Abstract
Ethanolamine is a critical chemical for petrochemical enterprises. When corrosion occurs in pipelines, equipment, and containers in petrochemical enterprises, minute amounts of metal ions are released. In this study, the thermal decomposition and nonisothermal kinetics of monoethanolamine (MEA) and MEA mixed with copper and zinc ions were analyzed using thermogravimetry (TG) and differential scanning calorimetry (DSC). The TG tests revealed that MEA mixed with copper (II) and zinc (II) began thermal decomposition at 75.2 and 60.3 °C, respectively, whereas pure MEA began thermal decomposition at 89.7 °C. Two exothermic peaks were observed in the DSC curves for MEA mixed with copper (II) and zinc (II), and thermokinetic parameters were obtained from DSC data. The apparent activation energy (Ea) of each stage was calculated using several nonisothermal kinetic methods, namely the ASTM E698, Kissinger–Akahira–Sunose, Starink, and Flynn–Wall–Ozawa methods. The Ea of pure MEA was 28.7 ± 2.5 kJ/mol, whereas that of the copper and zinc mixtures were 80.5 ± 1.1 and 46.8 ±1.7 kJ/mol, respectively. The results can be used to improve the intrinsic safety of storage tanks and petrochemical plants.
Similar content being viewed by others
Introduction
As a derivative of ethylene oxide, ethanolamine is a valuable product of amino alcohol consisting of monoethanolamine (MEA), diethanolamine (DEA), and triethanolamine (TEA). Ethanolamine may be used for a variety of applications, including use in the intermediates of pesticides1, medicines2, detergent emulsifiers, resins3, and rubber4. Ethanolamine may also be used in desulfurization processes to remove acid gas and in the decarburization designs of refineries5. Ethanolamine is colorless, viscous, volatile, unstable, easily oxidized, corrosive6, and may cause fire or explosions when exposed to potent oxidants, such as hydrogen peroxide in a heated container7. Thermal decomposition and combustion may occur during the preparation, transportation, or storage of ethanolamine because of temperature imbalance and heat accumulation. At a company in Taoyuan, Taiwan in 2007, a fire and explosion occurred in a storage tank area containing 17 tanks of chemicals. The raw chemical materials involved in the accident primarily comprised glacial acetic acid, propylene glycol methyl ether, diethylene glycol butyl ether, and MEA.
The petrochemical sector has begun to expand, and petrochemical facilities are connected by a multitude of pipelines. Common metal pipeline materials include copper, zinc, and iron8. Pipeline corrosion is a critical concern for petrochemical enterprises; long-term corrosion of pipelines may lead to leaks and ruptures. In such cases, fire or explosions will occur if a transported material is inflammable or explosive and encounters an effective ignition source. Additionally, pipeline corrosion releases metal ions with free radicals9, which causes catalytic decomposition reactions that play a critical role in chain reactions and result in exothermic events. Corroded pipelines have caused leakages, fires, and explosion accidents worldwide, resulting in considerable economic losses, negative social aftermath, and environmental hazards. The Kaohsiung gas explosion and Chevron refinery fire incident were caused by corroded pipelines and led to extensive economic, social, and environmental damages10.
Generally, if corroded pipelines ethanolamine, the content of metal ions in the ethanolamine will increase gradually; the excess metal content then causes ethanolamine to foam and become unusable as a cleaning gas. Thus, the metal content of ethanolamine directly affects its quality and cost. More critically, this metal content provokes an incompatibility reaction, which induces advanced catalyzation of the material; consequently, the subsequent reaction cannot be controlled. Ávila6 investigated the thermal decomposition of MEA, DEA, TEA, and methyldiethanolamine (MDEA) and concluded that MEA exhibited the lowest thermal stability. In other studies, scholars11,12 have examined ethanolamine complexities using numerous methods, such as mixing ethanolamine with various oxidation states of vanadium. However, the thermal behavior of ethanolamine combined with metal ions has not been addressed in the literature; hence, the mechanism of metal ions in the thermal decomposition of ethanolamine should be determined.
