Abstract
The biosynthesis and characterization of medium chain length poly-3-hydroxyalkanoates (mcl-PHA) produced by Pseudomonas putida Bet001 isolated from palm oil mill effluent was studied. The biosynthesis of mcl-PHA in this newly isolated microorganism follows a growth-associated trend. Mcl-PHA accumulation ranging from 49.7 to 68.9% on cell dry weight (CDW) basis were observed when fatty acids ranging from octanoic acid (C8∶0) to oleic acid (C18∶1) were used as sole carbon and energy source. Molecular weight of the polymer was found to be ranging from 55.7 to 77.7 kDa. Depending on the type of fatty acid used, the 1H NMR and GCMSMS analyses of the chiral polymer showed a composition of even and odd carbon atom chain with monomer length of C4 to C14 with C8 and C10 as the principal monomers. No unsaturated monomer was detected. Thermo-chemical analyses showed the accumulated PHA to be semi-crystalline polymer with good thermal stability, having a thermal degradation temperature (Td) of 264.6 to 318.8 (±0.2) oC, melting temperature (Tm) of 43. (±0.2) oC, glass transition temperature (Tg) of −1.0 (±0.2) oC and apparent melting enthalpy of fusion (ΔHf) of 100.9 (±0.1) J g−1.
Citation: Gumel AM, Annuar MSM, Heidelberg T (2012) Biosynthesis and Characterization of Polyhydroxyalkanoates Copolymers Produced by Pseudomonas putida Bet001 Isolated from Palm Oil Mill Effluent. PLoS ONE 7(9): e45214. https://doi.org/10.1371/journal.pone.0045214
Editor: Melanie R. Mormile, Missouri University of Science and Technology, United States of America
Received: May 8, 2012; Accepted: August 13, 2012; Published: September 20, 2012
Copyright: © Gumel et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Funding: This study was funded by University of Malaya research grants RG165-11AFR, PV36/2012A, UM.C/625/1/HIR/MOHE/05 and RP024-2012A. The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.
Competing interests: The authors have declared that no competing interests exist.
Introduction
The current increase in the utilization of polyhydroxyalkanoates (PHAs) in various industrial and biomedical applications is due to their biodegradability, compatibility, resorbability and piezoelectricity [1]. Their diverse chemical properties have made them a subject of many research interests. In fact, the diversity of different monomeric components in accumulated PHA that arises from superb biological polymerization system resulted in potentially diversified high-molecular weight polymeric materials. Growing concern over environmental pollution has heightened the interest in these biodegradable polymers over their chemically synthesized counterparts.
The low level of medium-chain-length PHA (mcl-PHA) and limited substrate utilization in different bacterial species, poses limitation to industrial production of these polymers [2]. The increasing demand of highly functionalized PHA for specialty applications, warrant the bio-prospecting of bacterial species capable of accumulating these biodegradable polymers. Several bacterial species known to accumulate PHA have been isolated from different ecological niches [3], [4], [5], [6], [7], [8]. Among the extensively studied bacterial species are those belonging to genus Pseudomonas [9], [10], [11], [12], [13], that are known to accumulate intracellular PHA under limited cell growth phase in the presence of abundant carbon source and minimal nutrient condition [14]. When fatty acid is fed to these bacteria, it passes through beta-oxidation biosynthetic pathway to produce the PHA intermediates thereby losing two (2) carbon atoms per each cycle [15], [16].
A number of published works use unsaturated fatty acids such as oleic acid (C18∶1) to produce mcl-PHA with unsaturated side-chain monomers [17], [18], [19], [20]. In this study, the growth and biosynthesis of mcl-PHA by a strain of Pseudomonas putida isolated from palm oil mill effluent are reported, along with characterization of the mcl-PHA copolymer produced when the bacterium is fed with oleic acid (C18∶1). For comparison, selected fatty acids viz. octanoic acid (C8∶0), dodecanoic acid (C12∶0) and hexadecanoic acid (C16∶0) were also tested as substrates.
