Abstract
Transparent electrodes have been widely used in electronic devices such as solar cells, displays and touch screens. Highly flexible transparent electrodes are especially desired for the development of next generation flexible electronic devices. Although indium tin oxide (ITO) is the most commonly used material for the fabrication of transparent electrodes, its brittleness and growing cost limit its utility for flexible electronic devices. Therefore, the need for new transparent conductive materials with superior mechanical properties is clear and urgent. Ag nanowire (AgNW) has been attracting increasing attention because of its effective combination of electrical and optical properties. However, it still suffers from several drawbacks, including large surface roughness, instability against oxidation and moisture and poor adhesion to substrates. These issues need to be addressed before wide spread use of metallic NW as transparent electrodes can be realized. In this study, we demonstrated the fabrication of a flexible transparent electrode with superior mechanical, electrical and optical properties by embedding a AgNW film into a transparent polymer matrix. This technique can produce electrodes with an ultrasmooth and extremely deformable transparent electrode that have sheet resistance and transmittance comparable to those of an ITO electrode.
Similar content being viewed by others
Introduction
Flexible electronic devices have attracted great attention due to their advantages over the devices fabricated by conventional bulk silicon technology. These advantages include excellent portability, conformal contact with curved surfaces, small weight and human friendly interfaces1,2,3. Indium tin oxide (ITO) is the most commonly used material for the fabrication of transparent electrodes, however, it is not suitable for flexible electronic devices because it is brittle and easily cracks under mechanical stress4,5. Recently, several other candidates for flexible transparent electrodes, including carbon nanotubes6,7, graphene8,9, conducting polymers10,11 and metal nanowires12,13 have been widely investigated as potential replacements for ITO. Among those candidates, Ag nanowire (AgNW) is considered as one of the most promising materials for flexible transparent electrodes due to its excellent optical transparency, electrical conductivity and mechanical flexibility14,15,16,17,18,19. However, because the rough surface of AgNW coating is likely to cause short circuits in the devices, its surface morphology posed a major challenge to its application in flexible electronic devices. The roughness of the deposited AgNW networks on a flat substrate is intrinsically large; the peak-to-peak roughness is more than twice the diameter of the wires, because of the random arrangement of networks through stacking of the wires20,21,22. Here, we demonstrate a novel and simple method for the fabrication of a ultrasmooth and extremely deformable flexible transparent electrode. The resultant AgNW embedded electrode exhibits a have high transparency and low sheet resistance those are comparable to ITO electrode.
Results
Fabrication of Ag nanowire embedded transparent electrode
The fabrication of the AgNW embedded transparent electrode followed a process schematically illustrated in Fig. 1a. As shown in the Supplementary Fig. S1, AgNW with an average diameter of 35 ± 5 nm and an average length of 25 ± 5 μm were employed in the fabrication. The AgNW dispersion obtained from NANOPYXIS was diluted with deionized water to a concentration of 3 mg/ml. It was then spin-coated on a pre-cleaned rigid substrate such as glass, Si wafer, or plastic, dried and annealed on a hotplate for 5 min at 100 °C to form a conductive AgNW coating. AgNW in the network were uniformly distributed and randomly oriented over the entire coating area. The electrical sheet resistance (Rs) and optical transparency of the AgNW coating depended on the density of AgNW, which was controlled by spin-coating rate (rpm). Lower spin rates resulted in smaller deviations of the AgNW density and better uniformity of the coating (Supplementary Fig. S1), which led to smaller deviations of the Rs values. Further, we used a commercial ultraviolet (UV) curable polymer of Norland Optical Adhesive (NOA) 63 as the transparent substrate. NOA 63 is a clear, colorless and liquid photopolymer, whose polymer cross-linking will occur under exposer to UV light. The solid NOA 63 exhibits excellent optical transparency over a wide spectral range and superior mechanical flexibility; and it is commonly used in nanometer-scale contact printing and imprint lithography, or as a template-stripping photopolymer substrate23,24. The NOA 63 liquid photopolymer was spin-coated on the AgNW films and then cured by a 365 nm UV irradiation at room temperature for 10 min. Following the curing, the resulting AgNW embedded NOA 63 electrode with a thickness of about 100 μm was peeled off and cut into various sample sizes. Cross-sectional transmission electron microscope (TEM) image of an AgNW embedded NOA 63 electrode is shown in Fig. 1b. By employing an elemental mapping technique in TEM, the spatial elemental profile of Ag atom was obtained and the result is presented in Fig. 1b. These results clearly show that the AgNW network is well embedded in the NOA 63 substrate, implying a complete transfer of the nanowires from the original rigid substrate to NOA 63.
The optical transmittance and Rs of AgNW embedded NOA 63 electrode were compared with those of the sputtered ITO film on polyethylene naphthalate (PEN). The transmittance was measured including the substrates. As shown in Fig. 1c, the transmittance of AgNW embedded NOA 63 electrode approaches 82.3% at 550 nm wavelength with Rs value of 16 ± 1.75 Ω/sq, which were comparable to those of commercially available ITO electrodes on PEN (Rs of 15 ± 3.04 Ω/sq with the transmittance of 85.0% at 550 nm). Since most of the AgNW are embedded in the NOA 63 substrate, the low sheet resistance is a strong indication for the infiltration of NOA 63 in the pores of AgNW networks dispersed over the rigid substrate. It also suggest that the electrical contacts between the conductive AgNW networks are intact after formation of NOA 63 substrate through photopolymerization. Moreover, the tightening effect of strong bonding between the NOA 63 matrix and AgNW network allows the improvement of AgNW–AgNW contact, which resulted in a slightly smaller Rs than the original Rs (20 ± 2.87 Ω/sq) of the AgNW layer on rigid substrate. A remarkable difference in the transmittance between the two samples was the excellent optical transparency of AgNW embedded NOA 63 electrode in the UV region as compared with ITO film. The AgNW shows localized surface plasmon resonance bands in the wavelength region around 350 nm25. The AgNW embedded NOA 63 electrode showed 59.5% optical transmittance at 335 nm and its transmittance is almost flat across all the measured wavelength regions. Because the transmission in metal nanowire film is predominantly controlled by the density of the networks, in this case the sparse AgNW networks resulted in unchanged optical transmittance. In contrast, the transmittance of ITO film dropped rapidly at wavelength below 400 nm and displayed fluctuations over the visible light region. In principle, ITO shows high absorption in the UV light region26,27, making it difficult for practical use as a transparent electrode over the entire UV light region. Considering this fact, the great advantage of the AgNW embedded NOA 63 electrode is its broad optical transparency, allowing its use as transparent electrode over the entire UV light region. Figure 1d presents a photograph of AgNW embedded transparent electrode, behind which is the Korea Institute of Materials Science (KIMS) symbol mark being clearly visualized.
Surface properties of AgNW embedded flexible transparent electrode
Figure 2 shows the images of scanning electron microscopy (SEM) and atomic force microscopy (AFM) of the ITO film on PEN substrate (Fig. 2a, d), AgNW coating on PEN substrate (Fig. 2b, e) and AgNW embedded NOA 63 electrode (Fig. 2c, e). The surface roughness of spin-coated AgNW layer on the rigid substrate was significantly larger than that of the commercially available ITO films. A root-mean-square surface roughness (RMS) of 10.676 nm and maximum peak-to-valley (Rpv) range of 79.8 nm were noted for the AgNW layer. The presence of protruding nanowires leads to localized height elevations and this large surface fluctuation induces a higher possibility of electrical short circuits in the devices. It is obvious that, apart from transparency and conductivity, surface roughness is clearly another attribute to affects the compatibility of transparent electrodes with the device. In contrast, the AgNW embedded NOA 63 electrode displays an ultrasmooth surface with a RMS of 0.4 nm and Rpv of 4.557 nm, as can be seen from the high magnification AFM images in Supplementary Fig. S2. This ultrafine surface morphology indicates that the spin-coated NOA 63 liquid photopolymer well permeated the AgNW network, filled the holes in the networks, as well as the voids at the interface between AgNW and the rigid substrate.
Extreme deformation of AgNW embedded flexible transparent electrode
In addition to the excellent transparency and surface morphology, the AgNW embedded NOA 63 electrode possesses superior mechanical flexibility, which is a desirable attribute for the emerging flexible electronic devices. Figure 3a shows a comparison of the changes in the resistance of the electrodes, including ITO film on PEN substrate, AgNW coating on PEN substrate and AgNW embedded NOA 63 electrode, as a function of bending radius. The presented values of the bending-induced compressive and tensile stresses in the films are the averages from ten samples for each type of electrode. The change in the resistance can be expressed as ΔR/R0, where ΔR is the actual change in the resistance after bending and R0 is the initial value. The AgNW coating on PEN showed fairly good mechanical flexibility with small ΔR/R0 value, even when a 2 mm bending radius was applied. In contrast, ITO film on PEN begun to crack when the bending radius approached to 5 mm, resulting in a sharp increase in the ΔR/R0 value. Since ITO is inherently brittle and can crack when exposed to a minute amount of strain. It is noteworthy that the ΔR/R0 value of the AgNW embedded NOA 63 electrode remained nearly constant (<0.25), even though the bending radius was 200 μm, which corresponded to a bending strain (ε) of 0.25%. Here ε = hs/(2R), where hs is the substrate thickness28. The AgNW embedded NOA 63 electrode's electrical properties were more robust to both compressive and tensile stresses (Inset of Fig. 3b) when compared to Ag NWs on PEN. This is attributed to the strong bonding between the NOA 63 matrix and AgNW network, which could prevent the sliding from occurring at the interface under the extreme bending. Moreover, the AgNW embedded NOA 63 electrode showed excellent bending fatigue strength, as shown in Fig. 3b, in respect to a constant bending radius of at 3.3 mm. Even after the bending was repeated for 1000 times, the ΔR/R0 value of AgNW embedded NOA 63 electrode was almost the same as its original value, whereas that of the ITO film on PEN increased dramatically. We also observed minute change in the electrical resistance of the AgNW embedded NOA 63 electrode under the extreme conditions of folding and crumpling (Fig. 3c, Supplementary Fig. S3). Figure 3d shows an AgNW embedded flexible transparent electrode wrapping around a pencil with a radius of 3 mm; and Fig. 3e shows examples of AgNW embedded NOA 63 electrode successfully attached to different materials with uneven surfaces, including a crumpled paper, sharp wooden edge, human skin, stringed textile and rubber products, using a double sided transparent Scotch tape, which enables the conformal contact with various material surfaces and makes the surface conductive without any surface treatment. Due to this excellent mechanical flexibility, the AgNW embedded NOA 63 electrode has a great potential to establish its applications as a transparent electrode platform in the flexible electronic devices.
Thermal oxidation stability and shape memory property
Furthermore, the AgNW coating on PEN and AgNW embedded NOA 63 electrode were placed in an environment of 100°C and 70% RH for 16 days to evaluate its thermal oxidation stability. Figure 4a shows the changes in the resistance after this thermal oxidation stability test. The ΔR/R0 value of AgNW on PEN increased dramatically when it was exposed to a high temperature and high humidity condition. It has been well known that AgNW can be easily oxidized when it is exposed to air. When AgNW is oxidized, the resistance of single nanowire and the junction will increase because of the formation of silver oxide on the surface of AgNW29,30. In contrast, the AgNW embedded NOA 63 electrode exhibited slightly increased ΔR/R0 value because the oxygen gas and moisture cannot permeate the NOA 63 matrix. Here the NOA 63 can act as a passivation layer to the fact that NOA63 is a mercapto ester-type solvent-less photopolymer31, allowing moderate UV curable cross-linking process, which resulted in lower density of statistical defects. A 3 M Scotch tape applied with finger pressure was unable to detach the AgNW from the AgNW embedded NOA 63 electrode (Inset of Fig. 4a) and the resistance of the electrode remained unchanged, thus suggesting strong adhesion.
Additionally, the AgNW embedded NOA 63 electrode showed excellent shape memory property. The electronic device failure as a result of mechanical fracture limits the lifetime and reliability of the devices and leads to an increasing amount of electronic waste. Shape memory polymer has been explored that could help alleviate these problems32,33. The shape memory property of AgNW embedded NOA 63 electrode is exemplarily demonstrated in Fig. 4b and Supplementary Movie S1, where the crumpled sheet rapidly recovered to its original flat shape at 100°C within 10 s. After the recovery, the resistance of the AgNW embedded NOA 63 electrode was measured and was found similar to its original value. The intrinsic mechanism for the shape memory property of polymer is the freezing and activation of the long range motion of polymer chain segments below and above glass transition temperature (Tg), respectively. The deformed electrodes therefore can reversibly relax back to the original shape when heated above Tg without the application of external tension or compression34.
