Next Article in Journal
Strategy for Encapsulation of CdS Quantum Dots into Zeolitic Imidazole Frameworks for Photocatalytic Activity
Previous Article in Journal
Ni-Rich Layered Oxide with Preferred Orientation (110) Plane as a Stable Cathode Material for High-Energy Lithium-Ion Batteries
Previous Article in Special Issue
Plasma-Assisted Chemical Vapor Deposition of F-Doped MnO2 Nanostructures on Single Crystal Substrates
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

RF Thermal Plasma Synthesis of Ultrafine ZrB2-ZrC Composite Powders

1
School of Mechanical and Energy Engineering, Huanghuai University, Zhumadian 463000, China
2
Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China
3
College of Chemistry and Materials Engineering, Beijing Technology and Business University, Beijing 100048, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2020, 10(12), 2497; https://doi.org/10.3390/nano10122497
Submission received: 8 November 2020 / Revised: 3 December 2020 / Accepted: 9 December 2020 / Published: 12 December 2020

Abstract

:
Ultrafine ZrB2-ZrC composite powders were synthesized via a radiofrequency (RF) thermal plasma process. Numerical simulation and thermodynamic analysis were conducted to predict the synthesis process, and experimental work was performed accordingly to demonstrate its feasibility. The as-prepared samples were characterized by XRD, FESEM, particle size analyzer, nitrogen/oxygen analyzer, Hall flowmeter, and the Brunner-Emmet-Teller (BET) measurements. The thermodynamic analysis indicated that ZrB2 was preferentially generated, rather than ZrC, and numerical simulation revealed that the solid raw materials could disperse well in the gaseous reactants, and experimental work showed that free carbon particles were easily removed from the products and the elements of Zr, B, C, and O exhibited a uniform distribution. Finally, ZrB2-ZrC composite powders with a particle size of about 100 nm were obtained, the surface area of which was 32.15 m2/g and the apparent density was 0.57 g/cm3.

1. Introduction

Borides and carbides of zirconium show a number of excellent properties, such as high melting point, low density, good wear resistance, high thermal and electrical conductivity, and good chemical stability, which makes them attractive candidates in the areas where wear–corrosion–oxidation resistance is demanded, such as high temperature electrodes, molten metal crucibles, thermal protection systems for hypersonic flights, atmospheric re-entry vehicles, rocket propulsion systems, and nose caps [1,2,3,4,5,6,7,8]. However, it is difficult to use single phase material to meet all the necessary requirements demanded by the extreme conditions encountered in aerospace engineering. Therefore, research efforts have now turned to the development of double or multiple phase ceramics [9,10,11,12]. It has been demonstrated that ZrB2-ZrC composites possess better properties, such as mechanical strength and oxidation resistance, than those of either individual component [13,14,15,16,17,18]. Sorrell reported that boride–carbide eutectic composites fabricated by a directional solidification method had very good physical and chemical properties [19]. Tsuchida and Yamamoto synthesized a ZrB2-ZrC composite by mechanically activating self-propagating high temperature synthesis (SHS) in a Zr/B/C elemental system [20].
During the past decade, there has been a growing appeal for the production of ceramic powders with ultrafine or nano-sized particles due to their excellent sintering ability and the improved mechanical properties of the formed nanograined materials [21,22,23]. The plasma synthesis process is one of the most efficient methods for producing ultrafine powders [24,25,26]. In the plasma system, a high-temperature flame (up to 10,000 K) provides enough energy for the evaporation of the raw materials and the high-temperature gradient helps to solidify the products rapidly, which is necessary for the formation of nanoparticles. The radiofrequency (RF) thermal plasma gas does not come into contact with electrodes and the operation environment is flexible from oxidizing to reducing atmosphere, which can eliminate possible sources of contamination.
RF thermal plasma for the powder synthesis originated from the spheroidization. High melting point metals, ceramic, or irregular-shaped glass micron powders were injected from the top of the plasma torch and heated rapidly in the plasma region, and subsequently cooled down at a high rate when they flew out of the plasma flame, and finally condensed to very fine spherical powders [27,28]. For the synthesis of nanopowders, there are two different ways known as physical vapor deposition (PVD) and chemical vapor deposition (CVD). In a typical plasma synthesis process, the raw materials evaporate in the high-temperature region, then react (if there are chemical reactions involved), and finally condense into fine particles. Hou synthesized single-crystalline α-Si3N4 nanospheres with a uniform size of ∼50 nm using coarse silicon nitride (5–10 μm) as starting powders in a one-step and continuous way [29]. Kim demonstrated scalable manufacturing of boron nitride nanotubes (BNNTs) directly from hexagonal BN (hBN) powders by using induction thermal plasma, with a high-yield rate approaching 20 g/h [30]. Kumar reported a new ultrafast gas-phase method for synthesizing highly crystalline titanate phase nanowires (NWs) using oxidation of either Ti metal (foils or powders) or spherical TiO2 powders with an atmospheric pressure microwave plasma [31]. It can be seen that the reaction system and powder composition were usually simple during early research.
Recently, there have been reports referencing complicated compounds and reactions. Westover demonstrated the theoretically guided plasma synthesis of high purity nanocrystalline Li3.5Si0.5P0.5O4 and fully amorphous Li2.7Si0.7P0.3O3.17N0.22 [32]. ZrB2 and ZrC nanopowders were successfully synthesized via vapor chemical deposition and the metallothermic synthesis route within the RF thermal plasma system, respectively [33,34].
In the present work, ZrB2-ZrC composite powders were synthesized via the thermal plasma route, in which ZrCl4, B, Mg, and CH4 were used as raw materials. Numerical simulation and thermodynamic analysis were conducted ahead to predict the synthesis process, and experimental work was performed accordingly to demonstrate its feasibility. The as-prepared samples were characterized by XRD, FE-SEM, particle size analyzer, nitrogen/oxygen analyzer, Hall flowmeter, and BET method. It is be demonstrated in this work that ultrafine ZrB2-ZrC composite powders can be synthesized successfully via the RF thermal plasma technique.

