Abstract
Patterns with controllable adhesion on superhydrophobic areas have various biomedical and chemical applications. Electrolyte jet machining technique (EJM), an electrochemical machining method, was firstly exploited in constructing dimples with various profiles on the superhydrophobic Al alloy surface using different processing parameters. Sliding angles of water droplets on those dimples firstly increased and then stabilized at a certain value with the increase of the processing time or the applied voltages of the EJM, indicating that surfaces with different adhesion force could be obtained by regulating the processing parameters. The contact angle hysteresis and the adhesion force that restricts the droplet from sliding off were investigated through experiments. The results show that the adhesion force could be well described using the classical Furmidge equation. On account of this controllable adhesion force, water droplets could either be firmly pinned to the surface, forming various patterns or slide off at designed tilting angles at specified positions on a superhydrophobic surface. Such dimples on superhydrophopbic surfaces can be applied in water harvesting, biochemical analysis and lab-on-chip devices.
Similar content being viewed by others
Introduction
Superhydrophobic surface, which has a water contact angle (CA) larger than 150°, is an ideal water-repellent surface due to the property of ultralow water affinity. Water droplets on the superhydrophobic surface can easily slide off when the surface is slightly tilted. This kind of surface has a large application prospect in the fields of self-cleaning1, drag reduction2, anti-icing3 and oil/water separation4,5,6,7. To date, numerous methods have been developed to fabricate superhydrophobic surfaces on different substrates8,9,10,11,12,13,14,15,16. Recently, based on the superhydrophobic surfaces, researchers began to pay more attention on controlling and regulating the adhesion of water droplets because of potential applications such as water harvesting, biochemical analysis and lab-on-chip devices17,18,19,20,21,22. Controlling water adhesion is usually achieved through adjusting localized microstructures, chemical compositions or both of them23. Different technologies such as plasma treatment24,25,26, laser irradiation18,20,27,28, lithography17,29, ink patterning19,30,31,32, etc.21,22, have been applied to realize those adhesion controllable surfaces. For instance, Chen et al. achieved groove patterns on the hydrophobic polydimethylsiloxane (PDMS) surface by a femtosecond laser. The prepared surface exhibits controllable water adhesion and anisotropic wetting properties20. Jiang et al. prepared a PDMS pillars-array film by a two-beam interference laser microfabrication system. With the curvature of the film varying, the superhydrophobicity from high-adhesion state to low-adhesion state can be reversibly turned18. Megaridis et al. used localized thermal treatment to create micro adhesion controllable superhydrophilic patterns on the superhydrophobic polysilsesquioxane-silica composite coatings and when the laser was applied, the pattern scale could be down to 100 μm28. Milionis et al. fabricated a surface with controllable adhesion by spray-coating of polytetrafluoroethylene sub-micrometer particles and hydrophobically capped oxide colloidal nanoparticles on the SU-8 micro-pillar patterns. It is feasible to fabricate low-adhesion superhydrophobic surfaces with localized high-adhesion areas17. Based on the principles of capillary-induced adhesion, Gao et al. presented three types of porous nano-structured layers, which can transform between high-adhesion state and low-adhesion state19. Among them, the femtosecond laser can be used to make nano-scaled features on a wide range of materials such as metal, polymer and silicon33,34, however, the high cost of this technique makes it difficult to be applied for large-scale industrial productions. Lithography is another technique to make micro and nano patterns on various substrates, however, it is difficult to control substrate roughness directly, which makes it unsuitable to regulate the roughness of the patterns and further control the adhesion. Additionally, it can be seen that most of the surfaces with controllable adhesion were constructed on the polymers, such as polyaniline, SU-8 and PDMS. Metal materials have various applications in engineering and agriculture due to the strong mechanical strength and good machinability. However, to the best of our knowledge, controllable adhesion state through structure arrangement on metal surface, which is expected to have many applications in engineering, has rarely been reported.
Low-surface-energy structures with different levels of roughness exhibit different levels of adhesions20,35; an extremely rough surface morphology with low surface energy endows the surface with superhydrophobicity, while smooth or ideally flat surfaces with low surface energy would be adhesively hydrophobic or even hydrophilic. Therefore, patterns with controllable adhesion on superhydrophobic surfaces, which have important potential applications in lab-on-chip devices, could be realized through regulating the localized roughness of the surface. Electrolyte jet machining (EJM) is a mild and easy-to-implement fabrication technique based on electrochemical dissolving principle of anode. This technique could be applied to machine patterns, e.g. dimples and lines, on diverse metal matrices. In addition, patterns with different levels of roughness could be realized by adjusting the processing parameters, such as processing time and processing voltage.
Herein, a method combining electrochemical etching, EJM and surface modification was presented for the first time to construct patterns with controllable adhesion on the superhydrophobic Al alloy surfaces. Firstly, electrochemical etching was applied to fabricate micro-nano structures on the Al alloy substrate. Then, dimples with different levels of roughness were obtained on the etched surface through EJM under different processing parameters. Finally, after modification with low surface energy materials, the dimples with different roughness exhibited different levels of adhesion. Such dimples could also be fabricated on diverse metal substrates to realize localized high adhesion. The adhesion mechanism was investigated through experiments.
Results
Fabrication of superhydrophobic surfaces with micro dimples for droplet manipulation
Micro dimples with various roughness and dimensions on the electrochemically etched Al plate were fabricated using the EJM technology (Fig. 1a), which is a mild machining method. After modification with the 0.05 mol/L ethanol solution of stearic acid, the electrochemically etched areas exhibit excellent superhydrophobicity while the dimples exhibit specific adhesion to droplets due to the lack of extremely rough structures. Sphere-like droplets can be pinned to the dimples forming different patterns or slide at designed angles without residual water left.
Figure 1b shows the top-view SEM images of the electrochemically etched Al surface. Large numbers of micro holes and protrusions homogeneously covered the surface. Micro rectangular-shaped plateaus with sizes of a few microns attached to each other and therefore formed the micro- and sub-micro-scale cavities (the dashed rectangle regions in Fig. 1b) and step-like structures (Fig. 1b). The dimple was produced on the aforementioned electrochemically etched surface by the EJM technique. Figure 1c was the SEM images of the dimple obtained by processing for 3 s at 100 V with a 520 μm inner diameter nozzle. The diameter of the dimple was about 680 μm (the left one in Fig. 1c) and the boundary between the edge of the dimple and the rough etched area was distinct (the middle one in Fig. 1c). The internal surface of the dimple was smoother than the outside superhydrophobic areas, has sub-micro-scale cracks and abundant protrusion with sizes ranging from 1 to 10 μm (the right one in Fig. 1c).
Figure 2a shows the Raman spectrum of the electrochemically etched area and the dimple surface after modification with stearic acid. The characteristic peaks around 2900 cm−1 correspond to the C-H bond of stearic acid, which indicates the etched area and the dimple surface were all well modified by the stearic acid36,37. Then the wettability was tested with 5 μL water droplets. The CA and the sliding angle (SA) were 162.1° and 9.5° respectively on the area without EJM treatment, indicating that the Al samples prepared by electrochemical etching have excellent superhydrophobicity and the water droplet on this area is in Cassie-Baxter state38. However, when water droplets were laid on the dimple, there appeared additional adhesion energy. Figure 2b,c show that 5 μL water droplets respectively touched the dimple and the superhydrophobic area. The dimple was processed for 3 s at 100 V using a 520 μm inner diameter nozzle. The droplet was easily released from the needle and pinned on the dimple when touching the dimple surface (Fig. 2b). On the contrary, the adhesion on the superhydrophobic surface was so small that the droplet just left the surface and kept sticking to the needle (Fig. 2c), indicating that the dimple has stronger adhesion energy than that of the superhydrophobic surface (See Supplementary Video S1). And a 15 μL water droplet would slide off at averaged 18.2° on that dimple, which was much higher than 5° on the superhydrophobic areas. More importantly, by adjusting the processing parameters, water droplets could slide off the dimples at designed angles without residual water left on it, which could be applied for lossless droplet manipulation.
Dimples with controllable adhesion
To systematically analyze the adhesion phenomena, dimples with various profiles were produced on the superhydrophobic Al surface with different processing parameters. 7 dimples marked as Dimple 1–7 were obtained by processing for 1 s, 2 s, 3 s, 5 s, 10 s, 15 s and 20 s at a voltage of 300 V using a 520 μm inner diameter nozzle. 11 dimples marked as 8–18 were processed for 3 s at voltages ranging from 100 V to 600 V with an increase of every 50 V. As the processing time or the applied voltages increased, the surface of the dimples got smoother and the boundary between the edge of the dimple and the rough superhydrophobic area gradually become distinct (Fig. 3). 3D models (Fig. 4a,b) and surface profiles (See Supplementary Fig. S1) of the dimples measured by a 3D surface profilometer also indicate that the dimple surface was rough at first and tended to smooth with the increase of either processing time or applied voltages. As shown in Fig. 4c, the roughness of the dimple surfaces declined rapidly from Ra 4.7 μm at 0 s to Ra 0.7 μm at a processing time of 5 s and then tended to stabilize at Ra 0.3 μm after 20 s. Figure 4d shows that the roughness decreased gradually to Ra 0.8 μm at an applied voltage of 400 V. This roughness variation with processing parameters also indicates that the EJM is a feasible technique to regulate the roughness of patterns on superhydrophobic surfaces.
SAs on Dimple 1–7 firstly increased with the increase of the processing time and then began to stabilize around 5 s while depths of the dimples increased linearly with the increasing processing time (Fig. 5a). Analogously, SAs on Dimple 8–18 increased with the increase of the applied voltages and tended to be steady after 250 V in spite of the linear increase of the depths of the dimples (Fig. 5b). And SAs of 15 μL droplets on the dimples fabricated by nozzles with inner diameters of 345 μm, 460 μm and 760 μm had the similar trend as (Fig. 5c).
Discussion
Based on the studies in the mid-twentieth century39–41, the adhesion force (Fadh) that restricts the droplet from sliding off an inclined surface is proportional to the width (Wdro) of the droplet-solid interface (Fig. 6a) that is perpendicular to the sliding direction. This can be expressed as the following semi-empirical Furmidge equation40:
where γLV is the liquid surface tension, and are the receding and advancing CA of the droplet on the surface. When the droplet was laid on the dimple area, the droplet-substrate interface turned into composite, that is, besides the Fs-adh between the droplet and superhydrophobic area (both advancing and receding CA of the etched superhydrophobic Al surface), there would be an additional contribution which is the adhesion force Fd-adh between the droplet and dimple surface (advancing CA of the superhydrophobic surface and receding CA of the dimple surface) to the overall adhesion force Foverall (Fig. 6b). Assuming these two adhesion force is independent, the predicted adhesion force Foverall that prevents the droplet from sliding away from a dimple can thereby be calculated as the following equation31:
where Wdim is the diameter of the fabricated dimple (Fig. 6c), is the receding CA of the droplet on the dimple, which can be experimentally measured. and are the receding and advancing CA of the droplet on the electrochemically etched superhydrophobic surface and Wdro is the overall droplet-substrate interfacial width, which can also be obtained by experimental measurements. Based on equation (2), it can be inferred that different adhesion force acting on the droplets could be realized by regulating the or the dimple diameter Wdim. As illustrated in Fig. 6d,e, the increase of either the processing time or the applied voltages would result in the decrease of , showing that the EJM technique can be applied to adjust the localized on a superhydrophobic surface. The adhesion force that prevents the droplets from sliding off can therefore be calculated based on equation (2) using the measured , Wdim and Wdro. The results shown in Fig. 6d,e demonstrate that the calculated values are in good agreement with the experimental values.