Discussion
Flexible organic solar cells were further fabricated by using the AgNW embedded NOA 63 electrode as described above to make them well suited for use in flexible electronic devices. Figure 4c shows the current density–voltage (J–V) characteristics of the devices as a function of bending radius under simulated AM 1.5 G illumination. The compressive stresses were delivered once every cycle and then the device performances were measured after the device was relaxed to back to planar shape. A blend of poly(4,8-bis-alkyloxybenzo(1,2-b:4,5-b′)dithiophene-2,6-diyl-alt-(alkyl thieno(3,4-b) thiophene-2-carboxylate)-2,6-diyl) (PBDTTT-C) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) was used as the photoactive layer in the devices. The J–V characteristics of the device showed a Fill factor (FF) of 37.87%, a short circuit current density (Jsc) of 10.92 mA/cm2, a open circuit voltage (Voc) of 0.74 V and a power conversion efficiency (PCE) of 3.07%. The J–V characteristics of the devices remained almost the same even after the cell was bent with a radius of 3.3 mm. In addition, the device using the AgNW embedded NOA 63 electrode also exhibited excellent mechanical durability under repeated bending; almost no change in its J–V characteristics even after 1000 bending cycles using a 3.3 mm bending radius (Fig. 4d). In addition, J-V characteristics of the organic solar cells fabricated various bottom electrodes was shown in Supplementary Fig. S5. The device using the AgNW on PEN exhibited a significant shunt leakage current. The large roughness values of AgNW coating on rigid substrates can cause this device shorting. In the case of the device using the ITO electrode, the cell efficiency was higher than that of device using the AgNW embedded NOA 63 electrode. The reason for the slightly lower cell efficiency seen in the latter device was the small decreases in their fill factor (FF) values. The AgNW network contains some empty spaces between the nanowires, which limit the contact area with the top photoactive layer. This prevents the efficient collection of charge carriers by the AgNW network when the diffusion length of the charge carrier is shorter than the average void between the AgNW networks, despite the low sheet resistance. This lateral charge collection issue can be resolved by filling the voids with a conductive buffer layer35.
In summary, we have demonstrated that a flexible transparent electrode with superior mechanical, electrical and optical properties can be fabricated by embedding the AgNW film into the transparent NOA 63 matrix. This technique can produce electrodes with an ultrasmooth and extremely deformable transparent electrode that have sheet resistance and transmittance comparable to those of an ITO electrode. The unique shape memory property allowed the flexible transparent electrode to be formed into various shapes. This deformation was reversible and only induced minimal change to its original conductive property. This electrode is demonstrated to be suitable for the fabrication of flexible organic solar cells. We believe that the technique presented here will offer extended possibility of employing AgNW embedded electrode in the development of various efficient flexible electronic devices.
Methods
Fabrication of AgNW embedded flexible transparent electrode
The AgNW films were fabricated using the spin-coating method and were formed on a pre-cleaned rigid substrate such as glass, Si wafer, or plastic. An as-received dispersion containing AgNW (NANOPYXIS) was spin-coated for 40 s at speeds ranging from 600 to 3000 rpm. The dispersion was well shaken before being used in the spin-coating process. The formed Ag NW films were annealed at 100°C for 5 min on a hotplate. NOA 63 was spin-coated on the AgNW films at 500 rpm and then cured with 365 nm UV irradiation at room temperature for 10 min. After the exposure, the resulting AgNW embedded NOA 63 with a thickness of about 100 μm was peeled off and cut into various sample sizes.
Fabrication of flexible organic solar cell
The ZnO precursor was prepared by dissolving zinc acetate dihydrate (Zn(CH3COO)2·2H2O, Aldrich, 99.9%, 1.64 g) and ethanolamine (NH2CH2CH2OH, Aldrich, 99.5%, 0.5 g) in 2-methoxyethanol (CH3OCH2CH2OH, Aldrich, 99.8%, 10 g) under vigorous stirring at 60°C for 30 min to the hydrolysis reaction in air. The ZnO precursor solution was spin-coated on top of the AgNW embedded NOA 63 electrode. The films were annealed at 150°C for 10 min in air. The ZnO film thickness was approximately 40 nm. The ZnO-coated substrates were transferred into a nitrogen-filled glove box. A solution containing a mixture of PBDTTT-C:PCBM (10 mg:20 mg) was dissoved in 1,2-dichlorobenzene (1 mL). The PBDTTT-C and PCBM used in this study were purchased from 1-material and Nano-C, respectively. The active layer was then spin-coated onto the ZnO-coated AgNW embedded NOA 63 electrode at 1000 rpm for 40 s after passing through a 0.20 μm PTFE syringe filter and the thickness of the active layer was about 100 nm. The PEDOT-PSS (Clevios 4083) diluted using isopropyl alcohol (IPA), with the ratio of PEDOT-PSS:IPA being 1:10, were deposited onto the active layer at 5000 rpm 60 s in a glove box. Finally, the Ag metal as top electrode was deposited through a shadow mask by thermal evaporation in a vacuum of about 5 × 10−6 Torr. The device area, defined through a shadow mask, was 0.38 cm2.