2. Materials and Methods

2.1. Materials

ZrCl4 (Zr + Hf ≥ 38%) was supplied by Yixian Jincheng Zirconium Industry Company (Jinzhou, China). B (95%) was supplied by Dandong Chemical Engineering Institute Company (Dandong, China). CH4 (99.999%), H2 (99.999%), and Ar (99.99%) were supplied by Qianxi Jingcheng Gas Industry Company (Beijing, China). Hydrochloric acid (36–38 wt.%) was supplied by Beijing Chemical Reagents Company (Beijing, China).

2.2. Synthesis

Figure 1 presents the schematic illustration and a picture of the RF thermal plasma processing system used in our laboratory, which consists of an RF generator, a plasma generator, a downward plasma torch, a 3-coil cylindrical reactor, a quenching chamber, a precursor feeding system, a powder-collecting filter, a gas supplier system, and an off-gas exhaust system. The reactor is operated in atmosphere and the pressure is usually adjusted in the range of −500 to −1000 Pa gauge during the operation of experiments. The RF generator (30 kW, 4 MHz) was supplied by Tieling High Frequency Equipment Factory, and the reactors were homemade in the Institute of Process Engineering, Chinese Academy of Sciences.
The raw materials of ZrCl4, B, and Mg were sifted through a 150 μm sieve and blended in a mechanical mixer. The reactor system was first purged with Ar to remove oxygen and moisture from the reactor, so that a separate inert atmosphere was prepared for the chemical synthesis procedure. A Plasma flame was generated using argon as both the plasma-forming gas and sheath gas. The reactor was heated by the plasma flame for about 5 min until the system reached a steady level, and then the raw materials were injected into the plasma flame in a continuous way with a homemade screw feeder. CH4 and H2 (if necessary) were mixed into the carrier gas and fed axially through the injection probe to the top of the plasma flame. The typical processing parameters for RF thermal plasma in our laboratory are given in Table 1.
For the synthesis of the ZrB2 powders, stoichiometric amounts of ZrCl4, B, and Mg were weighed with a 20% excess amount of Mg, in which the molar ratio of Zr/B/Mg/C = 1/2/2.4/0–0.1. For the synthesis of the ZrB2-ZrC composite powders, the mole ratio of Zr/B/Mg/C = 1/1/2.4/0.5. The feeding time was usually 10–20 min, and then the plasma flame was shut down. In order to protect the products from oxidizing at the high temperature, Ar was supplied continuously until the reactor system cooled down. The final products were collected from the powder-collecting filter, and a small part of them could be found at the bottom of the collector. The solid products needed further post-treatment with diluted hydrochloric acid. The process flow chart is provided in Figure 2.