In order to explore the potential applications of the dimples, 6 × 6 arrayed dimples processed for 5 s each at a voltage of 300 V with a 520 μm inner diameter nozzle were obtained on the superhydrophobic Al alloy surface (Fig. 7). The spacing between the dimples was 5 mm. The water droplets with volumes of 20 μL can stay steadily on the patterned surface (Fig. 7a) and would not slide off even the surface was tilted (Fig. 7b). When the surface was tilted at about 41°, all the water droplets would slide off (Fig. 7c). Figure 7d shows a heart-shaped pattern formed by the droplets on the arrayed dimples. The EJM technique follows the principle of anodic dissolution, so it can be extended to fabricate patterns on various metal matrixes. Figure 7e,f show a 2 × 2 dimple array with 5 mm spacing obtained on a superhydrophobic magnesium surface and 20 μL water droplets were pinned firmly on the tilted surface. By fabricating dimples with different parameters at specified positions, droplets could slide at designed angles with or without residual water left at appointed positions (see supplementary Video S2). Left to right, five 15 μL droplets on superhydrophobic area and on the four dimples slid at about 5°, 18°, 24°, 31° and 47° respectively (Fig. 7g). The four dimples on the superhydrophobic Al alloy surface were processed for 3 s at 100 V, 150 V, 200 V and 250 V with a 760 μm inner diameter nozzle.
For the EJM technique used in the experiment, the minimal dimple size depends on the inner diameters of the nozzles while the minimal distance between the dimples is closely related to the minimal dimple size and the precision of the motion platform. Therefore, technically, dimples with diameters of several tens of microns can be fabricated on various metal materials and the spacing between the dimples can also achieve the level of hundreds of microns. Supplementary Fig. S2 shows the minimal dimple array that was fabricated using our set-up EJM unit. The average diameter of the fabricated dimples is 150 μm and the distance between dimples is about 290 μm. Compared with laser, the EJM does suffer defects such as limited machinable materials and relatively low machining precision. However, the EJM unit is much cheaper and easier to construct, which makes it more suitable for large scale industrial productions.
In conclusion, electrolyte jet machining (EJM) was applied for the first time in constructing dimples with different levels of adhesion by regulating the processing parameters. The surface fabricated by EJM gradually smoothed with the increase of processing time and voltage. By adjusting the processing parameters, dimples with different levels of roughness and adhesion could be obtained at specified positions. Water droplets with different sizes may be firmly pinned to the surface forming various patterns and could slide off at designed angles at appointed positions. Based on this adhesion mechanism, this method could be applied in constructing various patterns with controllable adhesion on diverse metal matrixes. On account of these specific adhesion phenomena, this research can be applied for biological and optical fields such as trace analysis of aqueous solution, water harvesting and sensors.
Methods
Materials
6061 aluminum alloys plates (3 mm thick) were purchased from Suzhou Metal Material Manufacturer (China). Stearic acid [STA, CH3 (CH2)16COOH], NaCl and NaNO3 were purchased from Tianjin Kermel Chemical Reagent Co. (China). All chemicals were analytical grade reagents and were used as received.
Fabrication of micro-nano structures
The Al alloys samples (60 mm × 60 mm) were polished using #800 and #1500 abrasive papers and ultrasonically cleaned with deionized water to remove the oxide layer, grease and other impurities. The cleaned Al plate was then electrochemically etched at a current density of 600 mA·cm−2 for 8 min in the 0.1 mol·L−1 NaCl aqueous solution and subsequently ultrasonically rinsed with water to clear away the impurity particles on the surface.
Fabrication of superhydrophobic surfaces with micro dimples
The dimple patterns with various profiles on the etched Al plate were obtained using the EJM technique. This EJM machining system mainly consists of copper-sleeve cathode, nozzle fixture, electrolyte and quartz nozzle. The quartz nozzle is fixed on the nozzle fixture with sealant while the nozzle fixture is fixed on the copper sleeve through thread. When the cathodic copper sleeve and the anodic substrate was connected with high voltage DC power, the cyclic electrolyte would be charged negatively when flowing through the copper sleeve, subsequently shoot on the substrate and remove materials based on the electrochemical dissolving principle of anode. The glow discharge will occur in the EJM process when a high voltage is applied. Hence, the EJM process is a synthetic process that consists of electrochemical machining, chemical machining and electrical discharge machining process42. The electrolyte flows outward radially when impacting the workpiece surface. The hydraulic jump occurs at a certain distance from the center of the jet flow. Therefore, the current is concentrated in this region and materials could be removed selectively43–45.
