Vertically aligned nanorod-like rutileTiO2 single crystal nanowire bundles with superior electron transport and photoelectrocatalytic properties

Abstract

In this work, vertically aligned nanorod-like rutile TiO2 single crystal nanowire bundles were directly grown onto FTO conducting substrates via a facile, one-pot hydrothermal method. The fabricated nanorod-like rutile TiO2 single crystal nanowire bundles display a diameter range of 150–200 nm and a mean length of 0.9 μm. The nanorod-like bundles assemble by individual single crystal nanowires of 5–7 nm in diameter. The photoanode made of vertically aligned nanorod-like rutile TiO2 single crystal nanowire bundles shows excellent photoelectrocatalytic activity towards water oxidation, which is almost 3 times higher than that of the photoanode made of vertically aligned anatase TiO2 nanotube film of similar thickness. The high photoelectrocatalytic activity of the photoanode made of the nanorod-like rutile TiO2 single crystal nanowire bundles is mainly due to the superior photoelectron transfer property, which has been manifested by the inherent resistance (R0) of the rutile TiO2 film via a simple photoelectrochemical method. Using this approach, the calculated R0 values are 52.1 Ω and 71.0 Ω for the photoanodes made of vertically aligned nanorod-like rutile TiO2 single crystal nanowire bundles and the vertically aligned anatase TiO2 nanotubes, respectively. The lower R0 of the rutile TiO2 photoanode means a superior photoelectron transfer property. XPS valence-band spectra analysis indicates that the nanorod-like rutile TiO2 film has almost identical valence band position (1.95 eV) when compared to the anatase TiO2 nanotube film, meaning a similar oxidation capability, further confirming the superior photoelectron transport property of the nanorod-like rutile TiO2 single crystal nanowire bundles.

Graphical abstract: Vertically aligned nanorod-like rutile TiO2 single crystal nanowire bundles with superior electron transport and photoelectrocatalytic properties

Supplementary files

Article information

Article type
Paper
Submitted
30 Oct 2011
Accepted
08 Dec 2011
First published
22 Dec 2011

J. Mater. Chem., 2012,22, 2465-2472

Vertically aligned nanorod-like rutile TiO2 single crystal nanowire bundles with superior electron transport and photoelectrocatalytic properties

H. Zhang, X. Liu, Y. Li, Q. Sun, Y. Wang, B. J. Wood, P. Liu, D. Yang and H. Zhao, J. Mater. Chem., 2012, 22, 2465 DOI: 10.1039/C2JM15546J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements