Abstract
The 620 °C isothermal section of the Al–Zn–Fe–V quaternary system with the Al content fixed at 55 wt.% and the Al-rich corner of the Al–Fe–Zn ternary system at 620 °C have been determined by means of scanning electron microscopy coupled with energy dispersive X-ray spectroscopy and X-ray diffractometry. Two four-phase regions are identified in the isothermal section of the Al–Zn–Fe–V quaternary system. Two three-phase regions are found in the Al-rich corner of the Al–Fe–Zn ternary system. No new ternary and quaternary phases have been found in the present work.
References
[1] A.R.Marder: Prog. Mater. Sci.45 (2000) 191. 10.1016/S0079-6425(98)00006-1Search in Google Scholar
[2] H.P.Peng, X.P.Su, Z.Li, J.H.Wang, C.J.Wu, H.Tu, X.F.Lai: Surf. Coat. Technol.206 (2012) 4329. 10.1016/j.surfcoat.2012.01.048Search in Google Scholar
[3] R.P.Edavan, R.Kopinski: Corros. Sci.51 (2009) 2429. 10.1016/j.corsci.2009.06.028Search in Google Scholar
[4] S.H.Hwang, J.H.Song, Y.S.Kim: Mater. Sci. Eng. A390 (2005) 437. 10.1016/j.msea.2004.08.062Search in Google Scholar
[5] S.Kobayashi, T.Yakou: Mater. Sci. Eng. A338 (2002) 44. 10.1016/S0921-5093(02)00053-9Search in Google Scholar
[6] J.H.Selverian, A.R.Marder, M.R.Notis: Metall. Mater. Trans.A19 (1988) 1193. 10.1007/BF02662580Search in Google Scholar
[7] F.García, A.Salinas, E.Nava: Mater. Lett.60 (2006) 775. 10.1016/j.matlet.2005.10.010Search in Google Scholar
[8] Q.Li, Y.Z.Zhao, Q.Luo, S.L.Chen, J.Y.Zhang, K.C.Chou: J. Alloys Compd.501 (2010) 282. 10.1016/j.jallcom.2010.04.089Search in Google Scholar
[9] H.F.Li, J.S.Zheng, D.Y.Yu: J. Huazhong Univ. Sci. Tech.35 (2003) 107. 10.13245/j.hust.2003.05.038Search in Google Scholar
[10] T.B.Massalski, H.Okamoto, P.R.Subramanian, L.Kacprzak: Binary Alloy Phase Diagrams, 2nd Ed., ASM, Materials Park, OH, USA (1992).Search in Google Scholar
[11] F.Stein, M.Palm: Int. J. Mater. Res.98 (2007) 580. 10.3139/146.101512Search in Google Scholar
[12] K.W.Richter, H.Ipser: Z. Metallkd.91 (2000) 383.Search in Google Scholar
[13] W.Köster, T.Gödecke: Z. Metallkd.61 (1970) 649.Search in Google Scholar
[14] P.Perrot, J.C.Tissier, J.Y.Dauphin: Z. Metallkd.83 (1992) 786.Search in Google Scholar
[15] N.Y.Tang, X.P.Su: Metall. Mater. Trans. A33 (2002) 1559. 10.1007/s11661-002-0078-5Search in Google Scholar
[16] J.Nakano, D.V.Malakhov, S.Yamaguchi, G.R.Purdy: CALPHAD31 (2007) 125. 10.1016/j.calphad.2006.09.003Search in Google Scholar
[17] O.N.C.Uwakweh, Z.Liu: Metall. Mater. Trans. A28 (1997) 517. 10.1007/s11661-997-0039-0Search in Google Scholar
[18] E.H.Rennhack: Trans. AIME221 (1961) 775.Search in Google Scholar
[19] Q.Luo, J.L.Chen, Y.Li, F.Yang, Q.Li, Y.Wu, J.Y.Zhang, K.C.Chou: CALPHAD37 (2012) 116. 10.1016/j.calphad.2012.02.007Search in Google Scholar
[20] F.C.Yin, S.Zheng, X.M.Wang, Z.Li, M.X.Zhao: J. Phase Equilib.33 (2012) 167. 10.1007/s11669-012-0029-9Search in Google Scholar
[21] S.Zheng, F.C.Yin, Z.Li, Z.H.Long, M.X.Zhao: J. Alloys Compd.541 (2012) 204. 10.1016/j.jallcom.2012.07.051Search in Google Scholar
[22] E.M.Sokolovskaya, L.M.Badalova, E.F.Kazakova: Izv. Akad. Nauk SSSR, Met. (1987) 212.Search in Google Scholar
[23] E.M.Sokolovskaya, L.M.Badalova, E.F.Kazakova, N.V.Stroeva: Vestn. Mosk. Univ., Ser. 2: Khim.29 (1988) 303.Search in Google Scholar
[24] V.Raghavan: Phase Diagrams of Ternary Iron Alloys, Part 6, Indian Institute of Metals, Calcutta (1992).Search in Google Scholar
[25] V.Raghavan: J. Phase Equilib.23 (2002) 439. 10.1361/105497102770331406Search in Google Scholar
[26] G.Gautam: Materials Science International Team MSIT®: Light Metal Systems, Part 3, Springer-Verlag, Berlin (2005). 10.1007/10915998_2Search in Google Scholar
[27] M.Y.Zhao, L.Z.Song, X.B.Fan: The Boundary Theory of Phase Diagrams and Its Application, Beijing (2009) 135. 10.1007/978-3-642-02940-0_7Search in Google Scholar
© 2016, Carl Hanser Verlag, München