Abstracts

Gutta-percha points with calcium hydroxide

Apical seal of root canals with gutta-percha points with calcium hydroxide

Roberto Holland^I; Sueli Satomi Murata^II; Henrian Gonzaga Barbosa^I; Osvaldo Garlipp^I; Valdir de Souza^I; Eloi Dezan Junior^I

^IDiscipline of Endodontics, Department of Restorative Dentistry

^IIDepartment of Pediatric and Social Dentistry, Faculty of Dentistry of Araçatuba, UNESP, Araçatuba, SP, Brazil

^{Correspondence} Correspondence to Dr. Roberto Holland Departamento de Odontologia Restauradora, Faculdade de Odontologia de Araçatuba, UNESP R. José Bonifácio, 1193 16015-050 Araçatuba, SP, Brasil e-mail: rholland@foa.unesp.br

ABSTRACT

The objective of this research was to determine if gutta-percha points with calcium hydroxide [Ca(OH)₂] improve the apical seal after root canal filling and if the master point does it alone. Human single recently extracted teeth were biomechanically prepared and the root canals filled by the lateral condensation technique with ZOE and gutta-percha points, with or without calcium hydroxide. The teeth were placed into a 2% methylene blue solution in a vacuum environment for 24 h after which they were processed for stereomicroscope evaluation. Better results were observed with the teeth filled with gutta-percha points with calcium hydroxide (p=0.01). We conclude that these new points make a better apical seal and that these results can also be obtained with the calcium hydroxide master point associated with regular ones (p=0.05).

Key Words: calcium hydroxide, gutta-percha points, apical leakage.

RESUMO

Foi propósito deste trabalho observar se o uso de cones de guta-percha contendo Ca(OH)₂, promove melhora no selamento marginal apical e, também, se apenas o cone principal contendo essa droga produz esse efeito. Assim, dentes humanos extraídos foram preparados biomecânicamente e obturados pela técnica da condensação lateral com OZE e cones de guta-percha contendo ou não Ca(OH)₂. Após imersão dos espécimes em azul de metileno a 2%, em ambiente com vácuo, observou-se diferença estatisticamente significante entre os espécimes obturados com cones contendo Ca(OH)₂, comparativamente aos casos obturados com cones de guta percha comuns (p=0.01). Os resultados obtidos permitiram concluir que esses cones tornam as obturações mais herméticas e que esse efeito também pode ser obtido com o emprego do cone principal da mesma fórmula, aliado a cones acessórios comuns (p=0.05).

INTRODUCTION

The root canal must be hermetically filled in order to hinder the communication of its interior with periapical tissues. Many studies have been developed with the object of studying the factors that could influence the sealing property of root canal fillings. It has been demonstrated that the sealing efficiency is affected by the filling technique (1,2), the type of sealer (3), as well as the clinical procedures done before root canal filling (4). Other factors can modify the sealing property of root canal fillings, i.e., EDTA, camphorated p-monochlorophenol and a corticosteroid-antibiotic solution. It has been reported that remnants of these drugs can significantly decrease leakage after root canal filling (5).

Calcium hydroxide has been employed as a dressing in cases of tooth reimplantation (6), treatment of teeth with open apices (7,8), treatment of teeth with periapical lesions (9) and, more recently, as a routine dressing during root canal treatment (10). It has been reported that after use of some substances it is possible to observe their remnants in the root canal walls even after exhaustive attempts to remove them (11). For this motive, the presence of calcium hydroxide residue was investigated with the objective of evaluating if they modify the quality of the root canal filling (12). It has been reported that after use of a calcium hydroxide dressing, there is less leakage in root canal fillings with different sealers (5,13,14). This was also observed when this medication was employed as an apical plug (15).

These observations about the effect of calcium hydroxide on the amount of leakage stimulated the study of an experimental gutta-percha point with calcium hydroxide (Dentsply) in its formulation. Less leakage in root canal fillings with calcium hydroxide gutta-percha points than with regular points has been reported (16). However, Dentsply later altered the formulation of the gutta-percha points to comply with the new ISO specifications (ISO 6877). This modification decreased the amount of calcium hydroxide in the experimental gutta-percha points.

Thus, the subject of this paper is to observe if the modification in the amount of calcium hydroxide in the gutta-percha formulation has an influence on leakage after root canal filling with this type of point.

MATERIAL AND METHODS

Fifty single-rooted human teeth, recently extracted, were employed in this experiment. The coronal portion of the teeth was sectioned and the root canals were prepared biomechanically 1 mm short of the apical foramen up to a size 40 K file, before step-back instrumentation up to a #80 H file. During instrumentation, abundant and frequent irrigation with 1% sodium hypochlorite was done.

After biomechanical preparation, all roots were coated with a layer of Araldite (Brascola Ltda., São Bernardo do Campo, SP, Brazil), except for the area surrounding the apical foramen and the coronal opening. The root canals were then filled by the lateral condensation technique with zinc oxide eugenol sealer (ZOE; S.S. White, Artigos Dentários Ltda, Rio de Janeiro, RJ, Brazil) and gutta-percha points containing or not containing calcium hydroxide in their formula tion (Dentsply Industria e Comércio Ltda, Rio de Janeiro, RJ, Brazil).

Three experimental groups were constituted according to the type of gutta-percha points used: group I - root canals filled by the lateral condensation technique with ZOE sealer and regular gutta-percha points; group II - root canals filled by the lateral condensation technique with ZOE sealer and the main and auxiliary gutta-percha points with calcium hydroxide; group III - root canals filled by the lateral condensation technique with ZOE sealer and a calcium hydroxide main gutta-percha point and regular auxiliary gutta-percha points. Positive and negative control groups were also constituted. Some root canals were filled and all the roots were coated with Araldite (negative control). The positive control was constituted by root canals not filled. The 3 experimental groups and the 2 control groups were formed by 10 roots each. The coronal portion of the root canals of groups I, II and III was sealed with Araldite after filling. The apical portion of the roots of these 3 groups was immersed in water for 24 h to permit the hardening of the filling material and of Araldite in the coronal portion.

All specimens were then fully immersed into a 2% methylene blue solution (pH 7.0) inside a flask which was attached to a vacuum pump providing a vacuum of 0.002 mmHg for 15 min. Twenty-four hours later the teeth were washed, dried and grooved in a buccolingual direction without penetrating the root canal. A chisel was placed in the groove to split the root in half with gentle pressure. The filling material was removed and the greatest extent of linear dye penetration was recorded using a stereomicroscope with a graded eyepiece.

RESULTS

The positive control showed total leakage in all specimens and the negative control did not show leakage. The data for the 3 experimental groups (Table 1) were submitted to analysis of variance and the Tukey test, which showed that the use of calcium hydroxide gutta-percha points, and the main gutta-percha point with calcium hydroxide and regular auxiliary points provided significantly better sealing than with the regular main and auxiliary points (p=0.01). There was no statistically significant difference between the leakage when calcium hydroxide points or only the main calcium hydroxide point with regular auxiliary points were used (p>0.05).

DISCUSSION

In a previous experiment, it was reported that root canal filling with gutta-percha points containing calcium hydroxide exhibited less leakage than root canal filling with regular points (16). However, the formulation of the studied gutta-percha points was modified to comply with ISO specifications. In the present experiment, we observed that the decrease in the amount of calcium hydroxide in these points (Dentsply) did not alter the leakage previously observed. We also noted that the use of only the master point with calcium hydroxide gave almost the same results when both kinds of calcium hydroxide points were employed.

It is of interest to consider that calcium hydroxide on the external surface of the points, in contact with air, is gradually converted into calcium carbonate, which does not have the same properties of calcium hydroxide. However, calcium hydroxide located in the interior of the points may be protected from this alteration. Theoretically, the modified points would not have the same properties as the original points. Nevertheless, during lateral condensation, the calcium hydroxide located in the interior of the points could be released and thus converted into calcium carbonate (16,18).

Another question is what type of sealer would have leakage altered by contact with calcium hydroxide. It was reported that calcium hydroxide gutta-percha points improved leakage qualities of zinc oxide-eugenol sealers, Endomethasone and Grossman cement (16). When an intracanal calcium hydroxide dressing is employed it is possible to observe less leakage with the sealers AH 26, Fill Canal and Tubli Seal (13-15,17), but we do not know if the same will occur with the gutta-percha points containing this substance.

Various hypotheses have tried to explain the mechanism action of this drug when less leakage is observed (14,15). In the case of gutta-percha points, it is possible that an expansion of the sealer could occur when in contact with the alkaline pH of the points (16).

Another detail to be considered is the radiopacity of these points. For gutta-percha points, the ISO specification established a minimum radiopacity 6 times greater than that of aluminum. According to the manufacturer, the points we studied have a radiopacity 7 times greater than aluminum, however, they are less radiopaque than regular points.

In relation to the reported properties of the points it is necessary to consider that every procedure that improves the sealing quality is of interest if it does not harm its biological properties. Some researchers believe that it is difficult to evaluate the biological significance of major or minor dye leakage (19). The molecular weight of the bacterial endotoxin is greater than that of methylene blue (20). When it is evaluated directly, the leakage of endotoxin is less than the minor leakage of methylene blue (19). Thus, the real influence of the apical leakage on the healing process after root canal treatment must be better analyzed.

Accepted March 31, 2003

Publication Dates

History