2.3. Characterization

The crystalline phase of the as-prepared intermediate and final products was characterized by an X-ray diffractometer (XRD, X’pertPRO, Panalytical, Almelo, The Netherlands) in a 2θ range from 10° to 90°. Their size and morphology were inspected with field emission scanning electron microscopy (FESEM, JSM-6700 F; JEOL, Tokyo, Japan). The particle size distribution was measured using a LS particle size analyzer (Beckman Coulter LS 13 320, Nyon, Switzerland). The oxygen content was measured by an impulse-thermal conductivity method (Eltra ON-900, NCS, Beijing, China). The carbon content was measured by an infrared C-S measurer (NCS CS-3000, NCS, Beijing, China). The specific surface area was determined using a BET method. The apparent density was examined with the help of a Hall flowmeter.

3. Results and Discussion

3.1. Thermodynamic Calculation

The plasma synthesis of ZrB2 using ZrCl4, B, and Mg is ruled by the following reactions:
ZrCl4 + 2B + 2Mg → ZrB2 + 2MgCl2
ZrCl4 + CH4 → ZrC + HCl
Main reactions during the plasma processing can be expressed as below:
ZrCl4 + 2Mg → Zr + 2MgCl2
CH4 → C + 2H2
ZrCl4 + 2H2 → Zr + 4HCl
Zr + 2B → ZrB2
Zr + C → ZrC
The spontaneous direction of a reaction is usually judged by the change of the Gibbs-free energy ΔG. Thermodynamic calculation has been made based on the data given in the literature [35]. Figure 3 shows the free energies of the above reactions as a function of temperature.
ΔG value for reaction (1) is much lower than zero at the temperature, and the ΔG value for reaction (2) decreases as the temperature increases and becomes lower than zero at the temperature around 1000 °C, indicating both reactions could take place spontaneously at high temperature. ΔG value for reaction (6) is always lower than that of reaction (7) at a temperature below 3800 °C, indicating that ZrB2 is preferentially generated. Therefore, free C instead of B would exist in the resulting products when C and B in the starting materials excess the stoichiometric ratio.

3.2. Numerical Simulation

Fluent software is employed to simulate the system and analyze the flow field and particle trajectories in the reactor as reported in [36]. In the present work, a three-dimensional physical model is applied, and mass-flow-inlet boundary was selected. Figure 4 shows the velocity field. Figure 4a,b shows the carrier gas path lines and Figure 4c,d shows the particle tracks from different points of view. It can be seen that both the carrier gas and particles are well fixed at the central area in the reactor. Their main swelling parts exhibit a similar shape, and the carrier gas expands a bit wider than the particles. These simulation results indicate that the addition of CH4 to the (ZrCl4 + 2B + 2Mg) reaction system can form another well-distributed system.

