Abstract
La1 − x Ba x FeO3 − δ (x = 0–1) perovskites were prepared by the mechanical activation of mixtures of binary oxides in a centrifugal planetary ball mill for 3 min followed by calcination at 1100°C for 4 h, and their phase composition was determined by X-ray diffraction. All samples up to x = 0.8 are single-phase oxides with a perovskite structure. The x = 1 sample is a mixture of perovskite-and brownmillerite-type phases. An orthorhombic-to-cubic morphotropic transition is observed at x = 0.3. The catalytic activity of the perovskite samples in CO oxidation, chosen as a model reaction, depends nonmonotonically on the barium content of the catalyst. High catalytic activities are shown by the x = 0.8 and 0.3 samples.
Similar content being viewed by others
References
Ullmann, H., Trofimenko, N., Tietz, F., Stover, D., and Ahmad-Khanlou, A., Solid State Ionics, 2000, vol. 138, p. 79.
Isupova, L.A., Yakovleva, I.S., Gainutdinov, I.I., Pavlyukhin, Yu.T., and Sadykov, V.A., React. Kinet. Catal. Lett., 2004, vol. 81, no. 2, p. 373.
Seiyama, T., Catal. Rev. Sci. Eng., 1991, vol. 34, no. 4, p. 281.
Tejuca, L.G., Fierro, J.L.G., and Tascon, J.M.D., Adv. Catal., 1989, vol. 36, p. 237.
Popovskii, V.V., Teoreticheskie problemy kataliza (Theoretical Problems of Catalysis), Novosibirsk: Inst. Kataliza, 1977.
Baran, E.J., Catal. Today, 1990, vol. 8, p. 133.
Yue Wu, Tao Yu, and Bo-Sheng Dou, J. Catal., 1989, vol. 120, p. 88.
Isupova, L.A., Yakovleva, I.S., Tsybulya, S.V., Kryukova, G.N., Boldyreva, N.N., Alikina, G.M., Rogov, V.A., Vlasov, A.A., and Sadykov, V.A., Khim. Interes. Ust. Razv., 2002, vol. 10, no. 1, p. 77.
Isupova, L.A., Yakovleva, I.S., Alikina, G.M., Rogov, V.A., and Sadykov, V.A., Kinet. Katal., 2005, vol. 46, no. 5, p. 773 [Kinet. Catal. (Engl. Transl.), vol. 46, no. 5, p. 729].
Yakovleva, I.S., Isupova, L.A., Tsybulya, S.V., Chernysh, A.V., Boldyreva, N.N., Alikina, G.M., and Sadykov, V.A., J. Mater. Sci., 2004, vol. 39, p. 5517.
Dann, S.E., Currie, D.B., Weller, M.T., et al., J. Solid State Chem., 1994, vol. 109, p. 134.
Parras, M., Vallet-Regi, M., Gonzales-Calbet, J.M., Alario-Franco, M., and Grenier, J.C., J. Solid State Chem., 1988, vol. 74, p. 110.
Tsybulya, S.V., Cherepanova, S.V., and Solov’eva, L.P., Zh. Strukt. Khim., 1996, vol. 37, no. 2, p. 379.
Isupova, L.A., Pavlyukkin, Yu.T., Rogov, V.A., Alikina, G.M., Tsybulya, S.V., Yakovleva, I.S., and Sadykov, V.A., Mater. Res. Soc. Symp. Proc., 2005, vol. 848, FF 10.5.1.
Kupriyanov, M.F., Konstantinov, G.M., and Panich, A.E., Segnetoelektricheskie morfotropnye perekhody (Ferroelectric Morphotropic Transitions), Rostov-on-Don: Rostov. Gos. Univ., 1992.
Williamson, G.K. and Hall, W.H., Acta Metall., 1953, vol. 1, p. 22.
Isupova, L.A., Tsybulya, S.V., Kryukova, G.N., Rogov, V.A., Yakovleva, I.S., and Sadykov, V.A., Mixed Ionic Electronic Conducting Perovskites for Advanced Energy Systems, 2004, Boston: Kluwer, Vol. 39, p. 143.
Tsybulya, S.V., Kryukova, G.N., Isupova, L.A., Shmakov, A.N., Cherepanova, S.V., and Sadykov, V.A., Zh. Strukt. Khim., 1998, vol. 39, no. 1, p. 92.
Isupova, L.A., Yakovleva, I.S., Rogov, V.A., Alikina, G.M., and Sadykov, V.A., Kinet. Katal., 2004, vol. 45, no. 3, p. 473 [Kinet. Catal. (Engl. Transl.), vol. 45, no. 3, p. 446].
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © L.A. Isupova, A.N. Nadeev, I.S. Yakovleva, S.V. Tsybulya, 2008, published in Kinetika i Kataliz, 2008, Vol. 49, No. 1, pp. 142–146.
Rights and permissions
About this article
Cite this article
Isupova, L.A., Nadeev, A.N., Yakovleva, I.S. et al. Mechanochemical synthesis and physicochemical properties of La1 − x Ba x FeO3 − δ (0 ≤ x ≤ 1) perovskites. Kinet Catal 49, 133–137 (2008). https://doi.org/10.1134/S0023158408010175
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0023158408010175