Methods
Bacterial Isolation and Characterization
Pseudomonas putida Bet001 was isolated from palm oil mill effluent using isolation agar medium containing (g L−1): peptone 20; K2SO4 10; MgCl2.6H2O 1.4; irgasan 0.025; glycerol 25.2 and agar 13.6. Preliminary biochemical characterization was done using api® 20 NE (bioMerieux® USA) biochemical typing kits as stated in manufacturer’s guideline. Intracellular PHA accumulation was screened using both Sudan Black B and Nile red staining techniques according to literatures [21], [22]. Intracellular PHA granules accumulation was also observed using transmission electron microscopy (Philips CM12, United Kingdom). The morphology of the bacterial colonies isolated and the Gram staining characteristics were observed under Motic® microscope BA200 equipped with Moticam 2300 camera (Motic®, Japan). GF1 DNA extraction kit (Vivantis Sdn Bhd, Malaysia) was used to extract the bacterial DNA for the 16S rRNA molecular characterization according to manufacturer’s guidelines. Post PCR analysis was done by blasting of both forward and reverse sequences against sequences in GeneBank (NCBI) and RDPII (Ribosomal Database Project II) databases to search for homology sequences. The extracted DNA nucleotide sequence has been deposited in European Nucleotide Archive (ENA) with accession number HE573173.
Culture Conditions and Fermentation Process
Sterile growth medium (100 ml per each 250 ml conical flask) containing (g L−1): yeast extract 10.0 (Bacto™ USA), nutrient broth 15.0 (Merck, Germany) and ammonium sulfate 5.0 (Sigma Aldrich, Germany) was used as inoculum cultivation medium for the bacterium. 3% (v/v) of P. putida Bet001 stock inoculum was introduced into this medium aseptically and incubated in shaking incubator (Daihan LabTech®, Korea) at 30°C, 250 rpm for 24 hours. The biomass was harvested from 3 ml culture broth via centrifugation at 4°C, 9000 ×g for 10 min. The recovered biomass was seeded aseptically into PHA production medium. The medium contains sterile minerals of (g L−1) sodium ammonium hydrogen phosphate tetrahydrate [NaNH4HPO4.4H2O] 3.5, K2HPO4 5.7, KH2PO4 3.7, and 10 mM oleic acid (unless otherwise stated) at a pH of 7.0 (±0.1). Separate sterile solutions of 0.1 M MgSO4.7H2O and trace elements (MT) containing (g L−1): CaCl2.2H2O 1.47, CoCl2.6H2O 2.38, CuCl2.2H2O 0.17, FeSO4.7H2O 2.78, MnCl2.4H2O 1.98 and ZnSO4.7H2O 0.29 dissolved in 1 M HCl were aseptically added to the PHA production media prior to inoculation at 1.0% (v/v) and 0.1% (v/v), respectively. 5 g L−1 of harvested biomass from inoculum growth media was seeded into this medium (100 ml per 250 ml conical flask) aseptically and incubated as described previously for a total period of 48 hours unless otherwise stated. PHA extraction was done according to literature [10]. 5 g of vacuum dried biomass was suspended in 30 ml chloroform and refluxed at 60°C for 4 hours. The refluxed chloroform containing the extracted PHA was filtered out of the residual biomass debris using Buchner filter funnel equipped with sintered glass. The filtrate was then concentrated under vacuum using rotary evaporator at 40°C until about a fifth of the total volume. The polymer was precipitated out of the concentrate by dispersing it into a beaker containing excess cold methanol (at least 1∶4 volume ratio). The mcl-PHA obtained underwent a minimum of three-repeated purification process by sequential chloroform dissolution and methanol re-precipitation.
Biomass Estimation
A known biomass dry weight concentrations were used to prepare a standard calibration, using Jasco V-630 UV/VIS spectrophotometer (Jasco, Japan) at the absorbance of 600 nm. Aliquote samples were withdrawn aseptically at regular intervals and centrifuged at 9000 ×g for 10 min, then washed twice with 0.05 M phosphate buffer. After final centrifugation, the cells were re-suspended in the same buffer prior to absorbance reading against the phosphate buffer blank.
Residual Fatty Acid Quantification
The residual fatty acid estimation was done according to Marseno et al. [23] modified protocol. Cell free supernatant (1 ml) was mixed with n-heptane (3 ml) and centrifuge at 9000 × g to separate the residual fatty acid. 2 ml of the top layer of n-heptane was withdrawn into a test tube, to this solution, 200 µl of 5% (w/v) copper (II) acetate monohydrate solution (5 g copper (II) acetate monohydrate dissolved in 90 ml distilled water; pyridine and distilled water were respectively used to adjust the solution pH to 6 and bring the final volume to100 ml) was added and vortexed for 60 sec. This mixture was allowed to stand for 20 sec before it was read at 705 nm against distilled water blank using Jasco V-630 UV/VIS spectrophotometer (Jasco, Japan). A standard calibration was performed using a stock of different fatty acid concentrations (0.5 to 1 mM) that were made by dissolving the specified mass of fatty acid in n-heptane and treated as mentioned earlier.
Residual Ammonium Quantification
Residual ammonium was quantified using phenol hypochlorite method as described by Solorzano [24]. Cell free supernatant (2 ml) was diluted with distilled water to 5 ml. To this solution 0.2 ml of alcoholic phenol (10 g phenol in 90 ml absolute ethanol) was added followed by the addition of 0.2 ml of sodium nitroprusside solution (0.5 g sodium nitroprusside in 99.5 ml distilled water). Oxidizing solution (0.5 ml) was added to the mixture while agitating to ensure uniform indole-phenol coloration. The oxidizing solution was composed of 4∶1 mixture of alkaline solution to oxidizing reagent. The alkaline solution was composed of 100 g trisodium citrate, 5 g sodium hydroxide dissolved in 500 ml of distilled water. The oxidizing reagent was 1.5 N sodium hypochlorite solution. The mixture was then allowed to stand for an hour at room temperature (27°C) resulting in light-blue coloration that was measured as described above at 640 nm against blank distilled water. Residual ammonium concentration was then quantified in reference to standard calibration curve of known ammonium concentrations.
PHA Authentication
FTIR spectroscopy.
Attenuated total reflectance (ATR) FTIR was used to record the PHA spectrum on Perkin-Elmer FTIR spectrum-400 spectrometer (Perkin-Elmer Inc., Wellesley, MA, USA) at room temperature (27°C) and a scan range of 400 to 4000 cm−1 was applied for 10 scans. A paste of 0.01 g of the sample was prepared in dichloromethane. A liquid film of the mixture was then applied on to NaCl crystal window and the spectrum was read after the solvent has been dried.
Proton NMR analysis.
JEOL JNM-GSX 270 FT-NMR (JOEL Ltd, Tokyo, Japan) spectrometer was used to record the 1H NMR spectrum at 250 MHz against tetramethylsilane (TMS) internal reference standard. Approximately 5 mg PHA sample was dissolved in 2 ml deuterated chloroform (CDCl3) and filtered into NMR tube using borosilicate glass syringe equipped with 0.22 µm PTFE disposable filter (11807–25, Sartorius Stedim, Germany).
GC-MSMS analysis.
GC-MSMS was recorded on Agilent triple quadrupole 7000B (Agilent, USA), equipped with GCMSMS triple axis detector carrying Agilent HP-5 ms column (30 m length× 0.25 mm internal diameter× 0.25 µm film). PHA sample in the form of hydroxyalkanoic acids methyl esters were used for the GC-MSMS analysis according to method reported in literatures [25], [26]. Methanolyzed sample (1 µl) was automatically injected into the GC at a split ratio of 1∶50. The injection temperature was set at 280°C while the oven and column temperatures were programmed as 40°C for 1 min then increase to 120°C at 15°C min−1, hold for 2 min, and increase to 250°C at 10°C min−1 hold for 15 min. Helium was used as carrier gas at 48.3 ml min−1 and 0.41 bar pressure. Mass spectra were acquired at 1250 scan speed using electron impact energy of 70 eV at 200°C ion-source and 280oC interface temperatures respectively. Standard monomers of methyl hydroxyalkanoates (Larodan, Sweden) were used as reference for peak retention time and ionization mass determination.
Gel permeation chromatography (GPC).
Waters 600 (Waters Corp, Milford, MA, USA) equipped with a Waters refractive index detector (model 2414) having the following gel columns (7.8 mm internal diameter 300 mm) in series: HR1, HR2, HR5E and HR5E Waters Styragel HR-THF was used to record the chromatogram relative to calibration curve of standard monodisperse polystyrenes (3.72 x102, 2.63×103, 9.10×103, 3.79×104, 3.55×105, 7.06×105, 3.84×106 and 6.77×106 Da). The PHA samples were dissolved in tetrahydrofuran (THF) at a concentration of 2.0 mg mL−1, filtered through a 0.22 µm PTFE filter. 100 µL aliquot of the sample was injected at 40°C using THF as a mobile phase at a flow rate of 1.0 mL min−1.
Thermal Analyses
Differential scanning calorimetry (DSC).
The extracted PHA was subjected to differential thermal analysis using Mettler-Toledo differential scanning calorimeter (DSC 822e; Mettler-Toledo, USA) running STARe DSC ver 8.10 software; equipped with HAAKE EK90/MT digital immersion cooler (Thermo Fischer Scientific, USA). Scans were made at a temperature range of −60°C to 180°C with a heating rate of 10°C min−1 under a nitrogen flow rate of 0.12 L min−1at a head pressure of 1.5 bar. The melting temperature (Tm) was taken at the endothermic peak of the DSC thermogram. The endothermic melting enthalpy (ΔHm) was used to calculate the polymer crystallinity (Xp) on the basis of melting enthalpy (ΔHmo) of 100% crystalline PHB according to equation 1 as reported somewhere else [27], assuming 142 J g−1 as the melting enthalpy of 100% crystalline PHB as cited in literature [28].(1)
Results and Discussion
Strain Characterization and PHA Production
Sudan Black B staining was used in the microscopic observation for a possible accumulation of intracellular PHA by the isolated strain (Fig. 1a). Further confirmation of the presence of accumulated granule was made by transmission electron microscopy (Fig. 1b). The bacterial strain was further characterized using biochemical analyses and 16S rRNA molecular characterization. The biochemical analyses indicated a probability of 99.5% for the isolate to be identified as Pseudomonas putida. This result was corroborated by RDP blast neighbor-joining phylogenetic analysis (Fig. 2), where 99% analogy was observed between the isolate and Pseudomonas putida strains AJ785569, AN2, BCNU106, DQ060242 and DQ087528. This isolate was designated as P. putida Bet001and subsequently used in the PHA production using shake flask in a two-step batch fermentation process with different fatty acids as a sole carbon and energy source. PHA accumulation was observed to span from 49.7 to 68.9 dry weight % and was composed of varied monomer fractions ranging from 3-hydroxyhexanoate to 3-hydroxytetradecanoate depending on the culture conditions and the type of fatty acids used.
(A) phase contrast (X 100 magnification) and (B) T.E.M (X 5000 magnification) when cultivated on palmitic acid (C16∶0) at 30°C, 200 rpm for 48 h.
PHA Authentication
FTIR spectroscopy.
The extracted PHA sample was subjected to nondestructive attenuated total reflectance FT-IR. Observed infrared absorption at 3420.20 cm−1 was assigned to the hydroxyl group of the polymer chain [29]. Absorption band at 2955.76 cm−1 was assigned to asymmetric methyl group. Asymmetric CH2 of the lateral monomeric chains were assigned to the stretching vibration at 2925.98 cm−1. The absorption at 2855.99 cm−1 has been assigned to symmetrical CH3 and the intensity of the band has been reported to be due to conformational disorder obtained in the process of crystallization [28]. While the absorption band of 1741.44 cm−1 has been reported to be a PHA marker band assigned to carbonyl (C = O) ester bond stretching vibration according to Randriamahefa et al. [30]. The vibrations at 1659.50 and 1460.39 cm−1 have been assigned to bacterial intracellular amide (–CO–N–) I and II respectively (Fig. 3); furthermore, these bands were also reported to be species specific [30]. Absorption at 1378.83 cm−1 is assigned to terminal CH3 groups [12], while that at 1259.89 cm−1 is due to asymmetric C–O–C stretching vibration. Series of absorption bands at 1166.87 cm−1 to 619.39 cm−1 were assigned to C–O and C–C stretching vibration in the amorphous phase.
PHA proton NMR characterization.
The proton NMR spectrum of the produced PHA was characterized in reference to the internal standard trimethylsilane. The observed multiplet peaks number 1(δ 2.5 ppm) and triplet peaks 2 (δ 5.2 ppm) are assigned to methylene and methine protons of the α and β-carbon respectively [15], [16], [18], [31]. Contrary to some literatures assigning the observed triplets at chemical shift 2.3 ppm (Fig. 4) to unsaturation of PHA monomers [18], [26], upon further analysis using GCMSMS, we proposed the peak to be due to hydrophobic oleate and palmitate from cellular membrane lipids. Peak number 3 (δ 1.6 ppm) is assigned to methylene protons adjacent to the β-carbon in the side-chains [15], [16], [18], [31]. Peak number 4 (δ 1.3) and triplet number 5 (δ 0.9) are assigned to the methylene protons and terminal methyl proton of the side-chains respectively [15], [16], [18], [31].
Thermal Analyses
The calorimetric scan of the extracted PHA showed the endothermic melting temperature (Tm) of this polymer to be 43.0 (±0.2) oC, glass transition temperature (Tg) of −1.0 (±0.2) oC and apparent melting enthalpy of fusion (ΔHf) of 100.9 (±0.1) J g−1. The relatively low melting and glass transition temperatures were attributed to the random composition of 3HA monomers in the polymer (see later discussion). This observation was found to be in good agreement with what has been reported by Matsusaki et al. [32] when observing the PHA biosynthesis in recombinant Pseudomonas sp. 6 1–3 strain fed with dodecanoic acid (C12∶0). The bacterium produced random copolymer of PHA with endothermic melting temperature of 42°C. The observed high apparent heat of fusion could be due to the presence of long chain monomer fraction which in turn was reported to favor side-chain crystallization resulting in polymer with high apparent enthalpy of fusion. This observation was found to agree with reported literatures [15], [16], [33].
PHA thermal stability is an important parameter to be studied during polymer analyses as it reflects the maximum temperature the polymer can withstand before thermal decomposition. Thermal gravimetric analysis of the extracted polymer showed an increase in polymer thermal stability with increasing fatty acid chain length fed i.e. from C8∶0 to C18∶1 (thermal degradation temperature of 264.6 to 318.8oC ±0.2).This is attributed to the increase in the fractions of longer monomer such as 3HDD and 3HTD that became incorporated into the PHA from the metabolism of the longer fatty acid substrates (Table 1). It has been reported also that this increase in thermal stability could be due to random co-monomer chain-length that resulted in high side chain crystallization conferring thermal stability to the polymer [15], [33].
Effect of Carbon Source on the PHA Composition and Yield
The effect of different carbon source on PHA composition has been studied. The composition of PHA accumulated by P. putida Bet001 grown on different carbon sources at 30°C for 48 hours is presented in Table 1. PHA accumulation in the range of 49.7 to 68.9% (w/w) has been observed when the organism is fed with C8∶0 to C18∶1 fatty acids, with a polymer composition ranging from 3HB (four carbon atom length) to 3HTD (fourteen carbon atom length) except when oleic acid was used as substrate, a small amount of odd chain monomer i.e. 3HHp (seven carbon atom length) was also detected. At first, this was considered as possible contamination of the extracted polymer sample by cellular components. Thus, the purification step was repeated at least three times and the polymer re-extracted for GCMSMS analysis. The persistence of the strong signal detected by mass spectrometry for the presence of 3HHp entails re-consideration of the contamination hypothesis with non-PHA components. From the basic knowledge about β-oxidation of even carbon atom length of fatty acids, it is not clear at this point the exact reason for the incorporation of an odd carbon atom length monomer like 3HHp into the polymer when oleic acid (C18∶1) was used as a sole carbon and energy source for the bacterial growth and PHA accumulation, and not with other fatty acids tested.
Based on mass spectrometric analyses, feeding dodecanoic acid as sole carbon source resulted in PHA composed of four different monomers (3HHx 3.54 mole%, 3HO 38.19 mole%, 3HD 38.85 mole% and 3HDD 19.42 mole%). Similarly, Chung et al. [15] reported P. entomophila L48 to accumulate PHA having four different monomer units when fed with dodecanoic acid, with monomer fractions of 3HD (38.6%), 3HO (44.5%) as the dominant fractions. Feeding hexadecanoic acid as a carbon and energy source to P. putida Bet001 resulted in PHA with five different monomers (3HHx 4.06 mole%, 3HO 36.93 mole%, 3HD 34.78 mole%, 3HDD 17.97 mole% and 3HTD 6.26 mole%). When oleic acid (C18∶1) was fed under the same conditions, copolymer with up to seven different monomers of 3HB (1.52 mole%), 3HHx (5.01 mole%), 3HO (31.81 mole%), 3HD (24.07 mole%), 3HDD (22.86 mole%), 3HTD (14.05 mole%) and a small amount of odd carbon chain length monomer of 3-hydroxyheptanoate (3HHp) (0.68 mole mole%) were obtained. In contrast to other fatty acids tested, when oleic acid was fed, a short-chain length monomer of 3HB (four carbon atom length) accumulated. The accumulation of 3HB monomer was not detected in the bacterium when fatty acids C8∶0, C12∶0 and C16∶0 were fed. Again, similar to the accumulation of 3HHp, the exact reason for this observation is not clear at this stage. It was also observed that when oleic acid (C18∶1) was fed, no unsaturated PHA monomer was detected in the polymer produced. The most abundant monomers were C8 and C10 in all the samples tested, and this is in agreement with the hypothesis that PHA formed by Pseudomonads belonging to rRNA homology group I have C8 and C10 monomers as dominant components when grown on C8 to C18 fatty acids substrate [18], [34].
From the results presented in Table 1, the relationship between the PHA composition and the structure of the carbon source substrate showed that the PHA biosynthetic precursors in this bacterium are very likely fed by β-oxidation pathway.
Effect of Nitrogen Source Concentration on Specific Growth Rate (µ) and PHA Yield
The effect of nitrogen source concentration on specific growth rate and PHA yield during PHA biosynthesis in P. putida Bet001 is depicted in Fig. 5. It is clear that as the ammonium ion concentration increases from 0.01 to 0.1 g L−1, the specific growth (µ) also increases from 0.005 to 0.036 h−1with corresponding PHA yield of 13.4 to 68.9% (w/w) respectively. Increasing nitrogen source beyond this point resulted in a gradual plateau in the specific growth rate, probably due to the carbon source concentration began to be limited as in this study where the ammonium ion concentration was varied and the carbon source concentration was kept fixed. In a similar study, Annuar et al. [35] observed the increase in specific growth rate of P. putida PGA1 from 0 to 0.18 h−1 by increasing the ammonium ion concentration from 0 to 0.1 g L−1; further increase in ammonium ion concentration (0.6 to 0.8 g L−1) resulted in a decrease in the specific growth rate to 0.14 h−1. Interestingly, the PHA fraction from the total biomass also increases as the specific growth rate increases, indicating a growth associated PHA biosynthesis in this bacterium. The PHA fraction reached a constant value when specific growth rate became constant at high ammonium ion concentrations. This is in contrast with the recognized PHA accumulation in many Pseudomonas species, where the highest accumulation is observed when the specific growth rate of the organism is low under nutrient limitation/starvation [14], [18], [35]. The observed increase in the specific growth rate at low ammonium ion concentrations (≤0.1 g L−1) could probably be due to high ammonium uptake by the cells [35].
Influence of Carbon-nitrogen Molar Ratio on Biomass and Polymer Content
It has been observed that PHA content of the cell can be increased by changing the molar ratio between carbon-to-nitrogen (C:N) source (Table 2). By fixing the ammonium ion concentration at 0.1 g L−1 while varying the carbon source concentration; it is observed that increase in C:N molar ratio from 10 to 30 was followed by increase in percentage PHA accumulation and biomass from 16 to 69% and from 9.6 to 15.3 g L−1, respectively. The proportional increase in biomass with increase of C:N ratio up to 20, could indicate that below 20 carbon is limiting growth. Additional increase in C:N molar ratio after 20 however, did not results in further increase in biomass amount, as it is expected that the ammonium concentration no longer sufficient to sustain extended growth. The results from this experiment offer additional support for the growth-linked PHA accumulation in this bacterium. Maximum PHA accumulation at approximately 70% was found for C:N molar ratios of 25 and 30. The molecular weight of the PHA from the different C:N molar ratios tested fell within a narrow range of 37 to 75 kDa. The crystallinity (Xp) and poly dispersity index (PDI) remained constant at all the C:N molar ratio tested.
Conclusions
A chiral PHA copolymer consisting of monomers ranging from 3-hydroxybutyrate (3HB) to 3-hydroxytetradecanoate (3HTD) were synthesized by a new isolate P. putida Bet001 when fed with different fatty acids. The biosynthesis of the PHA by this new isolate is growth-associated. When fed with oleic acid (C18∶1), the PHA extracted from the isolate showed the presence of a monomer with odd carbon atom length i.e. 3-hydroxyheptanoate (3HHp). However, no unsaturated monomer was detected when oleic acid (C18∶1) was fed. P. putida Bet001 accumulated about 69% PHA on cell dry weight basis with good thermal stability, relatively high molecular weight and crystallinity.
Author Contributions
Conceived and designed the experiments: AMG MSMA. Performed the experiments: AMG. Analyzed the data: AMG MSMA TH. Contributed reagents/materials/analysis tools: MSMA. Wrote the paper: AMG MSMA.
References
- 1.
Rai R, Keshavarz T, Roether J, Boccaccini A, Roy I (2011) Medium chain length polyhydroxyalkanoates, promising new biomedical materials for the future. Mat Sci Eng R 72 29–47.
- 2. Gumel AM, Annuar MSM, Heidelberg T (2012) Effects of carbon substrates on biodegradable polymer composition and stability produced by Delftia tsuruhatensis Bet002 isolated from palm oil mill effluent. Polym Degradation Stab 97: 1227–1231.
- 3. Akaraonye E, Keshavarz T, Roy I (2010) Production of polyhydroxyalkanoates: the future green materials of choice. J Chem Technol Biotechnol 85: 732–743.
- 4.
Bohmert-Tatarev K, Mcavoy S, Peoples OP, Snell KD (2010) Stable, fertile, high polyhydroxyalkanoate producting plants and methods of producing them. US Patent App. 20,100/229,258.
- 5. Grothe E, Chisti Y (2000) Poly (ß-hydroxybutyric acid) thermoplastic production by Alcaligenes latus: Behavior of fed-batch cultures. Bioproc Biosyst Eng 22: 441–449.
- 6. Thomson N, Roy I, Summers D, Sivaniah E (2010) In vitro production of polyhydroxyalkanoates: achievements and applications. J Chem Technol Biotechnol 85: 760–767.
- 7. Yamane T (1992) Cultivation engineering of microbial bioplastics production. FEMS Microbiol Lett 103: 257–264.
- 8. Dalal J, Sarma PM, Lavania M, Mandal AK, Lal B (2010) Evaluation of bacterial strains isolated from oil-contaminated soil for production of polyhydroxyalkanoic acids (PHA). Pedobiologia 54: 25–30.
- 9. Allen AD, Anderson WA, Ayorinde FO, Eribo BE (2010) Biosynthesis and characterization of copolymer poly (3HB-co-3HV) from saponified Jatropha curcas oil by Pseudomonas oleovorans. J Ind Microbiol Biotechnol 37: 849–856.
- 10. Annuar MSM, Tan IKP, Ibrahim S, Ramachandran KB (2007) Production of medium-chain-length poly (3-hydroxyalkanoates) from crude fatty acids mixture by Pseudomonas putida. Food and Bioproducts Proc 85: 104–119.
- 11. Elbahloul Y, Steinbuchel A (2009) Large-scale production of poly (3-hydroxyoctanoic acid) by Pseudomonas putida GPo1 and a simplified downstream process. Appl Environ Microbiol 75: 643–651.
- 12. Sha K, Li D, Li Y, Zhang B, Wang J (2008) The chemoenzymatic synthesis of a novel CBABC-type pentablock copolymer and its self-assembled “crew-cut” aggregation. Macromolecules 41: 361–371.
- 13. Vishnuvardhan Reddy S, Thirumala M, Mahmood S (2009) Production of PHB and P (3HB-co-3HV) biopolymers by Bacillus megaterium strain OU303A isolated from municipal sewage sludge. World J Microbiol Biotechnol 25: 391–397.
- 14. Annuar MSM, Tan IKP, Ramachandran KB (2008) Evaluation of nitrogen sources for growth and production of medium-chain-length poly-(3-hydroxyalkanoates) from palm kernel oil by Pseudomonas putida PGA1. Asia-Pac J Mol Biol Biotechnol 16: 11–15.
- 15. Chung AL, Jin HL, Huang LJ, Ye HM, Chen JC, et al. (2011) Biosynthesis and characterization of poly (3-hydroxydodecanoate) by ß-oxidation inhibited mutant of Pseudomonas entomophila L48. Biomacromolecules 12: 3559–3566.
- 16. Liu Q, Luo G, Zhou XR, Chen G-Q (2011) Biosynthesis of poly(3-hydroxydecanoate) and 3-hydroxydodecanoate dominating polyhydroxyalkanoates by ß-oxidation pathway inhibited Pseudomonas putida. Metab Eng 13: 11–17.
- 17. Albuquerque MGE, Martino V, Pollet E, Avérous L, Reis MAM (2011) Mixed culture polyhydroxyalkanoate (PHA) production from volatile fatty acid (VFA)-rich streams: Effect of substrate composition and feeding regime on PHA productivity, composition and properties. J Biotechnol 151: 66–76.
- 18. Haba E, Vidal-Mas J, Bassas M, Espuny MJ, Llorens J, et al. (2007) Poly 3-(hydroxyalkanoates) produced from oily substrates by Pseudomonas aeruginosa 47T2 (NCBIM 40044): Effect of nutrients and incubation temperature on polymer composition. Biochem Eng J 35: 99–106.
- 19. Ni Y-Y, Kim DY, Chung MG, Lee SH, Park H-Y, et al. (2010) Biosynthesis of medium-chain-length poly(3-hydroxyalkanoates) by volatile aromatic hydrocarbons-degrading Pseudomonas fulva TY16. Bioresour Technol 101: 8485–8488.
- 20. Tan IKP, Kumar KS, Theanmalar M, Gan SN, Gordon Iii B (1997) Saponified palm kernel oil and its major free fatty acids as carbon substrates for the production of polyhydroxyalkanoates in Pseudomonas putida PGA1. Appl Microbiol Biotechnol 47: 207–211.
- 21. Burdon KL (1946) Fatty material in bacteria and fungi revealed by staining dried, fixed slide preparations. J Bacteriol 52: 665–678.
- 22. Spiekermann P, Rehm BHA, Kalscheuer R, Baumeister D, Steinbüchel A (1999) A sensitive, viable-colony staining method using Nile red for direct screening of bacteria that accumulate polyhydroxyalkanoic acids and other lipid storage compounds. Arch Microbiol 171: 73–80.
- 23. Marseno DW, Indrati R, Ohta Y (1998) A Simplified Method for Determination of Free Fatty Acids for Soluble and Immobilized Lipase Assay. Indon Food Nutr Prog 5: 79–83.
- 24. Solorzano L (1969) Determination of ammonia in natural waters by the phenolhypochlorite method. Limnol Oceanogr 14: 799–801.
- 25. Lee EY, Choi CY (1997) Structural identification of polyhydroxyalkanoic acid (PHA) containing 4-hydroxyalkanoic acids by gas chromatography-mass spectrometry (GC-MS) and its application to bacteria screening. Biotechnol Tech 11: 167–171.
- 26. Sin MC, Annuar MSM, Tan IKP, Gan SN (2010) Thermodegradation of medium-chain-length poly (3-hydroxyalkanoates) produced by Pseudomonas putida from oleic acid. Polym Degradation Stab 95: 2334–2342.
- 27. Dai Y, Lambert L, Yuan Z, Keller J (2008) Characterisation of polyhydroxyalkanoate copolymers with controllable four-monomer composition. J Biotechnol 134: 137–145.
- 28. López-Cuellar M, Alba-Flores J, Rodríguez J, Pérez-Guevara F (2011) Production of polyhydroxyalkanoates (PHAs) with canola oil as carbon source. Int J Biol Macromol 48: 74–80.
- 29. Bonduelle C, Martin-Vaca B, Bourissou D (2009) Lipase-catalyzed ring-opening polymerization of the O-carboxylic anhydride derived from lactic acid. Biomacromolecules 10: 3069–3073.
- 30. Randriamahefa S, Renard E, Guérin P, Langlois V (2003) Fourier transform infrared spectroscopy for screening and quantifying production of PHAs by Pseudomonas grown on sodium octanoate. Biomacromolecules 4: 1092–1097.
- 31. Huijberts G, Eggink G, de Waard P, Huisman GW, Witholt B (1992) Pseudomonas putida KT2442 cultivated on glucose accumulates poly (3-hydroxyalkanoates) consisting of saturated and unsaturated monomers. Appl Environ Microbiol 58: 536–544.
- 32. Matsusaki H, Abe H, Doi Y (2000) Biosynthesis and properties of poly (3-hydroxybutyrate-co-3-hydroxyalkanoates) by recombinant strains of Pseudomonas sp. 61–3. Biomacromolecules 1: 17–22.
- 33. Zhang HF, Ma L, Wang ZH, Chen GQ (2009) Biosynthesis and characterization of 3 hydroxyalkanoate terpolyesters with adjustable properties by Aeromonas hydrophila. Biotechnol Bioeng 104: 582–589.
- 34. Madison LL, Huisman GW (1999) Metabolic engineering of poly (3-hydroxyalkanoates): from DNA to plastic. Microbiol Mol Biol Rev 63: 21–53.
- 35. Annuar MSM, Tan IKP, Ibrahim S, Ramachandran KB (2006) Ammonium uptake and growth kinetics of Pseudomonas putida PGA1. Asia-Pac J Mol Biol Biotechnol 14: 1–10.