Abstract
The stability of the Mg-Zn-Y icosahedral quasicrystal (IQC) has been studied by long-term annealing of a single grain IQC in quartz tubes. Decomposition of the IQC was observed after annealing at high temperatures (T≥773 K) sealed in Ar. During the decomposition process, the quasilattice parameter aR was found to decrease, associated with a decrease in Mg content of the IQC phase as confirmed by quantitative x-ray energy dispersive spectroscopy analyses. In addition, a new cubic approximant has been found in the annealed samples. This cubic approximant has a face-centered cubic (fcc) structure with lattice parameter of a = 1.276 nm, which is about (1/τ) times smaller than that of the fcc W′-(MgZnY) with a = 2.05 nm reported previously (where τ is the golden ratio).
Similar content being viewed by others
References
Z.P. Luo, S.Q. Zhang, Y.L. Tang, D.S. Zhao, Scripta metall. mater., 28, 1513 (1993); 30, 393 (1994).
A. Niikura, A.P. Tsai, A. Inoue, T. Masumoto, Phil. Mag. Lett., 69, 351 (1994).
A. Langsdorf, F. Ritter, W. Assmus, Phil. Mag. Lett., 75, 381 (1997).
Z.P. Luo, H.X. Sui, S.Q. Zhang, Metall. Mater. Trans., 27 A, 1779 (1996).
N. Tamura, M. Beyss, K. Urban, Phil. Mag. Lett., 74, 89 (1996).
A.P. Tsai, A. Niikura, A. Inoue, T. Masumoto, J. Mater. Res., 12, 1468 (1997).
E. Abe, A.P. Tsai, Phys. Rev. Lett., 83, 753 (1999).
I.R. Fisher, Z. Islam, A.F. Panchula, K.O. Cheon, M.J. Kramer, P.C. Canfield, A.I. Goodman, Phil. Mag. B, 77, 1601 (1998).
A. Langsdorf, C. Seuring, F. Ritter, W. Assmus, Cryst. Res. Tech., 32, 1067 (1997).
K. Sugiyama, K. Yasuda, T. Ohsuna, K. Hiraga, Z. Kristallogr., 213, 537 (1998).
H. Takakura, A. Sato, A. Yamamoto, A.P. Tsai, Phil. Mag. Lett., 78, 263 (1998).
I.R. Fisher and M.J. Kramer, unpublished work.
Z.P. Luo, H. Hashimoto, Micron, 31, 487 (2000).
R. Sterzel, W. Assmus, A. Kounis, G. Miehe, H. Fuess, Phil. Mag. Lett., 80, 239 (2000).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Luo, Z.P., Tang, Y.L., Miller, D.J. et al. The Thermal Stability of a Single-Grain Mg-Zn-Y Icosahedral Quasicrystal. MRS Online Proceedings Library 643, 94 (2000). https://doi.org/10.1557/PROC-643-K9.4
Published:
DOI: https://doi.org/10.1557/PROC-643-K9.4