3.3. Experimental Results

ZrB2 and ZrC can be synthesized using (ZrCl4 + 2B + 2Mg) and (ZrCl4 + CH4) reaction systems, respectively, as reported in our previous work [33,34]. Otherwise, ZrC was also synthesized successfully using (ZrCl4 + C + 2Mg) reaction system, which is similar as the synthesis of ZrB2 reported in [33]. In order to avoid the possible contamination of oxygen residual or leaking in the reaction system for the solid-state synthesis (ZrCl4 + 2B + 2Mg or ZrCl4 + C + 2Mg), hydrogen was mixed into the carrier gas, so that low oxygen content can be achieved.
In the present work, the two reactions (ZrCl4 + 2B + 2Mg) and (ZrCl4 + CH4) coexist in one system, where solid raw materials including ZrCl4, B, and Mg were mixed in advance and CH4 was mixed into the carrier gas which carried the solid raw materials into the plasma flame through the axial injection probe.
The ratio between CH4, B, and ZrCl4 had great effects on the composition of the products. At the beginning of the experimental work, the mixed raw materials for the synthesis of ZrB2 powders were used, in which stoichiometric amounts of ZrCl4, B, and Mg were weighed with a 20% excess amount of Mg. Figure 5 shows the XRD pattern of the sample obtained with the mole ratio of CH4/ZrCl4 of 10%.
The diffraction peaks of (001), (100), (101), (002), (110), (102), (111), (200), (201), and (112) of a face-centered cubic (fcc) ZrB2 (JCPDS 00-034-0423) can be clearly observed in the XRD pattern shown in Figure 5. Furthermore, no obvious peaks of ZrC are displayed in the XRD pattern, which is also inconsistent with the conclusion that ZrB2 will be preferentially generated, from thermodynamic analysis.
In the present synthesis process, with a mole ratio of B/Zr of 2, the element B was sufficient and there was little chance of C combining with Zr. Therefore, excessive CH4 in the plasma reaction system led to free C in the plasma products. It was observed that there were some black samples floating on the surface of the solution during the post-treatment. The black samples were collected and dried at 110 °C for 120 min. Then, the black samples were confirmed as free C with an infrared C-S measurer, which could be removed from the products easily during the post treatment due to its light weight. Moreover, the C content of the final products measured was quite low. Table 2 displays the carbon contents and oxygen contents of the final products after acid leaching synthesized with a different mole ratio of CH4/ZrCl4.
C content was only 0.32% when the mole ratio of CH4/ZrCl4 was as high as 1/10. In order to demonstrate the separation efficiency of carbon nanoparticles, the sample after acid leaching was filtered and washed without removing the floating black samples on the surface of the solution and characterized using an infrared C-S measurer. The total C content was determined as 1.06%, which was much higher than that of the sample obtained when getting rid of the floating black samples. In consideration of the XRD characterization results, C mainly exists as free carbon instead of combined carbon because no peaks of ZrC are detected in the XRD pattern.
However, the addition of CH4 to the (ZrCl4 + 2B + 2Mg) reaction system can help to reduce the oxygen content of the final products. The decomposition products of CH4, H2, and free C would provide a stronger reduction environment and protect the reactants from oxidation. The sealing technique at the ultra-high-temperature region within plasma equipment is still a challenge. The addition of reducing gas to protect the reaction process can really contribute to the synthesis of low oxygen content products.
In order to get ZrB2-ZrC composite powders, the mole ratio of B/Zr was set at 1.0, and the mole ratio of C/Zr was set at 0.5. Figure 6 shows the XRD patterns of the sample, in which both diffraction peaks of (001), (100), (101), (002), (110), (102), (111), (200), (201), and (112) of face-centered cubic (fcc) ZrB2 (JCPDS 00-034-0423) and diffraction peaks of (111), (200), (220), (311), (222), and (400) of face-centered cubic (fcc) ZrC (JCPDS 03-065-0332) can be observed, indicating that the obtained products were ZrB2-ZrC composite powders.
Carbon and oxygen contents were also measured and are listed in Table 3. Carbon content is 5.29% when the mole ratio of C/B/Zr in the starting materials is set at 1:2:2. The theoretical content of C in ZrC and B in ZrB2 is 11.6% and 19.1%. Accordingly, the theoretical content of C in the ZrB2-ZrC composite powders (the mole ratio of ZrB2/ZrC: 1/1) is 5.6%, which is slightly higher than that detected by the impulse-thermal conductivity method. It can be seen that the oxygen content is 3.5%, indicating that some Zr exist as oxides instead of borides or carbides. Therefore, CH4 was not fully utilized to form ZrC. Part of CH4 was decomposed into free C and removed from the products during the post-treatment procedure.
Figure 7a shows a FESEM picture (insertion, magnified 1000 times) and a whole EDS spectrum of the RF thermal plasma synthesized ZrB2-ZrC composite powders when the mole ratio of C/B/Zr in the starting materials was set at 1:2:2. Figure 7b–e is the corresponding maps of the FESEM picture. It can be seen that the concentration of all main elements exhibits similar outlines with the FESEM picture, indicating that Zr, B, C, and O disperse uniformly in the sample. Figure 7f-–h shows FESEM pictures of the synthesized ZrB2-ZrC composite powders magnified 5000–40,000 times. The red circles are the magnified regions. The dispersed particles have clear edges and exhibit an average particle size ranging from 100 nm to 500 nm.
The particle size distribution of the powders measured using an LS particle size analyzer (Beckman Coulter LS 13 320, Nyon, Switzerland) is shown in Figure 8. D10, D25, D50, D75, and D90 of the synthesized powder are 0.744 μm, 1.094 μm, 1.630 μm, 2.425 μm, and 3.935 μm, respectively. The mean diameter, the median diameter, and mode diameter are 1.973 μm, 1.630 μm, and 1.593 μm, respectively. The ratio of mean/median is 1.210. It can be seen that the particle size measured by the particle size analyzer is much higher than that detected under FESEM, which may be attributed to most of the particles aggregating together instead of being monodisperse.
The surface area of the synthesized ZrB2-ZrC composite powders calculated by BET was 32.15 m2/g, and the apparent density examined with the help of a Hall flowmeter was 0.57 g/cm3. Detailed structure characterization and further application of the RF thermal plasma synthesized ZrB2-ZrC composite powders are in progress.