Bending test
To investigate the mechanical stability, an in-house bending test system was designed and applied. The system consists of two contact interface to induce compressive stressed to the sample, where one is fixed and immobile, while the other is allowed to move laterally. Supplementary Fig. S4 shows the procedure followed in the bending tests for the flexible transparent electrode and organic solar cells.
References
Kaltenbrunner, M. et al. An ultra-lightweight design for imperceptible plastic electronics. Nature 499, 458–463 (2013).
Chae, S. H. et al. Transferred wrinkled Al2O3 for highly stretchable and transparent graphene–carbon nanotube transistors. Nature Mater. 12, 403–409 (2013).
Wu, H. et al. A transparent electrode based on a metal nanotrough network. Nature Nanotech. 8, 421–425 (2013).
Kumar, A. & Zhou, C. W. The race to replace tin-doped indium oxide: which material will win? ACS Nano 4, 11–14 (2010).
Leterrier, Y. et al. Mechanical integrity of transparent conductive oxide films for flexible polymer-based displays. Thin Solid Films 460, 156–166 (2004).
Wu, Z. et al. Transparent, conductive carbon nanotube films. Science 305, 1273–1276 (2004).
Niu, C. M. Carbon nanotube transparent conducting films. Mater. Res. Soc. Bull. 36, 766–773 (2011).
Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710 (2009).
Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nature Nanotech. 5, 574–578 (2010).
Vosgueritchian, M., Liporni, D. J. & Bao, Z. Highly conductive and transparent PEDOT:PSS films with a fluorosurfactant for stretchable and flexible transparent electrodes. Adv. Funct. Mater. 22, 421–428 (2012).
Kirchmeyer, S. & Reuter, K. Scientific importance, properties and growing applications of poly(3,4-ethylenedioxythiophene). J. Mater. Chem. 15, 2077–2088 (2005).
Hu, L. B., Wu, H. & Cui, Y. Metal nanogrids, nanowires and nanofibres for transparent electrodes. Mater. Res. Soc. Bull. 36, 760–765 (2011).
Garnett, E. C. et al. Self-limited plasmonic welding of silver nanowire junctions. Nature Mater. 11, 241–249 (2012).
Song, M. et al. Highly Efficient and Bendable Organic Solar Cells with Solution-Processed Silver Nanowire Electrodes. Adv. Funct. Mater. 23, 4177–4184 (2013).
Lee, M. S. et al. High-Performance, Transparent and Stretchable Electrodes Using Graphene–Metal Nanowire Hybrid Structures. Nano Lett. 13, 2814–2821 (2013).
Jin, J. et al. High-performance hybrid plastic films: a robust electrode platform for thin-film optoelectronics. Energy Environ. Sci. 6, 1811–1817 (2013).
Yun, S. et al. Compliant silver nanowire-polymer composite electrodes for bistable large strain actuation. Adv. Mater. 24, 1321–1327 (2012).
Xu, F. & Zhu, Y. Highly Conductive and Stretchable Silver Nanowire Conductors. Adv. Mater. 24, 5117–5122 (2012).
Yu, Z. et al. Highly flexible silver nanowire electrodes for shape-memory polymer light-emitting diodes. Adv. Mater. 23, 664–668 (2011).
Gaynor, W., Burkhard, G. F., McGehee, M. D. & Peumans, P. Smooth Nanowire/Polymer Composite Transparent Electrodes. Adv. Mater. 23, 2905–2910 (2011).
Yu, Z. et al. Silver Nanowire-Polymer Composite Electrodes for Efficient Polymer Solar Cells. Adv. Mater. 23, 4453–4457 (2011).
Zeng, X. Y., Zhang, Q. K., Yu, R. M. & Lu, C. Z. A New Transparent Conductor: Silver Nanowire Film Buried at the Surface of a Transparent Polymer. Adv. Mater. 22, 4484–4488 (2010).
Park, J., Kim, Y. S. & Hammond, P. T. Chemically Nanopatterned Surfaces Using Polyelectrolytes and Ultraviolet-Cured Hard Molds. Nano Lett. 5, 1347–1350 (2005).
