article in Journal
The Application of Multi-Walled Carbon Nanotubes in Bone Tissue Repair Hybrid Scaffolds and the Effect on Cell Growth In Vitro
Next Article in Special Issue
Novel Oligo-Ester-Ether-Diol Prepared by Waste Poly(ethylene terephthalate) Glycolysis and Its Use in Preparing Thermally Stable and Flame Retardant Polyurethane Foam
Previous Article in Journal
Effect of Solvents on the Electrical and Morphological Characteristics of Polymer Solar Cells
Previous Article in Special Issue
Recent Advances in Bio-Based Flame Retardant Additives for Synthetic Polymeric Materials
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 11
Issue 2
10.3390/polym11020229
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
Erratum published on 19 April 2019, see Polymers 2019, 11(4), 724.
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Electrostatic-Interaction-Driven Assembly of Binary Hybrids towards Fire-Safe Epoxy Resin Nanocomposites

by
Lu Liu
1,2,†,
Wei Wang
3,4,†,
Yongqian Shi
1,*,
Libi Fu
5,
Lulu Xu
6 and
Bin Yu
4,*
1
College of Environment and Resources, Fuzhou University, 2 Xueyuan Road, Fuzhou 350116, China
2
Hefei Institute for Public Safety Research, Tsinghua University, 5999 Xiyou Road, Hefei, Anhui 230026, China
3
State Key Laboratory of Fire Science, University of Science and Technology of China, 96 Jinzhai Road, Anhui 230026, China
4
Department of Architecture and Civil Engineering, City University of Hong Kong, Tat Chee Avenue, Kowloon 999077, Hong Kong
5
College of Civil Engineering, Fuzhou University, 2 Xueyuan Road, Fuzhou 350116, China
6
School of Materials Science & Engineering, Nanyang Technological University, Singapore 639798, Singapore
*
Authors to whom correspondence should be addressed.
†
These authors contributed equally to this work (co-first author).
Polymers 2019, 11(2), 229; https://doi.org/10.3390/polym11020229
Submission received: 25 December 2018 / Revised: 25 January 2019 / Accepted: 27 January 2019 / Published: 1 February 2019
(This article belongs to the Special Issue Flame Retardancy of Polymeric Materials)
Browse Figures
Versions Notes

Abstract

:
Manganese dioxide (MnO2), as a promising green material, has recently attracted considerable attention of researchers from various fields. In this work, a facile method was introduced to prepare binary hybrids by fabricating three-dimensional (3D) zinc hydroxystannate (ZHS) cubes on two-dimensional (2D) MnO2 nanosheets towards excellent flame retardancy and toxic effluent elimination of epoxy (EP) resin. Microstructural analysis confirmed that the morphologies and structures of MnO2@ZHS binary hybrids were well characterized, implying the successful synthesis. Additionally, the morphological characterization indicated that MnO2@ZHS binary hybrids could achieve satisfactory interfacial interaction with the EP matrix and be well dispersed in nanocomposites. Cone calorimeter test suggested that MnO2@ZHS binary hybrids effectively suppressed the peak of heat release rate and total heat release of EP nanocomposites, performing better than MnO2 or ZHS alone. Condensed-phase analysis revealed that MnO2@ZHS binary hybrids could promote the char density and graphitization degree of char residues and thereby successfully retard the permeation of oxygen and flammable gases. Moreover, through the analysis of gas phase, it can be concluded that MnO2@ZHS binary hybrids could efficiently suppress the production of toxic gases during the degradation of EP nanocomposites. This work implies that the construction of 2D/3D binary hybrids with an interfacial interaction is an effective way to fabricate high-performance flame retardants for EP.

Graphical Abstract

1. Introduction

Epoxy resin (EP), one of the most important thermosetting polymers, has been widely used in the fields of furniture coatings [1], circuit boarding [2], aeronautical material [3], and so forth [4,5,6] in virtue of its excellent mechanical properties, outstanding optical property, glorious resistance to solvent and chemical corrosion, and high climate resistance. However, analogous to most other polymers, EP resin can be easily ignited and sharply spread, accompanied with large amounts of smoke and heat release. It is well known that smoke and toxic gases are the main reasons for death in fire accidents. Hence, to meet fire safety regulations and expand the use of EP in the fields that require flame resistance, a significant number of flame-retardant techniques for EP resins are developed. Some kinds of flame retardants have been gradually forbidden in most countries, due to toxic gases, such as hydrogen cyanide, contained in the pyrolysis products during the combustion process [7,8]. For instance, the most used brominated flame retardants often result in the formation of notorious pollutants, most notably, brominated and mixed halogenated dioxins [9,10]. Therefore, how to prepare green and effective flame retardants for EP remains a global topic for researchers.
In recent years, the nanoscale fillers, such as inorganic materials, have attracted considerable attention to impart polymers with excellent mechanical properties, antibacterial properties, flame retardancy, and so forth [11,12,13,14,15,16]. Generally, inorganic materials can endow polymers with excellent flame retardancy at a low loading. Moreover, different from other organic flame retardants, the incorporation of inorganic materials with a low addition will not deteriorate the mechanical properties of polymer materials. Inorganic materials with different morphologies and element composition show total flame retardancy mechanism towards a variety of polymers. Usually, one-dimensional inorganic materials, such as carbon nanotubes, FeOOH, and titanium dioxides [17,18,19,20,21], could form networks during the degradation process of the polymer matrix, which can play the function of physical barrier retarding the permeation of heat, oxygen, and pyrolysis products. Two-dimensional (2D) materials, including graphene, layered double hydroxides, molybdenum disulfide, and manganese dioxide (MnO2), are usually regarded as the most efficient in improving the flame retardancy of polymers in virtue of their large surface area [22,23,24], which can effectively delay the transfer of oxygen and toxic and flammable gases. For the three-dimensional materials, for instance, silica spheres, titanium dioxides spheres, and zinc hydroxystannate (ZHS) [25,26,27], these inorganic materials can also improve the flame retardancy of polymers; the catalytic charring effect and large inner specific surface area are the main reasons for the enhanced properties. It is reported that the Lewis acid catalyst forms an initial cation, promoting the Friedel–Crafts reaction, which can effectively build C–C bonds with aromatic compounds, thereby improving the char density [28]. In the case of ZHS cubes, such as metal hydroxides, they have been regarded as affinity probes, which possess the Lewis acidity [29]. Therefore, ZHS cubes are usually used as an efficient flame retardant to promote the formation of char residue.
Up to date, the concept of multicomponent systems has been applied in a variety of fields, including environment, lithium batteries, water research, and materials. In the case of materials, multicomponent systems can be realized by different methods. Very recently, the layer-by-layer technique has been employed to improve the flame retardancy of polymers such as cotton, polyamides, and flexible polyurethane foam [30,31]. This technique is mainly driven by the forces from electrostatic interactions, hydrogen bond interactions, and covalence bonds. A wide variety of functional molecules can be incorporated within the layer-by-layer coating, including polyelectrolytes and inorganic materials, to impart the matrix with the desired properties.
In this work, a binary component consisting of 2D MnO2 nanosheets and three-dimensional (3D) ZHS binary hybrids was synthesized by the self-assembly method to endow the EP matrix with flame retardancy and toxic suppression properties. In our previous works, MnO2 nanosheets were confirmed to have an excellent physical barrier effect during the degradation process in virtue of their two-dimensional structure [32,33]. Hence, fabrication of 2D/3D MnO2@ZHS binary hybrids was anticipated to achieve excellent flame retardancy and toxic effluent elimination, and the corresponding flame retardancy mechanism was also explored.

2. Materials and Methods

2.1. Raw Materials

All chemicals were of analytical grade and used as received without further purification. Zinc sulfate heptahydrate (ZnSO4·7H2O), sodium stannate trihydrate (Na2SnO3·3H2O), and potassium permanganate (KMnO4) were supplied by Sinopharm Chemical Reagent Co. Ltd. (Shanghai, China). Bisphenol-A type EP was purchased from Shixian Chemical Industry Co., Ltd. A curing agent (diaminodiphenylmethane) and sodium hydroxide were purchased from Sinopharm Chemical Reagent Co., Ltd.

2.2. Synthesis of MnO2 Nanosheets and ZHS Cubes

The synthesis process of MnO2 was according to the reported work [34]. In a typical process, 15 mmol of KMnO4 was completely dissolved in 750 mL of deionized water. Then, 200 mL of ethyl acetate was added into the above solution by constantly stirring. The solution was maintained at 95 °C and refluxed overnight. The obtained brown product was filtrated and washed with deionized water and ethanol consecutively, then dried at 80 °C for further use. In the case of ZHS cubes [25], 10 mmol of ZnSO4·7H2O was dissolved in 300 mL of deionized water at 25 °C. Once completely dissolved, the equal loading of Na2SnO3·H2O was added into the above solution. The continuous stirring was maintained for 4 h, and the white suspension was centrifuged and washed with deionized water several times and then dried at 60 °C overnight.

2.2.1. Preparation of MnO2@ZHS Binary Hybrid

MnO2@ZHS binary hybrid was prepared by a simple electrostatic adsorption method. MnO2 (1 g) was dispersed in 500 mL of deionized water with ultrasound-assisted mechanical agitation for 2 h. On the other hand, 0.2 g of ZHS was dispersed in 300 mL of deionized water under ultrasonic and mechanical stirring for 1 h. The pH value of ZHS suspension was adjusted to 5 by 0.1 M HCl solution and stirred for another 1 h. Subsequently, the ZHS suspension was dropwise added into the MnO2 suspension within 30 h by constant mechanical stirring. Finally, the mixed suspension was stirred and maintained for 4 h. The resultant was selected by centrifugation, washed by deionized water and dried at 80 °C overnight.

2.2.2. Preparation of Pure EP and EP Nanocomposites

The preparation of EP nanocomposites was in accordance with our previous works [18]. Typically, 1.22 g of MnO2@ZHS binary hybrid was added into 50 mL of acetone under ultrasonically assisted stirring to form a homogeneous suspension. Then, 50 g of premelted EP was poured into the above suspension under mechanical stirring and maintained over 6 h. Subsequently, the suspension was maintained at 100 °C for 12 h to remove the solvent. Thereafter, 10 g of premelted 4,4’-diaminodiphenylmethane was injected into the mixture under constant stirring. Finally, EP nanocomposites could be obtained after being cured at 100 °C for 2 h and 150 °C for 2 h, respectively. The sample was marked as EP/MnO2@ZHS 2%, and the others were fabricated by using the same strategy. The preparation process is illustrated in Figure 1.

2.3. Characterization

X-ray diffraction (XRD) measurements were performed using a Japan Rigaku D = Max-Ra rotating anode X-ray diffractometer (RIGAKU, Tokyo, Japan) equipped with a Cu–Ka tube and Ni filter (k = 0.1542 nm). Transmission electron microscopy (TEM) images were obtained using a JEOL JEM-100SX transmission electron microscope (JEOL, Tokyo, Japan) with an acceleration voltage of 100 kV. Thermogravimetric analysis (TGA) of as-prepared samples was undertaken using TGA-Q5000 apparatus (TA Co., New Castle, DE, USA) from 50 to 700 °C at a heating rate of 20 °C min−1. The weight of all samples was maintained within 3–5 mg in an open platinum pan. The morphologies of MnO2 materials with three different dimensions, coated with a gold layer in advance, were observed using scanning electron microscopy (SEM; AMRAY1000B, Beijing R&D Center of the Chinese Academy of Sciences, Beijing, China). TG-IR of the samples was performed using a TGA Q5000IR thermal gravimetric analyzer (TA Co., New Castle, DE, USA) that was interfaced to the Nicolet 6700 FTIR spectrophotometer (Thermo Scientific, Waltham, MA, USA). Approximately 5.0 mg of the sample was placed in an alumina crucible and heated from 30 to 800 °C at a heating rate of 20 °C min−1 (helium atmosphere, flow rate of 45 mL min−1). A combustion test was performed on the cone calorimeter (Fire Testing Technology, Derby, UK) according to ISO 5660 standard, using specimens with size of 100 × 100 × 3 mm3. Each specimen was exposed horizontally to an external heat flux of 35 kW m−2. X-ray photoelectron spectroscopy (XPS) was performed on a VG Escalab Mark II spectrometer (Thermo-VG Scientific Ltd., West Sussex, UK), using Al Kα excitation radiation (hυ = 1486.6 eV).

3. Results and Discussion

3.1. Characterization of MnO2@ZHS Binary Hybrid

TEM technique was employed to observe the morphologies of the MnO2 nanosheets and the MnO2@ZHS binary hybrid, and the morphologies of the MnO2 nanosheets and their hybrid are presented in Figure 2. As can be observed in Figure 2a, the MnO2 nanosheets show layered structure with large surface area, and the wrinkle belonging to the layers can be obviously observed. After the assembly procedure forced by electrostatic adsorption, ZHS cubes are successfully fabricated on the surface of MnO2. As is shown in Figure 2b–d, the ZHS cubes are firmly absorbed on the layers, and no ZHS cubes exist in the area beside the MnO2 nanosheets, indicating that there exist very strong electrostatic forces between the ZHS cubes and the MnO2 nanosheets. Moreover, the EDS spectrum of the MnO2@ZHS binary hybrid is presented in Figure 3. The EDS profile confirms the presence of corresponding elements such as Zn, Sn, Mn, and O. Figure 4 presents XRD patterns of the MnO2 nanosheets, ZHS cubes, and the MnO2@ZHS binary hybrid. It is evident that the MnO2@ZHS binary hybrid contains all the characteristic peaks of MnO2 and ZHS [35,36]. These results indicate that the crystalline structures of ZHS and MnO2 have no changes during the absorption procedure. Moreover, TGA was used to measure the thermal stability of the MnO2@ZHS binary hybrid and investigate the changes compared with that of the MnO2 nanosheets. Figure 5 shows the TGA curves of the MnO2 nanosheets and MnO2@ZHS binary hybrid. The thermal stability of the MnO2@ZHS binary hybrid is relatively lower than that of MnO2 nanosheets, due to the existence of predecomposition compared with MnO2. It is probably because of the separation of hydrate water from ZHS [37]. The further chemical state and element composition of MnO2 and MnO2@ZHS were explored by XPS test.
In Figure 6a, the XPS survey spectra of MnO2 and MnO2@ZHS are presented. The XPS survey spectra indicate that the MnO2@ZHS hybrid is mainly comprised of Mn, O, Sn, Zn, K, and C elements. The high-resolution Zn 2p3 and Sn 3d are also shown in Figure 6b,c. The binding energies of Zn 2p3 and Sn 3d are centered at 121.5 and 486.7 eV, respectively, which are attributed to Zn–O and Sn–O bonds [38]. Additionally, the high-resolution O1s spectra is exhibited in Figure 6d–f. The location at 529.8 eV is ascribed to the O–Mn–O bond, and the peak centered at 531.2 eV belongs to the O–Mn–H bond [39,40]. Additionally, it can be clearly found that the binding energy of O1s at around 532.3 eV attributed to the weak bond (-OH) of the MnO2@ZHS binary hybrid is higher than that of MnO2. This is reasonable due to the fabrication of ZHS, which is accompanied by abundant hydroxyl groups.

3.2. Interfacial Adhesion Beween MnO2@ZHS Binary Hybrid and EP Matrix

The morphology of the fracture surface of the samples is observed by SEM test, in order to further investigate the interfacial interaction between the nanofillers and EP matrix. As can be observed in Figure 7a, the fracture surface of pure EP shows smooth and clean. After the addition of MnO2 nanosheets, the surface of EP/MnO2 with a 2 wt % loading appears rough and wrinkled, indicating the improved interfacial interaction between the MnO2 nanosheets and EP matrix (Figure 7b). In the case of EP/MnO2@ZHS with different loadings, the wrinkles on the surface show deeper than the addition of MnO2, declaring that the interfacial interactions between the MnO2@ZHS binary hybrid and EP matrix are improved (Figure 7c–e). Moreover, as the loading of the MnO2@ZHS binary hybrid increases, the fish-like folds become more delicate. EP/MnO2@ZHS 2% exhibits the most delicate surface among the samples, which is reasonably due to the increase of MnO2@ZHS acting as stress points. Moreover, the EDS information of Figure 7e is listed in Figure 8, and the elements from the MnO2@ZHS binary hybrid can also be found. Therefore, the results obtained from SEM images demonstrate that the incorporation of MnO2@ZHS can improve the interfacial interaction between MnO2@ZHS and the EP matrix.

3.3. Thermal Stabilities of Pure EP and Its Nanocomposites Studied by TGA Test

The thermal stability of pure EP and EP nanocomposites is studied by TGA test, as shown in Figure 9. The onset decomposition temperature and the temperature at the maximal weight loss rate are denoted as T-10 and Tmax, respectively. Pure EP and EP nanocomposites exhibit the same degradation process, showing a one-stage degradation process, which is ascribed to the decomposition of macromolecular chains. Additionally, it can be seen that after the incorporation of MnO2, the char residue of EP/MnO2 at 800 °C increases compared with that of pure EP, but the T-10% and Tmax of EP/MnO2 decrease, which is possibly attributed to the catalysis effect from MnO2 promoting the predecomposition of the matrix and the degradation of metal oxides. In the case of EP/MnO2@ZHS nanocomposites, the values of T-10% and Tmax further decrease, which can be due to the predegradation of ZHS, thereby resulting in the predecomposition of the matrix. However, the increased residual content at 800 °C of EP/MnO2@ZHS nanocomposites is enhanced with the increase of the loading. Therefore, the addition of the MnO2@ZHS binary hybrid improves the char residue of the EP matrix.

3.4. Flame Retardancy Evaluated by Cone Calorimeter

The cone calorimeter is generally regarded as the most powerful tool to evaluate the force burning fire performance of materials through simulating a developing fire scenario on a fixed-sized specimen. The parameters, including peak heat release rate (PHRR) and total heat release (THR), are recognized as the crucial data for evaluating the fire safety of matrix. HRR and THR curves of pure EP and EP nanocomposites are presented in Figure 10. According to Figure 10a, incorporating MnO2 into the EP matrix can reduce the values of PHRR of EP nanocomposites, which is mainly attributed to the physical barrier effect. In the case of EP/MnO2@ZHS nanocomposites, all the values of PHRR are decreased as compared to that of pure EP. Moreover, as the amount of percent add-ons increases, the value of PHRR is further reduced. Thus, in terms of the decreased PHRR values, it can be indicated that the MnO2@ZHS hybrid shows the superior inhibition of heat release of the EP matrix. In addition, THR values of all EP nanocomposites shown in Figure 10b decrease obviously, in comparison with the pure one, showing that both MnO2 and the MnO2@ZHS binary hybrid can effectively suppress the heat release of EP nanocomposites during combustion. Moreover, the THR value of EP/MnO2@ZHS with a 2 wt % loading can achieve near 40% reduction, compared with the control EP, which is rarely attained for the nanocomposites. The results of cone calorimetry illustrate that the function of charring formation of ZHS is successfully grafted on the MnO2 nanosheets. The catalytic charring function, combined with the physical barrier effect from the MnO2 nanosheets, can significantly enhance the flame retardancy of EP nanocomposites.

3.5. Char Residues Analysis of EP and EP/MnO2@ZHS Nanocomposites

Digital photos of char residues of pure EP and EP nanocomposites are plotted in Figure 11, in order to directly observe their morphologies. As shown in Figure 11a, pure EP exhibits lower amount of char residues compared with other EP nanocomposites incorporated by MnO2@ZHS binary hybrids. According to Figure 11d, the char residue of EP/MnO2@ZHS 2% shows a larger volume, illustrating a more effective catalytic charring formation by MnO2@ZHS. Additionally, the char residues of EP nanocomposites are covered by yellow-colored materials, which are the pyrolysis products obtained by the degradation of the MnO2@ZHS binary hybrids. Usually, for inorganic nanocomposites, the inorganic fillers would transfer to the surface of the matrix during the decomposition process. These yellow-colored degradation products can act as the insulation barrier, delaying the permeation of oxygen and flammable gases, thereby reducing the values of both PHRR and THR.
To investigate the surface morphologies of char residues of pure EP and EP/MnO2@ZHS, the char residues studied here were obtained after cone calorimetry and imaged via SEM test. According to the char residue of pure EP portrayed in Figure 12a, deep cracks and collapses are obviously observed and thereby lead the oxygen and flammable gases to transfer easily. After the incorporation of MnO2@ZHS into the EP matrix, the char residue shows as more intact with less cracks (Figure 12b–d). Furthermore, as the loading increases up to 2 wt %, the surface of EP/MnO2@ZHS is very smooth, and there are no collapses and cracks, which can perfectly retard the permeation of oxygen and toxic and flammable products. Overall, SEM images visually confirm that the addition of MnO2@ZHS can significantly improve and perfect the char formation of EP nanocomposites. Besides, the Raman test was used to further study the inner graphitic structure of the char residues. As shown in Figure 12e–h, the Raman spectra of pure EP and EP nanocomposites all present two visible characteristic bands, namely, the D-band (1353 cm−1) and G-band (1592 cm−1), respectively attributed to the vibration of carbon atoms with dangling bonds in the plane terminations of disordered graphite or glass carbons and the vibration of sp2-bond carbon atoms in graphite layers. Generally, the ratio of the intensity of the D-band and G-band (ID/IG) is used to evaluate the graphitization degree of char residues. It is well recognized that sp2-bond carbon atoms in graphite layers can behave as insulation barriers retarding the transfer of heat, oxygen, and flammable products. For the value of ID/IG, the lower value means the better graphitic structure and physical insulation [41]. With the incorporation of MnO2@ZHS in the EP matrix, the value of ID/IG gradually becomes lower. As the loading increases, EP/MnO2@ZHS 2% exhibits the lowest value of ID/IG, compared with the others, indicating the most intact char structure. These results are in good agreement with the SEM results.
The XPS test was employed to further explore the carbon structure of interior and exterior char residues of pure EP and EP/MnO2@ZHS 2% and their flame retardancy mechanism, as plotted in Figure 13. For all the high-resolution C 1s spectra, it can be deconvoluted to three characteristic peaks centered at 284.6, 285.6, and 288.3 eV, assigned to aliphatic and aromatic species, hydroxyl group and/or ether, and carbonyl groups, respectively. It is generally accepted that the ratios of Cox /Ca (Cox: oxidized carbon; Ca: aliphatic and aromatic carbons) are employed to evaluate the thermal oxidative resistance of EP nanocomposites [18]. The lower value of Cox /Ca means better thermal oxidative resistance. It is found that the values of Cox /Ca in interior and exterior char residues of pure EP are 0.74 and 0.77, respectively, which are much higher than those of EP/MnO2@ZHS 2% (0.19 and 0.41). Therefore, based on these results, it can be well confirmed that MnO2@ZHS can promote the char density and graphitization degree of char residues, thereby efficiently enhancing the flame retardancy of the EP matrix.