4. Conclusions

An RF thermal plasma synthesis method was proposed for ZrB2-ZrC composite powders. Numerical simulation and thermodynamic analysis were conducted to predict the synthesis process, and experimental work was performed accordingly to demonstrate its feasibility. Several conclusions can be drawn from the results and discussion:
(1)
ZrB2 was preferentially generated rather than ZrC, and free C instead of B would exist in the resulting products when C and B exceed the stoichiometric ratio.
(2)
Solid raw materials could disperse well in the gaseous reactants, which leads to the uniform distribution of elements in ZrB2-ZrC composite powders.
(3)
Free carbon particles can be removed during post-treatment, and ZrB2-ZrC composite powders with a particle size of about 100 nm could be obtained.
(4)
The surface area of ZrB2-ZrC composite powders was 32.15 m2/g and the apparent density was 0.57 g/cm3.

Author Contributions

Conceptualization, L.B. and F.Y.; methodology, L.B. and H.J.; software, J.H.; validation, L.B. and F.Y.; formal analysis, W.L.; investigation, H.J.; resources, F.Y.; data curation, Y.O.; writing—original draft preparation, L.B.; writing—review and editing, Z.F. and Q.W.; visualization, Y.W.; supervision, F.Y.; project administration, L.B.; funding acquisition, L.B. and F.Y. All authors have read and agreed to the published version of the manuscript.

Funding

This research was sponsored by the National Natural Science Foundation of China (No. 11875284; No. 11535003) and Program for Science & Technology Innovation Talents in Universities of Henan Province (No. 21HASTIT020).