15 wt% NaNO3 aqueous solution was used as the electrolyte in the EJM process. The electrolyte pressure was 0.3 MPa. The interelectrode gap, that is, the distance between the tail end of quartz nozzle and the Al plate surface, is 1 mm. Dimples with different profiles were fabricated on the electrochemically etched Al plate under different processing parameters. After this process, the Al plate with these dimples was ultrasonically cleaned in the deionized water, subsequently, dried and immersed in 0.05 mol/L ethanol solution with stearic acid [CH3(CH2)16COOH] for 30 min to lower the surface energy and then a superhydrophobic Al alloy plate with specific dimples was obtained.
Characterization
The morphology of the samples was characterized by a scanning electron microscope (SEM, JSM-6360LV, Japan). The 3D models and surface profiles of samples were characterized by a 3D surface profilometer (ZYGO NewView 5022 3D optical surface profiler). Optical images of water droplets were captured by a CCD camera (Microvision MV-VD030SC, China). Contact angle is defined as the angle between the solid-liquid interface and the tangent of liquid-vapor interface at the contact point of solid-liquid-vapor46 and measured using a mapping program based on the definition at ambient temperature. Sliding angle is defined as the angle at which the water droplet begins to roll off the gradually inclined surface47 and was measured by a precision whirler.
Additional Information
How to cite this article: Yang, X. et al. Controlling the Adhesion of Superhydrophobic Surfaces Using Electrolyte Jet Machining Techniques. Sci. Rep. 6, 23985; doi: 10.1038/srep23985 (2016).
References
Fürstner, R., Barthlott, W., Neinhuis, C. & Walzel, P. Wetting and self-cleaning properties of artificial superhydrophobic surfaces. Langmuir 21, 956–961 (2005).
Bhushan, B. & Jung, Y. C. Natural and biomimetic artificial surfaces for superhydrophobicity, self-cleaning, low adhesion and drag reduction. Prog. Mater Sci. 56, 1–108 (2011).
Farhadi, S., Farzaneh, M. & Kulinich, S. A. Anti-icing performance of superhydrophobic surfaces. Appl. Surf. Sci. 257, 6264–6269 (2011).
Song, J. L. et al. Self-Driven One-Step Oil Removal from Oil Spill on Water via Selective-Wettability Steel Mesh. ACS Appl. Mater. Interfaces 6, 19858–19865 (2014).
Feng, L. et al. A super‐hydrophobic and super‐oleophilic coating mesh film for the separation of oil and water. Angew. Chem. Int. Ed. 43, 2012–2014 (2004).
Huang, X. F. & Lim, T. T. Performance and mechanism of a hydrophobic–oleophilic kapok filter for oil/water separation. Desalination 190, 295–307 (2006).
Lu, Y. et al. Creating superhydrophobic mild steel surfaces for water proofing and oil–water separation. J. Mater. Chem. A 2, 11628–11634 (2014).
Su, F. H. & Yao, K. Facile fabrication of superhydrophobic surface with excellent mechanical abrasion and corrosion resistance on copper substrate by a novel method. ACS Appl. Mater. Interfaces 6, 8762–8770 (2014).
Li, J. et al. Facile Spray-Coating Process for the Fabrication of Tunable Adhesive Superhydrophobic Surfaces with Heterogeneous Chemical Compositions Used for Selective Transportation of Microdroplets with Different Volumes. ACS Appl. Mater. Interfaces 6, 8868–8877 (2014).
Xu, W. J., Song, J. L., Sun, J., Lu, Y. & Yu, Z. Y. Rapid fabrication of large-area, corrosion-resistant superhydrophobic Mg alloy surfaces. ACS Appl. Mater. Interfaces 3, 4404–4414 (2011).
Wu, D. et al. Three‐Level Biomimetic Rice‐Leaf Surfaces with Controllable Anisotropic Sliding. Adv. Funct. Mater. 21, 2927–2932 (2011).
Safaee, A., Sarkar, D. K. & Farzaneh, M. Superhydrophobic properties of silver-coated films on copper surface by galvanic exchange reaction. Appl. Surf. Sci. 254, 2493–2498 (2008).
Yuan, Z. Q. et al. A novel preparation of polystyrene film with a superhydrophobic surface using a template method. J. Phys. D: Appl. Phys. 40, 3485 (2007).
Baldacchini, T., Carey, J. E., Zhou, M. & Mazur, E. Superhydrophobic surfaces prepared by microstructuring of silicon using a femtosecond laser. Langmuir 22, 4917–4919 (2006).
Lu, Y. et al. Robust self-cleaning surfaces that function when exposed to either air or oil. Science 347, 1132–1135 (2015).
Hsieh, C. T., Yang, S. Y. & Lin, J. Y. Electrochemical deposition and superhydrophobic behavior of ZnO nanorod arrays. Thin Solid Films 518, 4884–4889 (2010).
Milionis, A. et al. Spatially controlled surface energy traps on superhydrophobic surfaces. ACS Appl. Mater. Interfaces 6, 1036–1043 (2014).
Wu, D. et al. Curvature‐Driven Reversible In Situ Switching Between Pinned and Roll‐Down Superhydrophobic States for Water Droplet Transportation. Adv. Mater. 23, 545–549 (2011).
Lai, Y. K. et al. Designing superhydrophobic porous nanostructures with tunable water adhesion. Adv. Mater. 21, 3799–3803 (2009).
Yong, J. L. et al. A simple way to achieve superhydrophobicity, controllable water adhesion, anisotropic sliding and anisotropic wetting based on femtosecond-laser-induced line-patterned surfaces. J. Mater. Chem. A 2, 5499–5507 (2014).
Zhai, L. et al. Patterned superhydrophobic surfaces: toward a synthetic mimic of the Namib Desert beetle. Nano Lett. 6, 1213–1217 (2006).
Ding, C. M. et al. PANI nanowire film with underwater superoleophobicity and potential-modulated tunable adhesion for no loss oil droplet transport. Soft Matter 8, 9064–9068 (2012).
Yong, J. L. et al. Femtosecond laser weaving superhydrophobic patterned PDMS surfaces with tunable adhesion. J. Phys. Chem. C 117, 24907–24912 (2013).
Zhu, X. T., Zhang, Z. Z., Men, X. H., Yang, J. & Xu, X. H. Rapid formation of superhydrophobic surfaces with fast response wettability transition. ACS Appl. Mater. Interfaces 2, 3636–3641 (2010).
Jokinen, V., Sainiemi, L. & Franssila, S. Complex droplets on chemically modified silicon nanograss. Adv. Mater. 20, 3453–3456 (2008).
Balu, B., Breedveld, V. & Hess, D. W. Fabrication of “roll-off” and “sticky” superhydrophobic cellulose surfaces via plasma processing. Langmuir 24, 4785–4790 (2008).
Stojanovic, A., Artus, G. R. & Seeger, S. Micropatterning of superhydrophobic silicone nanofilaments by a near-ultraviolet Nd: YAG laser. Nano. Res 3, 889–894 (2010).
Schutzius, T. M., Bayer, I. S., Jursich, G. M., Das, A. & Megaridis, C. M. Superhydrophobic–superhydrophilic binary micropatterns by localized thermal treatment of polyhedral oligomeric silsesquioxane (POSS)–silica films. Nanoscale 4, 5378–5385 (2012).
Zahner, D., Abagat, J., Svec, F., Fréchet, J. M. & Levkin, P. A. A facile approach to superhydrophilic–superhydrophobic patterns in porous polymer films. Adv. Mater. 23, 3030–3034 (2011).
Li, L., Breedveld, V. & Hess, D. W. Hysteresis controlled water droplet splitting on superhydrophobic paper. Colloid. Polym. Sci. 291, 417–426 (2013).
Balu, B., Berry, A. D., Hess, D. W. & Breedveld, V. Patterning of superhydrophobic paper to control the mobility of micro-liter drops for two-dimensional lab-on-paper applications. Lab Chip 9, 3066–3075 (2009).
