Abstract
The corrosion products on steels exposed at two sites in Campeche, México and one site at Kure Beach, USA, have been investigated to determine the extent to which different marine conditions and exposure times control the oxide formation. The corroded coupons were analyzed by Mössbauer, Raman and infrared spectroscopy as well as X‐ray diffraction, in order to completely identify the oxides and map their location in the corrosion coating. The coating compositions were determined by Mössbauer spectroscopy using a new parameter, the relative recoilless fraction (F-value) which gives the atomic fraction of iron in each oxide phase from the Mössbauer sub‐spectral areas. For short exposure times, less than three months, an amorphous oxyhydroxide was detected after which a predominance of lepidocrocite (γ-FeOOH), and akaganeite (β-FeOOH) were observed in the corrosion coatings with the fraction of the later phase increasing at sites with higher atmospheric chloride concentrations. The analysis also showed that small clusters of magnetite (Fe3O4), and maghemite (γ(Fe2O3), were seen in the micro-Raman spectra but were not always identified by Mössbauer spectroscopy. For longer exposure times, goethite (α-FeOOH), was also identified but little or no β-FeOOH was observed. It was determined by the Raman analysis that the corrosion products generally consisted of inner and outer layers. The protective layer, which acted as a barrier to slow further corrosion, consisted of the α-FeOOH and nano-sized γ-Fe2O3 phases and corresponded to the inner layer close to the steel substrate. The outer layer was formed from high γ-FeOOH and low α-FeOOH concentrations.
Similar content being viewed by others
References
J.J. Carpio and O. Ricon Tricone, in: Proc. 2nd NACE Latin American Corrosion Congress, Rio de Janeiro, 1996 (Nace International, Houston, TX) paper #343.
L. Martinez Gomez and J.J. Carpio Perez, in: Proc. 2nd NACE Latin American Corrosion Congress, Rio de Janeiro, 1996 (NACE International, Houston, TX).
S.J. Oh, D.C. Cook and H.E. Townsend, in: Proc. Int. Conf. on the Application of the Mössbauer Effect, Rio de Janeiro, 1997, Hyperfine Interactions C (1998).
J.J. Carpio, J. Reyes, J. Salazar, A. Parra and L. Martinez, in: Proc. 2nd NACE Latin American Region Corrosion Congress, Rio de Janeiro, 1996 (NACE International, Houston, TX).
J.J. Carpio, J. Reyes, G. Hernandez-Duque and L. Martinez, in: Proc. Corrosion '95, 1995 (NACE International, Houston, TX) paper #238.
M. Yamashita, H. Nagano, T. Misawa and H.E. Townsend, in: Proc. 13th Int. Corrosion Congress, Melbourne, 1996, Vol. 1 (Australasian Corrosion Association, Victoria) p. 037/1.
Corrosion of Metals and Alloys †Corrosivity of Atmospheres †Classification, Standard 9223-92, International Standards Organization (1992).
Corrosion of Metals and Alloys †Corrosivity of Atmospheres †Guiding Values for Corrosivity Categories, Standard 9224-92, International Standards Organization (1992).
S.J. Oh, D.C. Cook and H.E. Townsend, Hyp. Interact. 112 (1998) 59.
E. De Grave and A. Van Alboom, Phys. Chem. Miner. 18 (1991) 337.
C.R. Shastry, J.J. Friel and H.E. Townsend, in: Degradation of Materials in the Atmosphere, ASTM STP 965, eds. S.W. Dean and T.S. Lee (ASTM, Philadelphia, PA, 1988) p. 5.
K. Knese, P. Wartewig, C. Michalk and S. Fischer, Hyp. Interact. 94 (1994) 1999.
Rights and permissions
About this article
Cite this article
Cook, D., Van Orden, A., Carpio, J. et al. Atmospheric corrosion in the Gulf of México. Hyperfine Interactions 113, 319–329 (1998). https://doi.org/10.1023/A:1012688003125
Issue Date:
DOI: https://doi.org/10.1023/A:1012688003125