Abstract
Planar defects were observed in a hot isostatically pressed Al–Cu–Fe alloy. The defects were determined to be perpendicular to the fivefold direction. They were also found to be regions where the quasiperiodicity in the five-fold direction was disrupted, resulting in a periodicity along this direction of 1.06 nm. The defects were stable up to approximately 750 °C. The defects were determined to be formed by the applied shear forces associated with the consolidation process. The displacement vector of the defects was determined to be in a twofold direction perpendicular to the periodic direction.
Similar content being viewed by others
References
J. Devaud-Rzepski, M. Cornier-Quiquandon, and D. Gratias, Third International Meeting on Quasicrystals and Incommensurate Structures (World Scientific, Vista Hermosa, Mexico, 1989), p. 498.
M. Wollgarten, D. Gratias, Z. Zhang, and K. Urban, Philos. Mag. A 64, 819 (1991).
M. Wollgarten, Z. Zhang, and K. Urban, Philos. Mag. Lett. 65, 1 (1992).
M. X. Dai, R. Wang, J. Gui, and Y. F. Yan, Philos. Mag. Lett. 64, 21 (1991).
Y. Yan, R. Wang, and J. Feng, Philos. Mag. Lett. 66, 197 (1992).
S. Ranganathan, R. Prasad, and N. K. Mukhopadhyay, Philos. Mag. Lett. 59, 257 (1989).
A. Singh and S. Ranganathan, J. Non-Cryst. Solids 153–154, 86 (1993).
R. Wang, Y. F. Yan, and K. H. Kuo, J. Non-Cryst. Solids 153–154, 103 (1993).
M. X. Dai and K. Urban, Philos. Mag. Lett. 67, 67 (1993).
M. Wollgarten, H. Lakner, and K. Urban, J. Non-Cryst. Solids 153–154, 108 (1993).
Z. Zhang, N. C. Li, and K. Urban, J. Mater. Res. 6, 366 (1991).
T. Shibuya, T. Hashimoto, and S. Takeuchi, Jpn. J. Appl. Phys. 29, L349 (1990).
S. S. Kang and J. M. Dubois, Philos. Mag. A 66, 151 (1992).
D. Bresson and D. Gratias, J. Non-Cryst. Solids 153–154, 468 (1993).
J. E. Shield, M. J. Kramer, and R. W. McCallum, J. Mater. Res. 9, 343 (1994).
M. Wollgarten, M. Beyss, K. Urban, N. Liebertz, and U. Köster, Phys. Rev. Lett. 71, 549 (1993).
J. E. Shield, M. J. Kramer, and R. W. McCallum, J. Mater. Res. 8, 1199 (1993).
J. E. Shield and M. J. Kramer, Philos. Mag. Lett. 69, 115 (1994).
P. Bancel, Quasicrystals: The State of the Art, edited by D. P. DiVincenzo and P. J. Steinhardt (World Scientific, Singapore, 1991), p. 23.
M. Wollgarten, R. Rosenfeld, M. Feuerbacher, C. Metzmacher, K. Urban, B. Baufeld, M. Bartsch, and R. Messerschmidt, Proceedings of the 5th International Conference on Quasicrystals, edited by C. Janot and R. Mosseri (World Scientific, London, 1996).
J. E. Shield and M. J. Kramer, Scripta Metall. 34, 913 (1996).
D. Levine, T. C. Lubensky, S. Ostlund, S. Ramaswamy, P. J. Steinhardt, and J. Toner, Phys. Rev. Lett. 54, 1520 (1985).
J. E. S. Socolar, T. C. Lubensky, and P. J. Steinhardt, Phys. Rev. B 34, 3345 (1986).
R. E. Reed-Hill, Physical Metallurgy Principles (Brooks/Cole Engineering Division, Monterey, CA, 1973), p. 655.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shield, J.E., Kramer, M.J. Deformation-induced planar defects in Al–Cu–Fe quasicrystals. Journal of Materials Research 12, 300–303 (1997). https://doi.org/10.1557/JMR.1997.0039
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1997.0039