Acknowledgments

The authors would thank Jinlin Li and Shulan Huang (from the Institute of Process Engineering, Chinese Academy of Sciences) for their guidance in the work.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Hassan, R.; Balani, K. Oxidation kinetics of ZrB2-and HfB2-powders and their SiC reinforced composites. Corros. Sci. 2020, 177, 109024. [Google Scholar] [CrossRef]
  2. Vafa, N.P.; Kakroudi, M.G.; Asl, M.S. Advantages and disadvantages of graphite addition on the characteristics of hot-pressed ZrB2–SiC composites. Ceram. Int. 2020, 46, 8561–8566. [Google Scholar] [CrossRef]
  3. Ang, C.; Seeber, A.; Wang, K.; Cheng, Y. Modification of ZrB2 powders by a sol–gel ZrC precursor-A new approach for ultra high temperature ceramic composites. J. Asian Ceram. Soc. 2013, 1, 77–85. [Google Scholar] [CrossRef] [Green Version]
  4. Li, M.; Ke, C.; Zhang, J. Synthesis of ZrB2 powders by molten-salt participating silicothermic reduction. J. Alloys Compd. 2020, 834, 155062. [Google Scholar] [CrossRef]
  5. Torabi, S.; Valefi, Z.; Ehsani, N. Ablation behavior of SiC/ZrB2 ultra-high temperature ceramic coatings by solid shielding shrouded plasma spray for high-temperature applications (temperature above 2000 °C). Surf. Coat. Technol. 2020, 403, 126271. [Google Scholar] [CrossRef]
  6. Bai, L.; Ni, S.; Jin, H.; He, J.; Ouyang, Y.; Yuan, F. ZrB2 powders with low oxygen content: Synthesis and characterization. Int. J. Appl. Ceram. Technol. 2017, 15, 508–513. [Google Scholar] [CrossRef]
  7. Shaa, J.J.; Wang, S.H.; Dai, J.X.; Zu, Y.F.; Li, W.Q.; Sha, R.Y. Improved microstructure and high temperature mechanical properties of C/C–SiC composites by introduction of ZrC nanoparticles. Ceram. Int. 2020, 46, 8082–8091. [Google Scholar] [CrossRef]
  8. Wu, X.; Su, Z.; Huang, Q.; Tong, K.; Xie, X.; Zeng, C. Effect of ZrC particle distribution on the ablation resistance of C/C-SiC-ZrC composites fabricated using precursor infiltration pyrolysis. Ceram. Int. 2020, 46, 16062–16067. [Google Scholar] [CrossRef]
  9. Ma, B.; Li, J. ZrB2-SiC-ZrC coating on ZrC ceramics deposited by plasma spraying. Results Phys. 2019, 15, 102550. [Google Scholar] [CrossRef]
  10. Rezapour, A.; Balak, Z. Fracture toughness and hardness investigation in ZrB2–SiC–ZrC composite. Mater. Chem. Phys. 2020, 241, 122284. [Google Scholar] [CrossRef]
  11. Liu, C.; Zhang, L.; Yuan, X.; Liu, H.; Li, C.; Hou, X. Preparation of ZrB2-ZrC-SiC-ZrO2 nanopowders with in-situ grown homogeneously dispersed SiC nanowires. Mater. Des. 2020, 196, 109186. [Google Scholar] [CrossRef]
  12. Wang, W.; Fu, Q.; Tan, B. Effect of in-situ grown SiC nanowires on the mechanical properties of HfC-ZrB2-SiC modified C/C composites. J. Alloys Compd. 2017, 726, 866e874. [Google Scholar] [CrossRef]
  13. Asl, M.S.; Nayebi, B.; Parvizi, S.; Ahmadi, Z.; Parvin, N.; Shokouhimehr, M.; Mohammadi, M. Toughening of ZrB2-based composites with in-situ synthesized ZrC from ZrO2 and graphite precursors. J. Sci. Adv. Mater. Devices 2020. [Google Scholar] [CrossRef]
  14. King, D.S.; Hilmas, G.E.; Fahrenholtz, W.G. Plasma arcwelding of ZrB2–20 vol% ZrC ceramics. J. Eur. Ceram. Soc. 2014, 34, 3549–3557. [Google Scholar]
  15. Xu, L.; Huang, H.; Liu, B.; Zou, H.; Zhao, G. In situ synthesis of ZrB2–ZrCx ceramic tool materials toughened by elongated ZrB2 grains. Mater. Des. 2013, 49, 226–233. [Google Scholar] [CrossRef]
  16. Kannan, R.; Rangaraj, L. Properties of Cf/SiC-ZrB2-TaxCy composite produced by reactive hot pressing and polymer impregnation pyrolysis (RHP/PIP). J. Eur. Ceram. Soc. 2019, 39, 2257–2265. [Google Scholar] [CrossRef]
  17. Zhang, S.; Wang, S.; Li, W.; Zhu, Y.; Chen, Z. Mechanical properties of the low-temperature reactive melt infiltrated ZrB2–ZrC based composites. Mater. Lett. 2012, 78, 81–84. [Google Scholar] [CrossRef]
  18. Chen, H.; Zeng, F.; Li, W.; Liu, J.; Gu, Y.; Zhang, F. Densification behavior and mechanical properties of spark plasma reaction sintered ZrB2–ZrC-B4C ceramics from B4C-Zr system. Ceram. Int. 2019, 45, 12122–12129. [Google Scholar] [CrossRef]