Huang, J. Y. et al. Multifunctional Superamphiphobic TiO2 Nanostructure Surfaces with Facile Wettability and Adhesion Engineering. Small 10, 4865–4873 (2014).
Gattass, R. R. & Mazur, E. Femtosecond laser micromachining in transparent materials. Nat. photonics 2, 219–225 (2008).
White, Y. V., Li, X., Sikorski, Z., Davis, L. M. & Hofmeister, W. Single-pulse ultrafast-laser machining of high aspect nano-holes at the surface of SiO 2. Opt. Express 16, 14411–14420 (2008).
Zhang, J. L., Li, J. & Han, Y. C. Superhydrophobic PTFE surfaces by extension. Macromol. Rapid Commun. 25, 1105–1108 (2004).
Wu, R. et al. Fabrication of nano-structured super-hydrophobic film on aluminum by controllable immersing method. Appl. Surf. Sci. 258, 5933–5937 (2012).
Snyder, R. G., Strauss, H. L. & Elliger, C. A. Carbon-hydrogen stretching modes and the structure of n-alkyl chains. 1. Long, disordered chains. J. Phys. Chem. 86, 5145–5150 (1982).
Cassie, A. & Baxter, S. Wettability of porous surfaces. Trans. Faraday Soc. 40, 546–551 (1944).
Bikerman, J. J. Sliding of drops from surfaces of different roughnesses. J. Colloid Sci. 5, 349–359 (1950).
Furmidge, C. Studies at phase interfaces I. The sliding of liquid drops on solid surfaces and a theory for spray retention. J. Colloid Sci. 17, 309–324 (1962).
Kawasaki, K. Study of wettability of polymers by sliding of water drop. J. Colloid Sci. 15, 402–407 (1960).
Natsu, W., Ikeda, T. & Kunieda, M. Generating complicated surface with electrolyte jet machining. Precis. Eng 31, 33–39 (2007).
Kunieda, M., Mizugai, K., Watanabe, S., Shibuya, N. & Iwamoto, N. Electrochemical micromachining using flat electrolyte jet. Ann. CIRP 60, 251–254 (2011).
Hackert-Oschätzchen, M., Martin, A., Meichsner, G., Zinecker, M. & Schubert, A. Microstructuring of carbide metals applying Jet Electrochemical Machining. Precis. Eng 37, 621–634 (2013).
Kai, S., Sai, H., Kunieda, M. & Izumi, H. Study on Electrolyte Jet Cutting. Procedia CIRP 1, 627–632 (2012).
Young, T. An essay on the cohesion of fluids. Philos. Trans. R. Soc. London 65–87 (1805).
Nakajima, A., Abe, K., Hashimoto, K. & Watanabe, T. Preparation of hard super-hydrophobic films with visible light transmission. Thin Solid Films 376, 140–143 (2000).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (NSFC, grant 90923022), the Fundamental Research Funds for the Central Universities (DUT15RC(3)066) and an Innovation and Creativity Fund for Doctoral Students Granted by Science & Technology Review (Grant No. KJDB2012010).
Author information
Authors and Affiliations
Contributions
X.Y. suggested the idea and performed the experiment. J.S. proposed the mechanism of the droplet adhesion and prepared most of the manuscript text. X.L. and Y.L. collected and analyzed the data. S.Z. and M.G. prepared the figures. W.X. supervised the experiments. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Yang, X., Liu, X., Lu, Y. et al. Controlling the Adhesion of Superhydrophobic Surfaces Using Electrolyte Jet Machining Techniques. Sci Rep 6, 23985 (2016). https://doi.org/10.1038/srep23985
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep23985
This article is cited by
-
Tailoring microbial response to stainless steel surfaces via electrolyte jet machining and electrodeposition
The International Journal of Advanced Manufacturing Technology (2023)
-
Droplet asymmetry and wetting dynamics on irregularly roughened surfaces
Journal of Coatings Technology and Research (2021)
-
Multifunctional substrate of Al alloy based on general hierarchical micro/nanostructures: superamphiphobicity and enhanced corrosion resistance
Scientific Reports (2016)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.