CuNb1−xTaxO3 (x ≤ 0.25) solid solutions: impact of Ta(v) substitution and Cu(i) deficiency on their structure, photocatalytic, and photoelectrochemical properties

Abstract

Solid solutions of Cu(I)-containing oxide p-type semiconductors provide key opportunities to probe the fundamental relationships between chemical compositions and crystal structures, bandgap sizes, band energies, and photoelectrochemical properties. Members of the CuNb1−xTaxO3 (0 < x ≤ 0.25) solid solution have been synthesized via high temperature solid-state methods. The structure of CuNbO3 was found to be Cu-deficient Cu0.965NbO3 after heating in air at 250 °C for 3 hours, i.e., under similar conditions as those used to prepare it as a polycrystalline film. Powder X-ray diffraction techniques confirmed the purity of each composition up to x ≤ 0.25 and the lattice parameters were refined as the molar ratio of Nb(V) and Ta(V) was varied (a = 9.499 to 9.506 Å, b = 8.439 to 8.451 Å, c = 6.768 to 6.781 Å and β = 90.847 to 90.694°). An increase in the amount of Ta(V) yielded a small blue shift of the bandgap size from ∼1.89 eV to ∼1.97 eV for CuNb1−xTaxO3 from x = 0 to 0.25. Polycrystalline films of each member of the CuNb1−xTaxO3 solid solutions produced relatively comparable p-type photocurrents of up to −0.5 mA cm−2, while the stability of the cathodic photocurrent also remained similar with increasing Ta(V) content. Mott–Schottky analysis of CuNb1−xTaxO3 showed that the conduction band edge of −1.5 (vs. SHE) provides a sufficient overpotential (∼800 mV) to drive the reduction of water to hydrogen gas at the surface. The capability of the solid solutions to drive hydrogen production was confirmed through suspended particle photocatalysis. Further characterization of the CuNb0.91Ta0.09O3 composition included scanning electron microscopy, X-ray photoelectron spectroscopy, and thermogravimetric analyses. These data show that Cu(I) is oxidized to Cu(II) as CuNb1−xTaxO3 is heated in air. Thus, the formation of Cu(II) rich regions at the surface, together with the Ta(V) content, are found to play important roles in the stability and magnitude of the cathodic photocurrents produced under visible-light irradiation. Importantly, these results demonstrate that solid solution compositions can be used in films for solar energy conversion, notwithstanding their inherent atomic disorder.

Graphical abstract: CuNb1−xTaxO3 (x ≤ 0.25) solid solutions: impact of Ta(v) substitution and Cu(i) deficiency on their structure, photocatalytic, and photoelectrochemical properties

Supplementary files

Article information

Article type
Paper
Submitted
21 Aug 2015
Accepted
16 Dec 2015
First published
18 Dec 2015

J. Mater. Chem. A, 2016,4, 3115-3126

Author version available

CuNb1−xTaxO3 (x ≤ 0.25) solid solutions: impact of Ta(V) substitution and Cu(I) deficiency on their structure, photocatalytic, and photoelectrochemical properties

B. Zoellner, S. Stuart, C. Chung, D. B. Dougherty, J. L. Jones and P. A. Maggard, J. Mater. Chem. A, 2016, 4, 3115 DOI: 10.1039/C5TA06609C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements