Microstructure and fatigue strength of the roller-bearing steel 100Cr6 (SAE 52100) after two-step bainitisation and combined bainitic–martensitic heat treatment

  • Hermann Vetters , Juan Dong , Hubert Bomas , Franz Hoffmann and Hans-Werner Zoch

Abstract

Possible processes for shortening the heat treatment of roller-bearing steels in the lower bainitic range were investigated by computer assisted dilatometric experiments and by practical heat treatment process simulations. Several processes were evaluated and used on the steel 100Cr6 (SAE 52100). The microstructures achieved have been investigated by metallography, X-ray analysis and electron microscopy. Influences on hardness, as well as on the fatigue strength were examined. No loss in hardness was achieved and the fatigue strength, determined by rotating bar fatigue tests, was enhanced significantly by the shortened treatments, particularly by the use of the two-step bainitic treatment. The results indicated that small amounts of retained austenite, homogeneously dispersed on a sub-microscopic scale, as obtained during various treatment cycles, have influenced the fatigue strength. By means of the processes evaluated the heat treatment time can be shortened to about 10–25% of the duration of complete bainitisation in the lower range.


Dedicated to Professor Eckard Macherauch on the occasion of the 80th anniversary of his birth

* Correspondence address, Prof. Dr. Hermann Vetters, IWT BREMEN, Badgasteinerstr. 3, D-28359 Bremen, Germany, E-mail: , Priv.: Baumeister Specht Str. 42, D-88161 Lindenberg, Germany, Tel./Fax: +498381807428

References

[1] O.Schaaber: Härterei-Techn. Mitt.4 (1950) 9.Search in Google Scholar

[2] F.Hengerer, G.Lucas, B.Nyberg: Härterei-Techn. Mitt.29 (1974) 71.Search in Google Scholar

[3] J.Slycke, C.Fajers, J.Volkmuth: Härterei-Techn. Mitt.57 (2002) 156.Search in Google Scholar

[4] E.Macherauch, O.Vöhringer: Härterei-Techn. Mitt.41 (1986) 71.Search in Google Scholar

[5] W.Jellinghaus: Arch. Eisenhüttenw.23 (1952) 11/12, 459.10.1002/srin.195200972Search in Google Scholar

[6] C.Li, J.L.Wang: Journal of Materials Science28 (1993) 2112.10.1007/BF00367570Search in Google Scholar

[7] H.K.D.H.Bhadheshia: Bainite in Steels, Inst. of Materials, London (1992).Search in Google Scholar

[8] M.Hillert: Scripta Mat.43 (2000) 831.10.1016/S1359-6462(00)00484-XSearch in Google Scholar

[9] H.I.Aaronson, G.Spanos, W.T.ReynoldsJr.: Scripta Mater.47 (2002) 139.10.1016/S1359-6462(02)00119-7Search in Google Scholar

[10] J.Dong, H.Vetters, H.-W.Zoch: Trans. Mat. Heat Treatment25 (2004) 5, 555.Search in Google Scholar

[11] M.Hunkel, Th.Lübben, F.Hoffmann, P.Mayr: Härterei-Techn. Mitt.54 (1999) 365.Search in Google Scholar

[12] H.Bomas, T.Linkewitz, P.Mayr: Fatigue and Fracture of Engineering Materials and Structures22 (1999) 733.Search in Google Scholar

[13] J.W.Christian, D.V.Edmonds: Phase Transformations in Ferrous Alloys; Warrendale, PA (1984) 293.Search in Google Scholar

[14] European Patents: EP 0896068 B1; EP 0794262 B1; EP 1248862 A1.Search in Google Scholar

[15] H.Vetters: Steel Research67 (1996) 408.10.1002/srin.199605511Search in Google Scholar

[16] W.T.ReynoldsJr., S.K.Liu, F.Z.Li, S.Hartfield, H.I.Aaronson: Met. Trans.A21 (1990) 1433.Search in Google Scholar

[17] G.Spanos, H.S.Fang, H.I.Aaronson: Met. Trans.A21 (1990) 1381.Search in Google Scholar

[18] Y.Ohmori: Scripta Mater.47 (2002) 201.10.1016/S1359-6462(02)00129-XSearch in Google Scholar

[19] H.S.Fang, J.B.Yang, Z.G.Yang, B.Z.Bai: Scripta Mat.47 (2002) 157.10.1016/S1359-6462(02)00122-7Search in Google Scholar

[20] T.Y.Hsu: Met. TransA21 (1990) 811.10.1007/BF02656564Search in Google Scholar

[21] G.B.Olson, H.K.D.H.Bhadheshia, M.Cohen: Met. Trans.A21 (1990) 805.Search in Google Scholar

[22] R.F.Hehemann: Phase transformations, ASM Ohio (1970) 397.Search in Google Scholar

[23] O.Vöhringer, E.Macherauch: Härterei-Techn. Mitt.32 (1977) 153.Search in Google Scholar

[24] H.Schwendemann: Die thermische Restaustenitstabilisierung bei den Stählen 100Cr6 und X210Cr12, Dr.-Ing. Diss.(Thesis), TU Karlsruhe (1981).Search in Google Scholar

[25] A.Schrader, F.Wever: Arch. Eisenhüttenwes.23 (1952) 489.Search in Google Scholar

[26] S.J.Matas, R.F.Heheman: Trans TMS AIME221 (1961) 179.Search in Google Scholar

[27] H.K.D.H.Bhadheshia, J.W.Christian: Met. Trans.A21 (1990) 767.Search in Google Scholar

[28] H.Vetters, K.Bullerdiek: Sonderbd. prakt. Metallographie33 (2002) 41.Search in Google Scholar

[29] H.Vetters: Z. Werkstoffe, Wärmebehandlung, Fertigung, Härterei-Techn. Mitt.57 (2002) 168.Search in Google Scholar

[30] C.Razim: Härterei-Techn. Mitt.23 (1968) 1.Search in Google Scholar

[31] S.Laue, C.Thoben, H.Bomas, R.Schröder, R.Kienzler: Z. Werkstoffe, Wärmebehandlung, Fertigung, Härterei-Techn. Mitt.60 (2005) 271.Search in Google Scholar

[32] D.Munz, K.Schwalbe, P.Mayr: Dauerschwingverhalten metallischer Werkstoffe, Braunschweig: Friedr. Vieweg+Sohn GmbH (1971).Search in Google Scholar

Received: 2006-5-25
Accepted: 2006-7-6
Published Online: 2013-05-31
Published in Print: 2006-10-01

© 2006, Carl Hanser Verlag, München

Downloaded on 12.5.2024 from https://www.degruyter.com/document/doi/10.3139/146.101388/html
Scroll to top button