The present study observed changes in the caloric value of MEA with the addition of various metal ions, namely copper (II) and zinc (II), by using thermogravimetry (TG), differential scanning calorimetry (DSC), and thermokinetic parameters, such as heat of decomposition (ΔHd), exothermic onset temperature (T0), and peak temperature (Tp)13,14,15, were obtained. The results revealed that the decomposition of MEA mixed with copper (II) and zinc (II) exhibited a reaction earlier than did the pure MEA. The apparent activation energy (Ea) of each stage was calculated using various thermokinetic models. The Ea of pure MEA was 28.7 ± 2.5 kJ/mol, whereas that of the copper and zinc mixtures were 80.5 ± 1.1 and 46.8 ± 1.7 kJ/mol, respectively. The results of this study may serve as a reference for the preparation, application, usage, storage, and disposal of MEA, and could be used to minimize thermal risk and enhance the intrinsic safety of storage tanks in petrochemical plants.
Experimental and Methods
Sample preparations
MEA of 99 mass% purity was purchased from Acros Organics (Thermo Fisher Scientific Ltd., New Jersey, USA). The chemical formula of MEA is C2H7NO, and its Chemical Abstracts Service number is 141-43-5. Copper and zinc ions, which are common metallic materials used in pipelines, were separated from CuBr2 and ZnBr2 (provided by Alfa Aesar Ltd., Haverhill, MA, USA). To prevent deterioration, all samples were stored in a dry and dark place.
TG experiments
TG experiments were performed using a Perkin Elmer Pyris 1 thermogravimetric analyzer (Waltham, Massachusetts, USA) with a balanced furnace and vertical design. TG and differential TG (DTG) curves revealed variations in the mass loss and its derivative when the temperature was increased16,17. For pure MEA samples, the experimental temperature ranged from 30.0 to 300.0 °C and heating rates of 5.0, 10.0, 15.0, 20.0, and 25.0 °C/min were applied. In total, 10.0 mg of samples were used. Experiments using MEA mixed with CuBr2 and ZnBr2 were conducted at a heating rate of 10.0 °C/min within the temperature range of 30.0–650.0 °C. All samples were placed in a platinum crucible. Tests proceeded under an air atmosphere with 20.0 mL/min flow. Three sets of experiment were performed to ensure the reliability of the results and experimental methodology.
DSC experiments
Thermal analysis tests were performed using a Mettler Toledo DSC-821 (Mettler Toledo International Inc., Columbus, OH, USA). Because of its ease and efficiency of operation, DSC is the standard instrument used in conventional thermoanalysis18. A DSC analysis was conducted to generate thermal curves denoting the temperature ranges of exothermic and endothermic reactions. Heat-flow data could be obtained from the area of the reactions19. The DSC-821 has been calibrated of heating rate at 4.0 °C/min before the experiment. In this study, DSC experiments were performed at heating rates of 2.0, 4.0, 6.0, 8.0, and 10.0 °C/min, and the test temperature range was set at 30.0–400.0 °C. STARe software was used to establish thermokinetic models and obtain kinetic parameters20,21. The sample sizes of MEA, MEA mixed with CuBr2, and MEA mixed with ZnBr2 were approximately 7.0 mg in each experiment. The sample ratio was approximately 2:1.