3.6. Gas-Phase Analysis of Pure EP and EP Nanocomposites

It is well known that the pyrolysis products of the EP matrix are extremely harmful to the health of humans. Here, TG-IR technique was adopted to study the composition of pyrolysis products during the degradation process of the EP matrix and further investigate the gas-phase mechanism. The FTIR spectra of the pyrolysis products of pristine EP and EP/MnO2@ZHS 2% are presented in Figure 14. It can be concluded that the composition of the pyrolysis products is rarely changed, and the characteristic peaks are strictly ascribed to the functional groups with unambiguous band positions, such as alkane groups mainly for allyl alcohol; hydrocarbons (2820–3120 m−1); aromatic compounds (750, 830, 1460, 1510, and 1610 cm−1); CO (2180 cm−1); CO2 (2356 cm−1); and water and/or phenol (ca. 3640–3670 cm−1) [26,33].
Figure 15a shows the Gram–Schmidt curves of EP and EP/MnO2@ZHS 2%. The incorporation of MnO2@ZHS binary hybrids obviously reduces the absorbance of pyrolysis products, rivalled by that of pure EP. Moreover, Figure 15b,c,f suggest that aromatic compounds and alkane groups are all effectively decreased, implying the reduction of organic gases and improved toxic effluent elimination. Additionally, Figure 15d,e respectively present the absorbance of CO and CO2, and it can be seen that as the absorbance of CO decreases, the absorbance of CO2 increases for all the nanocomposites. This could not have an alternative explanation that less pyrolysis gases penetrate the char, making the combustion more ventilated. Therefore, it might very well be a catalysis effect for conversion of CO into CO2. In summary, TG-IR results demonstrate that MnO2@ZHS binary hybrids can efficiently suppress the production of toxic gases during the degradation of EP nanocomposites, and the addition of binary hybrids can catalyze conversion of CO into CO2. The mechanism of catalytic conversion of CO into CO2 is proposed in Figure 16. Combined with the XPS results obtained from Figure 6, it is inferred that the capacity of Mn to adapt several oxidation states enables it to undergo oxygen reduction reactions, indicating MnO2 nanosheets can act as a reservoir for oxygen, analogous to the previous work [42]. Certainly, toxic gases in real scenarios only contain CO instead of a wide array of hydrocarbons. Therefore, the catalytic conversion of CO into CO2 is of great significance. In addition, the increase of CO2 can dilute the oxygen and flammable gases in the air and thereby retard the combustion process.

4. Conclusions

In this work, a facile method was introduced to synthesize binary hybrids by fabricating ZHS cubes on MnO2 nanosheets with better flame retardancy and toxic effluent elimination of EP. XRD, TEM, and XPS results confirmed the successful synthesis of MnO2@ZHS binary hybrids. Moreover, the SEM and TEM ultrathin images indicated that MnO2@ZHS binary hybrids could achieve strong interfacial interaction with the EP matrix and be well dispersed in nanocomposites. Cone calorimeter test suggested that MnO2@ZHS binary hybrids could effectively suppress the curves of HRR and THR of EP nanocomposites, performing better than MnO2 or ZHS alone. Condensed-phase analysis revealed that MnO2@ZHS binary hybrids could promote the char density and graphitization degree of char residues and thereby successfully retard the permeation of oxygen and flammable gases. Additionally, it was concluded that MnO2@ZHS binary hybrids could efficiently suppress the production of toxic gases during the degradation of EP nanocomposites through the analysis of gas phase.

Author Contributions

L.L. made the investigation and wrote the original draft. W.W. performed the methodology and formal analysis. L.L. and W.W. are the co-first authors. Y.S. performed the project administration and carefully made the investigation. L.F. polished language through the manuscript. L.X. assisted the improvement of language through the manuscript. B.Y. assisted the project administration and supervision. All authors checked the manuscript.

Funding

This research was funded by the Natural Science Foundation of China [Grant Nos. 51803031 and 71804026], and the Natural Science Foundation of Fujian Province, China [Grant No. 2018J05078].

