3D printed PLA Army-Navy retractors when used as linear retractors yield clinically acceptable tolerances

3D Printing in Medicine volume 5, Article number: 16 (2019) Cite this article

Abstract

Background

Modern low-cost 3D printing technologies offer the promise of access to surgical tools in resource scarce areas, however optimal designs for manufacturing have not yet been established. We explore how the optimization of 3D printing parameters when manufacturing polylactic acid filament based Army-Navy retractors vastly increases the strength of retractors, and investigate sources of variability in retractor strength, material cost, printing time, and parameter limitations.

Methods

Standard retractors were printed from various polylactic acid filament spools intra-manufacturer and inter-manufacturer to measure variability in retractor strength. Printing parameters were systematically varied to determine optimum printing parameters. These parameters include retractor width, thickness, infill percentage, infill geometry, perimeter number, and a reinforced joint design. Estimated retractor mass from computer models allows us to estimate material cost.

Results

We found statistically significant differences in retractor strength between spools of the same manufacturer and between manufacturers. We determined the true strength optimized retractor to have 30% infill, 3 perimeters, 0.25 in. thickness, 0.75 in. width, and has “Triangle” infill geometry and reinforced joints, failing at more than 15X the threshold for clinically excessive retraction and costs $1.25 USD.

Conclusions

The optimization of 3D printed Army-Navy retractors greatly improve the efficacy of this instrument and expedite the adoption of 3D printing technology in many diverse fields in medicine not necessarily limited to resource poor settings.

Background

Current literature explores the role of 3D printing in changing the surgical landscape through the new ability to create more resource efficient in-house surgical instruments, along with anatomical models of patients that assist in training and preoperative planning, prosthetics, personalized surgical equipment better suited for patient morphologies, and 3D printed implants [1,2,3,4,5,6,7,8,9,10,11,12,13,14]. Notably, these vast strides in 3D printing technologies are also allowing healthcare providers to create robust, low-cost medical and surgical equipment in resource scarce areas, such as in developing nations and in aerospace medicine where weight and space limitations exist [15,16,17]. 3D printing allows for rapid prototyping and manufacturing that expedites the improvement of medical equipment, examples of which are the development of better splints, syringes, and surgical suction tips [18,19,20]. Furthermore, it is shown that the high heat used during the 3D printing process sterilizes the final print [21]. Specifically, 3D printed polylactic acid (PLA) Army-Navy retractors offer a cheaper, lighter-weight, and more space-efficient alternative to traditional stainless steel Army-Navy retractors without compromising surgical retraction capabilities [22]. Army-Navy retractors are commonly used in a myriad of procedures involving retraction of shallow incisions and are listed at an online retail price of approximately $24 USD per retractor. Though literature exists in quantifying the mechanical strength of 3D printed Army-Navy retractors, none have sought to optimize printing settings and retractor designs, which could lead to additional discussion about improving the efficacy of 3D printed surgical instruments and allow healthcare providers in resource scarce areas to adopt this technology.

Methods

Software and design

Army-Navy retractor models were designed in Autodesk® Fusion 360™ (Autodesk®, Inc.). Standard Tessellation Language (STL) files of these models were exported from Autodesk Fusion 360 and imported into Slic3r Prusa Edition – 1.38.7–prusa3d (Prusa Research), a software that processes STL files into thin slices that can then be converted into g-codes, a numerical control programming language that provides spatial instructions to the 3D printer to guide the printing process, ultimately building the print one layer at a time. All prints in this study have layer heights of 0.15 mm. Print settings were systematically varied in Slic3r Prusa Edition to produce unique g-codes and ultimately determine the most strength optimal print settings for our designed PLA Army-Navy retractors.

Control retractors are set to have 20% infill, 2 perimeters, a “Grid” infill geometry, “Rectilinear” top/bottom fill pattern, default Slic3r Prusa Edition print settings, and are oriented horizontally so that no support material is needed (Fig. 1a, c). Infill geometry, infill percent, and perimeter number were changed, respectively, with all other parameters held constant in Slic3r Prusa Edition. For retractors with reinforced joints (Fig. 1b), differing retractor widths, and differing retractor thicknesses, separate retractor models were designed in Autodesk Fusion 360 and the corresponding STLs were imported separately into Slic3r.

