Abstract
The limitation and experimental CO2 sequestration degree of steel slag is the focus. The theoretical and the practical CO2 sequestration degree was assessed under mild operating conditions. After calculation in theory, it can be found that the CO2 sequestration limitation degree for every kilogram steel slag is about 442 g when taking magnesium into consideration, and the experimental CO2 sequestration degree for every kilogram slag is about 77 g, under the conditions that the liquid to solid ratio is 50 L/kg, CO2 flow is 0.5 L/min and the temperature of reaction is the ambient temperature. When solution NH6Cl and CH3COOH for experiments and other conditions keep the same, the actual potential CO2 sequestration for every kilogram slag is 69.3 g and 31.20 g respectively. Thus, optimization of process parameters like granularity of slag is necessary to enhance the carbon dioxide sequestration degree for steel slag.
Similar content being viewed by others
References
Tatsuro Ariyama, Michitaka Sato. Optimization of Ironmaking Process for Reducing CO2 Emissions in the Integrated Steel Works [J]. ISIJ International, 2006, 46(12): 1736.
Kato Yukitaka. Carbon Recycling for Reduction of Carbon Dioxide Emission From Ironmaking Process [J]. ISIJ International, 2010, 50(1): 181.
Cao Yi, Rong Zhu, Bo-yu Chen, et al. Experimental Research on Reducing the Dust of BOF in CO2 and O2 Mixed Blowing Steelmaking Process [J]. ISIJ International 2009, 49(11): 1694.
JIN Ren-jie, ZHU Rong, FEN Li-xin, et al. Experimental Study of Steelmaking With CO2 and O2 Mixed Blowing [J]. Journal of University of Science and Technology Beijing, 2007, 29(Supplement 1): 78 (in Chinese).
Sebastian Teir, Sanni Eloneva, Carl-Johan Fogelholm, et al. Dissolution of Steelmaking Slags in Acetic Acid for Precipitated Calcium Carbonate Production [J]. Energy, 2007, 32: 528.
Sanni Eloneva, Sebastian Teir, Carl-Johan Fogelholm, et al. Fixation of CO2 by Carbonating Calcium Derived From Blast Furnace Slag [J]. Energy, 2008, 33: 1461.
Lekakh S N, Robertson D G C, Rawlins C H, et al. Investigation of a Two-Stage Aqueous Reactor Design for Carbon Dioxide Sequestration Using Steelmaking Slag [J]. Metallurgical and Materials Transaction, 2008, 39B(3): 484.
Takeshi Yoshikawa, Shota Hirano, Nobumitsu Hirai, et al. Preparation of Porous Ceramics by the Hydrothermal Reaction of Blast Furnace Slag for Use in a Water-Retentive Material [J]. ISIJ International 2008, 48(9): 1322.
YE Guo-hua, TONG Xiong, LU Lu. Pretreatment for V-Bearing Steelmaking Slag by Beneficiation Methods and Its Effect on Followed Leaching Procedure [J]. The Chinese Journal of Nonferrous Metals, 2010, 20(11): 2233 (in Chinese).
LIU Ying-jin, SONG Bo, MAO Jing-hong, et al. Experimental Research on Ca Leaching From Steelmaking Slag [J]. Journal of the Chinese Rare Earth Society, 2008, 26 (Supplement 1): 94 (in Chinese).
Huijgen W J J, Witkamp G J, Comans R N J. Mineral CO2 Sequestration by Steel Slag Carbonation [J]. Environ Sci Technol, 2005, 39: 9676.
Huijgen W J J, Comans R N J. Mineral by Carbonation of Steel Slag for CO2 Sequestration: Leaching of Productions and Reaction Mechanisms [J]. Environ Sci Technol, 2006, 40: 2790.
Johnson D C, Macleod C L, Hills C D. Solidification of Stainless Steel Slag by Accelerated Carbonation [J]. Environ Sci Technol, 2003, 24: 671.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Key Technology Research and Development Program in 11th Five-Year Plan of China (2006BAE03A07)
Rights and permissions
About this article
Cite this article
Li, Jl., Zhang, Hn., Xu, Aj. et al. Theoretical and Experimental on Carbon Dioxide Sequestration Degree of Steel Slag. J. Iron Steel Res. Int. 19, 29–32 (2012). https://doi.org/10.1016/S1006-706X(13)60028-X
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(13)60028-X