Abstract
Strontium titanate (SrTiO3) thin films have been epitaxially grown on YB2Cu3O7−x (YBCO)/LaAlO3 at substrate temperatures of 660 to 700°C. X-ray diffraction (XRD) results indicated that single crystalline SrTiO3 thin films were epitaxially grown on the substrate with <100> orientation perpendicular to the substrates. The compositions of the films with different growth conditions were examined by Rutherford backscattering spectroscopy (RBS) and energy dispersive x-ray spectroscopy (EDX). The ratio of Sr/Ti is in the range of 0.9 to 1.1 for the films with a thickness of 1000-2000Å. The surface morphology of the films and the interfaces of the SrTiO3/YBCO structure were examined by scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). Very smooth surface and sharp interface were observed. The superconducting property of the YBCO layer, as measured by ac susceptibility, did not degrade after growth of SrTiO3 film. The dielectric constant as high as 320 was obtained at 100KHz. The leakage current density is less than 1×10−6A/cm2 at 3V operation.
Similar content being viewed by others
References
T. Sakumet al., Appl. Phys. Lett. 57 (23), 2431 (1990).
H. Yamaguchiet al., Jap. J. Appl. Phys. 30 (9B), 2197 (1991).
H. Yamaguchi et al., Proceedings of the 8th ISAF, 1992, pp.285.
R.F. Pinizzotto et al., Mat. Res. Soc. Symp. Proc. 243, 1992, pp.463.
E. Fujii et al., IEDM 1992, pp. 267.
H. Yamaguchi et al., Jap. J. Appi. Phys. 30 (9B), 2193 (1991).
J. Zhao, et al., Appl. Phys. Lett. 56 (23), 2342 (1990).
S. Liang, et al., presented at the 1993 MRS Fall Meeting, Boston, MA, 1993 (unpublished).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Liang, S., Chern, C., Shi, Z.Q. et al. MOCVD Growth of Epitaxial SrTiO3 Thin Films on YBa2 Cu3O7−x/LaAlO3. MRS Online Proceedings Library 335, 113–116 (1993). https://doi.org/10.1557/PROC-335-113
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-335-113