Fig. 1
figure 1

a Standard retractor design and b reinforced retractor design in inches. c The Army-Navy retractor is oriented on the print bed horizontally such that no support material is needed

Full size image

3D printer model and hardware

G-codes are loaded into an SD card and inserted into the Original Prusa i3 MK3 3D printer (Prusa Research) where the print can be selected and started. An Original Prusa i3 MK3 kit is priced at $750 USD and a fully assembled Original Prusa i3 MK3 3D printer is priced at $1000 USD. A 0.4 mm nozzle was used with the extruder temperature set to 235 °C for all layers and bed temperature was set to 60 °C for all layers. Essentium engineering grade 1.75 mm PLA was used, priced at $50/kg.

Mechanical testing

Mechanical testing was performed using a Nidec-Shimpo FGS-1000H hand wheel test stand and FG-3009 force gauge, where retractors were pulled until failure and the maximum force withstood was measured (Fig. 2). In this test stand, retractors were orientated so that the short arm of the retractor was placed on the force gauge hook and the long arm of the retractor was placed on the strap, such that the strap was as far away from the body of the retractor as possible to subject the retractors to similar torque.

Fig. 2
figure 2

Nidec-Shimpo FGS-1000H hand wheel test stand and FG-3009 force gauge with oriented retractor

Full size image

Using the Nidec-Shimpo force gauge and test stand, a stainless steel Army-Navy retractor was used to determine appropriate retractor strength, with 35 N +/− 5 N indicated by expert surgeons as strong or clinically excessive retraction causing tissue tearing and damage, based upon feel of the retractor on the surgeons’ hands.

Retractor sets

Four sets of control retractors were printed to test inter-spool and inter-manufacturer variability; three of these sets were printed using three separate Essentium PLA filament spools, and the remaining set was printed using MakerBot PLA filament (Table 1). The estimated mass of this retractor is 10.20 g, resulting in a material cost of $0.51 USD without machine expenses. The time to print these retractors is approximately 1 h 20 min. Two-tailed T-tests will be used to determine whether there exist statistically significant differences in retractor strength.

Table 1 Control retractor sets varied by spool and filament type
Full size table

To test whether infill geometry affects retractor strength, a single 20% infill, non-reinforced, 0.25 in. thickness, 0.5 in. width, and 2 perimeter Essentium filament retractor was printed for eleven different geometries: Rectilinear, Grid (default), Triangles, Stars, Cubic, Line, Honeycomb, 3D Honeycomb, Hilbert Curve, Archimedean Chords, and Octagram Spiral (Fig. 3). The “Concentric” geometry was found to be unprintable due to the narrowness of the retractor. The time to print these retractors ranged from 42 min (Rectilinear) to 1 h 20 min (Grid) depending on the complexity of the infill. The following infill geometries had a print time of less than 50 min: Rectilinear, Triangle, Stars, Cubic, and Line. The following infill geometries had a print time of more than 1 h: Honeycomb, 3D Honeycomb, Hilbert Curve, Archimedian Chords, Octagram Spiral, and Grid.

Fig. 3
figure 3

Retractor infill geometries

Full size image

These retractors were broken using a Nidec-Shimpo FGS-1000H hand wheel test stand and FG-3009 force gauge. From this data, the two strongest retractor geometries, “Cubic” and “Triangle”, and two weakest retractor geometries, “3D Honeycomb” and “Grid”, were studied further. For each of the geometries “Cubic”, “Triangle”, and “3D Honeycomb”, twelve retractors were printed. For the “Grid” geometry, retractor data from sets number 1, 2, and 4 were combined to create an aggregate Essentium filament control set and used as comparison.

To test how infill percent affects retractor strength, sets of non-reinforced, 0.25 in. thickness, 0.5 in. width, 2 perimeter Essentium filament retractors were printed at various infill percentages (Table 2). For 20% infill, retractors from the aggregate Essentium filament control set were used. The estimated mass of the retractors varied from 8.05 g to 27.39 g, resulting in a material cost of $0.40 to $1.37 USD without machine expenses. The time to print these retractors ranged from 40 min to 1 h 40 min, increasing as infill percentage increased.

Table 2 Retractors varied by infill percentage
Full size table

To test how perimeter number affects retractor strength, sets of 20% infill, non-reinforced, 0.25 in. thickness, and 0.5 in. width Essentium filament retractors were printed at various perimeter numbers (Table 3). Each perimeter is 0.15 mm. For 2 perimeter retractors, retractors from the aggregate Essentium filament control set were used. The estimated mass of the retractors varied from 10.20 g to 17.27 g, resulting in a material cost of $0.51 to $0.86 USD without machine expenses. The time to print these retractors ranged from 47 min to 54 min, increasing as perimeter number increased.

Table 3 Retractors varied by perimeter number
Full size table

To test how width affects retractor strength, sets of 20% infill, non-reinforced, 0.25 in. thickness, and 2 perimeter Essentium filament retractors were printed at various widths (Table 4). For 0.5 in. width retractors, retractors from the aggregate Essentium filament control set were used. The estimated mass of the retractors varied from 10.20 g to 20.39 g, resulting in a material cost of $0.51 to $1.02 USD without machine expenses. The time to print these retractors ranged from 1 h 28 min to 2 h 35 min, increasing as width increased.

Table 4 Retractors varied by width (inch)
Full size table

To test how thickness affects retractor strength at non-100% infill percentages, sets of 20% infill, non-reinforced, 0.5 in. width and 2 perimeter Essentium filament retractors were printed at various thicknesses (Table 5). For 0.25 in. thickness retractors, retractors from the aggregate Essentium filament control set were used. The estimated mass of the retractors varied from 8.08 g to 10.20 g, resulting in a material cost of $0.40 to $0.51 USD without machine expenses. The time to print these retractors ranged from 56 min to 1 h 20 min, increasing as thickness increased.

Table 5 Retractors varied by thickness (inch) at 20% infill
Full size table

To further test how thickness affects retractor strength at 100% infill, sets of 100% infill, non-reinforced, 0.5 in. width and 2 perimeter Essentium filament retractors were printed at various thicknesses (Table 6). The estimated mass of the retractors varied from 16.80 g to 27.39 g, resulting in a material cost of $0.84 to $1.37 USD without machine expenses. The time to print these retractors ranged from 1 h 50 min to 2 h 4 min, increasing as thickness increased.

Table 6 Retractors varied by thickness (inch) at 100% infill
Full size table

To test how reinforced joints affects retractor strength, sets of 40% infill, 0.25 in. thickness, 1 in. width, and 2 perimeter Essentium filament retractors were printed either reinforced or non-reinforced. 3 retractors were printed non-reinforced and 4 retractors were printed reinforced. The estimated mass of a non-reinforced and reinforced retractor, respectively, is 28.99 g and 32.78 g, resulting in a material cost of $1.45 and $1.64 USD without machine expenses. The time to print these retractors ranged from 2 h 31 min (non-reinforced) to 2 h 43 min (reinforced).

Results

Inter-spool and inter-manufacturer variability

Essentium filament control retractors failed at a load of 90.7 N +/− 3.3 N. MakerBot filament control retractors failed at a load of 108.6 N +/− 9.5 N. All retractors in this study failed at the joint connecting the body of the retractor to the long arm (Fig. 4).

Fig. 4
figure 4

a Broken standard retractors and b broken retractors with (top to bottom): 1 in. width with reinforced joints, 1 in. width, and 0.75 in. width

Full size image

Using a two-tailed T-test, the strength of retractors in Set 1 (Essentium PLA spool 1) was found to be statistically different than Sets 2 (Essentium PLA spool 2, p-value = 0.0012) and 4 (Essentium PLA spool 3, p-value = 0.0001); Sets 2 and 4 were not statistically different (p-value = 0.3783) (Fig. 5). The Essentium filament set, an aggregation of Sets 1, 2, and 4, was statistically different than the MakerBot PLA set, set 3 (MakerBot PLA, p-value = 0.0002) (Fig. 5). The data demonstrates statistically significant differences in retractor strength between spools of the same manufacturer and between manufacturers.

Fig. 5
figure 5

a Interspool and inter manufacturer variability affects control retractor strength. b Intermanufacturer variability affects control retractor strength. c Interspool variability affects control retractor strength

Full size image

Optimizing retractor parameters

As infill percent increased, retractor strength generally increased at 2 perimeters, with a spike at 40% infill. As predicted, 10% infill resulted in the weakest retractor, and 100% infill resulted in the strongest retractor. 40% and 80% infill resulted in retractors with comparable strengths (Fig. 6a). As perimeter number increased, retractor strength increased at 20% infill (Fig. 6b). As retractor width increased, retractor strength increased up to 0.75 in. then plateaued up to 1 in. (Fig. 6c). At 20% infill, retractor thickness was most optimal at 0.2 in. (Fig. 6d). At 100% infill, retractor strength increased as retractor thickness increased (Fig. 6e).

Fig. 6
figure 6

a As infill percent increases, retractor strength increases with a spike at 40%. b As perimeter number increases, retractor strength increases. c As retractor width increases, retractor strength increases up to 0.75 in. d Retractor thickness is most optimal at 0.2 in. at 20% infill. e Increasing retractor thickness increases retractor strength at 100% infill

Full size image

A 1 in. width retractor at 40% infill failed at 330.3 N +/− 2.1 N. A 1 in. width retractor at 40% infill with reinforced joints failed at 351.8 N +/− 6.1 N. At 20% infill, the two strongest geometries were “Cubic” and “Triangles”, which failed at 170.0 N +/− 4.8 N and 178.2 N +/− 4.2 N respectively; the two weakest geometries were the “3D Honeycomb” (99.0 N +/− 8.9 N) and “Grid” (97.0 N +/− 5.7 N).

Discussion

Retractor efficacy

All printed retractors in this optimization study have exceeded the threshold for clinically excessive retraction of 35 N by a large margin, at minimum by 2X and at maximum by 15X after determining optimal infill geometry, infill percentage, perimeter number, width, thickness, and design at the joints. Above 35 N, tissue injury becomes a clinical concern. Our control retractors, printed with default settings on average failed at almost 3X the load and the strongest retractors required almost 15X the load.

Generally, higher infill percentages, increased thickness, increased width, increased perimeter number and reinforced joints each lead to increased strength, print times, and material use. Depending on the availability of resources and time, print settings can be adjusted to create a sufficiently strong retractor while reducing cost, material use, and print time. The adaptability of 3D printing to various situations in medicine is a major strength and reason to adopt this technology. This is further accompanied by the fact that 3D prints are sterilized upon heating and extruding, allowing them to be used in sterile fields, and that they are substantially lower cost than traditional stainless steel retractors [21, 22].

Because retractor strength was greatest at 0.2 in. thickness for 20% infill retractors and retractor strength increased as retractor thickness increased for 100% infill retractors, we are led to conclude that the flexibility of retractors delay mechanical failure by reducing strain on the joints, the reliable point of failure. We hypothesize that the spike in retractor strength at 40% infill is also because of the bend and flex of the retractor reducing strain on the joints.

Regarding printing time, increasing perimeter number, increasing thickness, and adding reinforced joints did not substantially increase printing time. However, increasing width and infill percentage resulted in a marked increase in printing time, the former due to the addition of more layers and the latter increasing the time to build each layer.