Kim, S. H. et al. Simple Route to Hydrophilic Microfluidic Chip Fabrication Using an Ultraviolet (UV)-Cured Polymer. Adv. Funct. Mater. 17, 3493–3498 (2007).
Sun, Y., Yin, Y., Mayers, B. T., Herricks, T. & Xia, Y. Uniform Silver Nanowires Synthesis by Reducing AgNO3 with Ethylene Glycol in the Presence of Seeds and Poly(Vinyl Pyrrolidone). Chem. Mater. 14, 4736–4745 (2002).
Ferry, V. E., Polman, A. & Atwater, H. A. Modeling Light Trapping in Nanostructured Solar Cells. ACS Nano 5, 10055–10064 (2011).
Wu, H. et al. Electrospun Metal Nanofiber Webs as High-Performance Transparent Electrode. Nano Lett. 10, 4242–4248 (2010).
Park, S. I. et al. Theoretical and Experimental Studies of Bending of Inorganic Electronic Materials on Plastic Substrates. Adv. Funct. Mater. 18, 2673–2684 (2008).
Kim, A. et al. Highly Transparent Low Resistance ZnO/Ag Nanowire/ZnO Composite Electrode for Thin Films Solar Cells. ACS Nano 7, 1081–1091 (2013).
Ahn, Y., Jeong, Y. & Lee, Y. Improved Thermal Oxidation Stability of Solution-Processable Silver Nanowire Transparent Electrode by Reduced Graphene Oxide. ACS Appl. Mater. Interfaces 4, 6410–6414 (2012).
Ma, Y. & Sun, J. Humido- and Thermo-Responsive Free-Standing Films Mimicking the Petals of the Morning Glory Flower. Chem. Mater. 21, 898–902 (2009).
Lendlein, A. & Langer, R. Biodegradable, Elastic Shape-Memory Polymers for Potential Biomedical Applications. Science 296, 1673–1676 (2002).
Mohr, R. et al. Initiation of shape-memory effect by inductive heating of magnetic nanoparticles in thermoplastic polymers. Proc. Natl. Acad. Sci. USA 103, 3540–3545 (2006).
Meng, H. & Li, G. A review of stimuli-responsive shape memory polymer composites. Polymer 54, 2199–2221 (2013).
Leem, D. S. et al. Efficient Organic Solar Cells with Solution-Processed Silver Nanowire Electrodes. Adv. Mater. 23, 4371–4375 (2011).
Acknowledgements
This research was supported by the Pioneer Research Center Program (2013M3C1A3065525) through the National Research Foundation of Korea funded by the Ministry of Science, ICT & Future Planning.
Author information
Authors and Affiliations
Contributions
C.S.K., D.H.K. and S.J. conceived and designed the research. S.N., M.S., B.C., H.M.L., J.D.K., S.G.P., K.S.N., Y.J., S.H.J. and J.W.K. participated in materials preparation, device fabrication and data interpretation. S.H.K. and Y.C.P. carried out the TEM measurements. C.S.K., D.H.K. and S.J. wrote the paper. C.S.K. supervised the project. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
Supplementary information
Supplementary Information
Supplementary Movie S1
Rights and permissions
This work is licensed under a Creative Commons Attribution 3.0 Unported License. The images in this article are included in the article's Creative Commons license, unless indicated otherwise in the image credit; if the image is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the image. To view a copy of this license, visit http://creativecommons.org/licenses/by/3.0/
About this article
Cite this article
Nam, S., Song, M., Kim, DH. et al. Ultrasmooth, extremely deformable and shape recoverable Ag nanowire embedded transparent electrode. Sci Rep 4, 4788 (2014). https://doi.org/10.1038/srep04788
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep04788
This article is cited by
-
In/MgSe Terahertz Filters with Enhanced Optical Conduction and Light Absorption
Journal of Electronic Materials (2023)
-
Stearic acid-treated CNT/AgNW membrane for passive anti-icing, active deicing, and water drops monitoring
Journal of Materials Science: Materials in Electronics (2022)
-
Research on flexible silver nanowire electrode for organic light-emitting devices
Optoelectronics Letters (2021)
-
Optimal Design of PEDOT:PSS Polymer-Based Silver Nanowire Electrodes for Realization of Flexible Polymer Solar Cells
Macromolecular Research (2021)
-
High-performance Ag nanowires/PEDOT:PSS composite electrodes for PVDF-HFP piezoelectric nanogenerators
Journal of Materials Science: Materials in Electronics (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.