Nonisothermal kinetic methods
The dynamic parameter Ea was calculated in the nonisothermal experiment, which was performed in a growing environment. Kinetic analysis generally involves model-free and model-fitting methods22. The model-free method, also termed the isoconversional method, enhances analysis accuracy by excluding kinetic model functions23,24,25. In this method, the reaction rate is assumed to be only a function of temperature, and Ea values are compared at different conversions to corroborate the consistency of the reaction mechanism throughout the process26. Kinetic methods are divided into differential and integral methods27. In this study, the ASTM E698, Kissinger–Akahira–Sunose (KAS), Starink, and Flynn–Wall–Ozawa (FWO) methods were selected as representative methods for dynamic analysis. Table 1 presents the nonisothermal kinetic methods used for the present study and obtained from TG–DTG and DSC analysis to estimate the Ea. All of these methods were transformed using the nonisothermal kinetic equation, as presented in Eq. (1):
The value of Ea was calculated with the slope of a line respectively by using the equations of these four methods. In terms of Starink method, ln (β/T1.8) was plotted against 1/T with a slope of −1.0037 Ea/RT to obtain Ea.
Results and Discussion
Thermogravimetric analysis through TG testing
Figure 1 illustrates the TG and DTG curves of MEA at 5.0, 10.0, 15.0, 20.0, and 25.0 °C/min heating rates in an air atmosphere. The TG curves revealed that a single stage mass loss was observed within the temperature range of 50.0–200.0 °C, and decomposition was initially quick compared with other substances because of the volatility of MEA. The TG and DTG curves exhibited sufficient consistency. By increasing the heating rate, the reaction of mass loss became more intense; furthermore, the initial decomposition temperature (Ti), maximum decomposition temperature (Tm), and final decomposition temperature (Tf) all increased, as did the rate of mass loss, which reached 7.4%/min at a heating rate of 25.0 °C/min. The decomposition of all heating rates was complete without residues before the temperature reached 200.0 °C.
The TG and DTG curves of MEA and MEA individually mixed with CuBr2 and ZnBr2 at a heating rate of 10.0 °C/min in an air atmosphere are presented in Fig. 2. As indicated in the diagram, the mass-loss process of MEA mixed with CuBr2 consists of three stages. The first stage, which occurred between 50.0 and 230.0 °C with a mass loss of 78.3%, was attributed to the reaction of MEA and CuBr2. The second stage, which occurred between 230.0 and 450.0 °C with a mass loss of 6.9%, represented the decomposition of the remaining CuBr2. The third stage, which occurred between 450.0 and 700.0 °C, resulted in the formation of 5.6% of residues and corresponded to the formation of CuO. For MEA mixed with ZnBr2, the TG and DTG curves indicated two stages of mass loss. The first decomposition (30.0–200.0 °C) resulted in 60.0% mass loss and was caused by the reaction of MEA and ZnBr2. The mass loss (40.0%) of the second decomposition (at 200.0–700.0 °C) was caused by the decomposition of the remaining ZnBr2 without residues’ formation.
The calculated values of TG and DTG for various stages of the three samples are presented in Table 2, including the characteristic temperature and mass loss of each stage. As evident in these data, the reaction rate of MEA increased after copper (II) and zinc (II) had been added, and Ti and Tm decreased in the first stage. As indicated in Table 2, the addition of zinc (II) (Ti = 60.3 °C) catalyzed the reaction of MEA more quickly than did the addition of copper (II) (Ti = 75.2 °C).
Thermodynamics of DSC tests
The DSC curves of the three samples at a heating rate of 8.0 °C/min are displayed in Fig. 3. For MEA, exothermic and endothermic peaks were observed at 120.0 and 320.0 °C, respectively. The exothermic onset temperature (T0) and maximum decomposition temperature (Tp) were 89.5 and 130.3 °C, respectively. T0 can be defined by the intersection of a line drawn tangent to the steepest slope of the curve with the baseline; moreover, Tp is the maximum exothermic temperature that can be achieved in the exothermic interval. The curves of MEA mixed with CuBr2 and MEA mixed with ZnBr2 produced two exothermic peaks at approximately 120.0 and 320.0 °C, respectively. The first peak indicated that advanced canalization occurred after the addition of CuBr2 and ZnBr2 to MEA. T0 decreased to 79.2 and 69.6 °C, respectively, which is consistent with the results of the TG test, and Tp decreased to 117.6 and 110.5 °C, respectively. ΔHd was similar in the first peak for all three samples, namely 185.4, 199.6, and 151.6 J/g, respectively. For the second exothermic peak of MEA mixed with CuBr2 and ZnBr2, the respective values of Tp were 322.8 and 316.7 °C. The peak may be considered representative of the thermal decomposition of the remaining bromide. In this test, the influence of Br− in the decomposition of MEA could be disregarded because both metallic compounds contained negative ions.