Acknowledgments

The authors sincerely thank Yuan Hu for testing support.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wu, G.M.; Kong, Z.W.; Chen, J.; Huo, S.P.; Liu, G.F. Preparation and properties of waterborne polyurethane/epoxy resin composite coating from anionic terpene-based polyol dispersion. Prog. Org. Coat. 2014, 77, 315–321. [Google Scholar] [CrossRef]
  2. Hadi, P.; Xu, M.; Lin, C.S.; Hui, C.W.; McKay, G. Waste printed circuit board recycling techniques and product utilization. J. Hazard. Mater. 2015, 283, 234–243. [Google Scholar] [CrossRef] [PubMed]
  3. Zhang, H.; Wang, P.; Yang, J. Self-healing epoxy via epoxy–amine chemistry in dual hollow glass bubbles. Compos. Sci. Technol. 2014, 94, 23–29. [Google Scholar] [CrossRef] [Green Version]
  4. Guadagno, L.; Raimondo, M.; Vittoria, V.; Vertuccio, L.; Naddeo, C.; Russo, S.; De Vivo, B.; Lamberti, P.; Spinelli, G.; Tucci, V. Development of epoxy mixtures for application in aeronautics and aerospace. RSC Adv. 2014, 4, 15474–15488. [Google Scholar] [CrossRef]
  5. Vietri, U.; Guadagno, L.; Raimondo, M.; Vertuccio, L.; Lafdi, K. Nanofilled epoxy adhesive for structural aeronautic materials. Compos. Part B-Eng. 2014, 61, 73–83. [Google Scholar] [CrossRef]
  6. Shi, Y.Q.; Yu, B.; Zheng, Y.Y.; Guo, J.; Chen, B.H.; Pan, Z.M.; Hu, Y. A combination of POSS and polyphosphazene for reducing fire hazards of epoxy resin. Polym. Adv. Technol. 2018, 29, 1242–1254. [Google Scholar] [CrossRef]
  7. Watanabe, I.; Sakai, S.I. Environmental release and behavior of brominated flame retardants. Environ. Int. 2003, 29, 665–682. [Google Scholar] [CrossRef]
  8. Czégény, Z.; Jakab, E.; Blazsó, M.; Bhaskar, T.; Sakata, Y. Thermal decomposition of polymer mixtures of PVC, PET and ABS containing brominated flame retardant: Formation of chlorinated and brominated organic compounds. J. Anal. Appl. Pyrol. 2012, 96, 69–77. [Google Scholar] [CrossRef]
  9. Altarawneh, M.; Saeed, A.; Al-Harahsheh, M.; Dlugogorski, B.Z. Thermal decomposition of brominated flame retardants (BFRs): Products and mechanisms. Prog. Energ. Combust. 2019, 70, 212–259. [Google Scholar] [CrossRef]
  10. Altarawneh, M.; Dlugogorski, B.Z. Formation of polybrominated dibenzofurans from polybrominated biphenyls. Chemosphere 2015, 119, 1048–1053. [Google Scholar] [CrossRef] [Green Version]
  11. Blaiszik, B.; Sottos, N.; White, S. Nanocapsules for self-healing materials. Compos. Sci. Technol. 2008, 68, 978–986. [Google Scholar] [CrossRef]
  12. Noisser, T.; Reichenauer, G.; Husing, N. In Situ Modification of the silica backbone leading to highly porous monolithic hybrid organic–inorganic materials via ambient pressure drying. ACS Appl. Mater. Interfaces 2014, 6, 1025–1029. [Google Scholar] [CrossRef] [PubMed]
  13. Pourhashem, S.; Vaezi, M.R.; Rashidi, A. Investigating the effect of SiO2-graphene oxide hybrid as inorganic nanofiller on corrosion protection properties of epoxy coatings. Surf. Coat. Technol. 2017, 311, 282–294. [Google Scholar] [CrossRef]
  14. Yuan, B.; Hu, Y.; Chen, X.; Shi, Y.; Niu, Y.; Zhang, Y.; He, S.; Dai, H. Dual modification of graphene by polymeric flame retardant and Ni(OH)2 nanosheets for improving flame retardancy of polypropylene. Compos. Part A-Appl. Sci. Manuf. 2017, 100, 106–117. [Google Scholar] [CrossRef]
  15. Shi, Y.; Yu, B.; Duan, L.; Gui, Z.; Wang, B.; Hu, Y.; Yuen, R.K.K. Graphitic carbon nitride/phosphorus-rich aluminum phosphinates hybrids as smoke suppressants and flame retardants for polystyrene. J. Hazard. Mater. 2017, 332, 87–96. [Google Scholar] [CrossRef] [PubMed]
  16. Shi, Y.Q.; Yu, B.; Zheng, Y.Y.; Yang, J.; Duan, Z.P.; Hu, Y. Design of reduced graphene oxide decorated with DOPO-phosphanomidate for enhanced fire safety of epoxy resin. J. Colloid Interf. Sci. 2018, 521, 160–171. [Google Scholar] [CrossRef] [PubMed]
  17. Hapuarachchi, T.D.; Peijs, T. Multiwalled carbon nanotubes and sepiolite nanoclays as flame retardants for polylactide and its natural fibre reinforced composites. Compos. Part A-Appl. Sci. Manuf. 2010, 41, 954–963. [Google Scholar] [CrossRef]
  18. Wang, W.; Pan, H.; Shi, Y.; Pan, Y.; Yang, W.; Liew, K.M.; Song, L.; Hu, Y. Fabrication of LDH nanosheets on β-FeOOH rods and applications for improving the fire safety of epoxy resin. Compos. Part A-Appl. Sci. Manuf. 2016, 80, 259–269. [Google Scholar] [CrossRef]
  19. Chen, X.; Jiang, Y.; Jiao, C. Smoke suppression properties of ferrite yellow on flame retardant thermoplastic polyurethane based on ammonium polyphosphate. J. Hazard. Mater. 2014, 266, 114–121. [Google Scholar] [CrossRef] [PubMed]
  20. Wang, W.; Pan, H.; Shi, Y.; Yu, B.; Pan, Y.; Liew, K.M.; Song, L.; Hu, Y. Sandwichlike coating consisting of alternating montmorillonite and β-FeOOH for reducing the fire hazard of flexible polyurethane foam. ACS Sustain. Chem. Eng. 2015, 3, 3214–3223. [Google Scholar] [CrossRef]
  21. Pan, H.; Wang, W.; Pan, Y.; Song, L.; Hu, Y.; Liew, K.M. Formation of layer-by-layer assembled titanate nanotubes filled coating on flexible polyurethane foam with improved flame retardant and smoke suppression properties. ACS Appl. Mater. Interfaces 2014, 7, 101–111. [Google Scholar] [CrossRef] [PubMed]
  22. Yu, B.; Shi, Y.; Yuan, B.; Qiu, S.; Xing, W.; Hu, W.; Song, L.; Lo, S.; Hu, Y. Enhanced thermal and flame retardant properties of flame-retardant-wrapped graphene/epoxy resin nanocomposites. J. Mater. Chem. A 2015, 3, 8034–8044. [Google Scholar] [CrossRef]
  23. Wang, W.; Kan, Y.; Pan, H.; Pan, Y.; Li, B.; Liew, K.M.; Hu, Y. Phosphorylated cellulose applied for the exfoliation of LDH: An advanced reinforcement for polyvinyl alcohol. Compos. Part A-Appl. Sci. Manuf. 2017, 94, 170–177. [Google Scholar] [CrossRef]
  24. Zhou, K.; Gao, R.; Qian, X. Self-assembly of exfoliated molybdenum disulfide (MoS2) nanosheets and layered double hydroxide (LDH): Towards reducing fire hazards of epoxy. J. Hazard. Mater. 2017, 338, 343–355. [Google Scholar] [CrossRef] [PubMed]
  25. Wang, W.; Kan, Y.; Liu, J.; Liew, K.M.; Liu, L.; Hu, Y. Self-assembly of zinc hydroxystannate on amorphous hydrous TiO2 solid sphere for enhancing fire safety of epoxy resin. J. Hazard. Mater. 2017, 340, 263–271. [Google Scholar] [CrossRef] [PubMed]
  26. Wang, W.; Kan, Y.; Pan, Y.; Yuan, Y.; Liew, K.M.; Hu, Y. Urchinlike shells of TiO2 hollow spheres for improving the fire safety of epoxy resin. Ind. Eng. Chem. Res. 2017, 56, 1341–1348. [Google Scholar] [CrossRef]
  27. Gu, H.; Guo, J.; He, Q.; Tadakamalla, S.; Zhang, X.; Yan, X.; Huang, Y.; Colorado, H.A.; Wei, S.; Guo, Z. Flame-retardant epoxy resin nanocomposites reinforced with polyaniline-stabilized silica nanoparticles. Ind. Eng. Chem. Res. 2013, 52, 7718–7728. [Google Scholar] [CrossRef]
  28. Ran, S.; Guo, Z.; Han, L.; Fang, Z. Effect of a lewis acid catalyst on the performance of HDPE/BFR/GNPs composites. Ind. Eng. Chem. Res. 2014, 53, 4711–4717. [Google Scholar] [CrossRef]
  29. Li, L.P.; Zheng, T.; Xu, L.N.; Li, Z.; Sun, L.D.; Nie, Z.X.; Bai, Y.; Liu, H.W. SnO2–ZnSn(OH)6: A novel binary affinity probe for global phosphopeptide detection. Chem. Commun. 2013, 49, 1762–1764. [Google Scholar] [CrossRef]
  30. Carosio, F.; Alongi, J.; Malucelli, G. Layer by layer ammonium polyphosphate-based coatings for flame retardancy of polyester–cotton blends. Carbohydr. Polym. 2012, 88, 1460–1469. [Google Scholar] [CrossRef]
  31. Carosio, F.; Di Blasio, A.; Cuttica, F.; Alongi, J.; Frache, A.; Malucelli, G. Flame retardancy of polyester fabrics treated by spray-assisted layer-by-layer silica architectures. Ind. Eng. Chem. Res. 2013, 52, 9544–9550. [Google Scholar] [CrossRef]
  32. Wang, W.; Pan, Y.; Pan, H.; Yang, W.; Liew, K.M.; Song, L.; Hu, Y. Synthesis and characterization of MnO2 nanosheets based multilayer coating and applications as a flame retardant for flexible polyurethane foam. Compos. Sci. Technol. 2016, 123, 212–221. [Google Scholar] [CrossRef]
  33. Wang, W.; Kan, Y.; Yu, B.; Pan, Y.; Liew, K.M.; Song, L.; Hu, Y. Synthesis of MnO2 nanoparticles with different morphologies and application for improving the fire safety of epoxy. Compos. Part A-Appl. Sci. Manuf. 2017, 95, 173–182. [Google Scholar] [CrossRef]
  34. Sinha, A.K.; Pradhan, M.; Pal, T. Morphological evolution of two-dimensional MnO2 nanosheets and their shape transformation to one-dimensional ultralong MnO2 nanowires for robust catalytic activity. J. Phys. Chem. C 2013, 117, 23976–23986. [Google Scholar] [CrossRef]
  35. Wrobel, G.; Piech, M.; Dardona, S.; Ding, Y.; Gao, P.X. Seedless synthesis and thermal decomposition of single crystalline zinc hydroxystannate cubes. Cryst. Growth Des. 2009, 9, 4456–4460. [Google Scholar] [CrossRef]
  36. Ma, Z.; Shao, G.; Fan, Y.; Wang, G.; Song, J.; Shen, D. Construction of hierarchical α-MnO2 nanowires@ ultrathin δ-MnO2 nanosheets core–shell nanostructure with excellent cycling stability for high-power asymmetric supercapacitor electrodes. ACS Appl. Mater. Interfaces 2016, 8, 9050–9058. [Google Scholar] [CrossRef] [PubMed]
  37. Fu, X.; Huang, D.; Qin, Y.; Li, L.; Jiang, X.; Chen, S. Effects of preparation method on the microstructure and photocatalytic performance of ZnSn(OH)6. Appl. Catal. B-Environ. 2014, 148, 532–542. [Google Scholar] [CrossRef]
  38. Luo, P.; Zhang, H.; Liu, L.; Fang, L.; Wang, Y. Sandwich-like nanostructure of amorphous ZnSnO3 encapsulated in carbon nanosheets for enhanced lithium storage. Electrochim. Acta 2016, 219, 734–741. [Google Scholar] [CrossRef]
  39. Singu, B.S.; Hong, S.E.; Yoon, K.R. Ultra-thin and ultra-long α-MnO2 nanowires for pseudocapacitor material. J. Solid State Electr. 2017, 21, 3215–3220. [Google Scholar] [CrossRef]
  40. Li, D.; Li, W.; Deng, Y.; Wu, X.; Han, N.; Chen, Y. Effective Ti doping of δ-MnO2 via anion route for highly active catalytic combustion of benzene. J. Phys. Chem. C 2016, 120, 10275–10282. [Google Scholar] [CrossRef]
  41. Wang, W.; Pan, H.; Yu, B.; Pan, Y.; Song, L.; Liew, K.M.; Hu, Y. Fabrication of carbon black coated flexible polyurethane foam for significantly improved fire safety. RSC Adv. 2015, 5, 55870–55878. [Google Scholar] [CrossRef]
  42. Miran, H.A.; Altarawneh, M.; Jiang, Z.T.; Oskierski, H.; Almatarneh, M.; Dlugogorski, B.Z. Decomposition of selected chlorinated volatile organic compounds by ceria (CeO2). Catal. Sci. Technol. 2017, 7, 3902–3919. [Google Scholar] [CrossRef]
Polymers 11 00229 g001 550
Figure 1. Synthesis of MnO2@ZHS hybrids and flame retardancy mechanism in epoxy.
Figure 1. Synthesis of MnO2@ZHS hybrids and flame retardancy mechanism in epoxy.
Polymers 11 00229 g001
Polymers 11 00229 g002 550
Figure 2. TEM images of (a) MnO2 nanosheets, and (b–d) MnO2@ZHS hybrid.
Figure 2. TEM images of (a) MnO2 nanosheets, and (b–d) MnO2@ZHS hybrid.
Polymers 11 00229 g002
Polymers 11 00229 g003 550
Figure 3. EDS profile of MnO2@ZHS.
Figure 3. EDS profile of MnO2@ZHS.
Polymers 11 00229 g003
Polymers 11 00229 g004 550
Figure 4. XRD patterns of MnO2, ZHS, and MnO2@ZHS hybrid.
Figure 4. XRD patterns of MnO2, ZHS, and MnO2@ZHS hybrid.
Polymers 11 00229 g004
Polymers 11 00229 g005 550
Figure 5. TGA curves of MnO2 and MnO2@ZHS.
Figure 5. TGA curves of MnO2 and MnO2@ZHS.
Polymers 11 00229 g005
Polymers 11 00229 g006 550
Figure 6. (a) XPS survey spectra of MnO2 and MnO2@ZHS binary hybrid, (b) the high-resolution Zn 2p3, and (c) Sn 3d5 spectra of MnO2@ZHS binary hybrid, (d) O1s spectra of MnO2 and MnO2@ZHS binary hybrid, the deconvoluted O1s spectra of (e) MnO2 and (f) MnO2@ZHS binary hybrid.
Figure 6. (a) XPS survey spectra of MnO2 and MnO2@ZHS binary hybrid, (b) the high-resolution Zn 2p3, and (c) Sn 3d5 spectra of MnO2@ZHS binary hybrid, (d) O1s spectra of MnO2 and MnO2@ZHS binary hybrid, the deconvoluted O1s spectra of (e) MnO2 and (f) MnO2@ZHS binary hybrid.
Polymers 11 00229 g006
Polymers 11 00229 g007 550
Figure 7. SEM images of fracture surfaces cryogenically broken after immersion in liquid nitrogen of (a) pure EP, (b) EP/MnO2 2%, (c) EP/MnO2@ZHS 0.5%, (d) EP/MnO2@ZHS 1%, and e) EP/MnO2@ZHS 2%.
Figure 7. SEM images of fracture surfaces cryogenically broken after immersion in liquid nitrogen of (a) pure EP, (b) EP/MnO2 2%, (c) EP/MnO2@ZHS 0.5%, (d) EP/MnO2@ZHS 1%, and e) EP/MnO2@ZHS 2%.
Polymers 11 00229 g007
Polymers 11 00229 g008 550
Figure 8. EDS profile of EP/MnO2@ZHS 2%.
Figure 8. EDS profile of EP/MnO2@ZHS 2%.
Polymers 11 00229 g008
Polymers 11 00229 g009 550
Figure 9. (a) TGA curve of pure EP and EP nanocomposites under nitrogen condition. (b,c) represent magnified TGA profiles of (a) at different temperatures.
Figure 9. (a) TGA curve of pure EP and EP nanocomposites under nitrogen condition. (b,c) represent magnified TGA profiles of (a) at different temperatures.
Polymers 11 00229 g009
Polymers 11 00229 g010 550
Figure 10. (a) HRR and (b) THR curves of pure EP and EP nanocomposites evaluated by cone calorimeter.
Figure 10. (a) HRR and (b) THR curves of pure EP and EP nanocomposites evaluated by cone calorimeter.
Polymers 11 00229 g010
Polymers 11 00229 g011 550
Figure 11. Digital images of char residues for (a) pure epoxy, (b) EP/MnO2@ZHS 0.5%, (c) EP/MnO2@ZHS 1%, (d) EP/MnO2@ZHS 2% after cone calorimeter tests. The scale of these samples is 100 × 100 mm2.
Figure 11. Digital images of char residues for (a) pure epoxy, (b) EP/MnO2@ZHS 0.5%, (c) EP/MnO2@ZHS 1%, (d) EP/MnO2@ZHS 2% after cone calorimeter tests. The scale of these samples is 100 × 100 mm2.
Polymers 11 00229 g011
Polymers 11 00229 g012 550
Figure 12. SEM images and Raman spectra of the char residues of (a,e) pure EP, (b,f) EP/MnO2@ZHS 0.5%, (c,g) EP/MnO2@ZHS 1%, and (d,h) EP/MnO2@ZHS 2%.
Figure 12. SEM images and Raman spectra of the char residues of (a,e) pure EP, (b,f) EP/MnO2@ZHS 0.5%, (c,g) EP/MnO2@ZHS 1%, and (d,h) EP/MnO2@ZHS 2%.
Polymers 11 00229 g012
Polymers 11 00229 g013 550
Figure 13. The high-resolution C1s spectra of interior and exterior char residues of (a,b) pure EP and (c,d) EP/MnO2@ZHS 2%.
Figure 13. The high-resolution C1s spectra of interior and exterior char residues of (a,b) pure EP and (c,d) EP/MnO2@ZHS 2%.
Polymers 11 00229 g013
Polymers 11 00229 g014 550
Figure 14. FT-IR spectrum of pyrolysis products of pure EP and EP/MnO2@ZHS 2% composites at the maximum decomposition rate.
Figure 14. FT-IR spectrum of pyrolysis products of pure EP and EP/MnO2@ZHS 2% composites at the maximum decomposition rate.
Polymers 11 00229 g014
Polymers 11 00229 g015 550
Figure 15. Absorbance of pyrolysis products versus time for EP and its nanocomposites: (a) Gram–Schmidt; (b,c) aromatic compounds located at 1510 and 1610 cm−1; (d) CO; (e) CO2; and (f) hydrocarbons.
Figure 15. Absorbance of pyrolysis products versus time for EP and its nanocomposites: (a) Gram–Schmidt; (b,c) aromatic compounds located at 1510 and 1610 cm−1; (d) CO; (e) CO2; and (f) hydrocarbons.
Polymers 11 00229 g015
Polymers 11 00229 g016 550
Figure 16. The proposed mechanism of catalytic conversion of CO into CO2.
Figure 16. The proposed mechanism of catalytic conversion of CO into CO2.
Polymers 11 00229 g016

Share and Cite

MDPI and ACS Style

Liu, L.; Wang, W.; Shi, Y.; Fu, L.; Xu, L.; Yu, B. Electrostatic-Interaction-Driven Assembly of Binary Hybrids towards Fire-Safe Epoxy Resin Nanocomposites. Polymers 2019, 11, 229. https://doi.org/10.3390/polym11020229

AMA Style

Liu L, Wang W, Shi Y, Fu L, Xu L, Yu B. Electrostatic-Interaction-Driven Assembly of Binary Hybrids towards Fire-Safe Epoxy Resin Nanocomposites. Polymers. 2019; 11(2):229. https://doi.org/10.3390/polym11020229

Chicago/Turabian Style

Liu, Lu, Wei Wang, Yongqian Shi, Libi Fu, Lulu Xu, and Bin Yu. 2019. "Electrostatic-Interaction-Driven Assembly of Binary Hybrids towards Fire-Safe Epoxy Resin Nanocomposites" Polymers 11, no. 2: 229. https://doi.org/10.3390/polym11020229

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop