Abstract
TiO2 powder has been synthesized through hydrolysis-condensation of titanyl sulfate solution to a starting material of TiO2 nanorods formation. This processing was conducted by the solid separation of TiO2 from ilmenite by roasting ilmenite, acidic leaching (hydrolysis), and co-precipitation (condensation). Roasting of ilmenite was carried out by the addition of Na2S at a temperature of 800°C. While the acidic leaching process was conducted by sulfuric acid at a various concentrations of 3, 3.5, 4.5, 6, and 9 M. The result shown that the solubility optimum occurs in H2SO4 6 M condition. Separation of Fe impurities of TiO2 gel from titanyl sulfate (TiOSO4) solution was done through complexation using KCNS addition. The characteristic of TiO2 obtained using X-Ray Fluorescence (XRF) and X-Ray Diffraction (XRD) showed good crystallinity and purity. Further treatment of the TiO2 is the formation of one-dimensional nano-size (1-D nanorods) through a hydrothermal method under basic condition NaOH 12M solution. TiO2 nanorods were confirmed by Transmission Electron Microscope (TEM) which indicated that the diameter of TiO2 nanorods was about 7.02 nm in size.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.