True optimization and limitations

A retractor that is optimized to the greatest theoretical possible strength given the parameters in this study has 100% infill, 5 perimeters, 0.25 in. thickness, 1 in. width, and has reinforced joints. However, upon printing, it was discovered that this retractor was unprintable. This study revealed that 3D prints have a higher rate of failure as infill percentage increases. We believe that this may be due to the printer slicer software miscalculating the volume of plastic extruded, thereby attempting to fit greater amount of plastic in a layer than can actually fit. This then causes the plastic to overflow into upper layers, causing rough and uneven prints that may be pushed off the build plate by the extruder. Therefore, incrementally reducing infill percentage, perimeter number, and maintaining a 0.25 in. thickness in order to accommodate more plastic, we determined the true strength optimized retractor to have 30% infill, 3 perimeters, 0.25 in. thickness, 0.75 in. width, and has “Triangle” infill geometry and reinforced joints. This retractor fails at 534 N +/− 28.5 N, more than 15X the threshold for clinically excessive retraction, 35 N. The estimated mass of this retractor is 24.94 g, resulting in a material cost of $1.25 USD without machine expenses, only 5.2% the online retail price of a stainless steel Army-Navy retractor at $24 per unit. The time to print these retractors is approximately 2 h 14 min.

We acknowledge that even though interspool variability exists, our retractor sets were printed randomly using different spools. Even with this variability, we were still able to derive statistically significant differences in retractor strength as parameters were varied systematically.

Conclusion and future steps

This study demonstrates how even pre-optimized 3D printed PLA Army-Navy retractors have comparable surgical retraction capabilities to stainless steel retractors, but can be created in-house at a fraction of the cost and adopted in resource poor settings. These retractors fail at a force that greatly exceeds what is required for clinically excessive retraction, 35 N. The optimization of 3D printed Army-Navy retractors greatly improve the efficacy of this instrument and expedite the adoption of 3D technology in many diverse fields in medicine not necessarily limited to resource-poor settings. With the optimization of the 3D printed PLA Army-Navy retractor, a staple surgical instrument, researchers can pave the way towards and gain trust for an array of 3D printed medical supplies, allowing populations around the globe to receive higher quality health care and treatment.

A quantitative optimization of 3D printed Army-Navy retractors reveal their surgical capabilities to be comparable to commercial stainless steel retractors, but can be created in-house at a fraction of the cost and can be rapidly prototyped. This allows resource scarce areas to expand their access to high-quality medical equipment and direct their funds towards additional medical and social needs, improving healthcare around the world. Research on 3D printed surgical instruments opens additional discussion about the efficacy of 3D printed surgical tools and sparks a new field of research in 3D print optimization and dissemination.

Surgical use of these instruments, which are FDA class I devices, will require additional biocompatibility and sterilization validation. For medical use, this validation is done on the device level and not on the materials level. We know that PLA as a source material is biocompatible, but additives that are added to the PLA for coloring or for printability, may not be biocompatible [23]. There is data that supports that the fused deposition modeling printing process, where the thermoplastics are heated to above 200 °C, in our case 235 °C then extruded at high pressure through a 0.4 mm nozzle is in fact a sterilization process [21]. We have data from our lab that shows that post-processing of PLA prints can in fact be processed with steam sterilization, despite prior data that suggest that it would not be possible [24]. This is due to advances in PLA polymer technology and the ability to anneal and crystallize the PLA device after printing. This manuscript is intended as a pre-clinical evaluation and optimization of 3D printing technology. Additional research will be needed to assess performance after steam sterilization, printing with different nozzle diameters, and with different materials.

Availability of data and materials

Retractor STLs and data are available through the authors.

Abbreviations

PLA:

Polylactic Acid

STL:

Standard Tessellation Language

References

  1. Abdullah KA, Reed W. 3D printing in medical imaging and healthcare services. J Med Radiat Sci. 2018;65:237–9. https://doi.org/10.1002/jmrs.292.

    Article  PubMed  PubMed Central  Google Scholar 

  2. Brown C. 3D printing set to revolutionize medicine. Can Med Assoc J. 2017;189:E973–4. https://doi.org/10.1503/cmaj.1095442.

    Article  Google Scholar 

  3. Dodziuk H. Applications of 3D printing in healthcare. Pol J Cardio-Thorac Surg. 2016;3:283–93. https://doi.org/10.5114/kitp.2016.62625.

    Article  Google Scholar 

  4. George M, Aroom KR, Hawes HG, Gill BS, Love J. 3D Printed Surgical Instruments: The Design and Fabrication Process. World J Surg. 2017;41:314–9. https://doi.org/10.1007/s00268-016-3814-5.

    Article  PubMed  PubMed Central  Google Scholar 

  5. Hoang D, Perrault D, Stevanovic M, Ghiassi A. Surgical applications of three-dimensional printing: a review of the current literature & how to get started. Ann Transl Med. 2016;4:456. https://doi.org/10.21037/atm.2016.12.18.

    Article  PubMed  PubMed Central  Google Scholar 

  6. Kim GB, Lee S, Kim H, Yang DH, Kim Y-H, Kyung YS, Kim C-S, Choi SH, Kim BJ, Ha H, Kwon SU, Kim N. Three-Dimensional Printing: Basic Principles and Applications in Medicine and Radiology. Korean J Radiol. 2016;17:182. https://doi.org/10.3348/kjr.2016.17.2.182.

    Article  PubMed  PubMed Central  Google Scholar 

  7. Malik HH, Darwood ARJ, Shaunak S, Kulatilake P, El-Hilly AA, Mulki O, Baskaradas A. Three-dimensional printing in surgery: a review of current surgical applications. J Surg Res. 2015;199:512–22. https://doi.org/10.1016/j.jss.2015.06.051.

    Article  PubMed  Google Scholar 

  8. Mardis NJ. Emerging Technology and Applications of 3D Printing in the Medical Field. Mo Med. 2018;6:368–73.

    Google Scholar 

  9. Mishra S. Application of 3D printing in medicine. Indian Heart J. 2016;68:108–9. https://doi.org/10.1016/j.ihj.2016.01.009.

    Article  PubMed  PubMed Central  Google Scholar 

  10. Paul GM, Rezaienia A, Wen P, Condoor S, Parkar N, King W, Korakianitis T. Medical Applications for 3D Printing: Recent Developments. Mo Med. 2018;115(1):75-81.

  11. Shilo D, Emodi O, Blanc O, Noy D, Rachmiel A. Printing the Future—Updates in 3D Printing for Surgical Applications. Rambam Maimonides Med J. 2018;9:e0020. https://doi.org/10.5041/RMMJ.10343.

    Article  PubMed Central  Google Scholar 

  12. Squelch A. 3D printing and medical imaging. J Med Radiat Sci. 2018;65:171–2. https://doi.org/10.1002/jmrs.300.

    Article  PubMed  PubMed Central  Google Scholar 

  13. Sun Z. 3D printing in medicine: current applications and future directions. Quant Imaging Med Surg. 2018;8:1069–77. https://doi.org/10.21037/qims.2018.12.06.

    Article  PubMed  PubMed Central  Google Scholar 

  14. Tack P, Victor J, Gemmel P, Annemans L. 3D-printing techniques in a medical setting: a systematic literature review. Biomed Eng OnLine. 2016;15:115. https://doi.org/10.1186/s12938-016-0236-4.

    Article  PubMed  PubMed Central  Google Scholar 

  15. Ibrahim AMS, Jose RR, Rabie AN, Gerstle TL, Lee BT, Lin SJ. Three-dimensional Printing in Developing Countries. Plast Reconstr Surg - Glob Open. 2015;3:e443. https://doi.org/10.1097/GOX.0000000000000298.

    Article  PubMed  PubMed Central  Google Scholar 

  16. Brennan M, Bokhari F, Eddington D. Open Design 3D-Printable Adjustable Micropipette that Meets the ISO Standard for Accuracy. Micromachines. 2018;9:191. https://doi.org/10.3390/mi9040191.

    Article  PubMed Central  Google Scholar 

  17. Pavlosky A, Glauche J, Chambers S, Al-Alawi M, Yanev K, Loubani T. Validation of an effective, low cost, Free/open access 3D-printed stethoscope. PLoS One. 2018;13:e0193087. https://doi.org/10.1371/journal.pone.0193087.

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  18. Rothenberg S, Abdullah S, Hirsch J. 3D Printing Prototypes for Healthcare Professionals: Creating a Reciprocating Syringe. J Digit Imaging. 2017;30:566–71. https://doi.org/10.1007/s10278-017-9953-x.

    Article  PubMed  PubMed Central  Google Scholar 

  19. Visscher DO, te Slaa S, Jaspers ME, van de Hulsbeek M, Borst J, Wolff J, Forouzanfar T, van Zuijlen PP. 3D printing of patient-specific neck splints for the treatment of post-burn neck contractures. Burns Trauma. 2018;6:15. https://doi.org/10.1186/s41038-018-0116-1.

    Article  PubMed  PubMed Central  Google Scholar 

  20. Wang J, Yang L, Ma M, Li G, Xu S, Li Q, Xu Z, Liu J, Ye C. Development and Application of a No-Clog Surgical Suction Tip Using 3D Printing Technology. Med Sci Monit. 2018;24:6765–73. https://doi.org/10.12659/MSM.909900.

    Article  PubMed  PubMed Central  Google Scholar 

  21. Neches RY, Flynn KJ, Zaman L, Tung E, Pudlo N. On the intrinsic sterility of 3D printing. PeerJ. 2016;4:e2661. https://doi.org/10.7717/peerj.2661.

    Article  PubMed  PubMed Central  Google Scholar 

  22. Rankin TM, Giovinco NA, Cucher DJ, Watts G, Hurwitz B, Armstrong DG. Three-dimensional printing surgical instruments: are we there yet? J Surg Res. 2014;189:193–7. https://doi.org/10.1016/j.jss.2014.02.020.

    Article  PubMed  PubMed Central  Google Scholar 

  23. Anderson JM, Shive MS. Biodegradation and biocompatibility of PLA and PLGA microspheres. Adv Drug Deliv Rev. 2012;64:72–82. https://doi.org/10.1016/j.addr.2012.09.004.

    Article  Google Scholar 

  24. Rozema F, Bos R, Boering G, Van Asten J, Nijenhuis A, Pennings A. The effects of different steam-sterilization programs on material properties of poly(L-lactide). J Appl Biomater. 1991;2:23–8. https://doi.org/10.1002/jab.770020104.

    Article  CAS  PubMed  Google Scholar 

Download references

Acknowledgments

UCSF Department of Orthopaedic Surgery.

The article processing charge for this publication has been funded generously by the UCSF Open Access Publishing Fund.

Funding

UCSF Department of Orthopaedic Surgery.

Author information

Authors and Affiliations

  1. Department of Orthopaedic Surgery, University of California, San Francisco, CA, USA

    Joshua V. Chen, Alexis B. C. Dang, Carlin S. Lee & Alan B. C. Dang

  2. Department of Surgery, Orthopaedic Section, San Francisco VA Health Center, San Francisco, CA, USA

    Alexis B. C. Dang & Alan B. C. Dang

Authors
  1. Joshua V. Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Alexis B. C. Dang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Carlin S. Lee
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Alan B. C. Dang
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

JVC planned the experiment, designed the retractors, printed the retractors, collected retractor strength data, and wrote the manuscript. AD assembled and maintained 3D printer, and trained co-authors on 3D printing process. CSL printed the retractors and collected retractor strength data. ABD is the PI, provided funding, assembled and maintained 3D printer, and trained co-authors on 3D printing process and computer automated design. All authors read and approved the final manuscript.

Corresponding author

Correspondence to Joshua V. Chen.

Ethics declarations

Ethics approval and consent to participate

Not applicable

Consent for publication

Not applicable

Competing interests

Joshua V. Chen - none.

Alexis Dang – Stock Options: Printerprezz.

Carlin S. Lee - none.

Alan BC Dang – Paid employee: Printerprezz; Stock Options: Printerprezz.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Chen, J.V., Dang, A.B.C., Lee, C.S. et al. 3D printed PLA Army-Navy retractors when used as linear retractors yield clinically acceptable tolerances. 3D Print Med 5, 16 (2019). https://doi.org/10.1186/s41205-019-0053-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s41205-019-0053-z

Keywords

3D Printing in Medicine

ISSN: 2365-6271

Contact us