  19. Sorrell, C.; Beratan, H.; Bradt, R.; Stubican, V. Directional Solidification of (Ti, Zr) Carbide-(Ti, Zr) Diboride Eutectics. J. Am. Ceram. Soc. 2006, 67, 190–194. [Google Scholar] [CrossRef]
  20. Tsuchida, T. MA-SHS and SPS of ZrB2–ZrC composites. Solid State Ionics 2004, 172, 215–216. [Google Scholar] [CrossRef]
  21. Khanra, A.; Godkhindi, M.; Pathak, L. Sintering behaviour of ultra-fine titanium diboride powder prepared by self-propagating high-temperature synthesis (SHS) technique. Mater. Sci. Eng. A 2007, 454, 281–287. [Google Scholar] [CrossRef]
  22. Çamurlu, H.E.; Maglia, F. Preparation of nano-size ZrB2 powder by self-propagating high-temperature synthesis. J. Eur. Ceram. Soc. 2009, 29, 1501–1506. [Google Scholar] [CrossRef]
  23. Zhang, Y.; Li, R.; Jiang, Y.; Zhao, B.; Duan, H.; Li, J.; Feng, Z. Morphology evolution of ZrB2 nanoparticles synthesized by sol–gel method. J. Solid State Chem. 2011, 184, 2047–2052. [Google Scholar] [CrossRef]
  24. Zheng, J.; Yang, R.; Xie, L.; Qu, J.; Liu, Y.; Li, X. Inorganic Nanostructures: Plasma-Assisted Approaches in Inorganic Nanostructure Fabrication (Adv. Mater. 13/2010). Adv. Mater. 2010, 22, 1451–1473. [Google Scholar] [CrossRef] [PubMed]
  25. He, J.; Bai, L.; Jin, H.; Jia, Z.; Hou, G.; Yuan, F. Simulation and experimental observation of silicon particles’ vaporization in RF thermal plasma reactor for preparing Si nano-powder. Powder Technol. 2017, 313, 27–35. [Google Scholar] [CrossRef]
  26. Son, B.-K.; Lee, K.-H.; Kim, T.H.; Shin, M.-S.; Choi, S.-Y.; Cho, G. Purification and Nitrogen Doping of Nanothin Exfoliated Graphite Through RF Thermal Plasma Treatment. Nanomaterials 2019, 9, 995. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  27. Seo, J.H.; Kim, D.U.; Nam, J.S.; Hong, S.H.; Sohn, S.B.; Song, S.M. Radio Frequency Thermal Plasma Treatment for Size Reduction and Spheroidization of Glass Powders Used in Ceramic Electronic Devices. J. Am. Ceram. Soc. 2007, 90, 1717–1722. [Google Scholar] [CrossRef]
  28. Li, Y.-L.; Ishigaki, T. Spheroidization of Titanium Carbide Powders by Induction Thermal Plasma Processing. J. Am. Ceram. Soc. 2004, 84, 1929–1936. [Google Scholar] [CrossRef]
  29. Hou, G.; Cheng, B.; Ding, F.; Yao, M.; Mingshui, Y.; Yuan, F. Synthesis of Uniform α-Si3N4 Nanospheres by RF Induction Thermal Plasma and Their Application in High Thermal Conductive Nanocomposites. ACS Appl. Mater. Interfaces 2015, 7, 2873–2881. [Google Scholar] [CrossRef]
  30. Kim, K.S.; Couillard, M.; Shin, H.; Plunkett, M.; Ruth, D.; Kingston, C.T.; Simard, B. Role of Hydrogen in High-Yield Growth of Boron Nitride Nanotubes at Atmospheric Pressure by Induction Thermal Plasma. ACS Nano 2018, 12, 884–893. [Google Scholar] [CrossRef] [Green Version]
  31. Kumar, V.; Kim, J.H.; Jasinski, J.B.; Clark, E.L.; Sunkara, M.K. Alkali-Assisted, Atmospheric Plasma Production of Titania Nanowire Powders and Arrays. Cryst. Growth Des. 2011, 11, 2913–2919. [Google Scholar] [CrossRef]
  32. Westover, A.S.; Kercher, A.K.; Kornbluth, M.; Naguib, M.; Palmer, M.J.; Cullen, D.A.; Dudney, N.J. Plasma Synthesis of Spherical Crystalline and Amorphous Electrolyte Nanopowders for Solid-State Batteries. ACS Appl. Mater. Interfaces 2020, 12, 11570–11578. [Google Scholar] [CrossRef] [PubMed]
  33. Bai, L.; Jin, H.; Lu, C.; Yuan, F.; Huang, S.; Li, J. RF thermal plasma-assisted metallothermic synthesis of ultrafine ZrB2 powders. Ceram. Int. 2015, 41, 7312–7317. [Google Scholar] [CrossRef]
  34. Bai, L.; Zhang, H.; Jin, H.; Yuan, F.; Huang, S.; Li, J. Radio-Frequency Atmospheric-Pressure Plasma Synthesis of Ultrafine ZrC Powders. Int. J. Appl. Ceram. Technol. 2012, 10, E274–E281. [Google Scholar] [CrossRef]
  35. Knacke, O.; Kubaschewski, O.; Hesselmann, K. Thermochemical Properties of Inorganic Substances, 2nd ed; Springer: Berlin, Germany, 1991. [Google Scholar]
  36. Bai, L.; He, J.; Ouyang, Y.; Liu, W.; Liu, H.; Yao, H.; Li, Z.; Song, J.; Wang, Y.; Yuan, F.-L. Modeling and Selection of RF Thermal Plasma Hot-Wall Torch for Large-Scale Production of Nanopowders. Materials 2019, 12, 2141. [Google Scholar] [CrossRef] [PubMed] [Green Version]
Figure 1. Schematic illustration (a) and picture (b) of the radiofrequency (RF) thermal plasma processing system: (1) powder feeder; (2) injection probe; (3) circular nozzle; (4) water-cooled induction coil; (5) hot-chamber reactor; (6) cooling-chamber reactor.
Figure 1. Schematic illustration (a) and picture (b) of the radiofrequency (RF) thermal plasma processing system: (1) powder feeder; (2) injection probe; (3) circular nozzle; (4) water-cooled induction coil; (5) hot-chamber reactor; (6) cooling-chamber reactor.
Nanomaterials 10 02497 g001
Figure 2. Process flow chart for plasma synthesis of ultrafine ZrB2-ZrC composite powders.
Figure 2. Process flow chart for plasma synthesis of ultrafine ZrB2-ZrC composite powders.
Nanomaterials 10 02497 g002
Figure 3. Temperature dependences of the free energy of formation.
Figure 3. Temperature dependences of the free energy of formation.
Nanomaterials 10 02497 g003
Figure 4. Velocity field simulated by fluent: (a,b): carrier gas path lines; (c,d): particle tracks.
Figure 4. Velocity field simulated by fluent: (a,b): carrier gas path lines; (c,d): particle tracks.
Nanomaterials 10 02497 g004aNanomaterials 10 02497 g004b
Figure 5. XRD pattern of the sample obtained when the mole ratio of B/Zr was set at 2.0.
Figure 5. XRD pattern of the sample obtained when the mole ratio of B/Zr was set at 2.0.
Nanomaterials 10 02497 g005
Figure 6. XRD patterns of the samples obtained when the mole ratio of B/Zr was set at 1.0.
Figure 6. XRD patterns of the samples obtained when the mole ratio of B/Zr was set at 1.0.
Nanomaterials 10 02497 g006
Figure 7. FESEM picture (a) and the corresponding EDS maps (b: Zr; c: B; d: C; e: O) of the RF thermal plasma synthesized ZrB2-ZrC composite powders, and the highly magnified FESEM picture (f–h).
Figure 7. FESEM picture (a) and the corresponding EDS maps (b: Zr; c: B; d: C; e: O) of the RF thermal plasma synthesized ZrB2-ZrC composite powders, and the highly magnified FESEM picture (f–h).
Nanomaterials 10 02497 g007aNanomaterials 10 02497 g007b
Figure 8. Particle size distribution of the RF thermal plasma synthesized ZrB2-ZrC composite powders.
Figure 8. Particle size distribution of the RF thermal plasma synthesized ZrB2-ZrC composite powders.
Nanomaterials 10 02497 g008
Table 1. Typical processing parameters for RF thermal plasma in our laboratory.
Table 1. Typical processing parameters for RF thermal plasma in our laboratory.
NumbersParametersValues
1Power supply30 kW
2Plasma gas (Ar)2.0 m3/h
3Sheath gas (Ar)5.0 m3/h
4Carrier gas (Ar/CH4)0.2 m3/h
5Feed rate (CH4)0–0.6 L/min
6Feed rate (H2)0–0.3 L/min
7Feed rate (solid)4.0–16.0 g/min
Table 2. C and O contents of the products obtained with a different mole ratio of CH4/ZrCl4.
Table 2. C and O contents of the products obtained with a different mole ratio of CH4/ZrCl4.
CH4/ZrCl4Carbon ContentOxygen Content
006.06%
0.050.25%3.91%
0.100.32%3.45%
Table 3. Carbon and oxygen contents with different mole ratio of C/B/Zr.
Table 3. Carbon and oxygen contents with different mole ratio of C/B/Zr.
C/B/ZrCarbon ContentOxygen Content
1:2:25.29%3.5%
0.3:2:10.32%3.45%
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Bai, L.; Yuan, F.; Fang, Z.; Wang, Q.; Ouyang, Y.; Jin, H.; He, J.; Liu, W.; Wang, Y. RF Thermal Plasma Synthesis of Ultrafine ZrB2-ZrC Composite Powders. Nanomaterials 2020, 10, 2497. https://doi.org/10.3390/nano10122497

AMA Style

Bai L, Yuan F, Fang Z, Wang Q, Ouyang Y, Jin H, He J, Liu W, Wang Y. RF Thermal Plasma Synthesis of Ultrafine ZrB2-ZrC Composite Powders. Nanomaterials. 2020; 10(12):2497. https://doi.org/10.3390/nano10122497

Chicago/Turabian Style

Bai, Liuyang, Fangli Yuan, Zheng Fang, Qi Wang, Yuge Ouyang, Huacheng Jin, Jiaping He, Wenfu Liu, and Yinling Wang. 2020. "RF Thermal Plasma Synthesis of Ultrafine ZrB2-ZrC Composite Powders" Nanomaterials 10, no. 12: 2497. https://doi.org/10.3390/nano10122497

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop