Epitaxial ZnGa2O4 and Sr2CeO4 thin-film phosphors were successfully grown on (100) MgO, YSZ, and SrTiO3 single crystal substrates using pulsed laser ablation. Cathodoluminescence efficiency was remarkably enhanced by adding lithium in the ZnGa2O4 and ZnGa2O4:Mn for both blue and green light emitting thin-film phosphors. The highest efficiencies, in this experiment, were 0.35 and 0.29 lm/W at 1kV for as-deposited blue and green zinc gallate phosphor films, respectively. In case of Sr2CeO4 films, the highest luminescence was 0.14 lm/W at 1kV and 0.26 A/m2 for films annealed at 1000°C in air.
Similar content being viewed by others
Reference
S. L. Jones, D. Kumar, K.-G. Cho, R. Singh, and P. H. Holloway, Display, 19 151 (1999).
K.-G. Cho, D. Kumar, P. H. Holloway, and R. Singh, Appl. Phys. Lett., 73, 3058 (1998).
T. Minami, T. Maeno, Y. Kuroi, and S. Tanaka, Jpn. J. Appl. Phys., 34, L684 (1995).
Y. E. Lee, D. P. Norton, and J. D. Budai, Appl. Phys. Lett., 74, 3155 (1999).
S. Itoh, H. Toki, F. Kataoka, Y. Sato, K. Tamura, and Y. Kagawa, IEICE Trans. Electron, E82–C, 1808 (1999).
K.-S. Suh, S.-J. Jang, K.-I. Cho, S. Nahm, and J.-D. Byun, J. Vac. Sci. Technol., B16, 858 (1998).
Y. D. Jiang, F. Zhang, C. J. Summers, and Z. L. Wang, Appl. Phys. Lett., 74, 1677 (1999).
T. K. Tran, W. Park, J. W. Tomm. B. K. Wagner, S. M. Jacobsen, C. J. Summers, P. N. Yocom, and S. K. McCelland, J. Appl. Phys., 78 5691 (1995).
E. Danielson, M. Devenney, D. M. Giaquinta, J. H. Golden, R. C. Haushalter, E. W. McFarland, D. M. Poojary, C. M. Reaves, W. H. Weinburg, and X. D. Wu, J. Molecular Structure 470, 229 (1998).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lee, Y.E., Norton, D.P., Budai, J.D. et al. Epitaxial Oxide Thin-Film Phosphors for Low Voltage FED Applications. MRS Online Proceedings Library 621, 241 (2000). https://doi.org/10.1557/PROC-621-Q2.4.1
Published:
DOI: https://doi.org/10.1557/PROC-621-Q2.4.1