Figure 4 displays the temperature–heat flow curves of MEA mixed with (a) CuBr2 and (b) ZnBr2 at heating rates of 2.0, 4.0, 6.0, 8.0, and 10.0 °C/min. The DSC curves exhibited similar trends. The exothermic intervals of the first and second peaks were 50.0–180.0 and 200.0–380.0 °C, respectively, and T0 and Tp were delayed as the heating rates increased. For MEA mixed with ZnBr2 in the DSC experiments, regularity among T01, Tp1, and ΔHd1 with the increasing heating rates in the first peak could not be confirmed, as indicated in Fig. 4(b). These results can be attributed to the water adsorption of ZnBr2, which rendered the initial reaction unstable. However, the values of ΔHd in the second peak at different heating rates were between 99.5 and 124.7 J/g. For MEA mixed with CuBr2, the ΔHd results of the first and second peaks at five heating rates were 187.4–237.8 and 373.6–471.9 J/g, respectively. All thermokinetic parameter results are listed in Table 3.
Calculations and comparison of E a
Ea is a crucial kinetic parameter for evaluating the reactability of a substance. To further explore the effects of adding copper (II) and zinc (II) on the thermal stability of MEA, various nonisothermal kinetic methods were used to analyze the exothermic peaks in the DSC tests. Ea results were calculated for MEA and MEA mixtures at each experimental stage.
The ASTM E698 was first used to calculate the Ea of each set of experiments. Figure 5 displays the plots of \(\mathrm{ln}\,(\beta /{T}_{{\rm{p}}}^{2})\) versus 1/Tp for the four exothermic peaks according to the ASTM E698 method. The Ea results for the first and second peaks of MEA mixed with CuBr2 were 30.3 and 115.6 kJ/mol, and those for MEA mixed with ZnBr2 were 42.1 and 116.9 kJ/mol, respectively. However, the ASTM E698 method could not be used to reveal the overall trend of Ea at each conversion. The values for Ea acquired using the ASTM E698 method were slightly inaccurate for these experiments because of the basic assumptions of the method28. Subsequently, the KAS, Starink, and FWO methods were used for different conversions. The DSC curve exhibited artificiality in baseline selection during processing and analysis, especially for reactions at the beginning and end with device noise. Therefore, the conversion at the interval of α between 0.1 and 0.9 was selected for the kinetic analysis.
For the KAS, Starink, and FWO methods, general trends in Ea values can be identified at different conversions. Plots for the first peak of MEA mixed with ZnBr2 obtained using these three methods at different conversions are displayed in Fig. 6; the fitting plots deviated substantially at the conversions of 0.1–0.2 and 0.8–0.9. At the conversion of 0.3–0.7, the fitting plots were nearly parallel. Accordingly, the average of Ea was calculated within the interval of 0.3–0.7, as suggested in relevant studies22,29. The plots of other peaks that are not displayed in Fig. 6 were similar to this figure after fitting. Ea was readily calculated at different conversions using the slope of the curves in Fig. 6. Tables 4 and 5 list the Ea of MEA mixed with CuBr2 and ZnBr2 at different conversions. The variation of Ea at different conversions for these four exothermic peaks according to the KAS, Starink, and FWO methods is represented in Fig. 7. Similar results for Ea were obtained with the KAS and Starink methods, whereas the FWO method yielded a slightly higher Ea value.
Table 6 summarizes the calculated results of Ea and R2 for each nonisothermal method. The Ea of pure MEA was 28.7 ± 2.5 kJ/mol, which is lower than the value indicated in related studies6. For MEA mixed with CuBr2, the Ea of the first peak was 80.5 ± 1.1 kJ/mol, suggesting that the Ea of the mixture was higher than that of pure MEA. The data listed in Table 6, along with the curves delineated in Fig. 7, demonstrate that the Ea increased with conversion; this was likely because of a chemical reaction and the formation of a copper-alkanolamine complex30. The calculated value of Ea in the second stage was 125.9 ± 1.5 kJ/mol, which was slightly higher than the value reported in a relevant study31. This value may be attributable to the decomposition of the remaining CuBr2. For MEA mixed with ZnBr2, the Ea values of the first and second peaks were 46.8 ± 1.7 and 113.6 ± 1.9 kJ/mol, respectively. As indicated by the R2 values in Table 6, the FWO method was superior to other methods regarding the analysis of pure MEA and MEA mixtures and is widely used in thermokinetics analysis32.
Conclusions
In this study, the thermal decomposition and nonisothermal kinetics of pure MEA and MEA mixed with copper (II) and zinc (II) were illustrated using TG and DSC. In the TG tests, the thermal decomposition of MEA mixed with CuBr2 and ZnBr2 began at 75.2 and 60.3 °C, respectively; all mixtures produced prior decomposition reactions compared with pure MEA (89.7 °C).
In the DSC analysis, two exothermic peaks were observed after the addition of CuBr2 and ZnBr2 to MEA. Although no notable change in ΔHd occurred, T0 decomposed early at 79.2 and 69.6 °C in the copper and zinc mixtures, respectively. These results suggested that metal ions may provoke early reactions during the manufacturing process. These advanced reactions may lead to thermal decomposition of the material of interest at low temperatures, resulting in thermal hazards. Moreover, nonisothermal methods, namely the ASTM E698, KAS, Starink, and FWO methods, were used to analyze the decomposition kinetics of MEA and MEA mixtures. The fitting was insufficient in a single conversion compared with the R2 in different conversions. The Ea of pure MEA was 28.7 ± 2.5 kJ/mol. The Ea results of the copper and zinc mixtures were 80.5 ± 1.1 and 46.8 ± 1.7 kJ/mol, respectively. Chemical reactions caused by the addition of metal ions resulted in these results of higher Ea for the mixtures.
Ethanolamine is widely used in petrochemical industries, and the operation of such enterprises involves numerous unsafe processes. Because of the advanced reactions of metal ions to ethanolamine, corroded pipelines and equipment should be promptly replaced to reduce the likelihood of chemical disasters and ensure plant safety.
References
Caux, P., Weinberger, P. & Szabo, A. Effects of pesticide adjuvants on membrane lipid composition and fluidity in Lemna minor. Can. J. Bot. 71, 1291–1297 (1993).
Amjad, M., Sumrra, S. H., Akram, M. S. & Chohan, Z. H. Metal-based ethanolamine-derived compounds: a note on their synthesis, characterization and bioactivity. J. Enzyme Inhib. Med. Chem. 31, 88–97 (2016).
Müller, M., Militz, H. & Krause, A. Thermal degradation of ethanolamine treated poly(vinyl chloride)/wood flour composites. Polym. Degrad. Stab. 97, 166–169 (2012).
Krickl, S., Touraud, D. & Kunz, W. Investigation of ethanolamine stabilized natural rubber latex from Taraxacum kok-saghyz and from Hevea brasiliensis using zeta-potential and dynamic light scattering measurements. Ind. Crops. Prod. 103, 169–174 (2017).
Wang, T., Liu, F., Ge, K. & Fang, M. X. Reaction kinetics of carbon dioxide absorption in aqueous solutions of piperazine, N-(2-aminoethyl) ethanolamine and their blends. Chem. Eng. J. 314, 123–131 (2017).
de Ávila, S. G., Logli, M. A. & Matos, J. R. Kinetic study of the thermal decomposition of monoethanolamine (MEA), diethanolamine (DEA), triethanolamine (TEA) and methyldiethanolamine (MDEA). Int. J. Greenhouse Gas Control 42, 666–671 (2015).
Ak, M. A. et al. An experimental study on the hypergolic ignition of hydrogen peroxide and ethanolamine. Fuel 90, 395–398 (2011).
Huang, C. F. et al. Microcosmic thermal analysis of coal mixed with oxides at different temperatures. Int. J. Oil Gas Coal T. 18, 239–253 (2018).
Wessling, B. & Posdorfer, J. Corrosion prevention with an organic metal (polyaniline): corrosion test results. Electrochim. Acta 44, 2139–2147 (1999).
Tsai, Y. T., Ho, S. C., Huang, A. C. & Shu, C. M. Potential explosion hazard of polyester resin dust formed from a granulation process: Limiting oxygen concentration with different pressures. Appl. Therm. Eng. 135, 74–82 (2018).
Masoud, M. S., Ali, A. E., Ahmed, H. M. & Mohamed, E. A. Spectral studies and thermal analysis of new vanadium complexes of ethanolamine and related compounds. J. Mol. Struct. 1050, 43–52 (2013).
da Silva, R. D. C. & Cavalheiro, É. T. G. Synthesis, characterization, and thermal analysis of alginate and monoethanolamine product. J. Therm. Anal. Calorim. 120, 855–862 (2015).
Chang, R. H., Shu, C. M., Duh, Y. S. & Jehng, J. M. Calorimetric studies on the thermal hazard of methyl ethyl ketone peroxide with incompatible substances. J. Hazard. Mater. 141, 762–768 (2007).
Huang, A. C. et al. Thermal stability simulations of 1,1-bis(tert-butylperoxy)-3,3,5 trimethylcyclohexane mixed with metal ions. J. Therm. Anal. Calorim. 130, 949–957 (2017).
Tsai, Y. T., You, M. L., Qian, X. M. & Shu, C. M. Calorimetric techniques combined with various thermokinetic models to evaluate incompatible hazard of tert-butyl peroxy-2-ethyl hexanoate mixed with metal ions. Ind. Eng. Chem. Res. 52, 8206–8215 (2013).
Chen, C. X. et al. Oxy-fuel combustion characteristics and kinetics of microalgae Chlorella vulgaris by thermogravimetric analysis. Bioresour. Technol. 144, 563–571 (2013).
Deng, J. et al. Thermal behavior and micro characterization analysis of second-oxidized coal. J. Therm. Anal. Calorim. 127, 439–448 (2017).
Chen, W. T. et al. Structural characteristics and decomposition analyses of four commercial essential oils by thermal approaches and GC/MS. J. Therm. Anal. Calorim. 2, 1–11 (2017).
Laiwang, B. et al. Effects of UV for cycloaliphatic epoxy resin via thermokinetic models, novel calorimetric technology, and thermogravimetric analysis. Sci. Rep. 8, 15835 (2018).
Wu, S. H. et al. Thermal hazard analysis of triacetone triperoxide (TATP) by DSC and GC/MS. J. Loss Prev. Process Ind. 25, 1069–1074 (2012).
Lee, M. H., Chen, J. R., Shiue, G. Y., Lin, Y. F. & Shu, C. M. Simulation approach to benzoyl peroxide decomposition kinetics by thermal calorimetric technique. J. Taiwan Inst. Chem. Eng. 45, 115–120 (2014).
Abd-Elghany, M., Klapötke, T. M., Elbeih, A. & Zeman, S. Investigation of different thermal analysis techniques to determine the decomposition kinetics of ε-2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane with reduced sensitivity and its cured PBX. J. Anal. Appl. Pyrolysis 126, 267–274 (2017).
Huang, A. C., Chuang, Y. K., Huang, C. F. & Shu, C. M. Thermokinetic analysis of the stability of malic and salicylic acids in cosmeceutical formulations containing metal oxides. J. Therm. Anal. Calorim. 132, 165–172 (2017).
Iliyas, A., Hawboldt, K. & Khan, F. Thermal stability investigation of sulfide minerals in DSC. J. Hazard. Mater. 178, 814–822 (2010).
Vazquez-Pufleau, M., Chadha, T. S., Yablonsky, G. & Biswas, P. Carbon elimination from silicon kerf: Thermogravimetric analysis and mechanistic considerations. Sci. Rep. 7, 40535 (2017).
Cai, Z. L., Ma, X. Q., Fang, S. W., Yu, Z. S. & Lin, Y. Thermogravimetric analysis of the co-combustion of eucalyptus residues and paper mill sludge. Appl. Therm. Eng. 106, 938–943 (2016).
Ma, H., Zhang, X., Ju, F. & Tsai, S. B. A study on curing kinetics of nano-phase modified epoxy resin. Sci. Rep. 8, 3045 (2018).
Zhang, G. Z., Zhang, J., Wang, F. & Li, H. J. Thermal decomposition and kinetics studies on the poly (2,2-dinitropropyl acrylate) and 2,2-dinitropropyl acrylate-2,2-dinitrobutyl acrylate copolymer. J. Therm. Anal. Calorim. 122, 419–426 (2015).
Yan, Q., Zeman, S., Elbeih, A. & Zbynek, A. The influence of the semtex matrix on the thermal behavior and decomposition kinetics of cyclic nitramines. Cent. Eur. J. Energetic Mater. 10, 509–528 (2013).
Yonezawa, T., Tsukamoto, H., Yong, Y., Nguyen, M. T. & Matsubara, M. Low temperature sintering process of copper fine particles under nitrogen gas flow with Cu2+-alkanolamine metallacycle compounds for electrically conductive layer formation. RSC Adv. 6, 12048–12052 (2016).
Nobuyuki, T. & Masahiro, K. The Thermal decomposition of CuBr2Nh3 and CuBr2. Bull. Chem. Soc. Jpn. 43, 3468–3471 (1970).
Chen, W. C. & Shu, C. M. Prediction of thermal hazard for TBPTMH mixed with BPO through DSC and isoconversional kinetics analysis. J. Therm. Anal. Calorim. 126, 1937–1945 (2016).
Vyazovkin, S. et al. ICTAC Kinetics Committee recommendations for performing kinetic computations on thermal analysis data. Thermochim. Acta 520, 1–19 (2011).
Kissinger, H. E. Reaction kinetics in differential thermal analysis. Anal. Chem. 29, 1702–1706 (1957).
Akahira, T. & Sunose, T. Method of determining activation deterioration constant of electrical insulating materials. Res. Rep. Chiba. Inst. Technol. (Sci. Technol.) 16, 22–31 (1971).
Starink, M. A new method for the derivation of activation energies from experiments performed at constant heating rate. Thermochim. Acta 288, 97–104 (1996).
Ozawa, T. A new method of analyzing thermogravimetric data. Bull. Chem. Soc. Jpn. 38, 1881–1886 (1965).
Acknowledgements
The authors are grateful for experimental assistance from the Process Safety & Disaster Prevention Laboratory in Taiwan.
Author information
Authors and Affiliations
Contributions
Mengning Wei and An-Chi Huang performed the analysis, contributed the literature research, and wrote the paper; Chi-Min Shu and Lijing Zhang conceived the research theme and edited the paper.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wei, M., Huang, AC., Shu, CM. et al. Thermal Decomposition and Nonisothermal Kinetics of Monoethanolamine Mixed with Various Metal Ions. Sci Rep 9, 1592 (2019). https://doi.org/10.1038/s41598-018-38434-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-38434-1
This article is cited by
-
Calorimetric approach to establishing thermokinetics for cosmeceutical benzoyl peroxides containing metal ions
Journal of Thermal Analysis and Calorimetry (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.